A simple and controlled method of preparing uniform Ag midnanoparticles on Tollens-soaked silica spheres

Ag midnanoparticles (midnanoparticles are those particles whose diameters are in the range from 20 to 80 nm) with average size of 30-50 nm and tunable packing densities were formed on the surface of preformed Tollens-soaked silica spheres by a simple and controlled method. The process mainly involved two steps. In the first step the absorption of Ag(NH3)2(+) ions occurred on the silica spheres and in the second step Ag(NH3)2(+) ions on the silica spheres were reduced to Ag midnanoparticles in the presence of glucose solution. The amount of Ag midnanoparticles on the silica spheres could easily be tuned by varying the washing times in the process of preparing the Tollens-soaked silica spheres. The washing process also effectively avoided the reduction of Ag(NH3)2(+) ions and the nucleation of Ag particles in solution and easily produced more uniform Ag midnanoparticles on the silica spheres. Attributing to the uniform Ag midnanoparticles, the Ag midnanoparticle-coated silica spheres show unique optical properties in the UV-vis absorption spectra. The resulting Ag midnanoparticle-coated silica spheres were characterized with transmission electron microscopy, UV-vis-IR recording spectrophotometry, and X-ray photoelectron spectroscopy.     

New preparation method of gold nanoparticles on SiO2

It is shown that adsorption of the [Au(en)(2)](3+) cationic complex can be successfully employed for the deposition of gold nanoparticles (1.5 to 3 nm) onto SiO(2) with high metal loading, good dispersion, and small Au particle size. When the solution pH increases (from 3.8 to 10.5), the Au loading in the Au/SiO(2) samples increases proportionally (from 0.2 to 5.5 wt %), and the average gold particle size also increases (from 1.5 to 2.4 nm). These effects are explained by the increase in the amount of negatively charged sites present on the SiO(2) surface, namely, when the solution pH increases, a higher number of [Au(en)(2)](3+) species can be adsorbed. Extending the adsorption time from 2 to 16 h gives rise to an increase in the gold loading from 3.3 to 4.0 wt % and in the average particle size from 1.8 to 2.9 nm. Different morphologies of gold nanoparticles are present as a function of the particle size. Particles with a size of 3-5 nm show defective structure, some of them having a multiple twinning particle (MTP) structure. At the same time, nanoparticles with an average size of ca. 2 nm exhibit defect-free structure with well-distinguishable {111} family planes. TEM and HAADF observations revealed that Au particles do not agglomerate on the SiO(2) support: gold is present on the surface of SiO(2) only as small particles. Density functional theory calculations were employed to study the mechanisms of [Au(en)(2)](3+) adsorption, where neutral and negatively charged silica surfaces were simulated by neutral cluster Si(4)O(10)H(4) and negatively charged cluster Si(4)O(10)H(3), respectively. The calculation results are totally consistent with the suggestion that the deposition of gold takes place according to a cationic adsorption mechanism.     

Functionalized gold nanoparticles as phosphorescent nanomaterials and sensors

Ligand-capped gold nanoparticles were synthesized by capping monothiol derivatives of 2,2'-dipyridyl onto the surface of Au nanoparticles (Au-BT). The average size of the metal core is around 4 nm, with a shell of approximately 340 bipyridine ligands around the Au nanoparticle. The high local concentration of the chelating ligands ( approximately 5 M) around the Au nanoparticle makes these particles excellent ion sponges, and their complexation with Eu(III)/Tb(III) ions yields phosphorescent nanomaterials. Absorption spectral studies confirm a 1:3 complexation between Eu(III)/Tb(III) ions and bipyridines, functionalized on the surface of Au nanoparticles. The red-emitting Au-BT:Eu(III) complex exhibits a long lifetime of 0.36 ms with six line-like emission peaks, whereas the green-emitting Au-BT:Tb(III) complex exhibits a lifetime of 0.7 ms with four line-like emission peaks. These phosphorescent nanomaterials, designed by linking BT:Eu(III) complexes to Au nanoparticles, were further utilized as sensors for metal cations. A dramatic decrease in the luminescence was observed upon addition of alkaline earth metal ions (Ca(2+), Mg(2+)) and transition metal ions (Cu(2+), Zn(2+), Ni(2+)), resulting from an isomorphous substitution of Eu(III) ions, whereas the luminescence intensity was not influenced by the addition of Na(+) and K(+) ions. Direct interaction of bipyridine-capped Au nanoparticles with Cu(2+) ions brings the nanohybrid systems closer, leading to the formation of three-dimensional superstructures. Strong interparticle plasmon interactions were observed in these closely spaced Au nanoparticles.     

Synthesis and antibacterial property of hollow SiO2/Ag nanocomposite spheres

This paper presents a novel and facile method to fabricate hollow silica/sliver (SiO(2)/Ag) nanocomposite spheres. In this approach, the monodisperse hollow SiO(2) colloids bearing quantenary ammonium groups were prepared by dispersion polymerization combined sol-gel process and used as templates. The Ag(+) ions were first adsorbed onto the surfaces of the hollow SiO(2) beads via electrostatic interaction and then in situ reduced by the deprotonated silanol groups of the hollow SiO(2) beads, no extra reducing agents or catalysts were added during the reduction process. TEM, SEM and EDX analyses indicated that Ag nanoparticles were successfully deposited onto the surfaces of hollow SiO(2) beads. Some influencing parameters, such as the amount of quantenary ammonium groups in the inner wall of hollow SiO(2) colloids, Ag(+) ions concentration and reaction temperature, on the deposition of Ag nanoparticles onto SiO(2) colloids were investigated. Preliminary antibacterial tests indicated that these hollow nanocomposite spheres showed excellent antibacterial ability.     

Au/Ag核一壳结构复合纳米粒子形成机制的研究

在已制备好的Au纳米粒子表面,通过化学还原的方法沉积生长Ag包覆层,通过 控制Au, Ag的比列,制备了粒度均匀且粒径可控的Au/Ag核-壳结构纳米粒子。利用 UV-vis吸收光谱和透射电子显微镜（TEM）对SAu, Ag摩尔比为1：10的复合纳米粒 子的光学性质和形态进行随时监测,直接观察了核-壳结构纳米粒子的生长过程： 一部分Ag+在Au核表面还原生长,溶液中其余Ag+还原形成银的纳米团簇向粒子表面 的继续沉积生长,壳层增厚。     

Galvanic replacement reactions of active-metal nanoparticles

We present a systemic investigation of a galvanic replacement technique in which active-metal nanoparticles are used as sacrificial seeds. We found that different nanostructures can be controllably synthesized by varying the type of more noble-metal ions and liquid medium. Specifically, nano-heterostructures of noble metal (Ag, Au) or Cu nanocrystals on active-metal (Mg, Zn) cores were obtained by the reaction of active-metal nanoparticles with more noble-metal ions in ethanol; Ag nanocrystal arrays were produced by the reaction of active-metal nanoparticles with Ag(+) ions in water; spongy Au nanospheres were generated by the reaction of active-metal nanoparticles with AuCl(4)(-) ions in water; and SnO(2) nanoparticles were prepared when Sn(2+) were used as the oxidant ions. The key factors determining the product morphology are shown to be the reactivity of the liquid medium and the nature of the oxidant-reductant couple, whereas Mg and Zn nanoparticles played similar roles in achieving various nanostructures. When microsized Mg and Zn particles were used as seeds in similar reactions, the products were mainly noble-metal dendrites. The new approach proposed in this study expands the capability of the conventional nanoscale galvanic replacement method and provides new avenues to various structures, which are expected to have many potential applications in catalysis, optoelectronics, and biomedicine.     

Metal-ion induced transition from multi- to single-bilayer tubes in histidine bearing lipids and formation of monodisperse Au nanoparticles

We report that a histidine based cationic lipid forms multi-bilayer nanotubes and the addition of metal ions such as Cu(2+) and Au(3+) induces transformation into single-bilayer nanotubes owing to coordination of the metal ions on the nanotube surface. The morphological transition was detected with X-ray scattering and electron microscopy. IR showed that the metal coordination is presumably the major driving force. The reduction of Au(3+) ions on the tube surface produced gold nanoparticles attached on the nanotube surface. The nanoparticle was almost monodisperse with the average diameter of 1.7 nm and the standard deviation σ of 0.29, which is remarkably narrower than that of previously reported lipid systems. The obtained particles were stable and no further aggregation and growth was observed after one week, providing a powerful and facile tool for producing nanoparticles in a wide range of applications.     

Preparation of Silica Microspheres Containing Ag Nanoparticles

Two sol-gel fabrication processes were investigated to make silica spheres containing Ag nanoparticles: (1) a modified Stöber method for silica spheres below 1 m size, and (2) a SiO₂-film formation method on spheres of 3–;7 m size. The spheres were designed to incorporate silver nanoparticles of high ⁽³⁾ in a spherical optical cavity structure for the resonance effect. For the incorporation, interaction between [Ag(NH₃)₂]⁺ ion and Si-OH was important. In the Stöber method, the size of the silica spheres was determined by a charge balance of plus and minus ions on the silica surface. In the film formation method, the capture of Ag complex ion on the silica surface depended on whether the surface was covered with OH groups or not. After doping [Ag(NH₃)₂]⁺ into silica particles or SiO₂ films on the spheres, these ions w ere reduced by NaBH₄ to form silver nanoparticles. From plasma absorption at around 420 nm wavelength and TEM photographs of nanometer-sized silver particles, their formation inside the spherical cavity structures was confirmed.     

Green preparation of hollow mesoporous silica nanosphere inside-loaded gold nanoparticles and the catalytic activity

In this work, an active nano-catalyst with gold nanoparticles loaded in hollow mesoporous silica nanospheres (HMSNs/Au) was prepared by a one-pot sol-gel method, in which gold ions were loaded in hollow mesoporous silica spheres followed by sodium alginate reduction. The characterization of the HMSNs/Au were determined by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), N₂ adsorption–desorption isotherms (BET). The high catalytic activity of HMSNs/Au, denoted as apparent turn-over frequency (TOF), was detected by UV-Vis spectrophotometer for the catalytic reduction of 4-nitrophenol (74.5 h^?1) and 2-nitrophenol (108.7 h^?1) in the presence of sodium borohydride solution due to the small gold nanoparticles size and overall exposure of active sites. It is expected that this ecofriendly approach to prepare inorganic composited nanoparticles as high active catalysts based on hollow mesoporous materials was a promising platform for loading noble metal nanoparticles.     

Multiplexed analysis of silver(I) and mercury(II) ions using oligonucletide-metal nanoparticle conjugates

A colorimetric assay has been developed for the simultaneous selective detection of silver(I) and mercury(II) ions utilizing metal nanoparticles (NPs) as sensing element based on their unique surface plasmon resonance properties. In this method, sulfhydryl group modified cytosine-(C)-rich ssDNA (SH-C-ssDNA) was self-assembled on gold nanoparticles (AuNPs) to produce the AuNPs-C-ssDNA complex, and sulfhydryl group modified thymine-(T)-rich ssDNA (SH-T-ssDNA) was self-assembled on silver nanoparticles (AgNPs) to produce the AgNPs-T-ssDNA complex. Oligonucleotides (SH-C-ssDNA or SH-T-ssDNA) could enhance the AuNPs or AgNPs against salt-induced aggregation. However, the presence of silver(I) ions (Ag(+)) in the complex of ssDNA-AuNPs would reduce the stability of AuNPs due to the formation of Ag(+) mediated C-Ag(+)-C base pairs accompanied with the AuNPs color change from red to purple or even to dark blue. Moreover, the presence of mercury(II) ions (Hg(2+)) would also reduce the stability of AgNPs due to the formation of Hg(2+) mediated T-Hg(2+)-T base pairs accompanied with the AgNPs color change from yellow to brown, then to dark purple. The presence of both Ag(+) and Hg(2+) will reduce the stability of both AuNPs and AgNPs and cause the visible color change. As a result, Ag(+) and Hg(2+) could be detected qualitatively and quantitatively by the naked eye or by UV-vis spectral measurement. The lowest detectable concentration of a 5 nM mixture of Ag(+) and Hg(2+) in the river water was gotten by the UV-vis spectral measurement.     

Preparation and properties of silica–gold core–shell particles

Silica-metal core–shell particles, as for instance those having siliceous core and nanostructured gold shell, attracted a lot of attention because of their unique properties resulting from combination of mechanical and thermal stability of silica and magnetic, electric, optical and catalytic properties of metal nanocrystals such as gold, silver, platinum and palladium. Often, the shell of the core–shell particles consists of a large number of metal nanoparticles deposited on the surface of relatively large silica particles, which is the case considered in this work. Namely, silica particles having size of about 600 nm were subjected to surface modification with 3-aminopropyltrimethoxysilane. This modification altered the surface properties of silica particles, which was demonstrated by low pressure nitrogen adsorption at ?196 °C. Next, gold nanoparticles were deposited on the surface of aminopropyl-modified silica particles using two strategies: (i) direct deposition of gold nanoparticles having size of about 10 nm, and (ii) formation of gold nanoparticles by adsorption of tetrachloroauric acid on aminopropyl groups followed by its reduction with formaldehyde.The overall morphology of silica–gold particles and the distribution of gold nanoparticles on the surface of modified silica colloids were characterized by scanning electron microscopy. It was shown that direct deposition of colloidal gold on the surface of large silica particles gives more regular distribution of gold nanopartciles than that obtained by reduction of tetrachloroauric acid. In the latter case the gold layer consists of larger nanoparticles (size of about 50 nm) and is less regular. Note that both deposition strategies afforded silica–gold particles having siliceous cores covered with shells consisting of gold nanoparticles of tunable concentration.     

Recent progress in fluorescent and colorimetric chemosensors for detection of precious metal ions (silver, gold and platinum ions)

Due to the wide range of applications and biological significance, the development of optical probes for silver, gold and platinum ions has been an active research area in the past few years. This tutorial review focuses on the recent contributions concerning the fluorescent or colorimetric sensors for these metal ions, and is organized according to their structural classifications (for Ag(+) detection) and unique mechanisms between the sensors and metal ions (for Au(3+) and Pt(2+) detection).     

Bioinspired systems for metal-ion sensing: new emissive peptide probes based on benzo[d]oxazole derivatives and their gold and silica nanoparticles

Seven new bioinspired chemosensors (2-4 and 7-10) based on fluorescent peptides were synthesized and characterized by elemental analysis, (1)H and (13)C NMR, melting point, matrix-assisted laser desorption-ionization time-of-flight mass spectrometry (MALDI-TOF-MS), and IR and UV-vis absorption and emission spectroscopy. The interaction with transition- and post-transition-metal ions (Cu(2+), Ni(2+), Ag(+), Zn(2+), Cd(2+), Hg(2+), Pb(2+), and Fe(3+)) has been explored by absorption and fluorescence emission spectroscopy and MALDI-TOF-MS. The reported fluorescent peptide systems, introducing biological molecules in the skeleton of the probes, enhance their sensitivity and confer them strong potential for applications in biological fields. Gold and silica nanoparticles functionalized with these peptides were also obtained. All nanoparticles were characterized by dynamic light scattering, transmission electron microscopy, and UV-vis absorption and fluorescence spectroscopy. Stable gold nanoparticles (diameter 2-10 nm) bearing ligands 1 and 4 were obtained by common reductive synthesis. Commercial silica nanoparticles were decorated at their surface using compounds 8-10, linked through a silane spacer. The same chemosensors were also taken into aqueous solutions through their dispersion in the outer layer of silica core/poly(ethylene glycol) shell nanoparticles. In both cases, these complex nanoarchitectures behaved as new sensitive materials for Ag(+) and Hg(2+) in water. The possibility of using these species in this solvent is particularly valuable because the impact on human health of heavy- and transition-metal-ion pollution is very severe, and all analytical and diagnostics investigations involve a water environment.     

Au nanoparticle-enhanced surface plasmon resonance sensing of biocatalytic transformations

N-(3-Aminopropyl)-N'-methyl-4,4'-bipyridinium is coupled to tiopronin-capped Au nanoparticles (diameter ca. 2 nm) to yield methyl(aminopropyl)viologen-functionalized Au nanoparticles (MPAV(2+)-Au nanoparticles). In situ electrochemical surface plasmon resonance (SPR) measurements are used to follow the electrochemical deposition of the bipyridinium radical cation modified Au nanoparticles on an Au-coated glass surface and the reoxidation and dissolution of the bipyridinium radical cation film. The MPAV(2+)-functionalized Au nanoparticles are also employed for the amplified SPR detection of NAD(+) and NADH cofactors. By SPR monitoring the partial biocatalyzed dissolution of the bipyridinium radical cation film in the presence of diaphorase (DP) NAD(+) is detected in the concentration range of 1x10(-4) M to 2x10(-3) M. Similarly, the diaphorase-mediated formation of the bipyridinium radical cation film on the Au-coated glass surface by the reduction of the MPAV(2+)-functionalized Au nanoparticles by NADH is used for the amplified SPR detection of NADH in the concentration range of 1x10(-4) M to 1x10(-3) M.     

Ag/Au纳米粒子的没食子酸还原制备及其共振瑞利散射光谱测定人血清总蛋白

以没食子酸为还原剂和稳定剂,用种子生长法制备出粒径均匀、单分散性和稳定性好、近球形的Ag/Au 核壳纳米粒子.高分辨透射电镜(HRTEM)与 X-射线能量色散光谱仪(EDX)测试表明,在Ag/Au摩尔比为1:1.6时,Au已完全包裹在Ag纳米粒子表面时,平均粒径为25 nm.以此摩尔比制备的Ag/Au核壳纳米粒子为探针...     

Electrochemistry of conductive polymers 39. Contacts between conducting polymers and noble metal nanoparticles studied by current-sensing atomic force microscopy

Electrical properties of contacts formed between conducting polymers and noble metal nanoparticles have been examined using current-sensing atomic force microscopy (CS-AFM). Contacts formed between electrochemically prepared pi-conjugated polymer films such as polypyrrole (PPy), poly(3-methylthiophene) (P3MeT), as well as poly(3,4-ethylenedioxythiophene) (PEDOT) and noble metal nanoparticles including platinum (Pt), gold (Au), and silver (Ag) have been examined. The Pt nanoparticles were electrochemically deposited on a pre-coated PPy film surface by reducing a platinum precursor (PtCl62-) at a constant potential. Both current and scanning electron microscopic images of the film showed the presence of Pt islands. The Au and Ag nanoparticles were dispersed on the P3MeT and PEDOT film surfaces simply by dipping the polymer films into colloid solutions containing Au or Ag particles for specified periods (5 to approximately 10 min). The deposition of Au or Ag particles resulted from either their physical adsorption or chemical bonding between particles and the polymer surface depending on the polymer. When compared with PPy, P3MeT and PEDOT showed a stronger binding to Au or Ag nanoparticles when dipped in their colloidal solutions for the same period. This indicates that Au and Ag particles are predominantly linked with the sulfur atoms via chemical bonding. Of the two, PEDOT was more conductive at the sites where the particles are connected to the polymer. It appears that PEDOT has better aligned sulfur atoms on the surface and is strongly bonded to Au and Ag nanoparticles due to their strong affinity to gold and silver. The current-voltage curves obtained at the metal islands demonstrate that the contacts between these metal islands and polymers are ohmic.     

Selective dissolution of the silver component in colloidal Au and Ag multilayers: a facile way to prepare nanoporous gold film materials

Colloidal Au/Ag multilayer films were prepared by alternate assembly of Au nanoparticles with a size of 5 +/- 1.2 nm and Ag nanoparticles with a size of 10 +/- 2.4 nm by using 1,5-pentanedithiol as cross-linker. Nanoporous gold films with a ligament size of 26.7 +/- 4.6 nm were then prepared by selective dissolution of sacrificial templates of silver particles in colloidal Au/Ag multilayers. The complete dissolution of Ag particles in colloidal Au/Ag multilayers in a mixture solution of 3.0 mM HAuCl(4) and 3 M NaCl took place at room temperature without damage of the colloidal Au film. This method to prepare nanoporous gold films was further extended to the preparation of nanoporous gold nanotubes by depositing colloidal Au/Ag film on the inner wall of anodic aluminum oxides (AAO) followed by dissolution of colloidal Ag and removal of AAO templates.     

Sonochemical Processes and Formation of Gold Nanoparticles within Pores of Mesoporous Silica

Mesoporous silica with gold nanoparticles inside its pores was prepared by the soaking and ultrasound-induced reduction method. This new composite was characterized by X-ray diffraction (XRD), Brunauer-Emmett-Teller (BET), and high-resolution transmission electron microscopy (HRTEM) techniques. The results showed that nearly spherical-shaped gold nanoparticles, with mean size in diameter of 5.2 nm, are located in the pores, most of which are less than 6 nm in diameter. The ultrasonic irradiation time dependence of optical absorption for the soaked porous solid sample, as suggested by the variation in absorbance at 310 and 544 nm, indicated the reduction of Au (III) ions, and the nucleation and aggregation of gold nanoparticles within pores of mesoporous silica. Additionally, the reaction rates estimated phenomenologically by the absorbance decay at 310 nm for both the porous sample and the corresponding soaking solution presented the enhancement of the sonochemical reduction rate of Au (III) ions within pores of mesoporous silica. It is assumed that the extensive liquid-solid interfacial zones in the pores, due to the high specific surface areas and great porosity of the mesoporous solid, are the major regions where the efficient sonochemical reduction induced by the cavitation takes place. Copyright 2001 Academic Press.     

A facile synthesis and characterization of Ag, Au and Pt nanoparticles using a natural hydrocolloid gum kondagogu (Cochlospermum gossypium)

An environmentally benign method for the synthesis of noble metal nanoparticles has been reported using aqueous solution of gum kondagogu (Cochlospermum gossypium). Both the synthesis, as well as stabilization of colloidal Ag, Au and Pt nanoparticles has been accomplished in an aqueous medium containing gum kondagogu. The colloidal suspensions so obtained were found to be highly stable for prolonged period, without undergoing any oxidation. SEM-EDXA, UV-vis spectroscopy, XRD, FTIR and TEM techniques were used to characterize the Ag, Au and Pt nanoparticles. FTIR analysis indicates that -OH groups present in the gum matrix were responsible for the reduction of metal cations into nanoparticles. UV-vis studies showed a distinct surface plasmon resonance at 412 and 525 nm due to the formation of Au and Ag nanoparticles, respectively, within the gum network. XRD studies indicated that the nanoparticles were crystalline in nature with face centered cubic geometry. The noble metal nanoparticles prepared in the present study appears to be homogeneous with the particle size ranging between 2 and 10 nm, as evidenced by TEM analysis. The Ag and Au nanoparticles formed were in the average size range of 5.5±2.5 nm and 7.8±2.3 nm; while Pt nanoparticles were in the size range of 2.4±0.7 nm, which were considerably smaller than Ag and Au nanoparticles. The present approach exemplifies a totally green synthesis using the plant derived natural product (gum kondagogu) for the production of noble metal nanoparticles and the process can also be extended to the synthesis of other metal oxide nanoparticles.     

Heat-Induced Precipitation and Light-Induced Dissolution of Metal (Ag & Au) Nanoparticles in Hybrid Film

Metal nanoparticle-doped materials have attracted much attention because of their enhanced third-order nonlinear optical susceptibility. In their application, (1) controllable precipitation and (2) stability against photo-irradiation are essential concerns. Silver or gold nanoparticle-doped films were made from hybrid sol containing metal ions with their stabilizer on silica glass substrates by the sol-gel dip-coating technique and their heat-induced precipitation and photo-stability were investigated. The heat-induced precipitation up to 1000°C was remarkably different in Ag and Au nanoparticles. After 120–500°C heating, Ag nanoparticles with a wide range of radii were formed in the hybrid films. Above 500°C, organic groups were completely evacuated and at 800°C, mono-dispersed Ag nanoparticles with radii of 2–4 nm were precipitated in the resultant film. On the other hand, Au nanoparticles of 10 nm average radius precipitated at 120°C and showed no drastic change in subsequent heating up to 1000°C. Since Ag nanoparticle-doped film showed the photosensitive change, their photostability was investigated by irradiating them under Xenon lamp light. The 800°C-heating sample showed no decrease in the plasma absorption band at around 420 nm wavelength after 20 h light irradiation, but the band intensities in the 120–500°C-heating films decreased noticeably.