A novel blue-emitting phosphor LiSrPO4:Eu for white LEDs

A novel blue-emitting phosphor, LiSrPO₄:Eu²⁺, was prepared by the solid-state reaction and X-ray powder diffraction (XRD) analysis confirmed the formation of LiSrPO₄:Eu²⁺. Photoluminescence (PL) results showed that the phosphor can be efficiently excited by UV-visible light from 250 to 440 nm, and exhibited bright blue emission. The effects of the doped-Eu²⁺ concentration in LiSrPO₄:Eu²⁺ on the PL were investigated in detail. The results showed that the relative PL intensity increases with Eu²⁺-concentration increasing until a maximum intensity is reached, and then it decreases due to concentration quenching and a red-shift appears, which are explained satisfactorily with the luminescent theory. Upon excited with 396 nm light, the present synthesized phosphor has higher emission intensity than that from the commercial blue phosphor, BaMgAl₁₀O₁₇:Eu²⁺. Bright blue light-emitting diodes were fabricated by the combination of the synthesized LiSrPO₄:Eu²⁺ with ∼397 nm emitting InGaN-based chips.     

Sr7Zr(PO4)6∶xEu2+蓝色荧光粉的合成及其发光特性

通过高温固相反应合成了新型的蓝色荧光粉Sr₇Zr(PO₄)₆∶xEu²⁺。通过X射线粉末衍射(XRD)、紫外可见(UV-Vis)吸收光谱、荧光光谱研究了Sr₇Zr(PO₄)₆∶xEu²⁺材料的相纯度及荧光性质。结果表明,Eu²⁺掺杂获得的Sr₇Zr(PO₄)₆∶xEu²⁺荧光粉为纯相,且200~400 nm范围内的近紫外(NUV)光均能对其进行有效的激发。在315 nm的激发下,Sr₇Zr(PO₄)₆∶xEu²⁺荧光粉发射出峰值位于415 nm左右的蓝光,且Eu²⁺在Sr₇Zr (PO₄)₆基质中的最佳掺杂浓度为0.05,相应的CIE色度坐标为(0.164,0.021),比商用BaMgAl₁₀O₁₇∶Eu²⁺(BAM)蓝色荧光粉具有更高的色纯度。     

A novel red emitting phosphor Ca2SnO4: Eu

A novel red emitting phosphor, Eu³⁺-doped Ca₂SnO₄, was prepared by the solid-state reaction. X-ray powder diffraction (XRD) analysis confirmed the formation of Ca₂SnO₄: Eu³⁺. Field-emission scanning electron-microscopy (FE-SEM) observation indicated a narrow size-distribution of about 500 nm for the particles with spherical shape. Photoluminescence measurements indicated that the phosphor exhibits bright red emission at about 615 nm under UV excitation. The excellent luminescence properties make it possible as a good candidate for plasma display panels (PDP) application. Splitting of the ⁵D₀-⁷F_J transitions of Ca₂SnO₄: Eu³⁺ suggests that the Eu³⁺ ions occupied two nonequivalent sites in the crystallite. The luminescence lifetime measurement showed a bi-exponential decay, providing other evidence for the existence of two different environments for Eu³⁺ ions.     

A new promising phosphor, Na3La2(BO3)3:Ln (Ln=Eu, Tb)

We present an efficient way to search a host for ultraviolet (UV) phosphor from UV nonlinear optical (NLO) materials. With the guidance, Na₃La₂(BO₃)₃ (NLBO), as a promising NLO material with a broad transparency range and high damage threshold, was adopted as a host material for the first time. The lanthanide ions (Tb³⁺ and Eu³⁺)-doped NLBO phosphors have been synthesized by solid-state reaction. Luminescent properties of the Ln-doped (Ln=Tb³⁺, Eu³⁺) sodium lanthanum borate were investigated under UV ray excitation. The emission spectrum was employed to probe the local environments of Eu³⁺ ions in NLBO crystal. For red phosphor, NLBO:Eu, the measured dominating emission peak was at 613 nm, which is attributed to ⁵D₀-⁷F₂ transition of Eu³⁺. The luminescence indicates that the local symmetry of Eu³⁺ in NLBO crystal lattice has no inversion center. Optimum Eu³⁺ concentration of NLBO:Eu³⁺ under UV excitation with 395 nm wavelength is about 30 mol%. The green phosphor, NLBO:Tb, showed bright green emission at 543 with 252 nm excited light. The measured concentration quenching curve demonstrated that the maximum concentration of Tb³⁺ in NLBO was about 20%. The luminescence mechanism of Ln-doped NLBO (Tb³⁺ and Eu³⁺) was analyzed. The relative high quenching concentration was also discussed.     

Defect chemistry and VUV optical properties of the BaMgAl10O17:Eu-Ba0.75Al11O17.25:Eu solid solution

The optical properties of the BaMgAl₁₀O₁₇:Eu²⁺ (BAM)-Ba_0.75Al₁₁O_17.25:Eu²⁺ (BAL) solid solution have been studied using VUV excitation, emission and reflectance spectroscopy. Three unique Eu²⁺ emission centers are observed in a ratio that depends on the composition of the host and the dopant concentration. Two of the emission centers are assigned to Eu on normal Beevers-Ross sites and Eu on anti Beevers-Ross sites. The defect chemistry of this system is modeled based on the known behavior of the spinel (MgO·nAl₂O₃) system. Based on this model, the third Eu center can be assigned either to Eu near Al vacancies or to Eu associated with O atoms in the cation layer. In undoped materials exciton emission is observed, peaking at 263 nm in BAM and 285 nm in BAL. This emission may be the mechanism of host-to-activator energy transfer in these phosphors.     

Synthesis, vacuum ultraviolet and near ultraviolet-excited luminescent properties of GdCaAl3O7: RE (RE=Eu, Tb)

Vacuum ultraviolet (VUV) excitation and photoluminescent (PL) properties of Eu³⁺ and Tb³⁺ ion-doped aluminate phosphors, GdCaAl₃O₇:Eu³⁺ and GdCaAl₃O₇:Tb³⁺ have been investigated. X-ray diffraction (XRD) patterns indicate that the phosphor GdCaAl₃O₇ forms without impurity phase at 900 °C. Field emission scanning electron microscopy (FE-SEM) images show that the particle size of the phosphor is less than 3 μm. Upon excitation with VUV irradiation, the phosphors show a strong emission at around 619 nm corresponding to the forced electric dipole ⁵D₀→⁷F₂ transition of Eu³⁺, and at around 545 nm corresponding to the ⁵D₄→⁷F₅ transition of Tb³⁺. The results reveal that both GdCaAl₃O₇:RE³⁺ (RE=Eu, Tb) are potential candidates as red and green phosphors, respectively, for use in plasma display panel (PDP).     

La7O6(BO3)(PO4)2:Eu3+/Tb3+荧光材料的制备及其光致发光性能

采用优化的高温固相方法制备了稀土离子Eu³⁺和Tb³⁺掺杂的La₇O₆（BO₃）（PO₄）₂系荧光材料,并对其物相行为、晶体结构、光致发光性能和热稳定性进行了详细研究。结果表明,La₇O₆（BO₃）（PO₄）₂：Eu³⁺材料在紫外光激发下能够发射出红光,发射光谱中最强发射峰位于616 nm处,为⁵D₀→⁷F₂特征能级跃迁,Eu³⁺的最优掺杂浓度为0.08,对应的CIE坐标为（0.610 2,0.382 3）;La₇O₆（BO₃）（PO₄）₂：Tb³⁺材料在紫外光激发下能够发射出绿光,发射光谱中最强发射峰位于544 nm处,对应Tb³⁺的⁵D₄→⁷F₅能级跃迁,Tb³⁺离子的最优掺杂浓度为0.15,对应的CIE坐标为（0.317 7,0.535 2）。此外,对2种材料的变温光谱分析发现Eu³⁺和Tb³⁺掺杂的La₇O₆（BO₃）（PO₄）₂荧光材料均具有良好的热稳定性。     

Fabrication and optical properties of core-shell structured spherical SiO2@GdVO4:Eu phosphors via sol-gel process

Europium-doped nanocrystalline GdVO₄ phosphor layers were coated on the surface of preformed submicron silica spheres by sol-gel method. The resulted SiO₂@Gd_0.95Eu_0.05VO₄ core-shell particles were characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (FESEM), energy-dispersive X-ray spectra (EDS), transmission electron microscopy (TEM), photoluminescence (PL) spectra, low voltage cathodoluminescence (CL), time resolved PL spectra and kinetic decays. The XRD results demonstrate that the Gd_0.95Eu_0.05VO₄ layers begin to crystallize on the SiO₂ spheres after annealing at 600 ^°C and the crystallinity increases with raising the annealing temperature. The obtained core-shell phosphors have spherical shape, narrow size distribution (average size ca. 600 nm), non-agglomeration. The thickness of the Gd_0.95Eu_0.05VO₄ shells on the SiO₂ cores could be easily tailored by varying the number of deposition cycles (50 nm for four deposition cycles). PL and CL show that the emissions are dominated by ⁵D₀-⁷F₂ transition of Eu³⁺ (618 nm, red). The PL and CL intensities of Eu³⁺ increase with increasing the annealing temperature and the number of coating cycles. The optimum concentration for Eu³⁺ was determined to be 5 mol% of Gd³⁺ in GdVO₄ host.     

Photoluminescence of new red phosphor SrZnO2:Eu

SrZnO₂:Eu³⁺ has been synthesized by solid-state reaction and its photoluminescence in ultraviolet (UV)-vacuum ultraviolet (VUV) range was investigated. The broad bands around 254 nm are assigned to CT band of Eu³⁺-O²⁻. With the increasing of Eu³⁺ concentration, Eu³⁺ could occupy different sites, which leads to the broadening of CT band. A sharp band is observed in the region of 110-130 nm, which is related to the host absorption. The phosphors emit red luminescence centered at about 616 nm due to Eu³⁺⁵D₀→⁷F₂ both under 254 and 147 nm, but none of Eu²⁺ blue emission can be observed.     

Vacuum Ultraviolet Excited Photoluminescence Properties of Y2O2S：Eu^3＋,Bi^3＋ Phosphor

As an Hg-free lamp using phosphor, the Bi^3＋ and EH^3＋ co-doped Y2O2S phosphors were prepared and their luminescence properties under vacuum ultraviolet（VUV） excitation were investigated. The VUV photoluminescent intensity of Y2O2S：Eu^3＋ was weak, however, considerably stronger red emission at 626 nm with good color purity was observed in Y2O2S：Eu^3＋,Bi^3＋ systems. Investigation on the photoluminescence reveals that the strong VUV luminescence of Y2O2S：Eu^3＋,Bi^3＋ at 147 nm is mainly because the Bi^3＋ acts as a medium and effectively performs the energy transfer process： Y^3＋-O^2-→Bi^3＋→Eu^3＋, while the intense emission band at 172 nm is attributed to the absorption of the characteristic ^1So-^1P1 transition of Bi^3＋ and the direct energy transfer from Bi^3＋ to Eu^3＋. The Y2O2S：Eu^3＋,Bi^3＋ shows excellent VUV optical properties compared with the commercial （Y,Gd）BO3：Eu^3＋. Thus, the Y2O2S：Eu^3＋,Bi^3＋ can be a potential red VUV-excited candidate applied in Hg-free lamps for backlight of liquid crystal display.     

Fabrication and luminescent properties of the core-shell structured YNbO4:Eu/Tb@SiO2 spherical particles

The core-shell structured YNbO₄:Eu³⁺/Tb³⁺@SiO₂ particles were realized by coating the YNbO₄:Eu³⁺/Tb³⁺ phosphors onto the surface of spherical silica via a sol-gel process. The obtained materials were characterized by means of X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), Fourier transform IR spectroscopy (FT-IR), photoluminescence (PL) spectra, and cathodoluminescence (CL) spectra. The results indicate that 600 °C annealed samples consist of amorphous silica core and crystalline YNbO₄:Re shell, having perfect spherical morphology with uniform size distribution. Upon excitation by UV or electron beam, these phosphors show the characteristic ⁵D₀-⁷F_1-4 emission lines of Eu³⁺ and the characteristic ⁵D₄-⁷F_3-6 emission lines of Tb³⁺. The PL intensities of Eu³⁺ can be tuned by altering the annealing temperature and the coating number of YNbO₄:Eu³⁺ layers.     

Synthesis of Gd3PO7:Eu nanospheres via a facile combustion method and optical properties

Eu³⁺-doped Gd₃PO₇ nanospheres with an average diameter of ∼300 nm and a narrow size distribution have been prepared by a facile combustion method and structurally characterized by X-ray diffraction and field emission scanning electron microscopy. The luminescent properties were systemically studied by the measurement of excitation/emission spectra, and emission spectra under different temperatures, as well as by photostability. The strong red-emission intensity peaking at 614 nm originates the ⁵D₀→⁷F₂ transition and is observed under 254-nm irradiation, indicating that Eu³⁺ ions in Gd₃PO₇ mainly occupied non-centrosymmetry sites. The CIE1931 XY chromaticity coordinates of Gd₃PO₇:Eu³⁺ nanospheres are (x=0.654, y=0.345) in the red area, which is near the National Television Standard Committee standard chromaticity coordinates for red. Thus, Gd₃PO₇:Eu³⁺ nanospheres may be potential red-emitting phosphors for PDP and Xe-based mercury-free lamps.     

Rietveld refinement and photoluminescent properties of a new blue-emitting material: Eu activated SrZnP2O7

A new efficient blue phosphor, Eu²⁺ activated SrZnP₂O₇, has been synthesized at 1000 °C under reduced atmosphere and the crystal structure and photoluminescence properties have been investigated. The crystal structure of SrZnP₂O₇ was obtained via Rietveld refinement of powder X-ray diffraction (XRD) pattern. It was found that SrZnP₂O₇ crystallizes in space group of P2₁/n (no. 14), Z=4, and the unit cell dimensions are: a=5.30906(2) Å, b=8.21392(3) Å, c=12.73595(5) Å, β=90.1573(3)°, and V=555.390(3) Å³. Under ultraviolet excitation (200-400 nm), efficient Eu²⁺ emission peaked at 420 nm was observed, of which the luminescent efficiency at the optimal concentration of Eu²⁺ (4 mol%) was estimated to be 96% as that of BaMgAl₁₀O₁₇:Eu²⁺. Hence, the SrZnP₂O₇:Eu²⁺ exhibit great potential as a phosphor in different applications, such as ultraviolet light emitting diode and photo-therapy lamps.     

Photoluminescence properties of a novel phosphor, Na3La9O3(BO3)8:RE(RE=Eu,Tb)

The new oxyborate phosphors, Na₃La₉O₃(BO₃)₈:Eu³⁺ (NLBO:Eu) and Na₃La₉O₃(BO₃)₈:Tb³⁺ (NLBO:Tb) were prepared by solid-state reactions. The photoluminescence characteristics under UV excitation were investigated. The dominated emission of Eu³⁺ corresponding to the electric dipole transition ⁵D₀→⁷F₂ is located at 613 nm and bright green luminescence of NLBO:Tb attributed to the transition ⁵D₄→⁷F₅ is centered at 544 nm. The concentration dependence of the emission intensity showed that the optimum doping concentration of Eu and Tb is 30% and 10%, respectively.     

Preparation and optical properties of SrF2:Eu nanospheres

SrF₂:Eu³⁺ nanospheres with homogeneous diameter have been synthesized by a microemulsion-mediated hydrothermal method for the first time, in which quaternary microemulsion of CTAB/water/cyclohexane/n-pentanol was used. The possible reaction mechanism and the luminescent properties of SrF₂:Eu³⁺ nanospheres were also investigated in this paper. The morphology and grain sizes of final products were characterized by field emission scanning electron microscopy and transmission electron microscopy, indicating that most of the products were nanospheres with an average diameter of ∼50 nm. Room-temperature emission spectra, recorded under 394-nm excitation, showed that the transition of ⁵D₀ → ⁷F₁ emission be dominating in SrF₂:Eu³⁺ nanospheres. From the dependence of the luminescence intensity on the concentration of Eu³⁺ ions, the optimal dopant concentration is 2 mol%.     

空气中合成固溶体荧光粉Ba2(Zn, Mg)Si2O7:Ce3+,Eu2+,Eu3+及其发光特性

采用高温固相法在空气中合成了Ba_1.97-yZn_1-xMg_xSi₂O₇:0.03Eu,yCe³⁺系列荧光粉。分别采用X-射线衍射和荧光光谱对所合成荧光粉的物相和发光性质进行了表征。在紫外光330~360 nm激发下,固溶体荧光粉Ba_1.97-yZn_1-xMg_xSi₂O₇:0.03Eu的发射光谱在350~725 nm范围内呈现多谱峰发射,360和500 nm处有强的宽带发射属于Eu²⁺离子的4f⁶5d¹-4f⁷跃迁,590~725 nm红光区窄带谱源于Eu³⁺的⁵D₀-⁷F_J (J=1,2,3,4)跃迁,这表明,在空气气氛中,部分Eu³⁺在Ba_1.97-yZn_1-xMg_xSi₂O₇基质中被还原成了Eu²⁺;当x=0.1时,荧光粉Ba_1.97Zn_0.9Mg_0.1Si₂O₇:0.03Eu的绿色发光最强,表明Eu³⁺被还原成Eu²⁺离子的程度最大。当共掺入Ce³⁺离子后,形成Ba_1.97-yZn_0.9Mg_0.1Si₂O₇:0.03Eu,yCe³⁺荧光粉体系,其发光随着Ce³⁺离子浓度的增大由蓝绿区经白光区到达橙红区;发现名义组成为Ba_1.96Zn_0.9Mg_0.1Si₂O₇:0.01Ce³⁺,0.03Eu的荧光粉的色坐标为(0.323,0.311),接近理想白光,是一种有潜在应用价值的白光荧光粉。讨论了稀土离子在Ba₂Zn_0.9Mg_0.1Si₂O₇基质中的能量传递与发光机理。     

Host-sensitized emission of LiInW2O8 wolframites: From red-Eu to white-Dy phosphors

The LiInW₂O₈:Eu³⁺, LiInW₂O₈:Dy³⁺ and LiInW₂O₈:Eu³⁺/Dy³⁺ phosphors were synthesized by solid-state reaction and their photoluminescence properties were studied. Under UV excitation, the LiInW₂O₈:Eu³⁺ phosphor exhibits an intense red emission whereas the LiInW₂O₈:Dy³⁺ and LiInW₂O₈:Dy³⁺/Eu³⁺ phosphors show a white emission. The WO₆ octahedra play a major role in the luminescence of the host lattice, characterized by a blue emission under UV excitation. The emission of activator ion results from an efficient energy transfer from the LiInW₂O₈ host lattice to the Eu³⁺ and Dy³⁺ ions. The LiIn_0.97Dy³⁺_0.03W₂O₈ and LiIn_0.965 Dy³⁺_0.03Eu³⁺_0.005W₂O₈ samples, optimized for white emission, are interesting candidates for solid-state lighting applications.     

Preparation and photoluminescence property of a loose powder, Ca3Al2O6:Eu by calcination of a layered double hydroxide precursor

A novel red light-emitting material, Ca₃Al₂O₆:Eu³⁺, which is the first example found in the Ca₃Al₂O₆ host, was prepared by calcination of a layered double hydroxide precursor at 1350 °C. The precursor, [Ca_2.9−xAl₂Eu_x(OH)_9.8](NO₃)_2+x·2.5H₂O, was prepared by coprecipitation of metal nitrates with sodium hydroxide. The material is a loose powder composed of irregular particles formed from aggregation of particles of a few nanometers, as shown in scanning electron microscope (SEM) images. It was found that the photoluminescence intensity reached the maximum when the calcination temperature was 1350 °C and the concentration of Eu³⁺ was 1.0%. The material emits bright red emission at 614 nm under a radiation of λ=250 nm.     

La_7O_6(BO_3)(PO_4)_2∶Eu~(3+)/Tb~(3+)荧光材料的制备及其光致发光性能

采用优化的高温固相方法制备了稀土离子Eu~(3+)和Tb~(3+)掺杂的La_7O_6(BO_3)(PO_4)_2系荧光材料,并对其物相行为、晶体结构、光致发光性能和热稳定性进行了详细研究。结果表明,La_7O_6(BO_3)(PO_4)_2∶Eu~(3+)材料在紫外光激发下能够发射出红光,发射光谱中最强发射峰位于616 nm处,为5D0→7F2特征能级跃迁,Eu~(3+)的最优掺杂浓度为0.08,对应的CIE坐标为(0.610 2,0.382 3);La_7O_6(BO_3)(PO_4)_2∶Tb~(3+)材料在紫外光激发下能够发射出绿光,发射光谱中最强发射峰位于544 nm处,对应Tb~(3+)的5D4→7F5能级跃迁,Tb~(3+)离子的最优掺杂浓度为0.15,对应的CIE坐标为(0.317 7,0.535 2)。此外,对2种材料的变温光谱分析发现Eu~(3+)和Tb~(3+)掺杂的La_7O_6(BO_3)(PO_4)_2荧光材料均具有良好的热稳定性。     

Controlled synthesis and luminescent properties of Eu(Eu), Dy-doped Sr3Al2O6 phosphors by hydrothermal treatment and postannealing approach

In this work, Sr₃Al₂O₆: Eu²⁺ (Eu³⁺), Dy³⁺ phosphors have been prepared by hydrothermal treatment and subsequently postannealing approach, using Sr(NO₃)₂, Al(NO₃)₃·9H₂O, and CO(NH₂)₂ as starting materials. The as-obtained phosphors were characterized by means of XRPD, FESEM, and PL techniques. In addition, many reaction parameters were studied in detail, including the initial mole ratios, hydrothermal reaction temperature, calcination temperature and calcination atmosphere. Remarkably, two scientific merits exist herein: Sr₃Al₂O₆: Eu²⁺ (Eu³⁺), Dy³⁺ phosphors can be selectively obtained in a reducing atmosphere (H₂/Ar, 20%+80%) and in air, respectively; adding certain amount of sodium citrate can alter the shape and size of Sr₃Al₂O₆: Eu²⁺ (Eu³⁺), Dy³⁺ phosphors in essence. Besides, the luminescent properties of Sr₃Al₂O₆: Eu²⁺ (Eu³⁺), Dy³⁺ phosphors were studied by excitation spectra, emission spectra and decay curves.