Foaming of trans‐1,4‐polyisoprene (TPI) polymer was carried out through a batch process using nitrogen (N₂) as the blowing agent. TPI vulcanizates having varying crosslink densities were prepared by varying crosslinking agent content and curing time. The vulcanizates were then saturated with N₂ inside a pressure vessel at a pressure of 14 MPa and varying temperatures for 5 hours before effecting the foaming by rapidly quenching the pressure. The effects of varying the crosslinking agent content, silica filler content, and precuring time of the vulcanizates and the effects of varying the gas saturation temperature of foaming on the cell characteristics and physical properties of the foam prepared were investigated. The cells of the TPI foams had a spherical, closed structure. The density, expansion ratio, cell size, cell density, and tensile properties of the foams varied with varying crosslink density of the TPI vulcanizates as well as the saturation temperature of foaming. The important effects of crosslink density and saturation temperature on the N₂ solubility in the TPI matrix and thus on the foam expansion were discussed. The silica filler was found to be acting as a cell nucleating agent and reinforcing filler for the TPI foams.     

Effect of Supercritical Carbon Dioxide Conditions on PVDF/PVP Microcellular Foams

Supercritical carbon dioxide (ScCO₂) was used as a physical foaming agent to prepare poly(vinylidene f luoride)/poly(N-vinyl pyrrolidone) (PVDF/PVP) microstructure material. The effects of foaming conditions including saturation pressure, foaming temperature and foaming time on PVDF/PVP foams morphology, thermal and electrical behavior were systematically investigated by scanning electron microscope, differential scanning calorimeter and broadband dielectric spectrometer. Small cell and low cell density were achieved at low pressure of 12 MPa, as increasing saturation pressure, the average cell size increased first, and then decreased. The competition between the cell growth and cell nucleation played an important role in average cell size, which was directly related to ScCO₂ processing conditions. With increasing foaming temperature, cell size was increased and cell density was decreased, in a nearly linear manner. The variation of foaming time was considered to be closely related to the time for cells to grow. Thus, the results revealed that the average cell size enhanced with extending foaming time. The thermal properties of PVDF/PVP composites are slightly inf luenced by foaming parameters, and the dielectric constant of PVDF/PVP composite foams decreased with increasing volume expansion ratio.     

A novel method to prepare microcellular poly(vinyl alcohol) foam based on thermal processing and supercritical fluid

Combining the thermal processing and supercritical fluid technology develops a novel preparation method of microcellular poly(vinyl alcohol) (PVA). Water, as the plasticizer in system, can form the hydrogen bonding with pendant hydroxyl of PVA and weaken its strong intermolecular and intramolecular forces to realize the thermal processing. Supercritical carbon dioxide (sc‐CO₂) can easily dissolve into water‐plasticized PVA (WPVA) because of the destruction of crystal region caused by water, and the enhanced sc‐CO₂ solubility can greatly improve the foamability of WPVA. The porous structure generates through the saturation of sc‐CO₂ in WPVA sample and followed by pressure drop‐induced phase separation. The foaming behavior of WPVA was studied as a function of saturation pressure, foaming temperature, and saturation time. The cell density, cell size, and distribution of the obtained foam can be controlled by tuning processing conditions. The results revealed that the cell size decreased, and its distribution narrowed with saturation pressure increasing, or decrease of foaming temperature. But excessively increasing the saturation time generated a negative effect on the foaming behavior owing to the deteriorated plasticization effect resulted from the loss of water. Copyright © 2016 John Wiley & Sons, Ltd.     

All-cellulose nanocomposites by surface selective dissolution of bacterial cellulose

All-cellulose nanocomposites using bacterial cellulose (BC) as a single raw material were prepared by a surface selective dissolution method. The effect of the immersion time of BC in the solvent (lithium chloride/N,N-dimethylacetamide) during preparation on the nanocomposite properties was investigated. The structure, morphology and mechanical properties of the nanocomposites were characterized by X-ray diffraction, scanning electron microscopy, and tensile testing. The optimum immersion time of 10 min allowed the preparation of nanocomposites with an average tensile strength of 411 MPa and Young’s modulus of 18 GPa. With the longest immersion time of 60 min, the prepared composite sheet turns to express a very high toughness characteristic possessing a work-to-fracture as high as 16 MJ/m³. These biobased nanocomposites show high performances thanks to their unique structure and properties.     

Isolation and characterization of cellulose nanofibers from four plant cellulose fibers using a chemical-ultrasonic process

Cellulose nanofibers (CNFs) were isolated from four kinds of plant cellulose fibers by a chemical-ultrasonic treatment. The chemical composition, morphology, crystalline behavior, and thermal properties of the nanofibers and their intermediate products were characterized and compared. The CNFs extracted from wood, bamboo, and wheat straw fibers had uniform diameters of 10–40 nm, whereas the flax fibers were not uniformly nanofibrillated because of their initially high cellulose content. The chemical composition of each kind of nanofibers was mainly cellulose because hemicelluloses and lignin were significantly removed during chemical process. The crystallinity of the nanofibers increased as the chemical treatments were applied. The degradation temperature of each kind of nanofiber reached beyond 330 °C. Based on the properties of the CNFs, we expect that they will be suitable for use in green nanocomposites, filtration media and optically transparent films.     

Nanofibrillated cellulose (NFC) reinforced polyvinyl alcohol (PVOH) nanocomposites: properties, solubility of carbon dioxide, and foaming

Polyvinyl alcohol (PVOH) and its nanofibrillated cellulose (NFC) reinforced nanocomposites were produced and foamed and its properties—such as the dynamic mechanical properties, crystallization behavior, and solubility of carbon dioxide (CO₂)—were evaluated. PVOH was mixed with an NFC fiber suspension in water followed by casting. Transmission electron microscopy (TEM) images, as well as the optical transparency of the films, revealed that the NFC fibers dispersed well in the resulting PVOH/NFC nanocomposites. Adding NFC increased the tensile modulus of the PVOH/NFC nanocomposites nearly threefold. Differential scanning calorimetry (DSC) analysis showed that the NFC served as a nucleating agent, promoting the early onset of crystallization. However, high NFC content also led to greater thermal degradation of the PVOH matrix. PVOH/NFC nanocomposites were sensitive to moisture content and dynamic mechanical analysis (DMA) tests showed that, at room temperature, the storage modulus increased with decreasing moisture content. The solubility of CO₂ in the PVOH/NFC nanocomposites depended on their moisture content and decreased with the addition of NFC. Moreover, the desorption diffusivity increased as more NFC was added. Finally, the foaming behavior of the PVOH/NFC nanocomposites was studied using CO₂ and/or water as the physical foaming agent(s) in a batch foaming process. Only samples with a high moisture content were able to foam with CO₂. Furthermore, the PVOH/NFC nanocomposites exhibited finer and more anisotropic cell morphologies than the neat PVOH films. In the absence of moisture, no foaming was observed in the CO₂-saturated neat PVOH or PVOH/NFC nanocomposite samples.     

Thermal study on electrospun polyvinylpyrrolidone/ammonium metatungstate nanofibers: optimising the annealing conditions for obtaining WO<Subscript>3</Subscript> nanofibers

This article demonstrates how important it is to find the optimal heating conditions when electrospun organic/inorganic composite fibers are annealed to get ceramic nanofibers in appropriate quality (crystal structure, composition, and morphology) and to avoid their disintegration. Polyvinylpyrrolidone [PVP, (C₆H₉NO) _n ] and ammonium metatungstate [AMT, (NH₄)₆[H₂W₁₂O₄₀]·nH₂O] nanofibers were prepared by electrospinning aqueous solutions of PVP and AMT. The as-spun fibers and their annealing were characterized by TG/DTA-MS, XRD, SEM, Raman, and FTIR measurements. The 400–600 nm thick and tens of micrometer long PVP/AMT fibers decomposed thermally in air in four steps, and pure monoclinic WO₃ nanofibers formed between 500 and 600 °C. When a too high heating rate and heating temperature (10 °C min⁻¹, 600 °C) were used, the WO₃ nanofibers completely disintegrated. At lower heating rate but too high temperature (1 °C min⁻¹, 600 °C), the fibers broke into rods. If the heating rate was adequate, but the annealing temperature was too low (1 °C min⁻¹, 500 °C), the nanofiber morphology was excellent, but the sample was less crystalline. When the optimal heating rate and temperature (1 °C min⁻¹, 550 °C) were applied, WO₃ nanofibers with excellent morphology (250 nm thick and tens of micrometer long nanofibers, which consisted of 20–80 nm particles) and crystallinity (monoclinic WO₃) were obtained. The FTIR and Raman measurements confirmed that with these heating parameters the organic matter was effectively removed from the nanofibers and monoclinic WO₃ was present in a highly crystalline and ordered form.     

Structural evolution and magnetic properties of SrFe<Subscript>12</Subscript>O<Subscript>19</Subscript> nanofibers by electrospinning

The SrFe₁₂O₁₉/poly (vinyl pyrrolidone) (PVP) composite fiber precursors were prepared by the sol-gel assisted electrospinning with ferric nitrate, strontium nitrate and PVP as starting reagents. Subsequently, the M-type strontium ferrite (SrFe₁₂O₁₉) nanofibers were derived from calcination of these precursors at 750–1,000 °C.The composite precursors and strontium ferrite nanofibers were characterized by Fourier transform infrared spectroscopy, X-ray diffraction, scanning electron microscopy and vibrating sample magnetometer. The structural evolution process of strontium ferrite consists of the thermal decomposition and M-type strontium ferrite formation. After calcined at 750 °C for 2 h the single M-type strontium ferrite phase is formed by reactions of iron oxide and strontium oxide produced during the precursor decomposition process. The nanofiber morphology, diameter, crystallite size and grain morphology are mainly influenced by the calcination temperature and holding time. The SrFe₁₂O₁₉ nanofibers characterized with diameters of around 100 nm and a necklace-like structure obtained at 900 °C for 2 h, which is fabricated by nanosized particles about 60 nm with the plate-like morphology elongated in the preferred direction perpendicular to the c-axis, show the optimized magnetic property with saturation magnetization 59 A m² kg⁻¹ and coercivity 521 kA m⁻¹. It is found that the single domain critical size for these M-type strontium ferrite nanofibers is around 60 nm.     

Supercritical CO<Subscript>2</Subscript> assisted preparation of open-cell foams of linear low-density polyethylene and linear low-density polyethylene/carbon nanotube composites

The open-cell structure foams of linear low-density polyethylene (LLDPE) and linear low-density polyethylene (LLDPE)/multi-wall carbon nanotubes (MWCNTs) composites are prepared by using supercritical carbon dioxide (sc-CO₂) as a foaming agent. The effects of processing parameters (foaming temperature, saturation pressure, and depressurization rate) and the addition of MWCNTs on the evolution of cell opening are studied systematically. For LLDPE foaming, the foaming temperature and saturation pressure are two key factors for preparing open-cell foams. An increase in temperature and pressure promotes both the cell wall thinning and cell rupture, because a high temperature results in a decrease in the viscosity of the polymer, and a high pressure leads to a larger amount of cell nucleation. Moreover, for the given temperature and pressure, the high pressurization rate results in a high pressure gradient, favoring cell rupture. For LLDPE/MWCNTs foaming, the addition of MWCNTs not only promotes the cell heterogeneous nucleation, but also prevents the cell collapse during cell opening, which is critical to achieve the open-cell structures with small cell size and high cell density.     

Synthesis and characterization of novel magnetic Fe3O4/polyphosphazene nanofibers

Novel magnetic Fe₃O₄/polyphosphazene nanofibers were successfully prepared via a facile approach by ultrasonic irradiation. The structure and morphology were characterized by SEM, TEM, EDX, IR and XRD. The characterization results show that the magnetic Fe₃O₄/polyphosphazene nanofibers are several microns in length and 50–100 nm in diameter with Fe₃O₄ nanoparticles of 5–10 nm attached on the surface. The interaction between Fe₃O₄ nanoparticles and polyphosphazene nanofibers was thought as coordination behavior. TG curves show that the magnetic Fe₃O₄/polyphosphazene nanofibers have good thermostability and high magnetism content of about 44%. Magnetic studies show that the magnetic nanofibers exhibit good superparamagnetic properties with high magnetization saturation value of about 36 emu/g.     

Effect of heat treatment on particle growth and magnetic properties of electrospun Sr<Subscript>0.8</Subscript>La<Subscript>0.2</Subscript>Zn<Subscript>0.2</Subscript>Fe<Subscript>11.8</Subscript>O<Subscript>19</Subscript> nanofibers

Sr_0.8La_0.2Zn_0.2Fe_11.8O₁₉/poly(vinyl pyrrolidone) (PVP) composite fiber precursors were prepared by the sol–gel assisted electrospinning. Subsequently, the M-type ferrite Sr_0.8La_0.2Zn_0.2Fe_11.8O₁₉ nanofibers with diameters about 120 nm were obtained by calcination of these precursors at different heat treatment conditions. The precursor and resultant Sr_0.8La_0.2Zn_0.2Fe_11.8O₁₉ nanofibers were characterized by X-ray diffraction, scanning electron microscopy, transmission electron microscopy, energy-dispersive X-ray spectrometer and vibrating sample magnetometer. With the calcination temperature increased up to 1,000 °C for 2 h or the holding time prolonged to 12 h at 900 °C, the Sr_0.8La_0.2Zn_0.2Fe_11.8O₁₉ particles gradually grow into a hexagonal elongated plate-like morphology due to the dimensional control along the nanofiber length. These elongated plate-like particles will be linked one by one to form the nanofiber with a necklace-like morphology. The magnetic properties of the Sr_0.8La_0.2Zn_0.2Fe_11.8O₁₉ nanofibers are closely related to grain sizes, impurities and defects in the ferrite, which are influenced by the calcination temperature, holding time and heating rate. After calcined at 900 °C for 12 h with a heating rate of 3 °C/min, the optimized magnetic properties are achieved with the specific saturation magnetization 75.0 A m² kg⁻¹ and coercivity 426.3 kA m⁻¹ for the Sr_0.8La_0.2Zn_0.2Fe_11.8O₁₉ nanofibers.     

Novel technique to form electrode–electrolyte nanointerface in all-solid-state rechargeable lithium batteries

The electrode–electrolyte nanocomposites, where the nano-sized NiS electrode with large capacity was embedded in the 80Li₂S · 20P₂S₅ electrolyte with high Li⁺ conductivity, were successfully prepared by the mechanochemical method. Contact area of solid–solid interface between the electrode and the electrolyte was remarkably increased in the nanocomposites. All-solid-state cell using the nanocomposites as a working electrode exhibited larger capacity and better cycling performance than the cell using the electrode obtained by conventional hand-mixing of powders. The mechanochemical technique sheds light on a new formation process of electrode–electrolyte interfaces endowing solid-state batteries with high power density and high energy density.     

Facile preparation and characterization of anatase TiO2/nanocellulose composite for photocatalytic degradation of methyl orange

Anatase TiO₂/nanocellulose composite was prepared for the first time via a one-step method at a relatively low temperature by using cellulose nanofibers as carrier and tetrabutyl titanate as titanium precursor. The morphology, structure and element composition of the composite were characterized by SEM, EDS, TEM, XRD, XPS and UV–vis DRS. The specific surface area and thermal stability of the composite were investigated by N₂ adsorption–desorption and thermogravimetric analysis, respectively, and the band gaps of the prepared photocatalysts were calculated based on the UV–vis DRS results. In addition, the prepared composite was used for the photocatalytic degradation of methyl orange (aqueous solution, 40 mg L⁻¹). It was found that the composite had a good morphology and anatase crystal structure, and Ti-O-C bond was formed between TiO₂ and nanocellulose. The specific surface area of composite was increased and the thermal stability was decreased compared with the cellulose nanofiber. Moreover, the degradation rate of methyl orange was achieved as 99.72% within 30 min, and no obvious activity loss was observed after five cycles. This work might give some insights into the design of efficient photocatalysts for the treatment of organic dye wastewater.     

Cellulose nanofibers from curaua fibers

Curaua nanofibers extracted under different conditions were investigated. The raw fibers were mercerized with NaOH solutions; they were then submitted to acid hydrolysis using three different types of acids (H₂SO₄, a mixture of H₂SO₄/HCl and HCl). The fibers were analyzed by cellulose, lignin and hemicellulose contents; viscometry, X-ray diffraction (XRD) and thermal stability by thermogravimetric analysis (TG). The nanofibers were morphologically characterized by transmission electron microscopy (TEM) and their surface charges in suspensions were estimated by Zeta-potential. Their degree of polymerization (DP) was characterized by viscometry, crystallinity by XRD and thermal stability by TG. Increasing the NaOH solution concentration in the mercerization, there was a decrease of hemicellulose and lignin contents and consequently an increase of cellulose content. XRD patterns presented changes in the crystal structure from cellulose I to cellulose II when the fibers were mercerized with 17.5% NaOH solution. All curaua nanofibers presented a rod-like shape, an average diameter (D) of 6–10 nm and length (L) of 80–170 nm, with an aspect ratio (L/D) of around 13–17. The mercerization of fibers with NaOH solutions influenced the crystallinity index and thermal stability of the resulting nanofibers. The fibers mercerized with NaOH solution 17.5% resulted in more crystalline nanofibers, but thermally less stable and inferior DP. The aggregation state increases with the amount of HCl introduced into the extraction, due to the decrease of surface charges (as verified by Zeta Potential analysis). However, this release presented nanofibers with better thermal stability than those whose acid hydrolysis was carried out using only H₂SO₄.     

三明治结构rGO/Fe3O4@mSiO2载体的构筑及协同抗肿瘤性能

采用温和的反应条件,制备出三明治结构rGO/Fe_3O_4@mSiO_2,利用SEM、TEM、FTIR、XRD和N_2吸附-脱附等对其形貌和性能进行表征,考查了其对Hela细胞的毒性和细胞荧光成像效果,并探讨了其形成机理。实验结果表明:rGO/Fe_3O_4@mSiO_2具有较高的比表面积(217 m~2·g~(-1)),对抗癌药物五氟尿嘧啶(5-FU)的载药率达到57.34%;它还具有较好的磁性,磁饱和强度为32 emu·g-1;而且rGO/Fe_3O_4@mSiO_2纳米复合物在光照条件下具有优异的光热转换性能,对He La细胞表现出明显的杀伤效果。     

Microcellular structure of a thin polycarbonate sheet prepared by compression molding

Microcellular thin polycarbonate sheets have been prepared by compression molding with the cell size in the range of 2∼20 microns, and cell density larger than 10⁸ cells/cm³. The effect of processing parameters on the microcellular polycarbonate structure has been investigated. The cell size decreases with increasing foaming time till 8 minute and then increases. Besides this parameter slightly decreases with increasing foaming pressure, but increases with increasing temperature. The variation of cell density is contrary to that of cell size, and the foam density decreases with increasing foaming pressure and foaming temperature and displays a variable trend with increasing foaming time under different foaming pressures.     

Effects of strontium silicate on structure and magnetic properties of electrospun strontium ferrite nanofibers

The composite nanofibers of xSrSiO₃/(100 − x)SrFe₁₂O₁₉ (x = 0–13 wt%) with diameters around 110 nm have been prepared by calcination of the electrospun SrSiO₃/SrFe₁₂O₁₉/poly (vinyl pyrrolidone) (PVP) composite fibers at 800–900 °C. The composite nanofibers were characterized by Fourier transform infrared spectroscopy, X-ray diffraction, scanning electron microscopy and vibrating sample magnetometer. After calcined at 800° the M-type strontium ferrite is formed and the strontium silicate exists as an amorphous state when the calcination temperature below about 950 °C. The addition of SrSiO₃ has an obvious suppression effect on the strontium ferrite grain growth and the ferrite grain size decreases from 66.9 to 33.5 nm corresponding SrSiO₃ content from 0 to 9 wt% in the composite. The specific saturation magnetization (Ms) of the xSrSiO₃/(100 − x)SrFe₁₂O₁₉ composite nanofibers exhibits a continuous reduction from 58.0 to 45.6 A m² kg⁻¹ with the increase of SrSiO₃ content from 0 to 13 wt%. With addition of SrSiO₃ from 0 to 13 wt%, the coercivity of the composite nanofibers obtained at 900 °C initially increases, reaching a maximum value 501.1 kA m⁻¹ at the silicate content 7 wt%, and then shows a reduction tendency with the strontium silicate content increase further up to 13 wt%. This influence on the coercivity by strontium silicate can be attributed mainly to the ferrite grain growth suppression and the non-magnetic phase barrier for the domains misalignment.     

Ratiometric two-photon excited photoluminescence of quantum dots triggered by near-infrared-light for real-time detection of nitric oxide release in situ

Probe-donor integrated nanocomposites were developed from conjugating silica-coated Mn²⁺:ZnS quantum dots (QDs) with MoS₂ QDs and photosensitive nitric oxide (NO) donors (Fe₄S₃(NO)₇⁻, RBS). Under excitation with near-infrared (NIR) light at 808 nm, the Mn²⁺:ZnS@SiO₂/MoS₂-RBS nanocomposites showed the dual-emissive two-photon excited photoluminescence (TPEPL) that induced RBS photolysis to release NO in situ. NO caused TPEPL quenching of Mn²⁺:ZnS QDs, but it produced almost no impact on the TPEPL of MoS₂ QDs. Hence, the nanocomposites were developed as a novel QDs-based ratiometric TPEPL probe for real-time detection of NO release in situ. The ratiometric TPEPL intensity is nearly linear (R² = 0.9901) with NO concentration in the range of 0.01∼0.8 μM, which corresponds to the range of NO release time (0∼15 min). The detection limit was calculated to be approximately 4 nM of NO. Experimental results confirmed that this novel ratiometric TPEPL probe possessed high selectivity and sensitivity for the detection of NO against potential competitors, and especially showed high detection performance for NIR-light triggered NO release in tumor intracellular microenvironments. These results would promote the development of versatile probe-donor integrated systems, also providing a facile and efficient strategy to real-time detect the highly controllable drug release in situ, especially in physiological microenvironments.     

Synthesis and characterization of C60/polyaniline composites from interfacial polymerization

C₆₀/polyaniline (PANI) nanocomposites have been synthesized by the oxidative polymerization of aniline with ammonium peroxydisulfate in the presence of C₆₀ by using an interfacial reaction. When compared with the pure PANI nanofibers from the similar process, the diameter of the obtained C₆₀/PANI nanofibers was increased because of the encapsulation of C₆₀ into PANI during aniline polymerization, which resulted from the charge‐transfer interactions between C₆₀ and aniline fragment in PANI. In addition, the resulting C₆₀/PANI nanocomposites synthesized from the low initial C₆₀/aniline molar ratio (less than 1:25) showed the homogenous morphology composed of fiber network structures, which has an electrical conductivity as high as 1.1 × 10^?4 S/cm. However, the C₆₀/PANI nanocomposites from the higher initial C₆₀/aniline molar ratio (more than 1:15) showed the nonuniformly distributed morphology, and the electrical conductivity was decreased to 3.5 × 10^?5 S/cm. Moreover, the C₆₀/PANI nanocomposites from the interfacial reaction showed a higher value of electrical conductivity than the mechanically mixed C₆₀/PANI blends with the same C₆₀ content, because of the more evenly distributed microstructures. FTIR, UV–vis, and CV data confirmed the presence of C₆₀ and the significant charge‐transfer interactions in the resultant nanocomposites, which was responsible for the morphology development of the C₆₀/PANI and the variation of the electrical conductivity. © 2012 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys, 2012     

Fabrication‐controlled morphology of poly(butylene succinate) nano‐microcellular foams by supercritical CO2

Poly(butylene succinate) urethane ionomer (PBSUIs) foams with nano‐microcellular morphology were fabricated using supercritical CO₂ (sc‐CO₂) at different parameters. Effect of urethane ionic group (UIG) content (ranged from 1% to 5%) on the rheology and crystallization of PBSUIs were evaluated by intrinsic, dynamic rheological, X‐ray diffraction, and differential scanning calorimetry measurements. The results show that the complex viscosity of PBSUIs vastly improved, while their intrinsic viscosity and crystallinity decreased. They also evidenced that CO₂ promoted the formation of crystallites in the amorphous and increased the X_c of PBSU and PBSUIs foams. Scanning electron microscope was employed to explore the influences of UIG content and foaming parameters on the morphologies of PBSUIs microcellular foams, and it revealed that UIG content was the dominated factor. The cell size and cell densities of PBSUIs microcellular foams were smaller than 5.0 micrometers and higher than 1.5 × 10¹⁰ cells/cm³, respectively, even foamed at diverse variations of foam temperature and pressure. Interestingly, PBSUIs with 3% and 5% UIG content achieved microcellular foams in nano‐cells, high‐stretched elliptical shape. The mechanism was ascribed that these PBSUIs with high melt viscosities could retard the CO₂ bubbles to merge during the foam process and induce the cells to stretch and orient in depressururization direction. This study proposed a novel method for fabricating PBS nano‐microcellular foams.