A study on methanol steam reforming to CO2 and H2 over the La2CuO4 nanofiber catalyst

The La₂CuO₄ crystal nanofibers were prepared by using single-walled carbon nanotubes as templates under mild hydrothermal conditions. The steam reforming of methanol (SRM) to CO₂ and H₂ over such nanofiber catalysts was studied. At the low temperature of 150 °C and steam/methanol=1.3, methanol was completely (100%, 13.8 g/h g catalyst) converted to hydrogen and CO₂ without the generation of CO. Within the 60 h catalyst lifespan test, methanol conversion was maintained at 98.6% (13.6 g/h g catalyst) and with 100% CO₂ selectivity. In the meantime, for distinguishing the advantage of nanoscale catalyst, the La₂CuO₄ bulk powder was prepared and tested for the SRM reaction for comparison. Compared with the La₂CuO₄ nanofiber, the bulk powder La₂CuO₄ showed worse catalytic activity for the SRM reaction. The 100% conversion of methanol was achieved at the temperature of 400 °C, with the products being H₂ and CO₂ together with CO. The catalytic activity in terms of methanol conversion dropped to 88.7% (12.2 g/h g catalyst) in 60 h. The reduction temperature for nanofiber La₂CuO₄ was much lower than that for the La₂CuO₄ bulk powder. The nanofibers were of higher specific surface area (105.0 m²/g), metal copper area and copper dispersion. The in situ FTIR and EPR experiments were employed to study the catalysts and catalytic process. In the nanofiber catalyst, there were oxygen vacancies. H₂-reduction resulted in the generation of trapped electrons [e] on the vacancy sites. Over the nanofiber catalyst, the intermediate H₂CO/HCO was stable and was reformed to CO₂ and H₂ by steam rather than being decomposed directly to CO and H₂. Over the bulk counterpart, apart from the direct decomposition of H₂CO/HCO to CO and H₂, the intermediate H₂COO might go through two decomposition ways: H₂COO=CO+H₂O and H₂COO=CO₂+H₂.     

The direct decomposition of NO over the La2CuO4 nanofiber catalyst

The NO catalytic direct decomposition was studied over La₂CuO₄ nanofibers, which were synthesized by using single walled carbon nanotubes (CNTs) as templates under hydrothermal condition. The composition and BET specific surface area of the La₂CuO₄ nanofiber were La₂Cu_0.88²⁺Cu_0.12⁺O_3.94 and 105.0 m²/g, respectively. 100% NO conversion (turnover frequency-(TOF): 0.17 g_NO/g_catalyst s) was obtained over such nanofiber catalyst at temperatures above 300 °C with the products being only N₂ and O₂. In 60 h on stream testing, either at 300 °C or at 800 °C, the nanofiber catalyst still showed high NO conversion efficiency (at 300 °C, 98%, TOF: 0.17 g_NO/g_catalyst s; at 800 °C, 96%, TOF: 0.16 g_NO/g_catalyst s). The O₂ and NO temperature programmed desorption (TPD) results indicated that the desorption of oxygen over the nanofibers occurred at 80-190 and 720-900 °C; while NO desorption happened at temperatures of 210-330 °C. NO and O₂ did not competitively adsorb on the nanofiber catalyst. For outstanding the advantage of the nanostate catalyst, the usual La₂CuO₄ bulk powder was also prepared and studied for comparison.     

Synthesis of titanate, TiO2 (B), and anatase TiO2 nanofibers from natural rutile sand

Titanate nanofibers were synthesized by hydrothermal method (150 °C for 72 h) using natural rutile sand as the starting materials. TiO₂ (B) and anatase TiO₂ (high crystallinity) nanofibers with the diameters of 20-100 nm and the lengths of 10-100 μm were obtained by calcined titanate nanofibers for 4 h at 400 and 700 °C (in air), respectively. The samples characterized by XRD, SEM, TEM, SAED, HRTEM, and BET surface area. This synthesis method provides a simple route to fabricate one-dimensional nanostructured TiO₂ from low cost material.     

La0.6Sr1.4MnO4 layered perovskite anode material for intermediate temperature solid oxide fuel cells

La_0.6Sr_1.4MnO₄ (LSMO₄) layered perovskite with K₂NiF₄ structure was prepared and evaluated as anode material for La_0.8Sr_0.2Ga_0.83Mg_0.17O_3 − δ (LSGM) electrolyte supported intermediate temperature solid oxide fuel cells (IT-SOFCs). X-ray diffraction results show that LSMO₄ is redox stability. Thermal expansion coefficient of LSMO₄ is close to that of LSGM electrolyte. By adopting LSMO₄ as anode and La_0.6Sr_0.4Co_0.8Fe_0.2O₃ (LSCF) as cathode, maxium power densities of 146.6, 110.9 mW cm^− 2 with H₂ fuel at 850, 800 °C and 47.3 mW cm^− 2 with CH₄ fuel at 800 °C were obtained, respectively. Further, the cell demonstrated a reasonably stable performance under 180 mA cm^− 2 for over 40 h with H₂ fuel at 800 °C.     

Hydrothermal synthesis, characterization, and photocatalytic properties of Zn2SnO4

Nanosized Zn₂SnO₄ (ZTO) particles were successfully synthesized by a simple hydrothermal process in water/ethylene glycol mixed solution using amines (ethylamine, n-butylamine, n-hexylamine, and n-octylamine) as mineralizer. The products were characterized by X-ray diffractions (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and N₂ adsorption. The results indicated that the hydrothermal conditions, such as alkaline concentration (n-butylamine), reaction temperature, solvent composition, and the kind of amines, had an important influence on the composition, crystallinity, and morphology of the product. The as-synthesized ZTO samples exhibited high activities and durabilities for photodegradation of methyl orange and the activities were mainly affected by the crystallinities of the samples. A hexagonal-shaped ZTO (H-ZTO) sample was prepared in 0.53 M of n-butylamine solution at 180 °C for 20 h and its optical properties were characterized by UV-Vis diffuse reflectance and Photoluminescence (PL) spectra. Furthermore, the photocatalytic H₂ evolution reaction from ethanol aqueous solution over H-ZTO was also investigated.     

Direct syntheses of Lan+1NinO3n+1 phases (n=1, 2, 3 and ∞) from nanosized co-crystallites

A new direct route for the “bottom up” syntheses of phases in the La_n+1Ni_nO_3n+1 series (n=1, 2, 3 and ∞) has been achieved via single-step heat treatments of nanosized co-crystallized precursors. The co-crystallized precursors were prepared using a continuous hydrothermal flow synthesis system that uses a superheated water flow at ca. 400 °C and 24.1 MPa to produce nanoparticulate slurries. Overall, a significant reduction in time and number of steps for the syntheses of La₃Ni₂O₇ and La₄Ni₃O₁₀ was achieved compared with more conventional synthesis methods, which typically require multiple homogenization and reheating steps over several days.     

Effect of sintering on the ionic conductivity of garnet-related structure Li5La3Nb2O12 and In- and K-doped Li5La3Nb2O12

Garnet-structure related metal oxides with the nominal chemical composition of Li₅La₃Nb₂O₁₂, In-substituted Li_5.5La₃Nb_1.75In_0.25O₁₂ and K-substituted Li_5.5La_2.75K_0.25Nb₂O₁₂ were prepared by solid-state reactions at 900, 950, and 1000 °C using appropriate amounts of corresponding metal oxides, nitrates and carbonates. The powder XRD data reveal that the In- and K-doped compounds are isostructural with the parent compound Li₅La₃Nb₂O₁₂. The variation in the cubic lattice parameter was found to change with the size of the dopant ions, for example, substitution of larger In³⁺(r_CN6: 0.79 Å) for smaller Nb⁵⁺ (r_CN6: 0.64 Å) shows an increase in the lattice parameter from 12.8005(9) to 12.826(1) Å at 1000 °C. Samples prepared at higher temperatures (950, 1000 °C) show mainly bulk lithium ion conductivity in contrast to those synthesized at lower temperatures (900 °C). The activation energies for the ionic conductivities are comparable for all samples. Partial substitution of K⁺ for La³⁺ and In³⁺ for Nb⁵⁺ in Li₅La₃Nb₂O₁₂ exhibits slightly higher ionic conductivity than that of the parent compound over the investigated temperature regime 25-300 °C. Among the compounds investigated, the In-substituted Li_5.5La₃Nb_1.75In_0.25O₁₂ exhibits the highest bulk lithium ion conductivity of 1.8×10⁻⁴ S/cm at 50 °C with an activation energy of 0.51 eV. The diffusivity (“component diffusion coefficient”) obtained from the AC conductivity and powder XRD data falls in the range 10⁻¹⁰-10⁻⁷ cm²/s over the temperature regime 50-200 °C, which is extraordinarily high and comparable with liquids. Substitution of Al, Co, and Ni for Nb in Li₅La₃Nb₂O₁₂ was found to be unsuccessful under the investigated conditions.     

Compatibility evaluation between La2Mo2O9 fast oxide-ion conductor and Ni-based materials

The chemical reactivity of La₂NiO_4+δ and nickel metal or nickel oxide with fast oxide-ion conductor La₂Mo₂O₉ is investigated in the annealing temperature range between 600 and 1000 °C, using room temperature X-ray powder diffraction. Within the La₂NiO_4+δ/La₂Mo₂O₉ system, subsequent reaction is evidenced at relatively low annealing temperature (600 °C), with formation of La₂MoO₆ and NiO. The reaction is complete at 1000 °C. At reverse, no reaction occurs between Ni or NiO and La₂Mo₂O₉ up to 1000 °C. Together with a previous work [G. Corbel, S. Mestiri, P. Lacorre, Solid State Sci. 7 (2005) 1216], the current study shows that Ni-CGO cermets might be chemically and mechanically compatible anode materials to work with LAMOX electrolytes in solid oxide fuel cells.     

Preparation of Mn2O3 and Mn3O4 nanofibers via an electrospinning technique

Thin PVA/manganese acetate composite fibers were prepared by using sol-gel processing and electrospinning technique. After calcinations of the above precursor fibers, Mn₂O₃ and Mn₃O₄ nanofibers with a diameter of 50-200 nm could be successfully obtained. The fibers were characterized by TG-DTA, Scanning electron microscopy, FT-IR, WAXD, respectively. The results showed that the crystalline phase and morphology of nanofibers were largely influenced by the calcination temperature.     

Hydrothermal preparation and visible-light photocatalytic activity of Bi2WO6 powders

Bi₂WO₆ powder photocatalyst was prepared using Bi(NO₃)₃ and Na₂WO₄ as raw materials by a simple hydrothermal method at 150 °C for 24 h, and then calcined at 300, 400, 500, 600 and 700 °C for 2 h, respectively. The as-prepared samples were characterized with UV-visible diffuse reflectance spectra, fourier transform infrared spectra (FTIR), X-ray diffraction (XRD), scanning electron microscopy (SEM) and N₂ adsorption-desorption measurement. The photocatalytic activity of the samples was evaluated using the photocatalytic oxidation of formaldehyde at room temperature under visible light irradiation. It was found that post-treatment temperature obviously influenced the visible-light photocatalytic activity and physical properties of Bi₂WO₆ powders. At 500 °C, Bi₂WO₆ powder photocatalyst showed the highest visible-light photocatalytic activity due to the samples with good crystallization and high BET surface area.     

K2Mo4O13 phases prepared by hydrothermal synthesis

Hydrothermal synthesis in the K-Mo oxide system was investigated as a function of the pH of the reaction medium. Four compounds were formed, including two K₂Mo₄O₁₃ phases. One is a new low-temperature polymorph, which crystallizes in the orthorhombic, space group Pbca, with Z=8 and unit cell dimensions a=7.544(1) Å, b=15.394(2) Å, c=18.568(3) Å. The other is the known triclinic K₂Mo₄O₁₃, whose structure was re-determined from single crystal data; its cell parameters were determined as a=7.976(2) Å, b=8.345(2) Å, c=10.017(2) Å, α=107.104(3)°, β=102.885(3)°, γ=109.760(3)°, which are the standard settings of the crystal lattice. The orthorhombic phase converts endothermically into triclinic phase at ca. 730 K with a heat of transition of 8.31 kJ/mol.     

Preparation of a new pyrochlore-type compound Na0.32Bi1.68Ti2O6.46(OH)0.44 by hydrothermal reaction

A new pyrochlore-type Na_0.32Bi_1.68Ti₂O_6.46(OH)_0.44 with the cubic cell of a=10.339(5) Å was prepared by hydrothermal reaction using TiO₂ (anatase) and Bi₂O₃ in NaOH solution. This compound was obtained when the molar ratio of NaOH/TiO₂ was above 2 and the reaction temperature was above 240 °C. The TG-curve of as-prepared sample showed a mass loss of 0.8 mass% which was caused by release of OH group. This compound decomposed to a pyrochlore-type compound and a layered-type Na_0.5Bi_4.5Ti₄O₁₅ above 800 °C. The optical band gap of Na_0.32Bi_1.68Ti₂O_6.46(OH)_0.44 was estimated to be 2.5 eV.     

Crystal chemistry and crystallography of the SrR2CuO5 (R=lanthanides) phases

The crystal chemistry and crystallography of the compounds SrR₂CuO₅ (Sr-121, R=lanthanides) were investigated using the powder X-ray Rietveld refinement technique. Among the 11 compositions studied, only R=Dy and Ho formed the stable SrR₂CuO₅ phase. SrR₂CuO₅ was found to be isostructural with the “green phase”, BaR₂CuO₅. The basic structure is orthorhombic with space group Pnma. The lattice parameters for SrDyCuO₅ are a=12.08080(6) Å, b=5.60421(2) Å, c=7.12971(3) Å, V=482.705(4) Å³, and Z=8; and for the Ho analog are a=12.03727(12) Å, b=5.58947(7) Å, c=7.10169(7) Å, V=477.816(9) Å³, and Z=8. In the SrR₂CuO₅ structure, each R is surrounded by seven oxygen atoms, forming a monocapped trigonal prism (RO₇). The isolated CuO₅ group forms a distorted square pyramid. Consecutive layers of prisms are stacked in the b-direction. Bond valence calculations imply that residual strain is largely responsible for the narrow stability of the SrR₂CuO₅ phases with R=Dy and Ho only. X-ray powder reference diffraction patterns for SrDy₂CuO₅ and SrHo₂CuO₅ were determined.     

Preparation and performances of nanosized Ta2O5 powder photocatalyst

Nanosized-Ta₂O₅ powder photocatalyst was successfully synthesized by using sol-gel method via TaCl₅ butanol solution as a precursor. Ta₂O₅ species can be formed under 500 °C via the decomposition of the precursor. The crystalline phase of Ta₂O₅ powder photocatalyst can be obtained after being calcined above 600 °C for 4 h. The crystal size and particle size of Ta₂O₅ powder photocatalyst was about 50 nm. A good photocatalytic performance for the degradation of gaseous formaldehyde was obtained for the nanosized-Ta₂O₅ powder. The Ta₂O₅ powder formed at 700 °C for 4 h and at 650 °C for 12 h showed the best performance. The calcination temperature and time play an important role in the crystallization and photocatalytical performance of nanosized-Ta₂O₅ powder.     

Ion-beam irradiation of lanthanum compounds in the systems La2O3-Al2O3 and La2O3-TiO2

Thin crystals of La₂O₃, LaAlO₃, La_2/3TiO₃, La₂TiO₅, and La₂Ti₂O₇ have been irradiated in situ using 1 MeV Kr²⁺ ions at the Intermediate Voltage Electron Microscope-Tandem User Facility (IVEM-Tandem), Argonne National Laboratory (ANL). We observed that La₂O₃ remained crystalline to a fluence greater than 3.1×10¹⁶ ions cm⁻² at a temperature of 50 K. The four binary oxide compounds in the two systems were observed through the crystalline-amorphous transition as a function of ion fluence and temperature. Results from the ion irradiations give critical temperatures for amorphisation (T_c) of 647 K for LaAlO₃, 840 K for La₂Ti₂O₇, 865 K for La_2/3TiO₃, and 1027 K for La₂TiO₅. The T_c values observed in this study, together with previous data for Al₂O₃ and TiO₂, are discussed with reference to the melting points for the La₂O₃-Al₂O₃ and La₂O₃-TiO₂ systems and the different local environments within the four crystal structures. Results suggest that there is an observable inverse correlation between T_c and melting temperature (T_m) in the two systems. More complex relationships exist between T_c and crystal structure, with the stoichiometric perovskite LaAlO₃ being the most resistant to amorphisation.     

La3Ru8B6 and Y3Os8B6, new members of a homologous series R(A)nM3n−1B2n

Two new compounds, La₃Ru₈B₆ and Y₃Os₈B₆, were synthesized by arc melting the elements. Their structural characterization was carried out at room temperature on as-cast samples by using X-ray diffractometry. According to X-ray single-crystal diffraction results these borides crystallize in Fmmm space group (no. 69), Z=4, a=5.5607(1) Å, b=9.8035(3) Å, c=17.5524(4) Å, ρ=8.956 Mg/m³, μ=25.23 mm⁻¹ for La₃Ru₈B₆ and a=5.4792(2) Å, b=9.5139(4) Å, c=17.6972(8) Å, ρ=13.343 Mg/m³, μ=128.23 mm⁻¹ for Y₃Os₈B₆. The crystal structure of La₃Ru₈B₆ was confirmed from Rietveld refinement of X-ray powder diffraction data. Both La₃Ru₈B₆ and Y₃Os₈B₆ compounds are isotypic with the Ca₃Rh₈B₆ compound and their structures are built up from CeCo₃B₂-type and CeAl₂Ga₂-type structural fragments taken in ratio 2:1. They are the members of structural series R(A)_nM_3n−1B_2n with n=3 (R is the rare earth metal, A the alkaline earth metal, and M the transition metal). Structural and atomic parameters were also obtained for La_0.94Ru₃B₂ compound from Rietveld refinement (CeCo₃B₂-type structure, P6/mmm space group (no. 191), a=5.5835(9) Å, c=3.0278(6) Å).     

Synthesis, crystal structure, infrared and Raman spectra of Sr4Cu3(AsO4)2(AsO3OH)4·3H2O and Ba2Cu4(AsO4)2(AsO3OH)3

The two new compounds, Sr₄Cu₃(AsO₄)₂(AsO₃OH)₄·3H₂O (1) and Ba₂Cu₄(AsO₄)₂(AsO₃OH)₃(2), were synthesized under hydrothermal conditions. They represent previously unknown structure types and are the first compounds synthesized in the systems SrO/BaO-CuO-As₂O₅-H₂O. Their crystal structures were determined by single-crystal X-ray diffraction [space group C2/c, a=18.536(4) Å, b=5.179(1) Å, c=24.898(5) Å, β=93.67(3)°, V=2344.0(8) Å³, Z=4 for 1; space group P4₂/n, a=7.775(1) Å, c=13.698(3) Å, V=828.1(2) Å³, Z=2 for 2]. The crystal structure of 1 is related to a group of compounds formed by Cu²⁺-(XO₄)³⁻ layers (X=P⁵⁺, As⁵⁺) linked by M cations (M=alkali, alkaline earth, Pb²⁺, or Ag⁺) and partly by hydrogen bonds. In 1, worth mentioning is the very short hydrogen bond length, D···A=2.477(3) Å. It is one of the examples of extremely short hydrogen bonds, where the donor and acceptor are crystallographically different. Compound 2 represents a layered structure consisting of Cu₂O₈ centrosymmetric dimers crosslinked by As1φ₄ tetrahedra, where φ is O or OH, which are interconnected by Ba, As2 and hydrogen bonds to form a three-dimensional network. The layers are formed by Cu₂O₈ centrosymmetric dimers of CuO₅ edge-sharing polyhedra, crosslinked by As1O₄ tetrahedra. Vibrational spectra (FTIR and Raman) of both compounds are described. The spectroscopic manifestation of the very short hydrogen bond in 1, and ABC-like spectra in 2 were discussed.     

Synthesis of nano-sized crystalline oxide ion conducting fluorite-type Y2O3-doped CeO2 using perovskite-like BaCe0.9Y0.1O2.95 (BCY) and study of CO2 capture properties of BCY

Formation of nano-sized Y₂O₃-doped CeO₂ (YCO) was observed in the chemical reaction between proton conducting Y₂O₃-doped BaCeO₃ (BCY) and CO₂ in the temperature range 700-1000 °C, which is generally prepared by wet-chemical methods that include sol-gel, hydrothermal, polymerization, combustion, and precipitation reactions. BCY can capture CO₂ of 0.13 g per ceramic gram at 700 °C, which is comparable to that of the well-known Li₂ZrO₃ (0.15 g per ceramic gram at 600 °C). Powder X-ray diffraction (PXRD), energy dispersive X-ray analysis (EDX), laser particle size analysis (LPSA), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and ac impedance spectroscopy were employed to characterize the reaction product obtained from reaction between BCY and CO₂ and subsequent acid washing. PXRD study reveals presence of fluorite-like CeO₂ (a=5.410 (1) Å) structure and BaCO₃ in reaction products. TEM investigation of the acid washed product showed the formation of nano-sized material with particle sizes of about 50 nm. The electrical conductivity of acid washed product (YCO) in air was found to be about an order higher than the undoped CeO₂ reported in the literature.     

Syntheses of TiO2(B) nanowires and TiO2 anatase nanowires by hydrothermal and post-heat treatments

TiO₂(B) nanowires and TiO₂ anatase nanowires were synthesized by the hydrothermal processing in 10 M NaOH aq. at 150 °C followed by the post-heat treatment at 300-800 °C. As-synthesized Na-free titanate nanowires (prepared by the hydrothermal treatment and repeated ion exchanging by HCl (aq.) were transformed into TiO₂(B) structure with maintaining 1-D morphology at 300-500 °C, and further transformed into anatase structure at 600-800 °C with keeping 1-D shape. At 900 °C, they transformed into rod-shaped rutile grains. Microstructure of these 1-D TiO₂ nanomaterials is reported.     

Structural characterization and photocatalytic activity of hollow binary ZrO2/TiO2 oxide fibers

The formation of hollow binary ZrO₂/TiO₂ oxide fibers using mixed precursor solutions was achieved by activated carbon fibers templating technique combined with solvothermal process. The samples were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), N₂ adsorption, X-ray photoelectron spectroscopy (XPS), UV-vis, and infrared (IR) spectroscopy. The binary oxide system shows the anatase-type TiO₂ and tetragonal phase of ZrO₂, and the introduction of ZrO₂ notably inhibits the growth of TiO₂ nanocrystallites. Although calcined at 575 °C, all hollow ZrO₂/TiO₂ fibers exhibit higher surface areas (>113 m²/g) than pure TiO₂ hollow fibers. The Pyridine adsorption on ZrO₂/TiO₂ sample indicates the presence of stronger surface acid sites. Such properties bring about that the binary oxide system possesses higher efficiency and durable activity stability for photodegradation of gaseous ethylene and trichloromethane than P25 TiO₂. In addition, the macroscopic felt form for the resulting materials is more beneficial for practical applications than traditional catalysts forms.