The luminescent properties of CaYBO4:Ln(Ln=Eu, Tb) under UV-VUV range

The luminescent properties of CaYBO₄:Ln(Ln=Eu³⁺, Tb³⁺) were investigated under ultraviolet (UV) and vacuum ultraviolet (VUV) region. The CT band of Eu³⁺ at about 245 nm blue-shifted to 230 nm in VUV excitation spectrum; the band with the maximum at 183 nm was considered as the host lattice absorption. For the sample of CaYBO₄:0.08Tb³⁺, the bands at about 235 and 263 nm were assigned to the f-d transitions of Tb³⁺ and the CT band of Tb³⁺ was calculated according to Jφrgensen's theory. Under UV and VUV excitation, the main emission of Eu³⁺ corresponding to the ⁵D₀-⁷F₂ transition located at about 610 nm and two intense emission of Tb³⁺ from the ⁵D₄-⁷F₅ transition had been observed at about 542 and 552 nm, respectively. With the incorporation of Gd³⁺ into the host lattice of CaYBO₄, the luminescence of Tb³⁺ was enhanced while that of Eu³⁺ was decreased because of their different excitation mechanism.     

KBaPO4:Ln (Ln=Eu, Tb, Sm) phosphors for UV excitable white light-emitting diodes

This letter reports the novel three emission bands based on phosphate host matrix, KBaPO₄ doped with Eu²⁺, Tb³⁺, and Sm³⁺ for white light-emitting diodes (LEDs). The phosphors were synthesized by solid-state reaction and thermal stability was elucidated by measuring photoluminescence at higher temperatures. Eu²⁺-doped KBaPO₄ phosphor emits blue luminescence with a peak wavelength at 420 nm under maximum near-ultraviolet excitation of 360 nm. Tb³⁺-doped KBaPO₄ phosphor emits green luminescence with a peak wavelength at 540 nm under maximum near-ultraviolet excitation of 370 nm. Sm³⁺-doped KBaPO₄ phosphor emits orange-red luminescence with a peak wavelength at 594 nm under maximum near-ultraviolet excitation of 400 nm. The thermal stabilities of KBaPO₄:Ln (Ln=Eu²⁺, Tb³⁺, Sm³⁺), in comparison to commercially available YAG:Ce³⁺ phosphor were found to be higher in a wide temperature range of 25-300 °C.     

Observation of green emission from Ce-doped gadolinium oxide nanoparticles

Green emission at around 500 nm is observed in Gd₂O₃:Ce³⁺ nanoparticles and the intensity is highly dependent on the concentration of Ce³⁺ in the nanoparticles. The luminescence of this emission displays both picosecond (ps) and millisecond (ms) lifetimes. The ms lifetime is over four orders of magnitude longer than typical luminescence lifetimes (10-40 ns) of Ce³⁺ in traditional Ce³⁺ doped phosphors and therefore likely originates from defect states. The picosecond lifetime is shorter than the typical Ce³⁺ value and is also likely due to defect or surface states. When the samples are annealed at 700 °C, this emission disappears possibly due to changes in the defect moieties or concentration. In addition, a blue emission at around 430 nm is observed in freshly prepared Gd₂O₃ undoped nanoparticles, which is attributed to the stabilizer, polyethylene glycol biscarboxymethyl ether. On aging, the undoped particles show similar emission to the doped particles with similar luminescence lifetimes. When Eu³⁺ ions are co-doped in Gd₂O₃:Ce nanoparticles, both the green emission and the emission at 612 nm from Eu³⁺ are observed.     

Synthesis and luminescence properties of Eu, Ce and Tb-activated Sr3La2(BO3)4 under UV excitation

The spectroscopic properties in UV-excitable range for the phosphors of Sr₃La₂(BO₃)₄:RE³⁺ (RE³⁺=Eu³⁺, Ce³⁺, Tb³⁺) were investigated. The phosphors were synthesized by conventional solid-state reactions. The photoluminescence (PL) spectra and commission international de I'Eclairage (CIE) coordinates of Sr₃La₂(BO₃)₄:RE³⁺ were investigated. The f-d transitions of Eu³⁺, Ce³⁺ and Tb³⁺ in the host lattices are assumed and corroborated. The PL and PL excitation (PLE) spectra indicate that the main emission wavelength of Sr₃La₂(BO₃)₄:Eu³⁺ is 611 nm, and Sr₃La₂(BO₃)₄:Ce³⁺ shows dominating emission peak at 425 nm, while Sr₃La₂(BO₃)₄:Tb³⁺ displays green emission at 487, 542, 582 and 620 nm. These phosphors were prepared by simple solid-state reaction at 1000 °C. There are lower reactive temperature and more convenient than commercial phosphors. The Sr₃La₂(BO₃)₄:Tb³⁺ applied to cold cathode fluorescent lamp was found to emit green light and have a major peak wavelength at around 542 nm. These phosphors may provide a new kind of luminescent materials under ultraviolet excitation.     

Energy transfer from benzoic acid to lanthanide ions in benzoic acid-functionalized lanthanide-doped CaF2 nanoparticles

The preparation of benzoic acid-functionalized CaF₂:Ln³⁺ (Ln = Eu or Tb) nanoparticles and their sensitized luminescence are described in this report. First, to achieve sufficient proof for energy transfer from benzoic acid (BA) to lanthanide ions doped in nanoparticles, we employ Eu³⁺ as the microscopic probe and investigate the luminescent spectra of benzoic acid-functionalized CaF₂:Eu³⁺ (BA-CaF₂:Eu³⁺) nanoparticles. Next, to further reveal the difference between sensitized luminescence and common luminescence for Eu³⁺ doped in CaF₂ nanoparticles, we study the emission spectra of BA-CaF₂:Eu³⁺ nanoparticles excited at 286 nm and 397 nm, respectively. Finally, we analyze and compare the luminescent spectra of BA-CaF₂:Tb³⁺ and CaF₂:Ce³⁺, Tb³⁺ nanoparticles in detail. Our results indicate that both Eu³⁺ and Tb³⁺ doped in CaF₂ nanoparticles can be efficiently sensitized through benzoic acid.     

Synthesis and luminescence investigation of RE (Eu, Tb and Ce)-doped lithium silicate (Li2SiO3)

Synthesis and photoluminescence (PL) investigations of lithium metasilicate doped with Eu³⁺, Tb³⁺ and Ce³⁺ were carried out. PL spectra of Eu-doped sample showed peaks corresponding to the ⁵D₀→⁷F_j (j=1, 2, 3 and 4) transitions under ultraviolet excitation. Strong red emission coming from the hypersensitive ⁵D₀→⁷F₂ transition of Eu³⁺ ion suggested the presence of the dopant ion in structurally disordered environment. Tb³⁺-doped silicate sample showed blue-green emission corresponding to the ⁵D₄→⁷F_j (j=6, 5 and 4) transitions. Ce-doped sample under excitation from UV, showed a broad emission band in the region 350-370 nm with shoulders around 410 nm. The fluorescence lifetimes of Eu³⁺ and Tb³⁺ ions were found out to be 790 and 600 μs, respectively. For Ce³⁺, the lifetime was of the order of 45 ns. PL spectra of the europium- and terbium-doped samples were compared with commercial red (Y₂O₃:Eu³⁺) and green (LaPO₄:Tb³⁺) phosphors, respectively. It was found that the emission from the doped silicate sample was 37% of the commercial phosphor in case of the Tb-doped sample and 8% of the commercial phosphor in case of the Eu-doped sample.     

A white light emitting phosphor Sr1.5Ca0.5SiO4:Eu, Tb, Eu for LED-based near-UV chip: Preparation, characterization and luminescent mechanism

In this work, we report preparation, characterization and luminescent mechanism of a phosphor Sr_1.5Ca_0.5SiO₄:Eu³⁺,Tb³⁺,Eu²⁺ (SCS:ETE) for white-light emitting diode (W-LED)-based near-UV chip. Co-doped rare earth cations Eu³⁺, Tb³⁺ and Eu²⁺ as aggregated luminescent centers within the orthosilicate host in a controlled manner resulted in the white-light phosphors with tunable emission properties. Under the excitation of near-UV light (394 nm), the emission spectra of these phosphors exhibited three emission bands: one broad band in the blue area, a second band with sharp lines peaked in green (about 548 nm) and the third band in the orange-red region (588-720 nm). These bands originated from Eu²⁺ 5d→4f, Tb³⁺⁵D₄→⁷F_J and Eu³⁺⁵D₀→⁷F_J transitions, respectively, with comparable intensities, which in return resulted in white light emission. With anincrease of Tb³⁺ content, both broad Eu²⁺ emission and sharp Eu³⁺ emission increase. The former may be understood by the reduction mechanism due to the charge transfer process from Eu³⁺ to Tb³⁺, whereas the latter is attributed to the energy transfer process from Eu²⁺ to Tb³⁺. Tunable white-light emission resulted from the system of SCS:ETE as a result of the competition between these two processes when the Tb³⁺ concentration varies. It was found that the nominal composition Sr_1.5Ca_0.5SiO₄:1.0%Eu³⁺, 0.07%Tb³⁺ is the optimal composition for single-phased white-light phosphor. The CIE chromaticity calculation demonstrated its potential as white LED-based near-UV chip.     

Luminescence studies on lanthanide ions (Eu, Dy and Tb) doped YAG:Ce nano-phosphors

Yttrium aluminum garnet nanoparticles both undoped and doped with lanthanide ions (Ce³⁺, Eu³⁺, Dy³⁺ and Tb³⁺) having average size around 30 (±3 nm) nm were prepared by glycine nitrate combustion method followed by annealing at a relatively low temperature of 800 °C. Increase in the annealing temperature has been found to improve the luminescence intensity and for 1200 °C heated samples there exists strong energy transfer from Tb³⁺ to Ce³⁺ ions in YAG:Ce(2%),Tb(2%) nanoparticles as revealed by luminescence studies. Co-doping the YAG:Ce nanoparticles with Eu³⁺ results in significant decrease in the emission intensity of both Ce³⁺ and Eu³⁺ ions and this has been attributed to the oxidation of Ce³⁺ to Ce⁴⁺ and reduction of Eu³⁺ to Eu²⁺ ions. Dy³⁺ co-doping did not have any effect on the Ce³⁺ emission as there is no energy transfer between Dy³⁺ and Ce³⁺ ions.     

Low-voltage cathodoluminescence property of Li-doped Gd2−xYxO3:Eu

Cathodoluminescent (CL) spectra of Li-doped Gd_2−xY_xO₃:Eu³⁺ solid-solution (0.0?x?0.8) were investigated at low voltages (300 V-1 kV). The CL intensity is maximum for the composition of x=0.2 and gradually reduces with increasing the amount of substituted Y content. In particular, small (∼100 nm) particles of Li-doped Gd_1.8Y_0.2O₃:Eu³⁺ are obtained by firing the citrate precursors at only 650°C for 18 h. Relative red-emission intensity at 300 V of this phosphor is close to 180% in comparison with that of commercial red phosphor Y₂O₃:Eu³⁺. An increase of firing temperature to 900°C results in 400-600 nm sized spherical particles. At low voltages (300-800 V), the CL emission of 100 nm sized particles is much stronger than that of 400-600 nm sized ones. In contrast, the larger particles exhibit the higher CL emission intensity at high voltages (1-10 kV). Taking into consideration small spherical morphology and effective CL emission, Li-doped Gd_1.8Y_0.2O₃:Eu³⁺ appears to be an efficient phosphor material for low voltage field emission display.     

Photoluminescence investigations of Zn2SiO4 co-doped with Eu and Tb ions

Zinc silicate phosphors co-doped with Eu³⁺ ions and also with both Eu³⁺ and Tb³⁺ ions were prepared by high temperature solid state reaction in air or reducing atmosphere. The luminescence characteristics of the prepared phosphors were investigated. While in the samples prepared in air, Eu³⁺ emission was found to be dominant over Tb³⁺ emission, in the samples prepared in reducing atmosphere, intense Eu²⁺ emission at 448 nm was found to be predominant over narrow Tb³⁺ emission. Luminescence studies showed that Eu³⁺ ions occupy asymmetric sites in Zn₂SiO₄ lattice. The intense f-f absorption peak of Eu³⁺ at 395 nm observed in these phosphors suggests their potential as red emitting phosphors for near ultra-violet light emitting diodes.     

Photoluminescence properties of Sr(Y, Gd)2O4:Euunder VUV excitation

Vacuum ultraviolet (VUV) excitation and photoluminescence (PL) properties of Sr(Y, Gd)₂O₄ doped with Eu³⁺ were studied. The excitation spectra of SrY_1.9Eu_0.1O₄ and SrY_1.0Gd_0.9Eu_0.1O₄ had absorption in the VUV region with the absorption band edge at 149 nm, while the absorption of SrGd_1.9Eu_0.1O₄ in the VUV region was weak, which could be due to the narrow host band gap and no efficient energy transfer occurred in the VUV region. The PL spectra of all samples exhibited the characteristic emission of Eu³⁺ with the red ⁵D₀-⁷F₂ transition (611 nm) being the most prominent group.     

VUV-UV excited luminescent properties of LnCa4O(BO3)3:RE (Ln=Y, La, Gd; Re=Eu, Tb, Dy, Ce)

Calcium lanthanide oxyborate doped with rare-earth ions LnCa₄O(BO₃)₃:RE³⁺ (LnCOB:RE, Ln=Y, La, Gd, RE=Eu, Tb, Dy, Ce) was synthesized by the method of solid-state reaction at high temperature. Their fluorescent spectra were measured from vacuum ultraviolet (VUV) to visible region at room temperature. Their excitation spectra all have a broadband center at about 188 nm, which is ascribed to host absorption. Using Dorenbos’ and Jφrgensen's work [P. Dorenbos, J. Lumin. 91 (2000) 91, R. Resfeld, C.K. Jφrgensen, Lasers and Excite States of Rare Earth [M], Springer, Berlin, 1977, p. 45], the position of the lowest 5d levels E(Ln,A) and charge transfer band E_ct were calculated and compared with their excitation spectra.Eu³⁺ and Tb³⁺ ions doped into LnCOB show efficient luminescence under VUV and UV irradiation. In this system, Ce³⁺ ions do not show efficient luminescence and quench the luminescence of Tb³⁺ ions when Tb³⁺ and Ce³⁺ ions are co-doped into LnCOB. GdCOB doped with Dy³⁺ shows yellowish white light under irradiation of 254 nm light for the reason that Gd³⁺ ions transfer the energy from itself to Dy³⁺. Because of the existence of Gd³⁺, the samples of GdCOB:RE³⁺ show higher excitation efficiency than LaCOB:RE³⁺ and YCOB:RE³⁺, around 188 nm, which indicates that the Gd³⁺ ions have an effect on the host absorption and can transfer the excitation energy to the luminescent center such as Tb³⁺, Dy³⁺ and Eu³⁺.     

Luminescent properties of (Y,Gd)BO3:Bi,RE (RE=Eu, Tb) phosphor under VUV/UV excitation

Bi³⁺- and RE³⁺-co-doped (Y,Gd)BO₃ phosphors were prepared and their luminescent properties under vacuum ultraviolet (VUV)/UV excitation were investigated. Strong red emission for (Y,Gd)BO₃:Bi³⁺,Eu³⁺ and strong green emission for (Y,Gd)BO₃:Bi³⁺,Tb³⁺ are observed under VUV excitation from 147 to 200 nm with a much broader excitation region than that of single Eu³⁺-doped or Tb³⁺-doped (Y,Gd)BO₃ phosphor. Strong emissions are also observed under UV excitation around 265 nm where as nearly no luminescence is observed for single Eu³⁺-doped or Tb³⁺-doped (Y,Gd)BO₃. The luminescence enhancement of Bi³⁺- and RE³⁺-co-doped (Y,Gd)BO₃ phosphors is due to energy transfer from Bi³⁺ ion to Eu³⁺ or Tb³⁺ ion not only in the VUV region but also in the UV region. Besides, host sensitization competition between Bi³⁺ and Eu³⁺ or Tb³⁺ is also observed. The investigated phosphors may be preferable for devices with a VUV light 147-200 nm as an excitation source such as PDP or mercury-free fluorescent lamp.     

Synthesis and luminescent properties of nanoparticles GdCaAl3O7:RE (RE=Eu, Tb) via the sol-gel method

By using metal nitrates as starting materials and citric acid as complexing agent, GdCaAl₃O₇:Eu³⁺ and GdCaAl₃O₇:Tb³⁺ powder phosphors were prepared by a citrate-gel method. Thermal analysis (TG-DTG), X-ray diffraction (XRD), transmission electron microscope (TEM) and scanning electron microscope (SEM), photoluminescence excitation and emission, as well as kinetic decays were employed to characterize the resulting samples. The results of the XRD indicated the precursor samples began to crystallize at 800 °C and the crystallinity increased with elevation the annealing temperature. TEM images showed that the phosphor particles were basically of spherical shape, with good dispersion about a particle size of around 40-70 nm. Upon excitation with UV irradiation, it is shown that there is a strong emission at around 617 nm corresponding to the forced electric dipole ⁵D₀-⁷F₂ transition of Eu³⁺, and at around 543 nm corresponding to the ⁵D₄-⁷F₅ transition of Tb³⁺. The dependence of photoluminescence intensity on Eu³⁺ (or Tb³⁺) concentration and annealing temperature were also studied in detail.     

Sol-gel preparation and photoluminescence property of YBO3:Eu/Tb nanocrystalline thin films

YBO₃:Eu³⁺/Tb³⁺ nanocrystalline thin films were successfully deposited onto quartz glass substrates by Pechini sol-gel dip-coating method, using rare-earth nitrates and boric acid as starting materials. The crystal structure, morphology, chemical composition and photoluminescence property of the films were investigated by X-ray diffraction (XRD), atomic force microscopy (AFM), X-ray photoelectron spectroscopy (XPS), Fourier transform infrared (FTIR) spectroscopy and fluorescence spectrophotometer. The results of XRD, AFM, XPS and FTIR revealed that the films were composed of spherical YBO₃:Eu³⁺/Tb³⁺ nanocrystals with average grain size of 80 nm. The YBO₃:Eu³⁺ film exhibited strong orange emission at 595 nm and red emission at 615 nm, which were, respectively ascribed to the (⁵D₀→⁷F₁) and (⁵D₀→⁷F₂) transitions of Eu³⁺. The YBO₃:Tb³⁺ film showed dominant green emission at 545 nm due to the ⁵D₄-⁷F₅ transition of Tb³⁺.     

Sol-gel growth of Gd2MoO6:Eu nanocrystalline layers on SiO2 spheres (SiO2@Gd2MoO6:Eu) and their luminescent properties

SiO₂@Gd₂MoO₆:Eu³⁺ core-shell phosphors were prepared by the sol-gel process. X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), field emission scanning electron microscopy (FESEM), energy-dispersive X-ray spectra (EDS), transmission electron microscopy (TEM), photoluminescence (PL) spectra as well as kinetic decays were used to characterize the resulting SiO₂@Gd₂MoO₆:Eu³⁺ core-shell phosphors. The XRD results demonstrate that the Gd₂MoO₆:Eu³⁺ layers on the SiO₂ spheres begin to crystallize after annealing at 600 °C and the crystallinity increases with raising the annealing temperature. The obtained core-shell phosphors have a near perfect spherical shape with narrow size distribution (average size ca. 600 nm), are not agglomerated, and have a smooth surface. The thickness of the Gd₂MoO₆:Eu³⁺ shells on the SiO₂ cores could be easily tailored by varying the number of deposition cycles (50 nm for four deposition cycles). The Eu³⁺ shows a strong PL luminescence (dominated by ⁵D₀-⁷F₂ red emission at 613 nm) under the excitation of 307 nm UV light. The PL intensity of Eu³⁺ increases with increasing the annealing temperature and the number of coating cycles.     

Synthesis of Gd2Ti2O7:Eu, V phosphors by sol-gel process and its luminescent properties

A red-emitting phosphor material, Gd₂Ti₂O₇:Eu³⁺, V⁴⁺, by added vanadium ions is synthesized using the sol-gel method. Phosphor characterization by high-resolution transmission electron microscopy shows that the phosphor possesses a good crystalline structure, while scanning electron microscopy reveals a uniform phosphor particle size in the range of 230-270 nm. X-ray photon electron spectrum analysis demonstrates that the V⁴⁺ ion promotes an electron dipole transition of Gd₂Ti₂O₇:Eu³⁺ phosphors, causing a new red-emitting phenomenon, and CIE value shifts to x=0.63, y=0.34 (a purer red region) from x=0.57, y=0.33 (CIE of Gd₂Ti₂O₇:Eu³⁺). The optimal composition of the novel red-emitting phosphor is about 26% of V⁴⁺ ions while the material is calcinated at 800  °C. The results of electroluminescent property of the material by field emission experiment by CNT-contained cathode agreed well with that of photoluminescent analysis.     

Enhanced luminescent properties of Y3Al5O12:Tb,Ce phosphor prepared by spray pyrolysis

Yttrium aluminum garnet (YAG) particles doped with Tb³⁺ or double doped with Tb³⁺ and Ce³⁺ were prepared by spray pyrolysis and characterized by photo- and cathode-luminescence. It was tried to incorporate a broad band of Ce³⁺ activator into the line peaks of Tb³⁺ in YAG host without the reduction of emission intensity. Ce-codoped YAG:Tb particles showed a broad band emission due to the d-f transition of Ce³⁺ and a reduction in the intensity of emission peaks due to ⁵D₃-⁷F_j (j=3, 4, 5, 6) transition of Tb³⁺ when they were excited by the ultraviolet light of 270 nm. These results supported that an effective energy transfer occurs from Tb³⁺ to Ce³⁺ in YAG host. Codoping Ce³⁺ ions greatly intensified the excitation peak at 270 nm for the emission at 540 nm of Tb³⁺, which means that more lattice defects, involving in the energy absorption and transfer to Tb³⁺, are formed by the Ce³⁺ codoping. The finding gives a promising approach for enhancing the luminescence efficiency.     

Eu/Tb ions co-doped white light luminescence Y2O3 phosphors

Y₂O₃:Eu³⁺, Tb³⁺ phosphors with white emission are prepared with different doping concentration of Eu³⁺ and Tb³⁺ ions and synthesizing temperatures from 750 to 950 °C by the co-precipitation method. The resulted phosphors were characterized by X-ray diffraction (XRD) and photoluminescence (PL) spectroscopy. The results of XRD indicate that the crystallinity of the synthesized samples increases with enhancing the firing temperature. The photoluminescence spectra indicate the Eu³⁺ and Tb³⁺ co-doped Y₂O₃ phosphors show five main emission peaks: three at 590, 611 and 629 nm originate from Eu³⁺ and two at 481 and 541 nm originate from Tb³⁺, under excitation of 250-320 nm irradition. The white light luminescence color could be changed by varying the excitation wavelength. Different concentrations of Eu³⁺ and Tb³⁺ ions were induced into the Y₂O₃ lattice and the energy transfer from Tb³⁺→Eu³⁺ ions in these phosphors was found. The Commission International de l’Eclairage (CIE) chromaticity shows that the Y₂O₃:Eu³⁺, Tb³⁺ phosphors can obtain an intense white emission.     

Luminescent properties of RE-activated CaAl2B2O7 (RE=Tb, Ce) in VUV-visible region

RE³⁺-activated α- and β-CaAl₂B₂O₇ (RE=Tb, Ce) were synthesized with the method of high-temperature solid-state reaction. Their VUV excitation and VUV-excited emission spectra are measured and discussed in the present article. The charge transfer band of Tb³⁺ and Ce³⁺ is respectively calculated to be at 151±2 and 159±3 nm. All the samples show an activator-independent excitation peak at about 175 nm and an emission peak at 350-360 nm ascribed to the host absorption and emission band, respectively.