Properties of ZnO films grown on (0 0 0 1) sapphire substrate using H2O and N2O as O precursors by atmospheric pressure MOCVD

In this paper, we compare the properties of ZnO thin films (0 0 0 1) sapphire substrate using diethylzinc (DEZn) as the Zn precursor and deionized water (H₂O) and nitrous oxide (N₂O) as the O precursors, respectively in the main ZnO layer growth by atmospheric pressure metal–organic chemical vapor deposition (AP-MOCVD) technique. Surface morphology studied by atomic force microscopy (AFM) showed that the N₂O-grown ZnO film had a hexagonal columnar structure with about 8 μm grain diameter and the relatively rougher surface compared to that of H₂O-grown ZnO film. The full-widths at half-maximum (FWHMs) of the (0 0 0 2) and () ω-rocking curves of the N₂O-grown ZnO film by double-crystal X-ray diffractometry (DCXRD) measurement were 260 and 350 arcsec, respectively, indicating the smaller mosaicity and lower dislocation density of the film compared to H₂O-grown ZnO film. Compared to H₂O-grown ZnO film, the free exciton A (FX_A) and its three phonon replicas could be clearly observed, the donor-bound exciton A⁰X (I₁₀):3.353 eV dominated the 10 K photoluminescence (PL) spectrum of N₂O-grown ZnO film and the hydrogen-related donor-bound exciton D⁰X (I₄):3.363 eV was disappeared. The electron mobility (80 cm²/V s) of N₂O-grown ZnO film has been significantly improved by room temperature Hall measurement compared to that of H₂O-grown ZnO film.