Impedance spectroscopy analysis of AlGaN/GaN HFET structures

For HFET application a series of samples with 30 nm Al_xGa_1−xN (x=0.02–0.4) layers deposited at 1040°C onto optimised 2 μm thick undoped GaN buffers were fabricated. The Al_xGa_1−xN/GaN heterostructures were grown on c-plane sapphire in an atmospheric pressure, single wafer, vertical flow MOVPE system. Electrical properties of the Al_xGa_1−xN/GaN heterostructures and thick undoped GaN layers were evaluated by impedance spectroscopy method performed in the range of 80 Hz–10 MHz with an HP 4192A impedance meter using a mercury probe. The carrier concentration distribution through the layer thickness and the sheet carrier concentration were evaluated. A non-destructive, characterisation technique for verification of device heterostucture quality from the measured C–V and G–V versus frequency characteristics of the heterostructure is proposed.     

Luminescence studies of defects and piezoelectric fields in InGaN/GaN single quantum wells

Transmission electron microscopy (TEM), cathodoluminescence in the scanning electron microscope (SEM-CL) and photoluminescence (PL) studies were performed on a 30 nm GaN/2 nm In_0.28Ga _0.72N/2 μm GaN/(0 0 0 1) sapphire single quantum well (SQW) sample. SEM-CL was performed at low temperatures ≈8 K, and at an optimum accelerating voltage, around 4–6 kV to maximise the quantum well (QW) luminescence. The CL in the vicinity of characteristic “V-shaped” pits was investigated. The near band edge (BE) luminescence maps from the GaN showed bright rings inside the boundaries of the pits while the QW luminescence maps showed pits to be regions of low intensity. These observations are consistent with TEM observations showing the absence of QW material in the pits. Variations in both the BE and QW maps in the regions between the pits are ascribed to threading edge dislocations. The CL and PL QW luminescence was observed to blue-shift and broaden with increasing excitation intensity. This was accompanied by decreasing spatial resolution in the CL QW maps implying an increasing carrier diffusion length in the InGaN layer. The reasons for this behaviour are discussed. It is argued that screening of the piezoelectric field in the material may account for these observations.     

Emission studies of InGaN layers and LEDs grown by plasma-assisted MBE

We prepared InGaN layers on GaN/sapphire substrates using rf-MBE. Photoluminescence (PL) from these layers, grown at different temperatures T_S, shows that there is a strong tendency of GaN to form a separate phase as T_S is increased from 600°C to 650°C. Concomitant with the phase separation, the PL from the InGaN phase broadens, which indicates that indium composition in this phase becomes increasingly non-uniform. Indium compositions measured by Rutherford backscattering (RBS) are consistent with these results. We also observed an increase in PL intensity for InGaN layers grown at higher temperatures. In this paper, we also report on preparing a top-contact InGaN/GaN light emitting diode. The device was operated at 447 nm and had the emission line width of 37 nm with no observable impurity related features. The turn-on voltage was 3.0 V. The output power was 20 μW at 60 mA drive current.     

The effect of the AlxGa1−xN/AIN buffer layer on the properties of GaN/Si(1 1 1) film grown by NH3-MBE

We describe the growth of GaN on Si(1 1 1) substrates with Al_xGa_1−xN/AlN buffer layer by ammonia gas source molecular beam epitaxy (NH₃-GSMBE). The influence of the AlN and Al_xGa_1−xN buffer layer thickness and the Al composition on the crack density of GaN has been investigated. It is found that the optimum thickness is 120 and 250 nm for AlN and Al_xGa_1−xN layers, respectively. The optimum Al composition is between 0.3<x<0.6.     

Structure and thermal stability of MOCVD ZrO2 films on Si (1 0 0)

The structure and thermal stability of ZrO₂ films grown on Si (1 0 0) substrates by metalorganic chemical vapor deposition have been studied by high-resolution transmission electron microscopy, selected area electron diffraction and X-ray energy dispersive spectroscopy. As-deposited films consist of tetragonal ZrO₂ nanocrystallites and an amorphous Zr silicate interfacial layer. After annealing at 850°C, some monoclinic phase is formed, and the grain size is increased. Annealing a 6 nm thick film at 850°C in O₂ revealed that the growth of the interfacial layer is at the expense of the ZrO₂ layer. In a 3.0 nm thick Zr silicate interfacial layer, there is a 0.9 nm Zr-free SiO₂ region right above the Si substrate. These observations suggest that oxygen reacted with the Si substrate to grow SiO₂, and SiO₂ reacted with ZrO₂ to form a Zr silicate interfacial layer during the deposition and annealing. Oxygen diffusion through the tetragonal ZrO₂ phase was found to be relatively easier than through the monoclinic phase.     

Indium content determination related with structural and optical properties of InGaN layers

We studied the structural and optical properties of a set of nominally undoped epitaxial single layers of In_xGa_1−xN (0<x0.2) grown by MOCVD on top of GaN/Al₂O₃ substrates. A comparison of composition values obtained for thin (tens of nanometers) and thick (≈0.5 μm) layers by different analytical methods was performed. It is shown that the indium mole fraction determined by X-ray diffraction, measuring only one lattice parameter strongly depend on the assumptions made about strain, usually full relaxation or pseudomorphic growth. The results attained under such approximations are compared with the value of indium content derived from Rutherford backscattering spectrometry (RBS). It is shown that significant inaccuracies may arise when strain in In_xGa_1−xN/GaN heterostructures is not properly taken into account. Interpretation of these findings, together with the different criteria used to define the optical bandgap of In_xGa_1−xN layers, may explain the wide dispersion of bowing parameters found in the literature. Our results indicate a linear, E_g(x)=3.42−3.86x eV (x0.2), “anomalous” dependence of the optical bandgap at room temperature with In content for In_xGa_1−xN single layers.     

The transition from As-doped GaN, showing blue emission, to GaNAs alloys in films grown by molecular beam epitaxy

We have studied the transition from As-doped GaN showing strong blue emission (2.6 eV) at room temperature to the formation of GaN_1−xAs_x alloys for films grown by plasma-assisted molecular beam epitaxy. We have demonstrated that with increasing N-to-Ga ratio there is first an increase in the intensity of blue emission at about 2.6 eV and then a transition to the growth of GaN_1−xAs_x alloy films. We present a model based on thermodynamic considerations, which can explain how this might occur.     

Microstructure and ferroelectric properties of BaTiO3 films on LaNiO3 buffer layers by rf sputtering

We have fabricated LaNiO₃ and BaTiO₃ films using the rf sputtering method. The LaNiO₃ were deposited on Si substrates, demonstrating a (1 0 0) highly oriented structure and nanocrystalline characteristic with a grain size of 30 nm. The BaTiO₃ thin films were deposited on the LaNiO₃ buffer layers, and have exhibited a (1 0 0) texture with a thickness of 400 nm. A smooth interface is obtained between the LaNiO₃ bottom electrode and the BaTiO₃ film from cross-section observations by scanning electron microscopy. The bi-layer films show a dense and column microstructure with a grain size of 60 nm. Ferroelectric characterizations have been obtained for the BaTiO₃ films. The remnant polarization and coercive field are 2.1 μC/cm² and 45 kV/cm, respectively. The leak current measurements have shown a good insulating property.     

Growth and properties of Pb[(Zn1/3Nb2/3)0.91Ti0.09]O3 single crystals directly from melt

Pb[(Zn_1/3Nb_2/3)_0.91Ti_0.09]O₃ (PZNT91/9) single crystals were grown by a modified Bridgman method directly from melt using an allomeric Pb[(Mg_1/3Nb_2/3)_0.69Ti_0.31]O₃ (PMNT69/31) single crystal as a seed. X-ray diffraction (XRD) measurement confirmed that the as-grown PZNT91/9 single crystals are of pure perovskite structure. Electrical properties and thermal stabilization of PZNT91/9 crystals grown directly from melt exhibit different characters from those of PZNT91/9 crystals grown from flux, although segregation and the variation of chemical composition are not seriously confirmed by X-ray fluorescence analysis (XPS). The [0 0 1]-oriented PZNT91/9 crystals cut from the middle part of the as-grown crystal boules exhibit broad dielectric-response peaks at around 105 °C, accompanied by apparent frequency dispersion. The values of piezoelectric constant d₃₃, remnant polarization P_r, and induced strain are about 1800–2200 pC/N, 38.8 μC/cm², and 0.3%, respectively, indicating that the quality of PZNT crystals grown directly from melt can be comparable to those of PZNT91/9 single crystals grown from flux. However, further work deserves attention to improve the dielectric properties of PZNT crystals grown directly from melt. Such unusual characterizations of dielectric properties of PZNT crystals grown directly from melt are considered as correlating with defects, microinhomogeneities, and polar regions.     

Study of group-III binary and ternary nitrides using X-ray absorption fine structure measurements

It is demonstrated that the NEXAFS spectra are a “fingerprint” of the symmetry and the composition of the binary nitrides GaN, AlN and InN, as well as of their ternary alloys In_0.16Ga_0.84N and Al_yGa_1−yN. From the angular dependence of the N-K-edge NEXAFS spectra, the hexagonal symmetry of the under study compounds is deduced and the (p_x, p_y) or p_z character of the final state is identified. The energy position of the absorption edge (E_abs) of the binary compounds GaN, AlN and InN is found to red-shift linearly with the atomic number of the cation. The E_abs of the Al_yGa_1−yN alloys takes values in between those corresponding to the parent compounds AlN and GaN. Contrary to that, the E_abs of In_0.16Ga_0.84N is red-shifted relative to that of GaN and InN, probably due to ordering and/or phase separation phenomena. The EXAFS analysis results reveal that the first nearest-neighbour shell around the N atom, which consists of Ga atoms, is distorted in both GaN and Al_xGa_1−xN for x<0.5.     

Reduction of threading dislocations in migration enhanced epitaxy grown GaN with N-polarity by use of AlN multiple interlayer

High quality GaN layer was obtained by insertion of high temperature grown AlN multiple intermediate layers with migration enhanced epitaxy method by the RF-plasma assisted molecular beam epitaxy on (0 0 01) sapphire substrates. The propagating behaviors of dislocations were studied, using a transmission electron microscope. The results show that the edge dislocations were filtered at the AlN/GaN interfaces. The bending propagation of threading dislocations in GaN above AlN interlayers was confirmed. Thereby, further reduction of dislocations was achieved. Dislocation density being reduced, the drastic increase of electron mobility to 668 cm²/V s was obtained at the carrier density of 9.5×10¹⁶ cm⁻³ in Si doped GaN layer.     

Absorption spectra of GaN: film characterization by Urbach spectral tail and the effect of electric field

The absorption tail of undoped and Si-doped GaN films was investigated at different temperatures and under applied electric field. It was found that the spectral dependence of logarithm of absorption coefficient is combined of two linear functions: ln[(hν)]=C₁+(hν−E_g)/U₁ for hν<3.42 eV and ln[(hν)]=C₂+(hν−E_g)/U₂ for 3.44<hν<3.5 eV with Urbach energies U₁=400–470 meV and U₂=10–20 meV. The influence of an electric field effect on the absorption spectra follows the Dow and Redfield theory. It was shown that the intrinsic electric field about 10⁵ V/cm exists in our samples. The implemented analysis of the absorption spectra gives the qualitative method of film characterization.     

Growth of NaBi(WO4)2 crystal by modified-Bridgman method

NaBi(WO₄)₂ (NBW) crystals have been grown for the first time by modified-Bridgman method. Influences of some factors on the crystal growth process are discussed. X-ray powder diffraction experiments show that the unit cell parameters of NBW crystal are a=b=0.5284 nm, c=1.1517 nm, and V=0.3215 nm³. The differential thermal analysis shows that the NBW crystal melts at 923°C.     

Chemical mapping of InGaN MQWs

High power LEDs fabricated from InGaN/GaN layers have received much research interest. Hence, in this paper we identify structural and chemical defects resulting from the epitaxial growth of these layers, which directly effect the performance of the device. TEM, annular dark field imaging (ADF), energy filtered TEM (EFTEM) and X-ray mapping were used to study multiple quantum wells structures capped with a p-type GaN layer. TEM and ADF studies of the samples show a number of V-defects which are roughly 100–200 nm apart along the MQW. Each V-defect incorporates a pure edge ( ) dislocation, which runs through the apex of the V-defect up to the free surface. These V-defects contain GaN with no InGaN layers, suggesting that the capping layer has filled in the open V-defects.     

CrO2 (1 0 0) and TiO2 (1 0 0) film heteroepitaxy on a BaF2 (1 1 1)/Si (1 0 0) substrate

Multi-domained heteroepitaxial rutile-phase TiO₂ (1 0 0)-oriented films were grown on Si (1 0 0) substrates by using a 30-nm-thick BaF₂ (1 1 1) buffer layer at the TiO₂–Si interface. The 50 nm TiO₂ films were grown by electron cyclotron resonance oxygen plasma-assisted electron beam evaporation of a titanium source, and the growth temperature was varied from 300 to 600 °C. At an optimal temperature of 500 °C, X-ray diffraction measurements show that rutile phase TiO₂ films are produced. Pole figure analysis indicates that the TiO₂ layer follows the symmetry of the BaF₂ surface mesh, and consists of six (1 0 0)-oriented domains separated by 30° in-plane rotations about the TiO₂ [1 0 0] axis. The in-plane alignment between the TiO₂ and BaF₂ films is oriented as [0 0 1] TiO₂ || BaF₂ or [0 0 1] TiO₂ || BaF₂ . Rocking curve and STM analyses suggest that the TiO₂ films are more finely grained than the BaF₂ film. STM imaging also reveals that the TiO₂ surface has morphological features consistent with the BaF₂ surface mesh symmetry. One of the optimally grown TiO₂ (1 0 0) films was used to template a CrO₂ (1 0 0) film which was grown via chemical vapor deposition. Point contact Andreev reflection measurements indicate that the CrO₂ film was approximately 70% spin polarized.     

Study on the Ce substitution effects of BiFeO3 films on ITO/glass substrates

Ce substituted Bi_1−xCe_xFeO₃ (BCFO) films with x=0–0.15 were deposited on indium tin oxide (ITO)/glass substrates by sol–gel process annealed at 500 °C. Rhombohedral phase was confirmed by XRD study and no impure phases were observed till x=0.15. Substantially enhanced ferroelectricity was observed at room temperature due to the substitution of Ce. In the films with x=0.05 and 0.10, the double remnant polarization are 75.5 and 57.7 μC/cm² at an applied field 860 kV/cm. Moreover, the breakdown field was enhanced in the films with Ce substitution.     

Growth of Na modified potassium lithium niobate crystal by the Czochralski method

Transparent Na modified potassium lithium niobate (Na_0.23K_2.60Li_1.82Nb_5.35O_15.70; NKLN) crystal was successively grown by the Czochralski method using RF induction heating from melt composition Na₂O:K₂O : Li₂O:Nb₂O₅=2:30:25:43 mol%. NKLN crystal showed a tetragonal tungsten bronze structure with lattice constants a=12.5446±0.0010 Å and c=4.0129±0.0005 Å at room temperature. The dielectric constant along the c-axis ε₃₃ showed a sharp maximum around 480 °C. Optical transmission edge was 370 nm and optical transmission spectra showed no absorption at wavelengths ranging from 380 to 800 nm. The structural and optical properties of NKLN were similar to those of the near stoichiometric KLN crystals. We believe that the growth of NKLN by the Czochralski method has an advantage for a large size and high-quality crystal.     

First III–V-nitride-based violet laser diodes

InGaN multi-quantum-well (MQW) structure laser diodes (LDs) were grown by metalorganic chemical vapor deposition on a sapphire substrate with (11 0) orientation (A face). The mirror facet for a laser cavity was formed by cleaving the substrate along the (1 02) orientation (R-face). The structure of the LDs was an InGaN MQW/GaN/AlGaN separate confinement heterostructure (SCH). As an active layer, the InGaN MQW structure was used. The InGaN MQW LDs showed strong stimulated emission at a wavelength of 415.3 nm under pulsed current injection above 360 mA at room temperature. The laser threshold current density was 6 kA/cm². As a maximum characteristic temperature of the threshold current, T₀ = 313 K was obtained for the InGaN MQW/GaN/AlGaN SCH LDs.     

Defect reduction in GaN epilayers and HFET structures grown on (0 0 0 1)sapphire by ammonia MBE

The quality of GaN epilayers grown by molecular beam epitaxy on substrates such as sapphire and silicon carbide has improved considerably over the past few years and in fact now produces AlGaN/GaN HEMT devices with characteristics among the best reported for any growth technique. However, only recently has the bulk defect density of MBE grown GaN achieved levels comparable to that obtained by MOVPE and with a comparable level of electrical performance. In this paper, we report the ammonia-MBE growth of GaN epilayers and HFET structures on (0 0 0 1)sapphire. The effect of growth temperature on the defect density of single GaN layers and the effect of an insulating carbon doped layer on the defect density of an overgrown channel layer in the HFET structures is reported. The quality of the epilayers has been studied using Hall effect and the defect density using TEM, SEM and wet etching. The growth of an insulating carbon-doped buffer layer followed by an undoped GaN channel layer results in a defect density in the channel layer of 2×10⁸ cm⁻². Mobilities close to 490 cm²/Vs at a carrier density of 8×10¹⁶ cm⁻³ for a 0.4 μm thick channel layer has been observed. Growth temperature is one of the most critical parameters for achieving this low defect density both in the bulk layers and the FET structures. Photo-chemical wet etching has been used to reveal the defect structure in these layers.     

Properties of ZnO films grown on (0 0 0 1) sapphire substrate using H2O and N2O as O precursors by atmospheric pressure MOCVD

In this paper, we compare the properties of ZnO thin films (0 0 0 1) sapphire substrate using diethylzinc (DEZn) as the Zn precursor and deionized water (H₂O) and nitrous oxide (N₂O) as the O precursors, respectively in the main ZnO layer growth by atmospheric pressure metal–organic chemical vapor deposition (AP-MOCVD) technique. Surface morphology studied by atomic force microscopy (AFM) showed that the N₂O-grown ZnO film had a hexagonal columnar structure with about 8 μm grain diameter and the relatively rougher surface compared to that of H₂O-grown ZnO film. The full-widths at half-maximum (FWHMs) of the (0 0 0 2) and () ω-rocking curves of the N₂O-grown ZnO film by double-crystal X-ray diffractometry (DCXRD) measurement were 260 and 350 arcsec, respectively, indicating the smaller mosaicity and lower dislocation density of the film compared to H₂O-grown ZnO film. Compared to H₂O-grown ZnO film, the free exciton A (FX_A) and its three phonon replicas could be clearly observed, the donor-bound exciton A⁰X (I₁₀):3.353 eV dominated the 10 K photoluminescence (PL) spectrum of N₂O-grown ZnO film and the hydrogen-related donor-bound exciton D⁰X (I₄):3.363 eV was disappeared. The electron mobility (80 cm²/V s) of N₂O-grown ZnO film has been significantly improved by room temperature Hall measurement compared to that of H₂O-grown ZnO film.