Effect of substrate temperature on the growth of ITO thin films

Indium tin oxide (ITO) thin films were deposited onto glass substrates by rf magnetron sputtering of ITO target and the influence of substrate temperature on the properties of the films were investigated. The structural characteristics showed a dependence on the oxygen partial pressure during sputtering. Oxygen deficient films showed (4 0 0) plane texturing while oxygen-incorporated films were preferentially oriented in the [1 1 1] direction. ITO films with low resistivity of 2.05 × 10⁻³ Ω cm were deposited at relatively low substrate temperature (150 °C) which shows highest figure of merit of 2.84 × 10⁻³ square/Ω⋅     

Rapid thermal annealing of ITO films

Tin-doped indium oxide (ITO) films with 200 nm thickness were deposited on glass substrates by DC magnetron sputtering at room temperature. And they were annealed by rapid thermal annealing (RTA) method in vacuum ambient at different temperature for 60 s. The effect of annealing temperature on the structural, electrical and optical properties of ITO films was investigated. As the RTA temperature increases, the resistivity of ITO films decreases dramatically, and the transmittance in the visible region increases obviously. The ITO film annealed at 600 °C by RTA in vacuum shows a resistivity of 1.6 × 10⁻⁴ Ω cm and a transmittance of 92%.     

Thickness dependence of electrical properties of ITO film deposited on a plastic substrate by RF magnetron sputtering

Indium tin oxide (ITO) films with various thicknesses in range of 40-280 nm were prepared onto a plastic substrate (PMMA). Deposition was carried out with RF magnetron sputtering method and the substrate temperature was held at ∼70 °C, in lack of the thermal damage to the polymer substrate. Changes in microstructure and electrical properties of ITO films according to their thicknesses were investigated. It was found that amorphous layer with thickness of 80 nm was formed at the interface on the polymer substrate and polycrystalline ITO could be obtained above the thickness. Conductivity of ITO films was found to be strongly dependent on the crystallinity. Consequently, it is suggested that crystallinity of the deposited films should be enhanced at the initial stage of deposition and the thickness of amorphous region be reduced in order to prepare high quality ITO thin films on polymer substrates.     

Crystalline and photoluminescence characteristics of YVO4:Sm thin films grown by pulsed laser deposition under oxygen pressure

YVO₄:Sm³⁺ films were deposited on Al₂O₃ (0 0 0 1) substrates at various oxygen pressures changing from 13.3 to 46.6 Pa by using the pulsed laser deposition method. The crystallinity and surface morphology of these films were investigated by means of X-ray diffraction (XRD) and atomic force microscopy (AFM), respectively. The XRD pattern confirmed that YVO₄:Sm³⁺ film has zircon structure and the AFM study revealed that the films consist of homogeneous grains ranging from 100 to 400 nm. The room temperature photoluminescence (PL) spectra showed that the emitted radiation was dominated by a reddish-orange emission peak at 602 nm radiating from the transition of (⁴G_5/2→⁶H_7/2). The crystallinity, surface morphology, and photoluminescence spectra of thin-film phosphors were highly dependent on the deposition conditions, in particular, the substrate temperature. The surface roughness and photoluminescence intensity of these films showed similar behavior as a function of oxygen pressure.     

AlF3 film deposited by IAD with end-Hall ion source using SF6 as working gas

A novel and effective process to fabricate high quality fluoride thin films was presented. Aluminum fluoride films deposited by a conventional thermal evaporation with an ion-assisted deposition (IAD) using SF₆ as a working gas at around room temperature were investigated. In this study, the optimal voltage and current, 50 V and 0.25 A, were found according to the optical properties of the films: high refractive index (1.489 at 193 nm), low optical absorption and extinction coefficient (<10⁻⁴ at 193 nm) in the UV range. The physical properties of the film are high packing density and amorphous without columnar structure. It was proved that using SF₆ working gas in IAD process is a good choice and significantly improves the quality of AlF₃ films.     

Luminescent characteristics of CaTiO3:Pr thin films prepared by pulsed laser deposition method with various substrates

CaTiO₃:Pr³⁺ films were deposited on different substrates such as Al₂O₃ (0 0 0 1), Si (1 0 0), MgO (1 0 0), and fused silica using pulsed laser deposition method. The crystallinity and surface morphology of these films were investigated by XRD and SEM measurements. The films grown on the different substrates have different crystallinity and morphology. The FWHM of (2 0 0) peak are 0.18, 0.25, 0.28, and 0.30 for Al₂O₃ (0 0 0 1), Si (1 0 0), MgO (1 0 0), and fused silica, respectively. The grain sizes of phosphors grown on different substrates were estimated by using Scherrer's formula and the maximum crystallite size observed for the thin film grown on Al₂O₃ (0 0 0 1). The room temperature PL spectra exhibit only the red emission peak at 613 nm radiated from the transition of (¹D₂ → ³H₄) and the maximum PL intensity for the films grown on the Al₂O₃ (0 0 0 1) is 1.1, 1.4, and 3.7 times higher than that of the CaTiO₃:Pr³⁺ films grown on MgO (1 0 0), Si (1 0 0), and fused Sillica substrates, respectively. The crystallinity, surface morphology and luminescence spectra of thin-film phosphors were highly dependent on substrates.     

Dependence of photoluminescence from a-Si nanoparticles on the annealing time and exciting wavelength

Thin films of SiO_x having thickness of 0.2 μm and oxygen content x=1.5 or 1.7 are prepared by thermal evaporation of SiO in vacuum. Then some samples are furnace annealed for various times (in the range ) at 770 and 970 K and some others are rapid thermal annealed at 970 K for 30 and 60 s. Photoluminescence (PL) measurements are carried out at room temperature using the 442 nm line of a He-Cd laser and the 488 nm of an Ar laser for excitation. The effect of the annealing conditions and wavelength of the exciting light on the shape of the PL from these films is explored. The deconvolution of the PL spectra measured with the 442 nm line from samples annealed at 770 K for reveals two distinct PL bands peaked at around 2.3 and 2.5 eV, which do not shift appreciably with increasing annealing time. In addition, at longer annealing times, a weak third band is resolved centred in the range 2.0-2.1 eV. It exists in the spectra of all samples annealed at 970 K being more prominent in the samples with x=1.5. The intensity of this band shows different dependences on the annealing time in the films with different initial composition. The results obtained are discussed in terms of radiative recombination via defect states in the SiO_x matrix (the 2.5 eV band) or at the a-Si-SiO_x interface (the 2.3 eV band). The band centred in the 2.0-2.1 eV range is related to recombination in amorphous silicon nanoparticles grown upon annealing.     

Thickness dependence of structural, electrical and optical properties of indium tin oxide (ITO) films deposited on PET substrates

Without intentionally heating the substrates, indium tin oxide (ITO) thin films of thicknesses from 72 nm to 447 nm were prepared on polyethylene terephthalate (PET) substrates by DC reactively magnetron sputtering with pre-deposition substrate surfaces plasma cleaning. The dependence of structural, electrical, and optical properties on the films thickness were systematically investigated. It was found that the crystal grain size increases, while the transmittance, the resistivity, and the sheet resistance decreases as the film thickness was increasing. The thickest film (∼447 nm) was found of the lowest sheet resistance 12.6 Ω/square, and its average optical transmittance (400-800 nm) and the 550 nm transmittance was 85.2% and 90.4%, respectively. The results indicate clearly that dependence of the structural, electrical, and optical properties of the films on the film thickness reflected the improvement of the film crystallinity with the film thickness.     

Synthesis of zinc oxide nanosheet thin films and their improved field emission and photoluminescence properties by annealing processing

ZnO nanosheet thin films have been synthesized through a solvothermal route. These obtained nanosheets disperse quasi-vertically and homogenously on the copper substrates and range in thickness from 80 nm to 250 nm. The as-grown nanosheet thin films were then annealed in the oxygen-presented atmosphere. Field emission plots indicate that the value of turn-on field is reduced from 2.86 V/μm to 1.52 V/μm and the corresponding value of threshold field decreases from 7.19 V/μm to 4.45 V/μm after annealing processing. Room temperature photoluminescence spectrum from the sample annealed at 850 °C in almost pure oxygen atmosphere shows only UV emission and a blue shift while the visible light band is unobservable compared with those of the other two samples, indicating that the crystalline quality of the obtained zinc oxide nanosheet thin films is greatly improved through annealing treatment. This solution approach combined with annealing treatment can, therefore, be regarded as a convenient route to fabricate high-quality crystalline ZnO nanomaterials.     

Surface characterization and microstructure of ITO thin films at different annealing temperatures

In this study, the electron beam evaporation method is used to generate an indium tin oxide (ITO) thin film on a glass substrate at room temperature. The surface characteristics of this ITO thin film are then investigated by means of an AFM (atomic force microscopy) method. The influence of postgrowth thermal annealing on the microstructure and surface morphology of ITO thin films are also examined. The results demonstrate that the film annealed at higher annealing temperature (300 °C) has higher surface roughness, which is due to the aggregation of the native grains into larger clusters upon annealing. The fractal analysis reveals that the value of fractal dimension D_f falls within the range 2.16-2.20 depending upon the annealing temperatures and is calculated by the height-height correlation function.     

Effect of ambient hydrogen sulfide on the physical properties of vacuum evaporated thin films of zinc sulfide

Evaporated thin films of zinc sulfide (ZnS) have been deposited in a low ambient atmosphere of hydrogen sulfide (H₂S ∼10⁻⁴ Torr). The H₂S atmosphere was obtained by a controlled thermal decomposition of thiourea [CS(NH₂)₂] inside the vacuum chamber. It has been observed that at elevated substrates temperature of about 200 °C helps eject any sulfur atoms deposited due to thermal decomposition of ZnS during evaporation. The zinc ions promptly recombine with H₂S to give better stoichiometry of the deposited films. Optical spectroscopy, X-ray diffraction patterns and scanning electron micrographs depict the better crystallites and uniformity of films deposited by this technique. These deposited films were found to be more adherent to the substrates and are pinhole free, which is a very vital factor in device fabrication.     

Structural and photoluminescence characters of SnO2:Sb films deposited by RF magnetron sputtering

The Antimony-doped tin oxide (SnO₂:Sb) films have been prepared on glass substrates by RF magnetron sputtering method. The prepared samples are polycrystalline films with rutile structure of pure SnO₂ and have preferred orientation of (1 1 0) direction. XRD measurement did not detect the existence of Sb₂O₃ phase and Sb₂O₅ phase; Sb ions occupy the site of Sn ions and form the substitution doping. An intensive UV-violet luminescence peak near 392 nm is observed at room temperature. Photoluminescence (PL) properties influenced by sputtering power and annealing for the SnO₂:Sb films are investigated in detail and corresponding PL mechanism is discussed.     

Thermal stability of SiGe films on an ultra thin Ge buffer layer on Si grown at low temperature

The thermal stability of SiGe films on an ultra thin Ge buffer layer on Si fabricated at low temperature has been studied. The microstructure and morphology of the samples were investigated by high-resolution X-ray diffraction, Raman spectra and atomic force microscopy, and using a diluted Secco etchant to reveal dislocation content. After thermal annealing processing, it is observed that undulated surface, threading dislocations (TDs) and stacking faults (SFs) appeared at the strained SiGe layer, which developed from the propagation of a misfit dislocation (MD) during thermal annealing, and no SFs but only TDs formed in strain-relaxed sample. And it is found that the SiGe films on the Ge layer grown at 300 °C has crosshatch-free surface and is more stable than others, with a root mean square surface roughness of less than 2 nm and the threading dislocation densities as low as ∼10⁵ cm⁻². The results show that the thermal stability of the SiGe films is associated with the Ge buffer layer, the relaxation extent and morphology of the SiGe layer.     

Low-temperature ordering of L10 FePt phase in FePt thin film with AgCu underlayer

FePt (20 nm) films with AgCu (20 nm) underlayer were prepared on thermally oxidized Si (0 0 1) substrates at room temperature by using dc magnetron sputtering, and the films annealed at different temperature to examine the disorder–order transformation of the FePt films. It is found that the ordered L1₀ FePt phase can form at low annealing temperature. Even after annealing at 300 °C, the in-plane coercivity of 5.2 kOe can be obtained in the film. With increase in annealing temperature, both the ordering degree and coercivity of the films increase. The low-temperature ordering of the films may result from the dynamic stress produced by phase separation in AgCu underlayer and Cu diffusion into FePt phase during annealing.     

Fabrication of nanostructured CuInS2 thin films by ion layer gas reaction method

CuInS₂ thin films were prepared by a two-stage ion layer gas reaction (ILGAR) process in which the Cu and In precursors were deposited on glass substrate by using a simple and low-cost dip coating technique and annealed in H₂S atmosphere at different temperatures. The influence of the annealing temperature (250-450 °C) on the particle size, crystal structure and optical properties of the CuInS₂ thin films was studied. Transmission electron microscopy revealed that the particle radii varied in the range 6-21 nm with annealing. XRD and SAED patterns indicated polycrystalline nature of the nanoparticles. The optical band gap (E_g) varied from 1.48 to 1.56 eV with variation of particle size. The variation of Urbach tail with temperature indicated higher density of the defects for the films annealed at lower temperature. From the Raman study, it was observed that the FWHM of the A₁ mode at ∼292 cm⁻¹ corresponding to the chalcopyrite phase of CuInS₂ decreased with increasing annealing temperature.     

Microstructures and optical properties of Cu-doped ZnO films prepared by radio frequency reactive magnetron sputtering

Pure and Cu-doped ZnO (ZnO:Cu) thin films were deposited on glass substrates using radio frequency (RF) reactive magnetron sputtering. The effect of substrate temperature on the crystallization behavior and optical properties of the ZnO:Cu films have been studied. The crystal structures, surface morphology and optical properties of the films were systematically investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM) and a fluorescence spectrophotometer, respectively. The results indicated that ZnO films showed a stronger preferred orientation toward the c-axis and a more uniform grain size after Cu-doping. As for ZnO:Cu films, the full width at half maxima (FWHM) of (0 0 2) diffraction peaks decreased first and then increased, reaching a minimum of about 0.42° at 350 °C and the compressive stress of ZnO:Cu decreased gradually with the increase of substrate temperature. The photoluminescence (PL) spectra measured at room temperature revealed two blue and two green emissions. Intense blue-green luminescence was obtained from the sample deposited at higher substrate temperature. Finally, we discussed the influence of annealing temperature on the structural and optical properties of ZnO:Cu films. The quality of ZnO:Cu film was markedly improved and the intensity of blue peak (∼485 nm) and green peak (∼527 nm) increased noticeably after annealing. The origin of these emissions was discussed.     

Enhanced luminescent characteristics of laser-ablated GdVO4:Eu thin films by Li-doping

Li-doping has been used to improve luminescent characteristics of thin films. Influence of Li-doping on the crystallization, surface morphology and luminescent properties of GdVO₄:Eu³⁺ films have been investigated. Crystallinity and surface morphology of thin films have been very important factors to determine luminescent characteristics and depended on the deposition conditions. The GdVO₄:Eu³⁺ and Li-doped GdVO₄:Eu³⁺ thin films have been grown using pulsed laser deposition method on Al₂O₃ (0 0 0 1) substrates at a substrate temperature of 600 °C under an oxygen pressure of 13.33-53.33 Pa. The crystallinity and surface morphology of the films were investigated using X-ray diffraction (XRD) and atomic force microscope (AFM), respectively. A broadband incoherent ultraviolet light source with a dominant excitation wavelength of 310 nm and a luminescence spectrometer have been used to measure photoluminescence spectra at room temperature. The emitted radiation was dominated by the red emission peak at 619 nm radiated from the transition of ⁵D₀-⁷F₂ of Eu³⁺ ions. Particularly, the peak intensity of Li-doped GdVO₄ films was increased by a factor of 1.7 in comparison with that of GdVO₄:Eu³⁺ films. The enhanced luminescence results not only from the improved crystallinity but also from the reduced internal reflections caused by rougher surfaces. The luminescent intensity and surface roughness exhibited similar behavior as a function of oxygen pressure.     

Initial study on the structure and photoluminescence properties of SiC films doped with Al

SiC films doped with aluminum (Al) were prepared by the rf-magnetron sputtering technique on p-Si substrates with a composite target of a single crystalline SiC containing several Al pieces on the surface. The as-deposited films were annealed in the temperature range of 400-800 °C under nitrogen ambient. The thin films have been characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR) and scanning electron microscopy (SEM). The results show that the introduction of Al into films hinders crystalline formation process. And with the increase of annealing temperature, more Si particles are formed in the films, which strongly affect the optical absorption properties. The photoluminescence (PL) spectra of the samples show two peaks at 370 nm and 412 nm. The intensities of the PL peaks are evidently improved after Al doped. We attribute the origin of the two PL peaks to a kind of Si-related defect centres. The obtained results are expected to have important applications in modern optoelectronic devices.     

Room temperature photoluminescence from amorphous silicon nanoparticles in SiOx thin films

Amorphous SiO_x thin films with four different oxygen contents (x=1.15, 1.4, 1.5, and 1.7) have been prepared by thermal evaporation of SiO in vacuum and then annealed at 770 or 970 K in argon for various times ?40 min. The influence of annealing conditions and the initial film composition on photoluminescence (PL) from the annealed films has been explored. Intense room temperature PL has been observed from films with x?1.5, visible with a naked eye. It has been shown that PL spectra of most samples consists of two main bands: (i) a ‘green’ band centered at about 2.3 eV, whose position does not change with annealing conditions and (ii) an ‘orange-red’ band whose maximum moves from 2.1 to 1.7 eV with increasing annealing time and temperature and decreasing initial oxygen content. These observations have been explained assuming recombination via defect states in the SiO_x matrix for the first band and emission from amorphous Si nanoparticles for the second one.     

Structural and optical characterization of undoped, doped, and clustered ZnO thin films obtained by PLD for gas sensing applications

The synthesis by pulsed laser deposition technique of zinc oxide thin films suitable for gas sensing applications is herein reported. The ZnO targets were irradiated by an UV KrF^* (λ = 248 nm, τ_FWHM ∼7 ns) excimer laser source, operated at 2.8 J/cm² incident fluence value, whilst the substrates consisted of SiO₂(0 0 1) wafers heated at 150 °C during the thin films growth process. The experiments were performed in an oxygen dynamic pressure of 10 Pa. Structural and optical properties of the thin films were investigated. The obtained results have demonstrated that the films are c-axis oriented. Their average transmission in the visible-infrared spectral region was found to be about 85%. The equivalent refractive indexes and extinction coefficients were very close to those of the tabulated reference values. Doping with 0.5% Au and coating with 100 pulses of Au clusters caused but a very slight decrease (with a few percent) of both transmission and refractive index values. The coatings with the most appropriate optical properties as waveguides have been selected and their behavior was tested for butane sensing.