脂溶性CdSe/ZnS量子点脂质体复合物的制备及表征

在油相中成功合成了脂溶性CdSe/ZnS核壳量子点纳米粒,粒径平均为4.5 nm,量子产率达29%,发射波长为540 nm。通过薄膜分散法,以蛋黄卵磷脂、胆固醇为膜材,将脂溶性的CdSe/ZnS核壳量子点包覆于脂质体磷脂双分子层中,由于磷脂分子的两亲性,使得脂溶性的CdSe/ZnS核壳量子点同时又具有亲水性。通过透射电镜对脂质体形态进行了表征,倒置荧光显微镜证实了发光CdSe/ZnS核壳量子点成功包埋于脂质体双分子层中,包裹的发光CdSe/ZnS核壳量子点具有更稳定的发光及抗光漂白性质。     

硒化镉发光量子点的制备及其在有机发光器件中的应用

硒化镉量子点具有随粒径尺寸改变,而产生发光波长调变的特性,目前已被广泛研究。本研究是由化学溶胶法合成不同粒径尺寸的核壳型CdSe／ZnS硒化镉量子点,其表面包覆十六烷基胺,避免分子团聚现象。在由硒化镉成核温度的控制,成功地制备一系列具有各种尺寸粒径的核壳型硒化镉量子点(2—6nm)。本研究也合成了含有纳米金粒子于核壳型硒化镉量子点,实验结果发现：硒化镉发光效率明显的提高。在有机发光器件的应用方面,将发光波长为505nm核壳型CdSe／ZnS量子点掺入溶有发光波长为570nm铱化合物的氯仿溶液时,其溶液的光致发光光谱表明,原量子点的发光特性消失,只有铱化合物的发光依然存在,且其发光强度呈现明显增强趋势,我们推测此现象源自于量子点到铱化合物能量转移的机制。我们也以含有核壳型硒化镉量子点的铱化合物与PVK混合材料为发光层,成功的制作发光二极管器件,器件的发光效率因核壳型硒化镉的掺杂,明显提高2倍多。     

The Influence of Surface Trapping and Dark States on the Fluorescence Emission Efficiency and Lifetime of CdSe and CdSe/ZnS Quantum Dots

To investigate the influence of surface trapping and dark states on CdSe and CdSe/ZnS quantum dots (QDs), we studied the absorption, fluorescence intensity and lifetime by using one-and two-photon excitation, respectively. Experimental results show that both one- and two-photon fluorescence emission efficiencies of the QDs enhance greatly and the lifetime increase after capping CdSe with ZnS due to the effective surface passivation. The lifetime of one-photon fluorescence of CdSe and CdSe/ZnS QDs increase with increasing emission wavelength in a supralinear way, which is attributed to the energy transfer of dark excitons. On the contrary, the lifetime of two-photon fluorescence of bare and core-shell QDs decrease with increasing emission wavelength, and this indicates that the surface trapping is the dominant decay mechanism in this case.     

Experimental investigation of energy transfer between CdSe/ZnS quantum dots and different-sized gold nanoparticles

Hybrid nanostructures of quantum dots(QDs) and metallic nanostructure are attractive for future use in a variety of optoelectronic devices. For photodetection applications, it is important that the photoluminescence (PL) of QDs is quenched by the metallic nanostructures. Here, the quenching efficiency of CdSe/ZnS core-shell quantum dots (QDs) with different sized gold nanoparticles (NPs) films through energy transfer is investigated by measuring the PL intensity of the hybrid nanostructures. In our research, the gold NPs films are formed by the post-annealing of the deposited Au films on the quartz substrate. We find that the energy transfer from the QDs to the Au NPs strongly depends on the sizes of the Au NPs. For CdSe/ZnS QDs direct contact with the Au NPs films, the largest energy transfer efficiency are detected when the resonance absorption peak of the Au NPs is nearest to the emission peak of the CdSe/ZnS QDs. However, when there is a PMMA spacer between the QDs layer and the Au NPs films, firstly, we find that the energy transfer efficiency is weakened, and the largest energy transfer efficiency is obtained when the resonant absorption peak of the Au NPs is farthest to the emission peak wavelength of CdSe/ZnS QDs. These results will be useful for the potential design of the high efficiency QDs optoelectronic devices.     

Steady State and Time Resolved Spectroscopic Study of CdSe and CdSe/ZnS QDs:FRET Approach

This article highlights some physical studies on the relaxation dynamics and Förster resonance energy transfer (FRET) of semiconductor quantum dots (QDs) to proximal dye molecule and the way these phenomena change with core to core-shell QD is discussed. Efforts to understand the optical and carrier relaxation dynamics of CdSe and CdSe/ZnS QDs are made by using absorption, steady-state fluorescence and time-resolved fluorescence (TCSPC) techniques. Steady-state as well as time-resolved fluorescence measurements were employed to evaluate the QD PL quenching induced by the proximal Rhodamine 101 dye molecule and to examine the influence of deep trap states on energy transfer efficiency. The FRET parameters such as spectral overlap, Förster distance, intermolecular distance for each donor-acceptor pair are determined and variation of these parameters from core to core-shell QD is discussed.     

ZnS薄膜参数对有机/无机复合发光器件特性的影响

半导体量子点(QDs)具有发光效率高和发光波长可调等特点。采用胶体CdSe QDs作电致发光器件的有源材料,TPD(N,N′-biphenyl-N,N′-bis-(3-methylphenyl)-1,1′-biphenyl-4,4′-diamine)作空穴传输层,ZnS作电子传输层,研究了有机/无机复合发光器件ITO/TPD/CdSe QDs/ZnS/Ag的电致发光特性。TPD和CdSe QDs薄膜采用旋涂方法、ZnS薄膜采用磁控溅射方法沉积,器件表面平整。CdSe QDs的光致发光和电致发光谱峰位波长均位于～580 nm,属于量子点的带边激子发光。我们与以前的ITO/ZnS/CdSe QDs/ZnS/Ag发光器件结构进行了对比,发现新的器件结构的电致发光谱没有观察到QDs表面态的发光,而且新器件的发光强度是ITO/ZnS/CdSe QDs/ZnS/Ag结构的～10倍。发光效率的提高归因于碰撞激发与载流子注入两种发光机制并存的结果：一方面电子经过ZnS 层加速后,碰撞激发CdSe QDs发光;另一方面,空穴从TPD层注入CdSe QDs 与QDs中激发的电子复合发光。我们进一步研究了ZnS电子加速层厚度对发光特性的影响,选择ZnS薄膜的厚度分别是80,120 和160 nm,发现随着ZnS层厚度增大,器件启亮电压升高,EL强度增大,但是击穿电压降低。EL峰位随着ZnS厚度的减小发生明显蓝移,对上述实验现象进行了机理解释。     

CdSe/ZnSe/ZnS多壳层结构量子点的制备与表征

展示了一种简捷的多壳层量子点合成路线。在含有过量Se源的CdSe体系中直接注入Zn源,"一步法"合成了CdSe/ZnSe量子点;进一步以CdSe/ZnSe为"核",表面外延生长ZnS壳层制备了核/壳/壳结构CdSe/ZnSe/ZnS量子点。相对于以往报道的多壳层结构量子点的制备方法,该方法通过减少壳层的生长步骤有效地简化了实验操作,缩短了实验周期,同时减少对原料的损耗。对量子点进行高温退火处理,能够大幅提高CdSe/ZnSe/ZnS量子点的发光量子产率。透射电镜、XRD以及光谱研究表明:所制备的量子点接近球形,核与壳层纳米晶均为闪锌矿结构,最终获得的CdSe/ZnSe/ZnS量子点的光致发光量子产率达到53％。为了实现量子点的表面生物功能化,通过巯基酸进行了表面配体交换修饰,使量子点表面具有水溶性的羧基功能团,并且能够维持较高的光致发光量子产率。     

2018年2期电子期刊

光诱导功能退化是胶体量子点在应用中面临的主要挑战之一,本文针对这一问题研究了使用磁控溅射沉积SiO₂薄膜形成钝化层来提高CdSe/ZnS量子点发光稳定性的方法。首先,通过三正辛基膦辅助连续离子层吸附反应方法合成了615 nm发光的红色CdSe/ZnS量子点。然后将量子点旋涂在SiO₂/Si基片上,再通过磁控溅射方法在量子点上沉积了厚度为20 nm的SiO₂薄膜作为钝化层。使用连续波激光光源分别在空气气氛和真空条件下照射样品,研究了经过不同照射时间后钝化和未钝化量子点的稳态光致发光光谱。结果表明,随着照射时间的延长,没有SiO₂钝化的量子点的PL强度显著降低、PL峰值发生蓝移、FWHM不断增大。对比研究发现,由于SiO₂薄膜能够阻挡空气中的水和氧,减缓了量子点表面的光诱导氧化现象,因此显著提高了CdSe/ZnS量子点的稳定性。     

谷胱甘肽包被的CdSe/CdS量子点的直接水相制备及其对人血淋巴细胞的标记成像

首次用谷胱甘肽(GSH)作为稳定剂,在水溶液中制备了稳定地发射绿色荧光和橙色荧光的两种 CdSe/CdS核/壳结构的纳米量子点。用紫外-可见分光光度和荧光光谱方法研究了CdSe/CdS量子点的发光特性。透射电镜(TEM)结果表明CdSe/CdS量子点近似球形,在水中分散性良好,比CdSe量子点具有更优异的发光特性,发射光谱和吸收光谱都有红移现象。将CdSe/CdS量子点与鼠抗人CD3抗体连接,制备了水溶性CdSe/CdS-CD3复合物探针,对人血淋巴细胞进行标记和成像。结果表明用该探针对人血淋巴细胞成像清晰,其荧光在30 min的连续蓝光激发下无明显衰退,而FITC荧光在20 min内基本完全猝灭。     

Self-assembly of dandelion-like Fe3O4@C@BiOCl magnetic nanocomposites with excellent solar-driven photocatalytic properties

In comparison with conventional organic dyes, quantum dots (QDs) have unique optical and electronic properties, which provide QDs with a wide scope of prospective application in biology and biomedicine. However, the toxicity of QDs and the fluorescence intensity of labeled bacteria must precede their application in bacterial imaging and tracing in vivo. Here, we show that treatment with CaCl₂ significantly improved bacterial labeling efficiency of CdSe/ZnS QDs with the CdSe core size of ~3.1 nm (relative fluorescence unit (RFU) value and ratio of fluorescent E. coli) with rising CdSe/ZnS QDs concentration in a concentration-dependent manner. At 12.5 nmol/L CdSe/ZnS QDs concentration, labeled Escherichia coli (E. coli) DH5α appeared as short rod-shaped and luminescent with normal size, and the survival rate and ultrastructure did not change in comparison to the control. But the ratio of fluorescent bacteria and RFU were very low. However, the survival rate of transformed E. coli was significantly inhibited by high CdSe/ZnS QDs concentrations (≥25 nmol/L). Moreover, internalization of CdSe/ZnS QDs resulted in ultrastructure damage of transformed E. coli in a concentration-dependent manner (≥25 nmol/L). Therefore, CdSe/ZnS QDs may not suitable for tracing of bacteria in vivo. Moreover, our study also revealed that colony-forming capability assay and transmission electron microscopy could be used to comprehensively evaluate the toxicity of QDs on labeled bacteria. Our findings do provide a new direction toward the improvement and modification of QDs for use in imaging and tracing studies in vivo.     

ZnO作为电子传输层的绿光胶体CdSe量子点LED(QD-LED)的制备与表征

通过调节作为发光层的量子点的尺寸,可以制作出覆盖可见光(380～780 nm)以及近红外光谱的量子点LED(QD-LED),其光谱范围很窄且半高宽可达30 nm。然而量子点LED的寿命、亮度以及效率需要进一步提高才能满足商业化的需求。为了研究QD-LED器件的特性,本文采用523 nm波长的CdSe/ZnS核壳型量子点为发光层、poly-TPD为空穴传输层、ZnO为电子传输层,制备了绿光量子点LED,并表征了器件的特性。     

The effect of a gas environment on the fluorescence intensity of quantum-dot composite systems

The fluorescence kinetics of a composite structure based on colloidal CdSe/ZnS core-shell quantum dots deposited on an array of GaAs nanowires in atmospheres of different gases is studied upon excitation by cw laser radiation. It is suggested that the fluorescence enhancement mechanism consists in the transfer of part of the vibrational energy of quantum dots to surrounding gas molecules due to inelastic collisions.     

Phase transfer of agglomerated nanoparticles: deagglomeration by adsorbing grafted molecules and colloidal stability in polymer solutions

We aimed to develop liposomes for loading both cisplatin and quantum dots (QDs) for both drug delivery and bioimaging. The resultant quantum-dot-liposomes (QDLs) with cisplatin were characterized using dynamic light scattering, transmission electron microscopy (TEM), encapsulation efficiencies, and fluorescence intensity. QDLs composed of CdSe or CdSe/ZnS QDs represented a size of about 100?nm. The QDLs were prepared at a high QD loading efficiency of nearly 100?%. Most QDs were located within the liposomal bilayers as evidenced by TEM. Slow and sustained cisplatin release from QDLs was achieved. The cellular uptake of QDLs demonstrated effective internalization and significant fluorescence in melanoma cells. The signal derived from QDLs could be observed by different wavelength settings. The cisplatin-containing QDLs revealed higher cytotoxic activity compared to an equal dose of free cisplatin. CdSe/ZnS QDLs were intravenously administered to mice, and the biodistribution was observed with an in vivo imaging system. Significant fluorescence signal and cisplatin accumulation were detected in the brain and skin, as verified by ex vivo imaging and drug distribution. Liposomal inclusion could reduce the reticuloendothelial system uptake of QDs and cisplatin. QDLs evaluated in this study represent a new potential method for theranostic purposes.     

Complex formation of CdSe/ZnS/TOPO nanocrystal vs. molecular chaperone in aqueous solution by hydrophobic interaction

Feasibilities to stabilize CdSe/ZnS/trioctylphosphineoxide (TOPO) nanocrystals (quantum dots, QDs) in aqueous solutions with prefoldin macromolecules in their bioactive states are reported. Prefoldin is a jellyfish-shaped hexameric co-chaperone of the group II chaperonins. As a protein folding intermediate is captured within its central cavity, so CdSe/ZnS/TOPO QDs would also be included within this cavity. It is also found the QDs can be much more dispersed in aqueous solutions and suspended for certain period of time by adding trace amount of t-butanol in the buffer prior to the mixing of the QDs mother solution. While biochemical procedures are evaluated with ordinary fluorescence measurements, possible complex formations are also evaluated with TIRFM single-molecule detection techniques.     

ZnS:Ag/CdS: a new family of color-tunable quantum dots

ZnS:Ag/CdS quantum dots (QDs) have been synthesized by a reverse micelle process under ambient environment. Excited by 350?nm, the emission peak of ZnS:Ag/CdS QDs changes from 425 to 625?nm with increasing the thickness of CdS shells. Although the quantum yields of QDs decrease with CdS shells thickening, the luminescent brightness remains stable throughout. Compared with the traditional color-tunable CdSe QDs, the synthesis of ZnS:Ag/CdS QDs is less toxic and more economic. Therefore, this synthesis process can be regarded as an efficient way to fabricate a series of luminescent nanostructures for a variety of applications.     

界面电子转移对量子点荧光闪烁行为的影响

利用激光扫描共聚焦显微系统分别测量了CdSe/ZnS量子点在SiO2玻片表面、铟锡氧化物(ITO)纳米粒子表面和聚甲基丙烯酸甲酯(PMMA)薄膜表面上的荧光闪烁行为.研究发现,不同界面环境中量子点的亮态发光持续时间的概率密度都服从指数修正的幂律分布P(t)∝t-αexp(-t/μ).与处于SiO2玻片表面的情况相比,在ITO表面上的单量子点具有非常短暂的亮态发光持续时间,而在PMMA表面的单量子点亮态发光持续时间最长.这种荧光闪烁行为的不同主要归因于量子点与三种材料之间的界面电子转移特性.     

A Feasible and Quantitative Encoding Method for Microbeads with Multicolor Quantum Dots

Multicolor encoded beads were achieved by incorporating two color core-shell quantum dots (QDs) (CdSe/ZnS) to commercial polystyrene (PS) beads. By controlling the concentration ratios of the two quantum dots (QDs) in doping solutions, a series of codes with different intensity ratios were obtained. Based on the multiple encoded carboxylic modified polystyrene beads, fluorescent dyes labeled antibodies were distinguished successfully on the beads’ surface. It suggests that the encoded beads from this method have the practicability in biological applications and chemical analysis. Hai-Qiao Wang and Zhen-Li Huang authors contribute equally to this work     

Photostability comparison of CdTe and CdSe/CdS/ZnS quantum dots in living cells under single and two-photon excitations

The photostability is an outstanding feature of quantum dots (QDs) used as fluorescence probes in biological staining and cell imaging. To find out the related factors in the QD photostability, the photobleaching of naked CdTe QDs and BSA coated CdSe/CdS/ZnS QDs in human hepatocellular carcinoma (QGY) cells and human nasopharynx carcinoma (KB) cells were studied under single photon excitation (SPE) and two-photon excitation (TPE). In these two cell lines the cellular QDs were irradiated by a 405 nm continuous wave laser for SPE or an 800 nm femto-second (fs) laser for TPE. The QD photobleaching with the irradiation time was found to fit a biexponential decay. The fast decay plays a dominant role in the bleaching course and thus can be used as the parameter to quantitatively evaluate the QD photostability. The TPE decreased the QD photobleaching as compared to SPE. The BSA coated core/shell QDs had improved the photostability up to 4-5 times than the naked QDs due to the shielding effect of the QD shell. Therefore, it is better to use core/shell structured QDs as the fluorescence probe combining with a TPE manner for those long-term monitoring studies.     

Re-charging the luminescence states in CdSe/ZnS quantum dots at the conjugation to Osteopontin antibodies

The paper presents the original study of photoluminescence (PL) and Raman scattering spectra of core–shell CdSe/ZnS quantum dots (QDs) covered by the amine-derivatized polyethylene glycol (PEG) with luminescence interface states. First commercially available CdSe/ZnS QDs with emission at 640 nm (1.94 eV) covered by PEG polymer have been studied in nonconjugated states. PL spectra of nonconjugated QDs are characterized by a superposition of PL bands related to exciton emission in a CdSe core and to the hot electron–hole recombination via high energy luminescence states. The study of high energy PL bands in QDs at different temperatures has shown that these PL bands are related to luminescence interface states at the CdSe/ZnS or ZnS/polymer interface. Then CdSe/ZnS QDs have been conjugated with biomolecules—the Osteopontin antibodies. It is revealed that the PL spectrum of bioconjugated QDs changed essentially with decreasing hot electron–hole recombination flow via luminescence interface states. It is shown that the QD bioconjugation process to Osteopontin antibodies is complex and includes the covalent and electrostatic interactions between them. The variation of PL spectra due to the bioconjugation is explained on the basis of electrostatic interaction between the QDs and biomolecule dipoles that stimulates re-charging QD interface states. The study of Raman scattering of bioconjugated CdSe/ZnS QDs has confirmed that the antibody molecules have the electric dipoles. It is shown that CdSe/ZnS QDs with luminescence interface states are promising for the study of bioconjugation effects with specific antibodies and can be a powerful technique in biology and medicine.     

Stability and luminescence properties of CsPbBr3/CdSe/Al core-shell quantum dots

To improve the stability and luminescence properties of CsPbBr₃ QDs, we proposed a new core-shell structure for CsPbBr₃/CdSe/Al quantum dots (QDs). By using a simple method of ion layer adsorption and a reaction method, CdSe and Al were respectively packaged on the surface of CsPbBr₃ QDs to form the core-shell CsPbBr₃/CdSe/Al QDs. After one week in a natural environment, the photoluminescence quantum yields of CsPbBr₃/CdSe/Al QDs were greater than 80%, and the PL intensity remained at 71% of the original intensity. Furthermore, the CsPbBr₃/CdSe/Al QDs were used as green emitters for white light-emitting diodes (LEDs), with the LEDs spectrum covering 129% of the national television system committee (NTSC) standard color gamut. The core-shell structure of QDs can effectively improve the stability of CsPbBr₃ QDs, which has promising prospects in optoelectronic devices.