Crystal Structures, and Electrical Conducting and Magnetic Properties in the Plate Crystals of (Ethylenedithiotetrathiafulvalenoquinone-1,3-dithiolemethide)2·MX4 (M=Fe, Ga, X=Br; M=Fe, X=C1) Salts

By the reaction of a new donor molecule, ethylenedithiotetrathiafulvalenoquinone-1,3-dithiolemethide (1) with FeBr₃, GaBr₃ or FeCl₃ in CH₃CN/CS₂ charge transfer (CT) salts of 1 with counteranions of FeBr₄⁻, GaBr₄⁻ or FeCl₄⁻ (1₂·FeBr₄, 1₂·GaBr₄ and 1₂·FeCl₄) as plate crystals were obtained. Their crystal structures are apparently similar to each other, in which 1 molecules are dimerized in the parallel direction of their molecular long axes, and the dimers are stacked with changing the direction of the molecular long axes alternately to form a one- dimensional column. The counteranions intervene between the 1-stacked columns and are aligned in a zigzag manner. The room-temperature electrical conductivities of 1₂·FeBr₄ and 1₂·GaBr₄ are fairly high (10-15 S cm⁻¹), but a small value (0.8 S cm⁻¹) is obtained for 1₂·FeCl₄. For all CT salts, temperature dependences of electrical conductivity are semiconducting in spite of very small activation energies (30-90 meV). Based on the comparison between their electrical conducting and magnetic properties, it is suggested that the d spins of FeBr₄⁻ or FeCl₄⁻ ions exert almost no influence on the π conducting electrons in the 1-stacked column.     

Crystal chemistry of M[PO2(OH)2]2·2H2O compounds (M=Mg, Mn, Fe, Co, Ni, Zn, Cd): Structural investigation of the Ni, Zn and Cd salts

The compounds M[PO₂(OH)₂]₂·2H₂O (M=Mg, Mn, Fe, Co, Ni, Zn, Cd) were prepared from super-saturated aqueous solutions at room temperature. Single-crystal X-ray structure investigations of members with M=Ni, Zn, Cd were performed at 295 and 120 K. The space-group symmetry is P2₁/n, Z=2. The unit-cell parameters are at 295/120 K for M=Ni: a=7.240(2)/7.202(2), b=9.794(2)/9.799(2), c=5.313(1)/5.285(1) Å, β=94.81(1)/94.38(1)°, V=375.4/371.9 Å³; M=Zn: a=7.263(2)/7.221(2), b=9.893(2)/9.899(3), c=5.328(1)/5.296(2) Å, β=94.79(1)/94.31(2)°, V=381.5/377.5 Å³; M=Cd: a=7.356(2)/7.319(2), b=10.416(2)/10.423(3), c=5.407(1)/5.371(2) Å, β=93.85(1)/93.30(2)°, V=413.4/409.1 Å³. Layers of corner-shared MO₆ octahedra and phosphate tetrahedra are linked by three of the four crystallographically different hydrogen bonds. The fourth hydrogen bond (located within the layer) is worth mentioning because of the short O_h?O bond distance of 2.57-2.61 Å at room temperature (2.56-2.57 Å at 120 K); only for M=Mg it is increased to 2.65 Å. Any marked temperature-dependent variation of the unit-cell dimension is observed only vertical to the layers. The analysis of the infrared (IR) spectroscopy data evidences that the internal PO₄ vibrations are insensitive to the size and the electronic configuration of the M²⁺ ions. The slight strengthening of the intra-molecular P-O bonds in the Mg salt is caused by the more ionic character of the Mg-O bonds. All IR spectra exhibit the characteristic “ABC trio” for acidic salts: 2900-3180 cm⁻¹ (A band), 2000-2450 cm⁻¹ (B band) and 1550-1750 cm⁻¹ (C band). Both the frequency and the intensity of the A band provide an evidence that the PO₂(OH)₂ groups in M[PO₂(OH)₂]₂·2H₂O compounds form weaker hydrogen bonds as compared with other acidic salts with comparable O?O bond distances of about 2.60 Å. The observed shift of the O-H stretching vibrations of the water molecule in the order M=Mg>Mn≈Fe≈Co>Ni>Zn≈Cd has been discussed with respect to the influence of both the character and the strength of M↔H₂O interactions.     

Crystal chemistry and crystallography of the SrR2CuO5 (R=lanthanides) phases

The crystal chemistry and crystallography of the compounds SrR₂CuO₅ (Sr-121, R=lanthanides) were investigated using the powder X-ray Rietveld refinement technique. Among the 11 compositions studied, only R=Dy and Ho formed the stable SrR₂CuO₅ phase. SrR₂CuO₅ was found to be isostructural with the “green phase”, BaR₂CuO₅. The basic structure is orthorhombic with space group Pnma. The lattice parameters for SrDyCuO₅ are a=12.08080(6) Å, b=5.60421(2) Å, c=7.12971(3) Å, V=482.705(4) Å³, and Z=8; and for the Ho analog are a=12.03727(12) Å, b=5.58947(7) Å, c=7.10169(7) Å, V=477.816(9) Å³, and Z=8. In the SrR₂CuO₅ structure, each R is surrounded by seven oxygen atoms, forming a monocapped trigonal prism (RO₇). The isolated CuO₅ group forms a distorted square pyramid. Consecutive layers of prisms are stacked in the b-direction. Bond valence calculations imply that residual strain is largely responsible for the narrow stability of the SrR₂CuO₅ phases with R=Dy and Ho only. X-ray powder reference diffraction patterns for SrDy₂CuO₅ and SrHo₂CuO₅ were determined.     

Crystal growth and structural investigation of A2BReO6 (A=Sr, Ba; B=Li, Na)

Single crystals of the double perovskite rhenates A₂BReO₆ (A=Sr, Ba; B=Li, Na) were grown out of molten hydroxide fluxes. Single crystals of orange/yellow Ba₂LiReO₆, Ba₂NaReO₆ and Sr₂LiReO₆ were solved in the cubic, Fm-3m space group with a=8.1214(11) Å, 8.2975(3) Å, and 7.9071(15) Å, respectively, while Sr₂NaReO₆ was determined to be monoclinic P2₁/n with a=5.6737(6) Å, b=5.7988(6) Å, c=8.0431(8) Å, and β=90.02(6) °. The cubic structure consists of a rock salt lattice of corner-shared ReO₆ and MO₆ (M=Li, Na) octahedra which, in the monoclinic structure, are both tilted and rotated. A discrepancy exists between the symmetry of Sr₂LiReO₆ indicated by the single-crystal refinement of flux-grown crystals (cubic, Fm-3m) and the symmetry indicated by the powder diffraction data collected on polycrystalline samples prepared by the ceramic method (tetragonal, I4/m). It is possible that the cubic crystals are a kinetic product that forms in small quantities at low temperatures, while the powder represents the more stable polymorph that forms at higher reaction temperature.     

Syntheses, crystal structures and Raman spectra of Ba(BF4)(PF6), Ba(BF4)(AsF6) and Ba2(BF4)2(AsF6)(H3F4); the first examples of metal salts containing simultaneously tetrahedral BF4 and octahedral AF6 anions

In the system BaF₂/BF₃/PF₅/anhydrous hydrogen fluoride (aHF) a compound Ba(BF₄)(PF₆) was isolated and characterized by Raman spectroscopy and X-ray diffraction on the single crystal. Ba(BF₄)(PF₆) crystallizes in a hexagonal space group with a=10.2251(4) Å, c=6.1535(4) Å, V=557.17(5) Å³ at 200 K, and Z=3. Both crystallographically independent Ba atoms possess coordination polyhedra in the shape of tri-capped trigonal prisms, which include F atoms from BF₄⁻ and PF₆⁻ anions. In the analogous system with AsF₅ instead of PF₅ the compound Ba(BF₄)(AsF₆) was isolated and characterized. It crystallizes in an orthorhombic Pnma space group with a=10.415(2) Å, b=6.325(3) Å, c=11.8297(17) Å, V=779.3(4) Å³ at 200 K, and Z=4. The coordination around Ba atom is in the shape of slightly distorted tri-capped trigonal prism which includes five F atoms from AsF₆⁻ and four F atoms from BF₄⁻ anions. When the system BaF₂/BF₃/AsF₅/aHF is made basic with an extra addition of BaF₂, the compound Ba₂(BF₄)₂(AsF₆)(H₃F₄) was obtained. It crystallizes in a hexagonal P6₃/mmc space group with a=6.8709(9) Å, c=17.327(8) Å, V=708.4(4) Å³ at 200 K, and Z=2. The barium environment in the shape of tetra-capped distorted trigonal prism involves 10 F atoms from four BF₄⁻, three AsF₆⁻ and three H₃F₄⁻ anions. All F atoms, except the central atom in H₃F₄ moiety, act as μ₂-bridges yielding a complex 3-D structural network.     

Synthesis and structural investigation of the compounds containing HF2 anions: Ca(HF2)2, Ba4F4(HF2)(PF6)3 and Pb2F2(HF2)(PF6)

Three new compounds Ca(HF₂)₂, Ba₄F₄(HF₂)(PF₆)₃ and Pb₂F₂(HF₂)(PF₆) were obtained in the system metal(II) fluoride and anhydrous HF (aHF) acidified with excessive PF₅. The obtained polymeric solids are slightly soluble in aHF and they crystallize out of their aHF solutions. Ca(HF₂)₂ was prepared by simply dissolving CaF₂ in a neutral aHF. It represents the second known compound with homoleptic HF environment of the central atom besides Ba(H₃F₄)₂. The compounds Ba₄F₄(HF₂)(PF₆)₃ and Pb₂F₂(HF₂)(PF₆) represent two additional examples of the formation of a polymeric zigzag ladder or ribbon composed of metal cation and fluoride anion (MF⁺)_n besides PbF(AsF₆), the first isolated compound with such zigzag ladder. The obtained new compounds were characterized by X-ray single crystal diffraction method and partly by Raman spectroscopy. Ba₄F₄(HF₂)(PF₆)₃ crystallizes in a triclinic space group P1¯ with a=4.5870(2) Å, b=8.8327(3) Å, c=11.2489(3) Å, α=67.758(9)°, β=84.722(12), γ=78.283(12)°, V=413.00(3) Å³ at 200 K, Z=1 and R=0.0588. Pb₂F₂(HF₂)(PF₆) at 200 K: space group P1¯, a=4.5722(19) Å, b=4.763(2) Å, c=8.818(4) Å, α=86.967(10)°, β=76.774(10)°, γ=83.230(12)°, V=185.55(14) ų, Z=1 and R=0.0937. Pb₂F₂(HF₂)(PF₆) at 293 K: space group P1¯, a=4.586(2) Å, b=4.781(3) Å, c=8.831(5) Å, α=87.106(13)°, β=76.830(13)°, γ=83.531(11)°, V=187.27(18) Å³, Z=1 and R=0.072. Ca(HF₂)₂ crystallizes in an orthorhombic Fddd space group with a=5.5709(6) Å, b=10.1111(9) Å, c=10.5945(10) Å, V=596.77(10) Å³ at 200 K, Z=8 and R=0.028.     

Synthesis, structure and magnetic properties of the S=1/2, one-dimensional antiferromagnet, Y5Re2O12

Single crystals of Y₅Re₂O₁₂ have been grown, and the crystal structure has been determined by X-ray diffraction. This compound crystallizes in space group C2/m with cell dimensions of a=12.4081(10) Å b=5.6604(5)Å, c=7.4951(6) Å, β=107.837(3)°, Z=2. The final refinement led to R1=0.0238, WR2=0.0459 for 1053 observed reflections with F>4σ(F₀). Edge-sharing ReO₆ octahedra form infinite linear [ReO₂O_4/2]_n chains along the b direction with alternating short and long Re-Re distances. Three crystallographically independent yttrium atoms surround O2 to form OY₄ tetrahedra, which share edges and corners in the ab plane to form a two-dimensional Y₅O₄ network which separates the [ReO₂O_4/2]_n magnetic chains. This compound is therefore isostructural with the series Ln₅Re₂O₁₂Ln=Gd-Lu, which have been known since 1969. The average Re oxidation state is +4.5 in the chains and a reasonable, if qualitative MO scheme results in one unpaired electron per Re dimer. Consistent with this, magnetic susceptibility data can be fitted to the one-dimensional antiferromagnetic Heisenberg model with S=1/2 and parameters J^intra/k=−89(1)K, g=2.15(4) and χ(TIP)=5(1)×10⁻⁴ emu/mol. There is no sign of long-range magnetic order down to 2 K. These results are contrasted with those for the isostructural Y₅Mo₂O₁₂.     

Crystal and magnetic structures of the brownmillerite compound Ca2Fe1.039(8)Mn0.962(8)O5

The crystal and magnetic structures of the brownmillerite material, Ca₂Fe_1.039(8)Mn_0.962(8)O₅ were investigated using powder X-ray and neutron diffraction methods, the latter from 3.8 to 700 K. The compound crystallizes in Pnma space group with unit cell parameters of a=5.3055(5) Å, b=15.322(2) Å, c=5.4587(6) Å at 300 K. The neutron diffraction study revealed the occupancies of Fe³⁺ and Mn³⁺ ions in both octahedral and tetrahedral sites and showed some intersite mixing and a small, ∼4%, Fe excess. While bulk magnetization data were inconclusive, variable temperature neutron diffraction measurements showed the magnetic transition temperature to be 407(2) K below which a long range antiferromagnetic ordering of spins occurs with ordering wave vector k=(000). The spins of each ion are coupled antiferromagnetically with the nearest neighbors within the same layer and coupled antiparallel to the closest ions from the neighboring layer. This combination of intra- and inter-layer antiparallel arrangement of spins forms a G-type magnetic structure. The ordered moments on the octahedral and tetrahedral sites at 3.8 K are 3.64(16) and 4.23(16) μ_B, respectively.     

La3Ru8B6 and Y3Os8B6, new members of a homologous series R(A)nM3n−1B2n

Two new compounds, La₃Ru₈B₆ and Y₃Os₈B₆, were synthesized by arc melting the elements. Their structural characterization was carried out at room temperature on as-cast samples by using X-ray diffractometry. According to X-ray single-crystal diffraction results these borides crystallize in Fmmm space group (no. 69), Z=4, a=5.5607(1) Å, b=9.8035(3) Å, c=17.5524(4) Å, ρ=8.956 Mg/m³, μ=25.23 mm⁻¹ for La₃Ru₈B₆ and a=5.4792(2) Å, b=9.5139(4) Å, c=17.6972(8) Å, ρ=13.343 Mg/m³, μ=128.23 mm⁻¹ for Y₃Os₈B₆. The crystal structure of La₃Ru₈B₆ was confirmed from Rietveld refinement of X-ray powder diffraction data. Both La₃Ru₈B₆ and Y₃Os₈B₆ compounds are isotypic with the Ca₃Rh₈B₆ compound and their structures are built up from CeCo₃B₂-type and CeAl₂Ga₂-type structural fragments taken in ratio 2:1. They are the members of structural series R(A)_nM_3n−1B_2n with n=3 (R is the rare earth metal, A the alkaline earth metal, and M the transition metal). Structural and atomic parameters were also obtained for La_0.94Ru₃B₂ compound from Rietveld refinement (CeCo₃B₂-type structure, P6/mmm space group (no. 191), a=5.5835(9) Å, c=3.0278(6) Å).     

Synthesis, crystal structure, infrared and Raman spectra of Sr4Cu3(AsO4)2(AsO3OH)4·3H2O and Ba2Cu4(AsO4)2(AsO3OH)3

The two new compounds, Sr₄Cu₃(AsO₄)₂(AsO₃OH)₄·3H₂O (1) and Ba₂Cu₄(AsO₄)₂(AsO₃OH)₃(2), were synthesized under hydrothermal conditions. They represent previously unknown structure types and are the first compounds synthesized in the systems SrO/BaO-CuO-As₂O₅-H₂O. Their crystal structures were determined by single-crystal X-ray diffraction [space group C2/c, a=18.536(4) Å, b=5.179(1) Å, c=24.898(5) Å, β=93.67(3)°, V=2344.0(8) Å³, Z=4 for 1; space group P4₂/n, a=7.775(1) Å, c=13.698(3) Å, V=828.1(2) Å³, Z=2 for 2]. The crystal structure of 1 is related to a group of compounds formed by Cu²⁺-(XO₄)³⁻ layers (X=P⁵⁺, As⁵⁺) linked by M cations (M=alkali, alkaline earth, Pb²⁺, or Ag⁺) and partly by hydrogen bonds. In 1, worth mentioning is the very short hydrogen bond length, D···A=2.477(3) Å. It is one of the examples of extremely short hydrogen bonds, where the donor and acceptor are crystallographically different. Compound 2 represents a layered structure consisting of Cu₂O₈ centrosymmetric dimers crosslinked by As1φ₄ tetrahedra, where φ is O or OH, which are interconnected by Ba, As2 and hydrogen bonds to form a three-dimensional network. The layers are formed by Cu₂O₈ centrosymmetric dimers of CuO₅ edge-sharing polyhedra, crosslinked by As1O₄ tetrahedra. Vibrational spectra (FTIR and Raman) of both compounds are described. The spectroscopic manifestation of the very short hydrogen bond in 1, and ABC-like spectra in 2 were discussed.     

Synthesis and structure of a 1,6-hexyldiamine heptaborate, [H3N(CH2)6NH3][B7O10(OH)3]

A new 1,6-hexyldiamine heptaborate, [H₃N(CH₂)₆NH₃][B₇O₁₀(OH)₃] (1), has been solvothermally synthesized and characterized by single-crystal X-ray diffraction, FTIR, elemental analysis, and thermogravimetric analysis. Compound 1 crystallizes in monoclinic system, space group P2₁/n with a=8.042(2) Å, b=20.004(4) Å, c=10.103(2) Å, and β=90.42(3)°. The anionic [B₇O₁₀(OH)₃]_n²ⁿ⁻ layers are interlinked via hydrogen bonding to form a 3D supramolecular network containing large channels, in which the templated [H₃N(CH₂)₆NH₃]²⁺ cations are located.     

Quaternary selenostannates Na2−xGa2−xSn1+xSe6 and AGaSnSe4 (A=K, Rb, and Cs) through rapid cooling of melts. Kinetics versus thermodynamics in the polymorphism of AGaSnSe4

The quaternary alkali-metal gallium selenostannates, Na_2−xGa_2−xSn_1+xSe₆ and AGaSnSe₄ (A=K, Rb, and Cs), were synthesized by reacting alkali-metal selenide, Ga, Sn, and Se with a flame melting-rapid cooling method. Na_2−xGa_2−xSn_1+xSe₆ crystallizes in the non-centrosymmetric space group C2 with cell constants a=13.308(3) Å, b=7.594(2) Å, c=13.842(3) Å, β=118.730(4)°, V=1226.7(5) Å³. α-KGaSnSe₄ crystallizes in the tetragonal space group I4/mcm with a=8.186(5) Å and c=6.403(5) Å, V=429.1(5) Å³. β-KGaSnSe₄ crystallizes in the space group P2₁/c with cell constants a=7.490(2) Å, b=12.578(3) Å, c=18.306(5) Å, β=98.653(5)°, V=1705.0(8) Å³. The unit cell of isostructural RbGaSnSe₄ is a=7.567(2) Å, b=12.656(3) Å, c=18.277(4) Å, β=95.924(4)°, V=1741.1(7) Å³. CsGaSnSe₄ crystallizes in the orthorhombic space group Pmcn with a=7.679(2) Å, b=12.655(3) Å, c=18.278(5) Å, V=1776.1(8) Å³. The structure of Na_2−xGa_2−xSn_1+xSe₆ consists of a polar three-dimensional network of trimeric (Sn,Ga)₃Se₉ units with Na atoms located in tunnels. The AGaSnSe₄ possess layered structures. The compounds show nearly the same Raman spectral features, except for Na_2−xGa_2−xSn_1+xSe₆. Optical band gaps, determined from UV-Vis spectroscopy, range from 1.50 eV in Na_2−xGa_2−xSn_1+xSe₆ to 1.97 eV in CsGaSnSe₄. Cooling of the melts of KGaSnSe₄ and RbGaSnSe₄ produces only kinetically stable products. The thermodynamically stable product is accessible under extended annealing, which leads to the so-called γ-form (BaGa₂S₄-type) of these compounds.     

Novel microporous zirconium silicate (K2ZrSi3O9·2H2O) from high temperature phase transformation

A new microporous zirconosilicate K₂ZrSi₃O₉·2H₂O (AV-15) has been prepared by high-temperature phase transformation at 910 °C. Its structure has been determined ab initio from powder X-ray diffraction data. The unit cell is orthorhombic, space group C222₁ (no. 20), Z=4 with cell dimensions: a=8.105(3), b=10.684(5), c=12.030(5) Å, V=1041.76(7) Å³. The framework connection of AV-15 is essentially the same as the previously reported sodium stannosilicate AV-10 while the locations of potassium and water molecules in the former are quite different from those of the sodium and water molecules in AV-10. In AV-10 sodium and water molecules form a sinucoidal chain, while potassium and water molecules build up a linear chain in AV-15. The water molecules in AV-15 are lost on heating with a typical zeolitic behaviour. SEM shows that the particle sizes and habits of AV-15 and parent umbite material are the same. The ²⁹Si MAS NMR spectrum of AV-15 displays two resonances at ca. −89.4 and −90.1 ppm in a 1:2 intensity ratio. Thermogravimetry analysis confirms the existence of water in this material.     

The non-centrosymmetric borate oxides, MBi2B2O7 (M=Ca, Sr)

Two novel noncentrosymmetric borates oxides, MBi₂B₂O₇ or MBi₂O(BO₃)₂ (MCa, Sr), have been synthesized by solid-state reactions in air at temperatures in the 600-700 °C range. Their crystal structures have been determined ab initio and refined using powder neutron diffraction data. CaBi₂B₂O₇ crystallizes in the orthorhombic Pna2₁ space group with a=8.9371(5) Å, b=5.4771(3) Å, c=12.5912(7) Å, Z=4, R_wp=0.118, χ²=2.30. SrBi₂B₂O₇ crystallizes in the hexagonal P6₃ space group with a=9.1404(4) Å, c=13.0808(6) Å, Z=6, R_wp=0.115, χ²=4.15. Large displacement parameters suggest the presence of disorder in SrBi₂B₂O₇ as also revealed by diffuse 2×a superstructure reflections in electron diffraction patterns. Both structures are built of identical (001) neutral layers of corner-sharing BO₃ triangles and MO₆ trigonal prisms forming six-membered rings in which Bi₂O groups are located. Adjacent layers are stacked in a staggered configuration and connected through weak Bi-O bonds. A moderate efficiency for second harmonic generation (SHG) has been measured for a powder sample of CaBi₂B₂O₇ (d_eff=2d_eff(KDP)).     

Synthesis and magnetic properties of rare earth ruthenates, Ln5Ru2O12 (Ln=Pr, Nd, Sm-Tb)

Single crystals of Ln₅Ru₂O₁₂ (Ln=Pr, Nd, Sm-Tb) were grown out of either NaOH or KOH fluxes in sealed silver tubes. The crystals of all the phases were observed to be twinned as confirmed by TEM studies. The series crystallize in the C2/m monoclinic system with lattice parameters, a=12.4049(4)-12.7621(6) Å, b=5.8414(2)-5.9488(3) Å, c=7.3489(2)-7.6424(4) Å, β=107.425(3)-107.432(2)° and Z=2. The crystal structure is isotypic with the defect/disorder model of Ln₅Re₂O₁₂ (Ln = Y, Gd) and consists of one dimensional edge shared RuO₆ octahedral chains separated by a two dimensional LnO_x polyhedral framework. Magnetic measurements indicate paramagnetic and antiferromagnetic behavior for Ln=Nd, Sm-Gd and Ln=Tb, respectively.     

Structure and conductivity of strontium-doped cerium orthovanadates Ce1−xSrxVO4 (0≤x≤0.175)

A-site substituted cerium orthovanadates, Ce_1−xSr_xVO₄, were synthesised by solid-state reactions. It was found that the solid solution limit in Ce_1−xSr_xVO₄ is at x=0.175. The crystal structure was analysed by X-ray diffraction and it exhibits a tetragonal zircon structure of space group I4₁/amd (1 4 1) with a=7.3670 (3) and c=6.4894 (1) Å for Ce_0.825Sr_0.175VO₄. The UV-vis absorption spectra indicated that the compounds have band gaps at room temperature in the range 4.5-4.6 eV. Conductivity measurements were performed for the first time up to the strontium solid solution limit in air and in dry 5% H₂/Ar with conductivity values at 600 °C ranging from 0.3 to 30 mS cm⁻¹ in air to 30-45 mS cm⁻¹ in reduced atmosphere. Sample Ce_0.825Sr_0.175VO₄ is redox stable at a temperature below 600 °C although the conductivity is not high enough to be used as an electrode for solid oxide fuel cells.     

Crystal growth, structure determination, and optical properties of new potassium-rare-earth silicates K3RESi2O7 (RE=Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu)

Single crystals of K₃RESi₂O₇ (RE=Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu) were grown from a potassium fluoride flux. Two different structure types were found for this series. Silicates containing the larger rare earths, RE=Gd, Tb, Dy, Ho, Er, Tm, Yb crystallize in a structure K₃RESi₂O₇ that contains the rare-earth cation in both a slightly distorted octahedral and an ideal trigonal prismatic coordination environment, while in K₃LuSi₂O₇, containing the smallest of the rare earths, lutetium is found solely in an octahedral coordination environment. The structure of K₃LuSi₂O₇ crystallizes in space group P6₃/mmc with a=5.71160(10) Å and c=13.8883(6) Å. The structures containing the remaining rare earths crystallize in the space group P6₃/mcm with the lattice parameters of a=9.9359(2) Å, c=14.4295(4) Å, (K₃GdSi₂O₇); a=9.88730(10) Å, c=14.3856(3) Å, (K₃TbSi₂O₇); a=9.8673(2) Å, c=14.3572(4) Å, (K₃DySi₂O₇); a=9.8408(3) Å, c=14.3206(6) Å, (K₃HoSi₂O₇); a=9.82120(10) Å, c=14.2986(2) Å, (K₃ErSi₂O₇); a=9.80200(10) Å, c=14.2863(4) Å, (K₃TmSi₂O₇); a=9.78190(10) Å, c=14.2401(3) Å, (K₃YbSi₂O₇). The optical properties of the silicates were investigated and K₃TbSi₂O₇ was found to fluoresce in the visible.     

Transition metal tetramolybdate dihydrates MMo4O13·2H2O (M=Co,Ni) having a novel pillared layer structure

Hydrothermal synthesis in the M/Mo/O (M=Co,Ni) system was investigated. Novel transition metal tetramolybdate dihydrates MMo₄O₁₃·2H₂O (M=Co,Ni), having an interesting pillared layer structure, were found. The molybdates crystallize in the triclinic system with space group P−1, Z=1 with unit cell parameters of a=5.525(3) Å, b=7.058(4) Å, c=7.551(5) Å, α=90.019(10)°, β=105.230(10)°, γ=90.286(10)° for CoMo₄O₁₃·2H₂O, and a=5.508(2) Å, b=7.017(3) Å, c=7.533(3) Å, α=90.152(6)°, β=105.216(6)°, γ=90.161(6)° for NiMo₄O₁₃·2H₂O The structure is composed of two-dimensional molybdenum-oxide (2D Mo-O) sheets pillared with CoO₆ octahedra. The 2D Mo-O sheet is made up of infinite straight ribbons built up by corner-sharing of four molybdenum octahedra (two MoO₆ and two MoO₅OH₂) sharing edges. These infinite ribbons are similar to the straight ones in triclinic-K₂Mo₄O₁₃ having 1D chain structure, but are linked one after another by corner-sharing to form a 2D sheet structure, like the twisted ribbons in BaMo₄O₁₃·2H₂O (or in orthorhombic-K₂Mo₄O₁₃) are.     

Effects of partial anion substitution on the thermoelectric properties of silver(I) chalcogenide halides in the system Ag5Q2X with Q=Te, Se and S and X=Br and Cl

A selection of mixed conducting silver chalcogenide halides of the general formula Ag₅Q₂X with Q=sulfur, selenium and tellurium and X=chlorine and bromine has been investigated due to their thermoelectric properties. Recently, the ternary counterpart Ag₅Te₂Cl showed a defined d¹⁰-d¹⁰ interaction in the disordered cation substructure at elevated temperatures where Ag₅Te₂Cl is present in its high temperature α-phase. A significant drop of the thermal diffusivity has been observed during the β−α phase transition reducing the values from 0.12 close to 0.08 mm² s⁻¹. At the same transition the thermopower reacts on the increasing silver mobility and jumps towards less negative values.Thermal conductivities, thermopower and thermal diffusivity of selected compounds with various grades of anion substitution in Ag₅Q₂X were determined around the silver-order/disorder β−α phase transition. A formation of attractive interactions could be observed for selenium substituted phases while no effect was detected for bromide and sulfide samples. Depending on the grade and type of substitution the thermopower changes significantly at and after the β−α phase transition. Thermal conductivities are low reaching values around 0.2-0.3 W m⁻¹ K⁻¹ at 299 K. Partial anion exchange can substantially tune the thermoelectric properties in Ag₅Q₂X phases.     

Anomalous octahedral distortion and multiple phase transitions in the metal-ordered manganite YBaMn2O6

By means of powder X-ray diffraction, powder neutron diffraction and transmission electron microscopy (TEM), we determined the crystal structures of a metal-ordered manganite YBaMn₂O₆ which undergoes successive phase transitions. A high-temperature metallic phase (T_c1=520 K<T) crystallizes in a triclinic P1 with the following unit cell: Z=2, a=5.4948(15) Å, b=5.4920(14) Å, c=7.7174(4) Å, α=89.804(20)°, β=90.173(20)°, γ=91.160(4)°. The MnO₆ octahedral tilting is approximately written as a⁰b⁻c⁻, leading to a significant structural anisotropy within the ab plane. The structure for T_c2<T<T_c1 is a monoclinic P2 (Z=2, a=5.5181(4) Å, b=5.5142(4) Å, c=7.6443(3) Å, β=90.267(4)°) with an a⁻b⁻c⁻ tilting. The structural features suggest a d_x²−y² orbital ordering (OO). Below T_c2=480 K, crystallographically inequivalent two octahedra show distinct volume difference, due to the Mn³⁺/Mn⁴⁺ charge ordering. The TEM study furthermore revealed a unique d_3x²−r²/d_3y²−r² OO with a modified CE structure. It was found that the obtained crystal structures are strongly correlated to the unusual physical properties. In particular, the extremely high temperature at which charge degree of freedom freezes, T_c2, should be caused by the absence of the structural disorder and by heavily distorted MnO₆ octahedra.