Dye-dependent studies on droplet pattern and electro-optic behaviour of polymer dispersed liquid crystal

In order to study the droplet pattern and electro-optic (EO) behaviour of polymer dispersed liquid crystal (PDLC) with the addition of dye, dichroic polymer dispersed liquid crystal (DPDLC) films were prepared using a nematic liquid crystal (NLC), photo-curable polymer (NOA 65) and anthraquinone blue dichroic dye (B2), in equal ratio (1:1) of polymer and liquid crystal (LC) by polymerisation induced phase separation (PIPS) technique. Dichroic dye was taken in different concentration (wt./wt. ratio) as 0.0625%, 0.125%, 0.25%, 0.5% and 1% of the LC mixture in DPDLC films. Initially, in an open circuit when there is no proviso for external electric field (0 V), LC droplets in polymer matrix exhibited bipolar pattern, though on closing the circuit with the increase of electric field pattern of droplets starts changing, LC molecules align along the direction of applied electric field and aligned completely relatively at higher field (30 V), which illustrate vertical radial pattern. Further, results show that the DPDLC film containing 0.0625% dye concentration with consistent average droplet size ~4.30 μm, exhibits the best transmission at lower operating voltage.     

Orientational control of liquid crystal molecules via carbon nanotubes and dichroic dye in polymer dispersed liquid crystal

Polymer dispersed liquid crystals (PDLCs) using nematic liquid crystal and photo-curable polymer (NOA 65) were prepared by polymerisation-induced phase separation technique, in equal ratio (1:1) of polymer and liquid crystal (LC). We demonstrate that doping of small amount (0.125%, wt./wt.) of multiwall carbon nanotubes (CNTs) and orange azo dichroic dye in PDLC generously controlled the molecular orientation, dynamics of LC in droplet and size of droplets. The effects of multiwall CNTs and dye on PDLCs were studied in terms of transition temperature, droplet morphology, transmittance characteristic, contrast ratio and response time. The results exhibited that the values of the threshold electric fields were reduced from 8 V/µm (pure PDLC) to 1.18 and 1.72 V/µm, doped with multiwall CNTs and dye, respectively. The CNTs-doped PDLC shows faster switching response as compared with pure PDLC and dye-doped PDLC. However, dye-doped PDLC shows much higher contrast among all PDLC samples. Further, the results also illustrate that the birefringence value of LC in PDLCs was changed with doping of CNTs and dye.     

Liquid Crystal-Polymer Composite Materials

Polymer dispersed liquid crystal (PDLC) films can be switched electrically from a light-scattering off-state to a highly transparent on-state. Thin films were prepared via a polymerization-induced phase separation process, using electron beam radiation. The liquid crystal (LC)/polymer materials were obtained from blends of an eutectic nematie mixture E7 and a polyester acrylate-based polymer precursor. The optical and electro-optical properties of the PDLC films obtained depend strongly on the LC concentration. The LC solubility limit in the polymer matrix and the fractional amount of LC contained in the droplets were determined by means of calorimetrie measurements.     

Propriétés optiques et thermophysiques de composites polyméres-cristaux liquides (PDLC)

Polymer dispersed liquid crystal (PDLC) films can be switched electrically from a light scattering off-state to a highly transparent on-state. Thin films were prepared via a polymerization-induced phase separation process using electron beam radiation. The liquid crystal (LC)/polymer materials were obtained from blends of a eutectic nematic mixture E7 and a polyester acrylate based polymer precursor. The optical and electrooptical properties of the obtained PDLC films strongly depend on the LC concentration. The LC solubility limit in the polymer matrix and the fractional amount of LC contained in the droplets were determined by calorimetric measurements.     

Effect of electric field on phase separation of polymer dispersed liquid crystal

The kinetics of the polymerization induced phase separation of liquid crystal (LC)/monomer mixture has been investigated by means of depolarized light intensity technique and polarized light microscope (PLM). To examine the effect of the electric field, a DC electric field was applied across the mixtures during the phase separation process. The kinetic study indicates that the phase separation process is accelerated when the electric field is applied. The morphologies of the formed polymer dispersed liquid crystal (PDLC) films were observed by PLM. The electric field applied during the phase separation process yields the PDLC with small LC domains and fine morphologies. The clearing temperature (T_NI) of the formed PDLC films was measured by the PLM and it is found that the T_NI increases with the applied electric field intensity.     

Effects of the structures of epoxy monomers on the electro-optical properties of heat-cured polymer-dispersed liquid crystal films

Polymer-dispersed liquid crystal (PDLC) films were prepared from thermal polymerisation-induced phase separation in heat-curable monomers/nematic liquid crystal (LC) mixtures. For PDLCs with a certain amount of LCs, the microstructure and the refractive index of polymer networks could be influenced by the relative content of epoxy monomers, owing to their different chemical structures. The effect of these factors on the electro-optic properties of films was also investigated.     

Polymer dispersed liquid crystals: relation between formulation, electro-optical properties and morphology

Polymer Dispersed Liquid Crystal (PDLC) films investigated in this work are obtained by phase separation induced by photopolymerization of a homogeneous 'prepolymer/liquid crystal' mixture. We show a close relation between the formulation/conditions of preparation of the materials, their morphology and their electro-optical properties. The effect of the mutual compatibility of the prepolymer and the liquid crystal on film performances is investigated using 'model systems' that consist of pure components. Finally, both SALS experiments and a Fourier Transform procedure lead to a simple model in which LC domains are separated by polymer walls.     

The investigation of molecular affinity involved in poly(ethylene glycol)-based polymer-dispersed liquid crystal display

Acrylic polyethylene glycol(PEG)-based polymer-dispersed liquid crystal (PDLC) films have been fabricated to investigate the effect of intermolecular interactions on PDLC performance. For this purpose, the amphiphilic liquid crystal and polymers are selected as PDLC composite materials. The acrylic PEG contents are varied from 0 to 66.66 mol wt.% in order to understand the effects of different levels of additions on the microstructure and electro-optical properties of the PDLC films. For this intention, polarized optical microscopy and UV–vis spectroscopy are used. The extent of phase separation and anchoring energy are also examined using Fourier transform infrared (FTIR) spectroscopy and contact angle measurements in consequence of acrylic PEG addition. The contrast ratio, threshold voltage, as well as saturation voltage, tended to increase with the addition of acrylic PEG. The molecular affinity involved in the polymer matrix and LC molecules affected the phase separation which is responsible for the formation of domain size; this accordingly changed the electro-optical properties of PDLC film.     

The complete morphological,electro-optical and dielectric study of dichroic dye-doped polymer-dispersed liquid crystal

Polymerisation-induced phase separation method was used to prepare dye-doped polymer-dispersed liquid crystal (DPDLC) films consisting of nematic liquid crystal, photo-curable pre-polymer and a dichroic dye. The change occurring on droplets morphology with the change in dye concentration and voltage was investigated by means of polarising optical microscope and scanning electron microscope. Electro-optic behaviour of these composite films in the presence of an externally applied AC electric field (0–100 V, 200 Hz) and temperature range 25–50°C was evaluated using He–Ne laser. The maximum absorbance of dye and effect of electric field on the absorbance of dye was studied using UV-Vis spectrophotometer. Dielectric relaxation spectroscopy was carried out in the frequency range 20 Hz–20 MHz and over the temperature range 25°C–90°C. Dielectric parameters such as distribution parameter, relaxation frequency, relaxation strength and relaxation time of these DPDLC films were calculated, and the modelling of experimental data was done using Debye and Cole–Cole method.     

Study on the electro-optical properties of polyimide-based polymer-dispersed liquid crystal films

The reflectivity control device, initially developed for attitude control, is utilised to control the solar sail orbit by switching the states between absorption and specular reflection. Actually, the major parts of the device are the polymer-dispersed liquid crystal (PDLC) films. Here, PDLC films based on polyimide (PI) as polymer matrix and a low molecular weight LC can be prepared by the thermally induced phase separation (TIPS) method. The influences of cooling rate and the content of LC on the size and uniformity of LC droplets dispersed in a polymer matrix by a TIPS process were investigated. It was found that a fast cooling rate gave smaller droplet sizes and hence a more uniform distribution as compared to the ones produced under a slow cooling rate. If the LC content was increased, the droplet size would be increased. Furthermore, the effect of LC droplet size on the electro-optical properties of the PI-based PDLC films was discussed, such as transmittance, threshold voltage, driving voltage and contrast ratio (CR).     

Effects of the fluorinated liquid crystal molecules on the electro-optical properties of polymer dispersed liquid crystal films

The different fluorinated liquid crystal (LC) molecules doped to E8 were used as LC component to prepare polymer dispersed liquid crystal (PDLC) films. The mass fraction of the LC mixture is fixed 50.0 wt%. Results indicate that doping 8.0 wt% fluorinated LC molecule ME3CP to E8 significantly reduced the driving voltage of the PDLC films, and the driving voltage reduced with the rise of mass fraction of ME3CP. Besides, the terminal flexible chain length of the fluorinated LC molecule influenced the LC mixture properties based on E8, such as the dielectric anisotropy, birefringence and viscosity of the LC mixture, and the morphology and the electro-optical properties of PDLC films were controlled not only by the physical properties of the LC mixture, but also by the terminal flexible chain length of the fluorinated LC molecule .     

Effects of monomer structure on the morphology of polymer networks and the electro-optical properties of polymer-dispersed liquid crystal films

Polymer-dispersed liquid crystal (PDLC) films were prepared by photochemical polymerisation with a series of (meth)acrylate monomers. The effects of monomer structure on the morphology of polymer networks in the PDLC films were studied. The acrylate monomers without sidegroup chain formed uniform polymer networks. The methacrylate monomers with methyl as their sidegroup chains formed lace-like networks. The size of the LC droplets increased with increasing the length of the flexible chain of both methacrylate and acrylate monomers. Meanwhile, the effects of the morphology of the polymer network on the electro-optical properties of PDLC films were also investigated.     

The effect of mono-sized liquid crystal domains on electro-optical properties in a polymer dispersed liquid crystal prepared by using monodisperse poly(methylmethacrylate)/liquid crystal microcapsules

Highly mono-sized poly(methyl methacrylate) (PMMA)/liquid crystal (LC) microcapsules having a mono-sized single LC domain were prepared by the solute codiffusion method and solvent evaporation. The size of the LC domain in the microcapsules could be controlled by the amount of LC introduced during the swelling stage. The electro-optical properties of the polymer dispersed liquid crystal (PDLC) prepared by using the microcapsules was highly improved. In particular, the threshold voltage was lowered and the switching behaviour with an applied electric field was sharpened drastically compared with PDLC prepared simply by solvent evaporation-induced phase separation.     

大分子引发剂分子量对接枝聚合物基体的PDLC电光性能的影响

以可逆加成-断裂链转移(RAFT)、引发转移终止(iniferter)活性自由基聚合相结合的方法,用一步法制备了不同分子量的大分子引发剂RAFT-PS-co-PCMSI(MI),并通过紫外光聚合诱导相分离法制备了以接枝聚合物为基体的聚合物分散液晶(PDLC)膜.研究了不同分子量的MI对PDLC的微观形貌,关闭状态透光率,阈值电压,饱和电压以及记忆效应等方面的影响.研究表明,降低PDLC中MI的分子量,会使得液晶微滴粒径增大,阈值电压(Vth)、饱和电压(Vsat)减小,记忆效应、关闭状态透光率升高.     

The effect of mono-sized liquid crystal domains on electro-optical properties in a polymer dispersed liquid crystal prepared by using monodisperse poly(methylmethacrylate)/liquid crystal microcapsules

Highly mono-sized poly(methyl methacrylate) (PMMA)/liquid crystal (LC) microcapsules having a mono-sized single LC domain were prepared by the solute codiffusion method and solvent evaporation. The size of the LC domain in the microcapsules could be controlled by the amount of LC introduced during the swelling stage. The electro-optical properties of the polymer dispersed liquid crystal (PDLC) prepared by using the microcapsules was highly improved. In particular, the threshold voltage was lowered and the switching behaviour with an applied electric field was sharpened drastically compared with PDLC prepared simply by solvent evaporation-induced phase separation.     

Studies on the electro-optical and the light-scattering properties of PDLC films with the size gradient of the LC droplets

Polymer dispersed liquid crystal (PDLC) films with the size gradient of the LC droplets were prepared based on the epoxy/acrylate hybrid polymer matrix. The ultraviolet (UV) intensity gradient was induced by the UV-absorbing dye over the thickness of the samples. Taking advantage of the difference between the epoxy monomers and acrylate monomers in polymerisation rates and the UV intensity gradient, the gradient distribution of the LC droplet size was formed in PDLC films. The effect of the size gradient of the LC droplets on the electro-optical and the light-scattering properties of PDLC films was investigated. The results showed that due to the size gradient distribution of the LC droplets, PDLC films could exhibit the strong light scattering in the UV-visible-near infrared (VIS-NIR) region. Consequently, it provides a potential approach for modulating NIR light transmittance.     

Preparation and electro‐optical properties of polymer dispersed liquid crystal films with relatively low liquid crystal content

In this paper, polymer dispersed liquid crystals (PDLC) films with LC content as low as 40 wt% were prepared, and the electro‐optical properties were carefully investigated. To accomplish this, different (meth)acrylate copolymerizaiton monomers have been used. The electro‐optical properties and morphologies of the PDLC films were strongly influenced by the chemical structure of copolymerization monomers (hydroxypropyl methacrylate (HPMA), glycidyl methacrylate, hydroxypropyl acrylate) and their feed ratio. Lower driven voltage and higher contrast ratio were achieved when the PDLC films showed a morphology with suitably LC domain size. At high HPMA content, a thin polymer film was formed on the surface of PDLC samples, which is beneficial to decrease the total LC content in PDLC devices. Copyright © 2013 John Wiley & Sons, Ltd.     

The physical properties of alkene-terminated liquid crystal molecules/E8 mixture and the electro-optical properties as they doped in polymer-dispersed liquid crystal systems

Effects of the content of fluorinated alkene-terminated liquid crystal (LC) molecules on the physical properties of the fluorinated alkene-terminated LC/E8 mixture were studied. The morphology and electro-optical properties as they doped in polymer-dispersed liquid crystal (PDLC) films were investigated. The detailed discussion of the obtained results is given. As a result, comparing with the physical properties of the series of LC mixtures with the same content of the analogous fully saturated compounds doped with E8, we find that the birefringence is significantly larger for the LC mixture with the alkene-terminated materials. Both fluorinated alkene-terminated LC molecules and the analogous fully saturated compounds doped with E8 reduce the driving voltage of PDLC films. Moreover, PDLC films with the fluorinated alkene-terminated LC molecules possessed higher contrast ratio and faster response time than that of the PDLC films prepared by adding the same mass fraction of the analogous fully saturated compounds. Thus, the ability to manipulate physical properties of LC mixture and electro-optical properties of PDLC films by changing the LC molecular structures may have future relevance for new LC structures design and applications of PDLC films.     

Size control of phase‐separated liquid crystal droplets in a polymer matrix based on the phase diagram

When a mixture of liquid crystal (LC) and photo reactive monomer is irradiated by UV light, polymerization occurs and LC droplets form through phase separation, producing polymer dispersed LCs (PDLCs). Although size control of LC droplets and reduced amounts of LC in PDLC films are important in applications, precise size control of LC droplets at a low LC fraction has not yet been accomplished. In this study, the phase diagrams of the LC/initial monomer and the LC/polymer during polymerization were used to control LC droplet size at various LC fractions. Both the relative position of the sample in the initial phase diagram and the shift of the phase separation line during polymerization were shown to be important in determining the size of LC droplets. Our results are expected to provide a new strategy for precise size control of LC droplets especially at a low LC fraction range, which would be a great help for PDLC applications. © 2012 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys, 2012     

Morphology of epoxy/acrylic polymer‐dispersed liquid‐crystal film in DICY thermal cure

A polymer‐dispersed liquid‐crystal (PDLC) film was prepared from UV‐curable acrylic, thermally curable epoxy, and a liquid‐crystal (LC) mixture with a fixed LC content of 40 wt %. The UV irradiation and heat treatments were in sequential steps. At first, a phase diagram of a binary mixture of LC (E63) and epoxy [diglycidyl ether of polypropylene glycol (DER736)] was established to understand their miscibility. Then, the phase‐separation temperatures and morphologies of pre‐UV‐cured films with different equivalent DER736/dicyandiamide (DICY) molar ratios were observed. Finally, the polymerization‐induced phase‐separation behavior and morphology of the PDLC film were studied by real‐time observation while the film was maintained at 130 °C under the microscope. The results showed that the acrylic network would not affect the phase‐separation behavior of the E63/DER736 mixture. In both thermally induced and polymerization‐induced phase separations, the undissolved DICY particles acted as nucleation agents and were capable of inducing E63 to separate out early. © 2000 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 38: 2033–2042, 2000