层状纳米纤维素膜/PVA复合水凝胶的制备与力学性能研究

采用叠层复合与物理相分离的方法制备了层状纳米细菌纤维素(BC)膜/聚乙烯醇( PVA)复合水凝胶.研究了聚乙烯醇的质量百分数、BC膜的复合层数以及制备条件对复合水凝胶力学性能的影响;通过扫描电镜( SEM)观察比较了复合水凝胶中BC膜层与PVA界面结合情况.结果表明,复合水凝胶的力学性能与PVA的质量百分数和BC膜含水...     

多孔β-磷酸三钙/壳聚糖/聚乙烯醇复合水凝胶的制备与性能

以NaCl为致孔剂,采用溶盐致孔法制备了多孔β-磷酸三钙/壳聚糖/聚乙烯醇（β-TCP/CS/PVA）复合水凝胶材料。 通过对比其含水率、溶胀比、拉伸强度、X射线衍射谱图、SEM和热重分析曲线,探讨了在相同环境下壳聚糖与β-磷酸三钙（β-TCP）的不同用量对聚乙烯醇(PVA)的结晶度以及对材料性能的影响。 此复合材料含水率为70%~76%。 当壳聚糖与β-TCP的质量比为2∶8时,复合材料的拉伸强度为0.56 MPa,断裂伸长率达到370%,其较好的力学性能,足以承受正常人眼压,可用作人工角膜周边支架材料。     

聚苯胺／聚乙烯醇导电复合膜的制备及性质研究

用较简单的化学氧化现场吸附聚合法（ｉｎ－ｓｉｔｕｐｏｌｙｍｅｒｉｚａｔｉｏｎ）制得了聚苯胺（ＰＡｎ）／聚乙烯醇（ＰＶＡ）导电复合膜．该膜具有较好的导电性和机械性能；其电导率可达５．８ｓ／ｃｍ，拉伸强度达１３ＭＰａ，断裂伸长率为１１０％左右．本文讨论了制备的各种条件对复合膜导电性能及力学性能的影响、稳定性及电化学活性；并采用循环伏安曲线、扫描电镜（ＳＥＭ）、ＦＴＩＲ谱及元素分析对该复合膜的结构和性能进行了表征．     

肝素钠/聚乙烯醇复合水凝胶的制备与性能

通过循环冷冻-解冻法,制成了肝素钠/聚乙烯醇(HS/PVA)复合水凝胶材料。 探讨了不同质量分数肝素钠对复合水凝胶材料的可见光透过率、含水率、亲水性、力学性能以及肝素钠释放量的影响。 结果表明,复合水凝胶的可见光透过率为92%以上,溶胀平衡的含水率为72%~78%,亲水性较纯PVA水凝胶有所提升,拉伸强度和断裂伸长率都稍有下降。 细胞粘附实验结果表明,适量的肝素钠的释放可以达到减少细胞粘附的效果。 这种HS/PVA复合水凝胶材料有望用作人工角膜中心区材料。     

PVA改性PAMPS-PAM超高力学性能双网络水凝胶的制备

采用紫外光引发聚合制备了聚乙烯醇(PVA)改性的聚(2-丙烯酰胺基-2-甲基丙磺酸)-聚丙烯酰胺(PAMPS-PAM)双网络(DN)水凝胶.测定并比较了PVA改性前后PAMPS-PAM双网络水凝胶的溶胀动力学;通过扫描电子显微镜(SEM)观察了单网络水凝胶的结构;测定PVA改性前后PAMPS-PAM双网络水凝胶的压缩及拉伸性能.结果表明,经PVA改性后的PAMPS-PAM双网络水凝胶有较高的溶胀比;0.82%PVA用量的PAMPS-PAM双网络水凝胶在90%压缩形变率下仍保持完整、最大拉伸应力达到0.5 MPa,大幅提高PAMPS-PAM双网络水凝胶的力学性能.     

强韧抗溶胀水凝胶的简单构筑及性能

以聚乙烯醇(PVA)和壳聚糖(CS)为原料, 采用循环冻融法制备了前驱体水凝胶(PVA-CS), 并经过浸泡氯化钠溶液和透析后处理构筑了强韧抗溶胀复合水凝胶(PVA-CS-6.16-30). 采用扫描电子显微镜(SEM)、 傅里叶变换红外光谱仪(FTIR)、 X射线衍射分析仪(XRD)、 差示扫描量热分析仪(DSC)及流变仪表征了两种水凝胶的微观结构, 采用拉力机测试了其机械性能. 结果表明: 由于结晶微区、 氢键及链缠结等协同交联作用, PVA-CS-6.16-30具备高效能量耗散机制. 与前驱体PVA-CS相比, PVA-CS-6.16-30的交联密度由7.69×10^?4 mol/cm³增加至9.97×10^?4 mol/cm³, 自由水含量由62.8%降低至52.6%, 网络尺寸由6.11 nm降低至5.21 nm, 凝胶分数由58.6%增加至86.8%, PVA结晶度由14.8%增加至17.2%, 其抗拉强度、 断裂伸长率、 韧性及抗压强度分别为2.9 MPa, 229%, 3.3 MJ/m³和7.6 MPa. 此外, 该复合水凝胶还具有优异的耐溶胀与抗蠕变性能. 在37 ℃的PBS缓冲溶液中浸泡7 d后, 其抗拉和抗压强度分别高达2.8和7.5 MPa, 优于常见水凝胶. 商品化的原料、 简单的构筑方法及优异的综合性能有望推动水凝胶在组织工程和生物医疗领域的应用.     

聚乙烯醇/聚乙烯吡咯烷酮/碘复合水凝胶的制备与性能

采用低温冷冻的方法, 通过改变聚乙烯醇(PVA)和聚乙烯吡咯烷酮碘络合物(PVP-I)的配比、 冷冻时间、 冷冻-解冻循环次数, 制备出一种可调控力学性能的PVA/PVP-I复合水凝胶. 研究了该复合水凝胶的机械 性能、 微观结构、 碘缓释性能和抑菌性质. 研究结果表明, PVA/PVP-I复合水凝胶可调控的力学性质可以满足伤口敷料对水凝胶力学性质的需求; 复合水凝胶的网络结构可以有效降低碘在紫外线下的分解速度, 实现对碘的稳定保护作用及控制释放, 从而发挥水凝胶持续抑菌性能, 为抑菌水凝胶的设计制备提供了新思路.     

组分对含羟基磷灰石/脂肪族聚氨酯复合骨组织工程支架的理化性能及生物学性能的影响

以异佛尔酮二异氰酸酯为聚氨酯硬段,通过原位聚合使聚合过程中释放的气体发泡,制备了用作骨组织工程材料的羟基磷灰石/脂肪族聚氨酯多孔支架.系统考察了不同组成配方,即羟基磷灰石(HA)含量、发泡剂含量以及聚氨酯(PU)软硬段的比例对三维支架材料的机械性能和微观孔隙结构等的影响,并通过体外细胞培养和体内肌肉植入初步评价了该复合...     

聚乙烯醇/壳聚糖复合水凝胶的物理化学性质

测定了聚乙烯醇(PVA)和壳聚糖(CS)复合水凝胶的平衡含水量、熔融焓、等温溶胀动力学和非等温失水动力学等性质,讨论了水凝胶的组成和制备参数对这些性质的影响.结果显示:PVA/CS复合水凝胶具有适宜于软骨修复替代材料的网络结构和平衡含水量.CS与PVA复合减弱了凝胶的结晶度,但却增强了水与凝胶支架的相互作用.尽管水凝胶力学拉伸强度有所降低,但却优化了凝胶的生物相容性和降解能力.PVA/CS复合水凝胶是一种潜在的软骨修复材料,作为一种理论研究的模型体系,它将促进热力学在复杂医用材料方面的应用.     

聚富马酸丙二醇酯/羟基磷灰石复合多孔水凝胶的制备及其矿化性能研究

采用二步法合成了可降解的聚富马酸丙二醇酯(poly(propylene fumarate),PPF),并和N-乙烯基吡咯烷酮(N-vinyl pyrrolidone,NVP)共聚,以1,4-二氧六环为溶剂,通过改变溶剂的量制备了溶胀性能不同的PPF水凝胶.采用万能力学测试仪和扫描电子显微镜分别表征了水凝胶的压缩模量和形貌结构.选择20％ PPF和10％ NVP的聚合体系,预掺3％的纳米羟基磷灰石(hydroxyapatite,HA),以氯化钠粒子为致孔剂,制备了孔径在280～450 μm的纳米复合多孔水凝胶,使其压缩模量提高了61％.模拟体液矿化10天的结果显示,磷灰石成核位点的存在和良好的与外界液体环境物质交换的能力,促进了多孔水凝胶表面磷灰石的沉积,说明HA的复合可以有效提高PPF多孔水凝胶的成骨活性.     

Viscoelasticity,mechanical properties,and in vivo biocompatibility of injectable polyvinyl alcohol/bioactive glass composite hydrogels as potential bone tissue scaffolds

Abstract

An injectable composite hydrogel composed of polyvinyl alcohol (PVA) and bioactive glass (BG) particles were synthesized by a physical crosslinking approach. The morphology, mechanical properties, and viscoelasticity of the PVA/BG composite hydrogel were characterized. Scanning electronic microscopy (SEM) showed uniform and homogeneous distribution of BG particles throughout the composite hydrogel. The incorporation of 2.5?wt% of BG particles in the composite hydrogel formulations, enhanced the static compressive strength and static elastic modulus by 325% and 150%, respectively. The storage molds (G′) was greater than the loss modules (G′′) at all the frequency range studied, which revealed a self-standing elastic composite hydrogel with a smooth injectability. The PVA/BG composite hydrogel was also implanted subcutaneously in the dorsal region of adult male rats. After 4?weeks of implantation, no inflammatory cells were seen within and around the implant, which indicated that the composite hydrogel was biocompatible. The properties of the synthesized injectable PVA/BG composite hydrogel demonstrate its capability toward bone regeneration.     

Preparation and characterization of PVA/SA/HA composite hydrogels for wound dressing

A composite hydrogel based on, by introducing, polyvinyl alcohol, sodium alginate, and hyaluronic acid was fabricated using CaCl₂ as a cross-linker. The physical properties including morphology, water vapor transmission rate, and hydrophilicity were investigated. All PVA/SA/HA composite hydrogels with different compositions had highly homogeneous and interconnected pores, and the morphologies of the PVA/SA/HA hydrogels ranged from fibrous structure to irregular structure with increasing content of SA. The introduction of sodium alginate enhanced the hydrophilicity and water vapor transmission capacity of the hydrogel; however, the hydrophilicity of the composite hydrogels decreased with the increasing cross-linker content.     

原位复合法制备层状结构的壳聚糖/羟基磷灰石纳米材料

用原位复合法制备了高性能的壳聚糖/羟基磷灰石(CS/HA)纳米复合材料.用预先沉积的壳聚糖膜将含有羟基磷灰石前驱体的壳聚糖溶液与凝固液隔离,同时控制壳聚糖沉积与羟基磷灰石前驱体转化为羟基磷灰石的过程,使其缓慢且有序地进行.当pH值改变时,质子化的壳聚糖分子链在负电层诱导下有序沉积并形成层状结构与羟基磷灰石原位生成CS/HA,并实现二者分子级复合.XRD和TEM测试证实原位生成的磷酸盐是羟基磷灰石,且其颗粒长约为100nm,宽30～50nm.SEM结果表明,用原位复合法制备的材料具有层状结构,CS/HA(质量比100/5)纳米复合材料弯曲强度高达86MPa,比松质骨的高3～4倍,相当于密质骨的1/2,有望用于可承重部位的组织修复材料.     

Bentonite Reinforced Tough Composite Hydrogels as Potential Artificial Articular Cartilage

Novel tough composite hydrogels were prepared from inorganic bentonite(IB), polyvinyl alcohol(PVA) and polyethylene glycol(PEG) by means of a freeze-thaw technique, during which IB acted as multifunctional physically crosslinking junction and a filler to bridge the 3D network hydrogel; while the physical adsorption between IB and the polymer chains served as sacrificial bonds and increased the energy dissipation efficiency. The effects of different content of IB(w_IB) on the morphological, thermal, swelling, and mechanical properties of the hydrogels were investigated. It was found that the added IB promoted the material crosslinking and stability, and the mechanical properties of the hydrogels were significantly improved with increasing w_IB. The highest tensile stress of the hydrogel was achieved(1.1 MPa) when w_IBwas 5%. The synthesized hydrogels with high mechanical strength and low friction coefficient are potential candidate materials for artificial cartilage.     

Fabrication of a high-strength hydrogel with an interpenetrating network structure

Hydrogels have potential applications in many fields, but the poor mechanical strength has limited their further development. In this article, we designed a high-strength hydrogel with an interpenetrating network (IPN) structure from polyacrylamide (PAM) and poly(vinyl alcohol) (PVA). Synthesis parameters, such as PVA/AM mass ratio, crosslinker dosage and elongation time were carried out for high tensile strength and elongation. The results showed that chemical crosslinking, physical entanglement and PVA precipitates were the dominant parameters for the improvement of mechanical properties. The PVA structure transferred from crystal to amorphous due to intermolecular and intramolecular interactions (such as hydrogen bond and self-crosslinking). PVA precipitates scatterred in the brittle PAM matrix homogeneously which dispersed the applied stress and improved the hydrogel toughness. The tensile strength and elongation were extremely high, they were 2.4 MPa and 3100%, respectively. The simple method is versatile in synthesizing high-strength IPN hydrogels using many kinds of polymer species.     

Swelling and Reswelling Characteristics of Cross-Linked Poly(vinyl alcohol)/Chitosan Hydrogel Film

Poly(vinyl alcohol) (PVA), hydrogel was prepared by using glutaraldehyde as a cross-linking agent. The blend semi-synthetic hydrogel film, consisting of PVA and chitosan, was prepared from a solvent-casting technique and characterized for their intermolecular interactions using infrared method. The swelling and reswelling behaviors, as well as mechanical properties of the synthetic and semi-synthetic gels were examined by weighing and tensile testing, respectively. Cross-linking the two types of polymer with glutaraldehyde produces a film with lower crystallinity and smaller swelling and reswelling degrees, but having improved mechanical properties. Also, the two types of films show a pH-dependent swelling characteristic. It was found that, the reswelling properties of synthetic hydrogels can be improved by blending PVA with certain ratio of natural polymer. This blending film, can be improve sandy soil properties for cultivation, such as, controlled release of water.     

化学-物理法制备聚乙烯醇/壳聚糖/纳米羟基磷灰石复合水凝胶及其性能

采用化学 物理交联法制备了聚乙烯醇/壳聚糖/纳米羟基磷灰石（PVA/CS/n-HA）复合水凝胶材料。 通过对比其含水率、拉伸强度、红外光谱和TG谱图,探讨了PVA含量及戊二醛加入量对材料性能的影响。 结果表明,m(PVA)∶m（CS+n-HA）=5∶1,戊二醛质量分数为2%时,复合水凝胶材料具有较好的综合性能：含水率为82.0%、拉伸强度为2.14 MPa、断裂伸长率为343.26%;同步热分析表明,25~140 ℃,仅存在水分的蒸发,直至360 ℃材料才发生分解,说明材料的热稳定性良好;红外分析表明,CS与戊二醛发生了交联反应。     

羟基磷灰石/聚乙烯醇/壳聚糖水凝胶在模拟体液中的力学性能

从仿生学角度出发,将自制的人工角膜支架材料羟基磷灰石/聚乙烯醇/壳聚糖(n-HA/PVA/CS)浸泡在模拟体液中,对材料的含水率及力学性能进行了测试,并利用扫描电镜、X射线衍射仪、电感耦合等离子体原子发射光谱仪及热重分析仪研究了材料在模拟体液中的形貌、晶体结构、元素组成及热稳定性.结果表明,在模拟体液中,n-HA/PVA/CS复合水凝胶的含水率为80%~86%,具有较高的拉伸强度,能承受正常眼压,且热稳定性较好.在浸泡后期,n-HA/CS/PVA复合材料对Ca2+的吸附和释放达到动态平衡;而其表面含有微量的纳米羟基磷灰石沉积,有利于纤维细胞的长入.     

A nanofibrous composite membrane of PLGA-chitosan/PVA prepared by electrospinning

Tissue engineering scaffolds produced by electrospinning feature a structural similarity to the natural extracellular matrix. In this study, poly(lactide-co-glycolide) (PLGA) and chitosan/poly(vinyl alcohol) (PVA) were simultaneously electrospun from two different syringes and mixed on the rotating drum to prepare the nanofibrous composite membrane. The composite membrane was crosslinked by glutaraldehyde vapor to maintain its mechanical properties and fiber morphology in wet stage. Morphology, shrinkage, absorption in phosphate buffered solution (PBS) and mechanical properties of the electrospun membranes were characterized. Fibroblast viability on electrospun membranes was discussed by MTT [3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyl tetrazolium bromide] assay and cell morphology after 7 days of culture. Results indicated that the PBS absorption of the composite membranes, no matter crosslinked or not, was higher than the electrospun PLGA membrane due to the introduction of hydrophilic components, chitosan and PVA. After crosslinking, the composite membrane had a little shrinkage after incubating in PBS. The crosslinked composite membrane also showed moderate tensile properties. Cell culture suggested that electrospun PLGA-chitosan/PVA membrane tended to promote fibroblast attachment and proliferation. It was assumed that the nanofibrous composite membrane of electrospun PLGA-chitosan/PVA could be potentially used for skin reconstruction.     

原位沉析法制备可吸收壳聚糖/羟基磷灰石棒材

利用原位沉析法制备出一种以壳聚糖 (Chitosan ,CS)为基体 ,羟基磷灰石 (Hydroxyapatite,HA)为填料的新颖的复合材料 ,系统研究了HA含量对复合材料的力学性能和吸水率的影响 .CS HA的弯曲强度为 6 7 8(MPa) ,弯曲模量为 3 3(GPa) ,剪切强度为 2 1 2 (MPa) ,压缩强度为 4 7 8(MPa) ,均比人的自然骨高 2～ 3倍 ,基本满足了作为骨折内固定材料的力学性能的要求 .HA加入到CS使CS HA复合材料的吸水率下降 ,有助于延缓其力学强度在湿态环境下的衰减