Effect of electron beam on structural,linear and nonlinear properties of nanostructured Fluorine doped ZnO thin films

Electron beam induced effects on Fluorine doped ZnO thin films (FZO) grown by chemical spray pyrolysis deposition technique were studied. The samples were exposed to 8 MeV electron beam at different dose rate ranging from 1 kGy to 4 kGy. All films exhibit a polycrystalline nature which shows an increase in crystallanity with irradiation dosages. The electron beam irradiation effectively controls the films surface morphology and its linear optical characteristics. Z-Scan technique was employed to evaluate the sign and magnitude of nonlinear refractive index and nonlinear absorption coefficient using a continuous wave laser at 632.8 nm as light source. Enhancement in the third order nonlinear optical properties was were noted due to electron beam irradiation. Tailoring the physical and NLO properties by electron beam, the FZO thin films becomes a promising candidate for various optoelectronic applications such as phase change memory devices, optical pulse compression, optical switching and laser pulse narrowing.     

Microwave irradiation on carbon black: Studies on the transformation of particles into nano-balls,nano-sticks and nano-onion like structures

The solid-state transformation behavior of carbon black (CB) nanoparticles after irradiated with microwave energy was studied with and without influence of a metal catalyst. The CB sample was exposed to microwave radiation at power of 900 W from the oven and collected after 15 min and after 30 min and 45 min of irradiation. The samples were characterized using X-ray diffraction measurements, Raman spectroscopy, scanning electron microscopy, high-resolution transmission electron microscopy (HRTEM) and thermogravimetric analysis. Characterization of the samples prepared without catalyst shows that microwave irradiation can transform CB nanoparticles into nano–balls and nano–stick like structures. While nanoballs of almost 300–500 nm diameter are visible in all the samples irrespective of microwave irradiation time, amorphous nano-stick like structure are present only in the sample collected after 30 min of microwave irradiation. CB irradiated together with a metal catalyst resulted in metal-encapsulated onion like structures with perfectly arranged graphene layers.     

Three-dimensional space charge cartographies by FLIMM in electron irradiated polymers

High resolution three-dimensional space charge cartographies obtained on 50 μm PTFE samples by using FLIMM technique are presented in this article. Samples were irradiated by a 30 keV electron beam. Charges were injected according to the grid pattern put on the sample during irradiation. A new measurement strategy associated with a new set-up leads to an improvement in measurements accuracy and precision. With this new strategy, measurements were performed rapidly, at a chosen depth and with a low lateral resolution in order to map the space charge profile in the whole sample and to choose a study area. After selecting an interesting area, space charge cartographies were carried out with a very high lateral resolution of about 1 μm. The irradiated zones according to the grid pattern were well reconstructed and the injection depth did not exceed 4 μm.     

Diffraction patterns and nonlinear optical properties of gold nanoparticles

Stable gold nanoparticles have been prepared by using soluble starch as both the reducing and stabilizing agents; this reaction was carried out at 40 °C for 5 h. The obtained gold nanoparticles were characterized by UV–Vis absorption spectroscopy, transmission electron microscopy (TEM) and z-scan technique. The size of these nanoparticles was found to be in the range of 12–22 nm as analyzed using transmission electron micrographs. The optical properties of gold nanoparticles have been measured showing the surface plasmon resonance. The second-order nonlinear optical (NLO) properties were investigated by using a continuous-wave (CW) He–Ne laser beam with a wavelength of 632.8 nm at three different incident intensities by means of single beam techniques. The nonlinear refractive indices of gold nanoparticles were obtained from close aperture z-scan in order of 10^?7 cm²/W. Then, they were compared with diffraction patterns observed in far-field. The nonlinear absorption of these nanoparticles was obtained from open aperture z-scan technique. The values of nonlinear absorption coefficient are obtained in order of 10^?1 cm/W.     

Study on the bias-dependent effects of proton-induced damage in CdZnTe radiation detectors using ion beam induced charge microscopy

The influence of damage induced by 2 MeV protons on CdZnTe radiation detectors is investigated using ion beam induced charge (IBIC) microscopy. Charge collection efficiency (CCE) in irradiated region is found to be degraded above a fluence of 3.3 × 10¹¹ p/cm² and the energy spectrum is severely deteriorated with increasing fluence. Moreover, CCE maps obtained under the applied biases from 50 V to 400 V suggests that local radiation damage results in significant degradation of CCE uniformity, especially under low bias, i. e., 50 V and 100 V. The CCE nonuniformity induced by local radiation damage, however, can be greatly improved by increasing the detector applied bias. This bias-dependent effect of 2 MeV proton-induced radiation damage in CdZnTe detectors is attributed to the interaction of electron cloud and radiation-induced displacement defects.     

Analysis of microscopic parameters of surface charging in polymer caused by defocused electron beam irradiation

The relationship between microscopic parameters and polymer charging caused by defocused electron beam irradiation is investigated using a dynamic scattering-transport model. The dynamic charging process of an irradiated polymer using a defocused 30 keV electron beam is conducted. In this study, the space charge distribution with a 30 keV non-penetrating e-beam is negative and supported by some existing experimental data. The internal potential is negative, but relatively high near the surface, and it decreases to a maximum negative value at z = 6 μm and finally tend to 0 at the bottom of film. The leakage current and the surface potential behave similarly, and the secondary electron and leakage currents follow the charging equilibrium condition. The surface potential decreases with increasing beam current density, trap concentration, capture cross section, film thickness and electron–hole recombination rate, but with decreasing electron mobility and electron energy. The total charge density increases with increasing beam current density, trap concentration, capture cross section, film thickness and electron–hole recombination rate, but with decreasing electron mobility and electron energy. This study shows a comprehensive analysis of microscopic factors of surface charging characteristics in an electron-based surface microscopy and analysis.     

Ultrastructural analysis of the low level laser therapy effects on the lesioned anterior tibial muscle in the Gerbil

Low level laser therapy (LLLT) is known for its positive results but studies on the biological and biomodulator characteristics of the effects produced in the skeletal muscle are still lacking. In this study the effects of two laser dosages, 5 or 10 J/cm², on the lesioned tibial muscle were compared. Gerbils previously lesioned by 100 g load impact were divided into three groups: GI (n = 5) controls, lesion non-irradiated; GII (n = 5), lesion irradiated with 5 J/cm² and GIII (n = 5), lesion irradiated with 10 J/cm², and treated for 7 consecutive days with a laser He–Ne (λ = 633 nm). After intracardiac perfusion, the muscles were dissected and reduced to small fragments, post-fixed in 1% osmium tetroxide, dehydrated in increasing alcohol concentrations, treated with propylene oxide and embedded in Spurr resin at 60 °C. Ultrafine cuts examined on a transmission electron microscope (Jeol 1010) revealed in the control GI group a large number of altered muscle fibers with degenerating mitochondria, intercellular substance containing degenerating cell fragments and budding blood capillaries with underdeveloped endothelial cells. However, groups GII and GIII showed muscle fibers with few altered myofibrils, regularly contoured mitochondria, ample intermembrane spaces and dilated mitochondrial crests. The clean intercellular substance showed numerous collagen fibers and capillaries with multiple abluminal processes, intraluminal protrusions and several pinocytic vesicles in endothelial cells. It was concluded that laser dosages of 5 or 10 J/cm² delivered by laser He–Ne (λ = 633 nm) during 7 consecutive days increase mitochondrial activity in muscular fibers, activate fibroblasts and macrophages and stimulate angiogenesis, thus suggesting effectivity of laser therapy under these experimental conditions.     

Color filters featuring high transmission efficiency and broad bandwidth based on resonant waveguide-metallic grating

A one-dimensional transmission color filter based on a resonant waveguide-metallic subwavelength grating was numerically investigated by employing rigorous coupled-wave analysis (RCWA) and genetic algorithm (GA). The hybrid numerical method is used to determine the optimal parameters (the grating period, filling factor, grating thickness, and waveguide thickness) of two waveguide-grating structures, namely a double-layer resonant waveguide-metallic grating and a triple-layer resonant waveguide-metallic grating. The optical responses of these structures are evaluated and compared in terms of the ideal transmission efficiency aiming at the central wavelengths of 645 nm, 546 nm, and 455 nm of red (R), green (G), and blue (B) lights, respectively, over the visible region (380–780 nm). The results show that the optical performance of the double-layer with silver grating achieves the highest transmission efficiency of 82% (R), 81% (G), and 66% (B); and the largest bandwidth of about 125 nm (R), 118 nm (G), and 85 nm (B). Compared with existing color filters, the proposed device not only obtains a higher transmission and broader bandwidth, but it also suppresses redundant spectral peaks and transmission sidebands.     

Multi-spectral antireflection coating on zinc sulphide simultaneously effective in visible,eye safe laser wave length and MWIR region

In recent years multi-spectral device is steadily growing popularity. Multi-spectral antireflection coating effective in visible region for sighting system, laser wavelength for ranging and MWIR region for thermal system can use common objective/receiver optics highly useful for state of art thermal instrumentation. In this paper, design and fabrication of antireflection coating simultaneously effective in visible region (450–650 nm), Eye safe laser wave length (1540 nm) and MWIR region (3.6–4.9 μm) has been reported. Comprehensive search method of design was used and the number of layers in the design was optimised with lowest evaluated merit function studied with respect to various layers. Finally eight-layer design stack was established using hafnium oxide as high index layer and silicon-di-oxide as low index coating material combination. The multilayer stack had been fabricated by using electron beam gun evaporation system in Symphony 9 vacuum coating unit. During layer deposition the substrate was irradiated with End-Hall ion gun. The evaporation was carried out in presence of oxygen and layer thicknesses were measured with crystal monitor. The result achieved for the antireflection coating was 85% average transmission from 450 to 650 nm in visible region, 95% transmission at 1540 nm and 96% average transmission from 3.6 to 4.9 μm in MWIR region.     

Electron beam irradiation induced changes in the dielectric and electro-optical properties of a room temperature nematic display material 4-(trans-4′-n-hexylcyclohexyl) isothiocyanatobenzoate (6CHBT)

Dielectric and electro-optical studies of a pure and electron beam irradiated liquid crystalline compound 4-(trans-4′-n-hexylcyclohexyl) isothiocyanatobenzoate have been carried out. Dielectric anisotropy, relaxation frequency, activation energy and distribution parameter of an observed non-collective mode corresponding to the molecular rotation about the short axes have been determined as a function of temperature and irradiation dose whereas threshold and switching voltages, splay elastic constant are determined as a function of irradiation dose. The relaxation frequencies initially decrease up to an irradiation dose of 40 kGy but thereafter increase due to irradiation. The activation energies are increased up to irradiation dose of 40 kGy but around 60 kGy dose of irradiation, we found decrease in the activation energy. Electro-optical measurements show the lowering of the threshold voltage with sufficient improvement in the steepness of the transmission voltage curves due to irradiation. The observed changes in the dielectric and electro-optical properties are related with the cis–trans isomerization due to electron beam irradiation.     

Preparation of micro-foils for TEM/STEM analysis from metallic powders

A technique has been developed which facilitates the preparation of electro-polished micro-foil transmission electron microscopy (TEM) specimens, which have previously been machined out of ≈100 μm diameter metallic powder particles using a Focussed Ion Beam (FIB) instrument. The technique can be used to create small volume TEM specimens from most metallic powder particles and bulk metal samples. This is especially useful when the matrices are ferritic steels, which are often difficult to image in the electron microscope, since the necessary aberration corrections change as the sample is tilted in the magnetic field of the objective lens.Small samples, such as powder particles, were attached to gold support grids using deposited platinum and were then ion milled to approximately 2 μm thickness in a focussed ion beam (FIB) instrument. Subsequently, the specimen assemblies were electropolished for short durations under standard conditions, to produce large (5 μm × 5 μm) electron transparent regions of material. The specimens produced by this technique were free from FIB related artefacts and facilitated atomic resolution scanning-TEM (STEM) imaging of ferritic and nickel matrices containing, for example, yttrium rich oxide nano-dispersoids.     

Effect of calcination temperature on phase transformation,structural and optical properties of sol–gel derived ZrO2 nanostructures

Zirconia (ZrO₂) nanostructures of various sizes have been synthesized using sol–gel method followed by calcination of the samples from 500 to 700 °C. The calcined ZrO₂ powder samples were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), Fourier-transform infra-red spectroscopy (FT-IR), UV–visible spectroscopy (UV–vis.), Raman spectroscopy (RS) and thermogravimetric analysis (TGA). The phase transformation from tetragonal (t) to monoclinic (m) was observed. The average diameter of the ZrO₂ nanostructures calcined at 500, 600 and 700 °C was calculated to be 8, 17 and 10 nm, respectively. The ZrO₂ sample calcined at 500 °C with tetragonal phase shows a direct optical band gap of 5.1 eV. The value of optical band gap is decreased to 4.3 eV for the ZrO₂ calcined at 600 °C, which contains both tetragonal (73%) and monoclinic (27%) phases. On further calcination at 700 °C, where the ZrO₂ nanostructures have 36% tetragonal and 64% monoclinic phases, the optical band gap is calculated to be 4.8 eV. The enhancement in optical band gap for ZrO₂ calcined at 700 °C may be due to the rod like shape of ZrO₂ nanostructures. The tetragonal to monoclinic phase transformation was also confirmed by analyzing Raman spectroscopic data. The TG analysis revealed that the ZrO₂ nanostructure with dominance of monoclinic phase is found to be more stable over the tetragonal phase. In order to confirm the phase stability of the two phases of ZrO₂, single point energy is calculated corresponding to its monoclinic and tetragonal structures using density functional theory (DFT) calculations. The results obtained by theoretical calculations are in good agreement with the experimental findings.     

EPR and UV spectroscopic investigations of sucrose irradiated with heavy-ion particles

Crystalline sucrose irradiated with C and Si ions is investigated with EPR and UV spectroscopy. Samples are treated at different doses of radiation in the region 20–300 Gy and linear energy transfer (LET) values of 39.6, 49 and 58 keV μm^?1 for C ions and 60 keV μm^?1 for Si ions. All samples exhibit identical EPR spectra due to radiation-induced stable sucrose radicals. At given constant LET the EPR signal responses are linear to the absorbed doses of Si and C ions. Water solutions of irradiated sucrose exhibit UV absorption maximum at 267 nm due to the product of radical recombination. The intensity of this band is stronger at irradiation with Si than with C ions. UV absorption is more sensitive to heavy-ion species irradiation than the EPR signals.     

Third-order nonlinear optical response of newly synthesized accepter/donor substituted propylidene aryloxy acet hydrazide

A class of organic compounds namely propylidene aryloxy acet hydrazide derivatives were synthesized. The third-order nonlinear optical properties and optical limiting studies of the compounds were investigated using the single beam Z-scan technique at 532 nm. The Z-scan study reveals that the compounds exhibit a self-defocusing effect at 532 nm. The calculated values of nonlinear refractive index, third-order nonlinear optical susceptibility and second order molecular hyperpolarizability are of the order of 10^?11 esu, 10^?13 esu and 10^?31 esu, respectively. The compounds exhibit good optical limiting properties at the wavelength used.     

Spectroscopic characterizations of individual single-crystalline GaN nanowires in visible/ultra-violet regime

Spectroscopic investigations of individual single-crystalline GaN nanowires with a lateral dimensions of ～30–90 nm were performed using the spatially resolved technique of electron energy-loss spectroscopy in conjunction with scanning transmission electron microscope showing a 2-Å electron probe. Positioning the electron probe upon transmission impact and at aloof setup with respect to the nanomaterials, we explored two types of surface modes intrinsic to GaN, surface exciton polaritons at ～8.3 eV (～150 nm) and surface guided modes at 3.88 eV (～320 nm), which are in visible/ultra-violet spectral regime above GaN bandgap of ～3.3 eV (～375 nm) and difficult to access by conventional optical spectroscopies. The explorations of these electromagnetic resonances might expand the current technical interests in GaN nanomaterials from the visible/UV range below ～3.5 eV to the spectral regime further beyond.     

Thermal stability of iron nitrides prepared by mixing laser and plasma beam nitriding technology

Thermal stability of iron nitrides prepared by mixing laser and plasma beam nitriding (LPN) technology was studied. The treated samples were annealed in vacuum at different temperature from 473 K to 1273 K. The phases were detected by X-ray diffraction (XRD), the nitride’s contents were calculated from the patterns of XRD, and the microstructures were analyzed by scanning electron microscope (SEM). Three critical temperatures (473 K, 673 K, and 1273 K) are found. Due to deeper nitriding layer in the LPN sample, the nitrides is more stable than that in laser-produced sample at the annealing temperature higher than 973 K. It is important and central for some potential industrial productions and applications.     

Sonochemical preparation of SbSeI gel

A novel sonochemical method for direct preparation of nanocrystalline antimony selenoiodide (SbSeI) has been established. The SbSeI gel was synthesized using elemental Sb, Se, and I in the presence of ethanol under ultrasonic irradiation (35 kHz, 2 W/cm²) at 50 °C for 2 h. The product was characterized by using techniques such as powder X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-ray analysis (EDAX), high-resolution transmission electron microscopy (HRTEM), selected area electron diffraction (SAED), and optical diffuse reflection spectroscopy (DRS). The SEM and HRTEM investigations exhibit that the as-prepared samples are made up of large quantity nanowires with lateral dimensions of about 20–50 nm and lengths reaching up to several micrometers and single crystalline in nature.     

Focused electron beam induced deposition as a tool to create electron vortices

Focused electron beam induced deposition (FEBID) is a microscopic technique that allows geometrically controlled material deposition with very high spatial resolution. This technique was used to create a spiral aperture capable of generating electron vortex beams in a transmission electron microscope (TEM). The vortex was then fully characterized using different TEM techniques, estimating the average orbital angular momentum to be ∼0.8ℏ per electron with almost 60% of the beam ending up in the ℓ = 1 state.