Effect of Co doping on the magnetic properties of La0.85Ag0.15(Mn1−yCoy)O3

The mixed valent manganites (La_0.85Ag_0.15)MnO₃ with perovskite structure has been prepared by doping up to 50% of Co at the Mn site. Paramagnetic (PM) to ferromagnetic (FM) transitions have been observed in all the prepared materials. However, the long-range magnetic ordering observed in (La_0.85Ag_0.15)MnO₃ is systemically reduced to cluster glass-type (short-range) of FM ordering due to the introduction of Co. The FM transition temperature was found to decrease with increase in Co doping up to 20% and for further increase in Co doping, the T_c was found to increase. They are explained on the basis of competition between FM double exchange interactions in Mn–O–Mn and Co–O–Co networks. In addition to PM–FM transition, evidences of FM to antiferromagnetic (AFM), and AFM to reentrant spin-glass transitions have been observed. The shift in spin-glass freezing temperature, T_f has been observed from the frequency variation of ac susceptibility measurements. The observed magnetic transitions are explained on the basis of magnetic interactions in different Mn–O–Mn, Mn–O–Co and Co–O–Co networks and such transitions are also observed from the measurement of third harmonic susceptibility. Metal–insulator transition and colossal magneto-resistivity have been observed up to 10% of Co doping.     

The effects of Cu doping on the magnetoresistive behavior of perovskites La0.7Ca0.3MnO3

The electronic and magnetic properties of Cu-doped perovskite La_0.7Ca_0.3Mn_1−xCu_xO₃ obtained by doping Cu on its Mn sites have been studied. The perovskite structure was found to remain intact up to the highest doping level of x=0.20. At low Cu concentration (x=0.05) the temperature-dependence of resistivity of the material exhibited up to two peaks corresponding to the magnetic transitions from the PM to the FM phase, and from the FM to the AFM phase. In general, the doping level was found to suppress the ferromagnetic ordering of the material, increase its resistivity, and produce large values of magnetoresistance near the resistivity peak. These results were explained as due to the formation of the antiferromagnetic phase.     

High-temperature ferromagnetism in Zn1−xMnxO semiconductor thin films

Clear evidence of ferromagnetic behavior at temperatures >400 K as well as spin polarization of the charge carriers have been observed in Zn_1−xMn_xO thin films grown on Al₂O₃ and MgO substrates. The magnetic properties depended on the exact Mn concentration and the growth parameters. In well-characterized single-phase films, the magnetic moment is 4.8 μ_B/Mn at 350 K, the highest moment yet reported for any Mn doped magnetic semiconductor. Anomalous Hall effect shows that the charge carriers (electrons) are spin-polarized and participate in the observed ferromagnetic behavior.     

Magnetic and electronic phase transitions and magnetoresistance effect in the Pr0.5−xLaxSr0.5MnO3 (, 0.15) system

The electronic and magnetic phase transitions of Pr_0.5−xLa_xSr_0.5MnO₃ with x=0.10 and 0.15 were investigated. The M(T) and ρ(T) curves for these samples clearly show transitions from antiferromagnetic insulator to ferromagnetic semiconductor, ferromagnetic metal and finally to paramagnetic semiconductor as the temperature is increased from 5 to 300 K. Especially, two obvious protrudent peaks in the magnetoresistance curves MR(T) for these samples were clearly observed in the relative low magnetic field, 1 T. One peak appears at around the antiferromagnet-ferromagnet transition temperature T_N (150 K) with MR≈−23%, another occurs at around the ferromagnet-paramagnet transition temperature T_C(275 K ) with MR≈−8.2%. In addition, when the magnetic field was increased, the temperature corresponding to the MR peak at T_N shifts to lower temperature while the temperature corresponding to the MR peak at T_C is fixed.     

Temperature dependence of the electrical resistivity of amorphous Co80−xErxB20 alloys

The temperature dependence of the electrical resistivity of amorphous Co_80−xEr_xB₂₀ alloys with x=0, 3.9, 7.5 and 8.6 prepared by melt spinning in pure argon atmosphere was studied. All amorphous alloys investigated here are found to exhibit a resistivity minimum at low temperature. The electrical resistivity exhibits logarithmic temperature dependence below the temperature of resistivity minimum T_min. In addition, the resistivity shows quadratic temperature behavior in the interval T_min<T<77 K. At high temperature, the electrical resistivity was discussed by the extended Ziman theory. For the whole series of alloys, the composition dependence of the temperature coefficient of electrical resistivity shows a change in structural short range occurring in the composition range 8–9 at%.     

Phase formation and magnetic properties of Nd2Fe14B-type Nd16Co76B8−xCx alloys and their hydrides

An attempt is made to synthesize Nd₂Co₁₄C compound by mechanical alloying Nd₁₆Co₇₆B_8−xC_x (0x8) alloys and subsequent annealing. Phase formation and magnetic properties of Nd₂Fe₁₄B-type Nd₁₆Co₇₆B_8−xC_x alloys and their hydrides are investigated. The Nd₂Co₁₄(B,C) phase with Nd₂Fe₁₄B-type structure is formed for Nd₁₆Co₇₆B_8−xC_x (0x7) alloys, while NdCo₇C_δ phase with TbCu₇-type structure is observed in Nd₁₆Co₇₆C₈ alloy. The lattice parameter c of the Nd₂Co₁₄(B,C) phase decreases with increasing the carbon content. A limit volume of the unit cell to form the Nd₂Fe₁₄B-type structure is estimated to be 0.870 nm³. The spin-reorientation temperature T_SR increases with increasing the carbon content, due to an enhancement of magnetocrystalline anisotropy caused by carbon substitution for boron. After hydrogenation, the lattice expansion is observed for Nd₁₆Co₇₆B_8−xC_x (0x7) alloys. The spin-reorientation temperature of Nd₁₆Co₇₆B_8−xC_xH_y (0x7) is much lower than that of the host alloys. Some structural and magnetic properties of hypothetic Nd₂Co₁₄C and Nd₂Co₁₄CH_y compounds are estimated by extrapolation.     

Charge ordering in the electron doped Ca1−xYxMnO3 manganites

Structural studies on the electron doped Ca_1−xY_xMnO₃ are presented. At 300 K, orthorhombic O-phase was observed in all cases, associated to low electric resistivity and high Curie–Weiss temperature. For samples with x>0.07, structural phase transitions to more distorted orthorhombic and monoclinic phases were found at T<170K. In these phases only weak ferromagnetic interactions were observed.     

脱氧La0.5Ca0.5MnO3样品的铁磁-反铁磁转变和电阻率变化

研究了氧空位对La_0.5Ca_0.5MnO₃ （LCMO）多晶块材的电输运和磁性质的影响. 随着氧空位的增加, 样品在高温段的电阻率一直增加, 并满足绝热小极化子模型, 而低温段的电阻率先下降后上升, 并出现明显的dR/dT>0的行为, 直至最后变为绝缘的. 氧空位的增加抑止了反铁磁相的出现, 使得脱氧的LCMO样品不发生反铁磁转变, 进一步增加氧空位则会抑制铁磁相. 关键词： 0.5Ca_0.5MnO₃')" href="#">La_0.5Ca_0.5MnO₃ 反铁磁相变 铁磁相变 脱氧     

Double peak behavior of resistivity curves in Cd doped LaMnO3 perovskite systems

The effect of Cd doping on transport, magnetotransport, and magnetic properties has been investigated in the perovskite La_1−xCd_xMnO₃ (0x0.5) systems. The ρ(T) curves exhibit a sharp metal insulator transition (T_p1), which is close to paramagnetic to ferromagnetic transition (T_c) obtained from M−T curves for all samples. In addition, ρ(T) curves for Cd doped samples exhibit another broad transition (T_P2) below T_p1. This transition becomes more prominent and the transition temperature (T_p2) shifts to lower temperature with increasing Cd content. Such double peak behavior in the ρ(T) curve is attributed to the phase separation between the ferromagnetic metallic phases and the ferromagnetic insulating phases induced by the electronic inhomogeneity in the samples.     

Magnetocaloric and magnetoresistance properties of La2/3Sr1/3Mn1−xCoxO3 compounds

Structural, magnetic, magnetoresistance and magnetocaloric studies on La_2/3Sr_1/3Mn_1−xCo_xO₃ compounds were reported. The samples were prepared by the conventional ceramic method. X-ray analysis showed the presence of one phase only, in all studied samples. From electrical resistance measurements it was found that the samples show large negative magnetoresistance behavior. The magnetic measurements were performed in a large temperature range, 4.2–750 K and external magnetic fields up to 5 T. The adiabatic magnetic entropy changes, |ΔS|, were determined from magnetization data. Large magnetocaloric effect (MCE) has been obtained in all studied samples.     

The effect of isoelectronic substitution on the magneto-resistance of Sr2−xBaxFeMoO6

We report results from structural, transport and magnetic measurements on polycrystalline Sr_2−xBa_xFeMoO₆ (x=0, 1 and 2) half-metallic double perovskites. We find a large low field magneto-resistance (MR) of −25% at 0.8 T and 77 K for samples that have high resistivities. We show that the low field tunneling MR can be modeled by assuming that there is a disordered region near the insulating grain boundaries as proposed by Serrate et al. It is the magnetization from this region rather than the bulk magnetization that determines the MR in polycrystalline samples.     

Charge ordering and structural transitions in Pr0.5Sr0.41Ca0.09MnO3

The structural and magnetic transitions in Pr_0.5Sr_0.41Ca_0.09MnO₃ have been investigated by neutron diffraction and electron microscopy. Two structural transitions, Imma to I4/mcm and I4/mcm to Pmmn, are observed by decreasing the temperature. Two magnetic transitions, from a paramagnetic insulating to a ferromagnetic metallic and from a ferromagnetic metallic to an antiferromagnetic insulating states at T_C=250 K and T_N=180 K, respectively, are also observed. The structures of these three forms have been determined from neutron powder diffraction data. The first important result concerns the low temperature antiferromagnetic CE type and charge ordered structure, which has been refined in the Pmmn space group, without any constraint. This structure is completely long range ordered, with two Mn-sites, Mn³⁺ in tetragonally elongated octahedra, and Mn⁴⁺, off-centered in nearly regular octahedra. The second important point concerns the abrupt character of the structural transition from the I4/mcm to the Pmmn structure, without any appearance of incommensurability. The magnetic and transport properties of this compound are compared with those of Pr_0.5Sr_0.5MnO₃.     

High hydrostatic pressure effect on magnetic state of anion-deficient La0.70Sr0.30MnOx perovskite manganites

The magnetic state of La_0.70Sr_0.30MnO_x (x=2.85, 2.80) anion-deficient manganites is studied experimentally under hydrostatic pressure up to 5.2 GPa. These materials possessing the properties of a spin-glass state. The La_0.70Sr_0.30MnO_2.85 exhibits a coexistence of the rhombohedral (R3¯c) and tetragonal (I4/mcm) crystal structures and below T_f 50 K the spin-glass state is formed. The La_0.70Sr_0.30MnO_2.80 exhibits the tetragonal (I4/mcm) crystal structure. For this compound a phase-separated magnetic state below T_f is formed, involving coexistence of C-type antiferromagnetic (AFM) clusters within spin-glass matrix. In both compounds the crystal structure and magnetic states remain stable upon compression. Under the hydrostatic pressure up to 1 GPa, the La_0.70Sr_0.30MnO_2.85 is a spin glass with a smeared phase transition to the paramagnetic state. The freezing temperature T_f of the magnetic moments of the ferromagnetic clusters increases at a rate of 4.30 K/GPa and the magnetic ordering temperature T_MO increases at a rate of 12.90 K/GPa. The enhancement of the ferromagnetic properties of La_0.70Sr_0.30MnO_2.85 anion-deficient manganite under hydrostatic pressure is explained by the redistribution of oxygen vacancies and a decrease in the unit cell parameters.     

Effect of Si/Ge ratio on resistivity and thermopower in Gd5SixGe4−x magnetocaloric compounds

The effect of Si/Ge ratio on resistivity and thermopower behavior has been investigated in the magnetocaloric ferromagnetic Gd₅Si_xGe_4−x compounds with x=1.7-2.3. Microstructural studies reveal the presence of Gd₅(Si,Ge)₄-matrix phase (5:4-type) along with traces of secondary phases (5:5 or 5:3-type). The x=1.7 and 2.0 samples display the presence of a first order structural transition from orthorhombic to monoclinic phase followed by a magnetic transition of the monoclinic phase. The alloys with x=2.2 and 2.3 display only magnetic transitions of the orthorhombic phase. A low temperature feature apparent in the AC susceptibility and resistivity data below 100 K reflects an antiferromagnetic transition of secondary phase(s) present in these compounds. The resistivity behavior study correlates with microstructural studies. A large change in thermopower of −8 μV/K was obtained at the magneto-structural transition for the x=2 compound.     

Tb掺杂双层锰氧化物La_(4/3)Sr_(5/3)Mn_2O_7的磁熵变和电输运性质

研究了Tb掺杂对双层锰氧化物La_(4/3)Sr_(5/3)Mn_2O_7磁熵变和电输运性质的影响.样品采用传统固相反应法制备,两样品的名义组分可以表示为(La_(1-x)Tb_x)_(4/3)Sr_(5/3)Mn_2O_7(x=0,0.025),磁场为7 T时的最大磁熵变?S_M分别为-4.60 J/(kg·K)和-4.18 J/(kg·K).比较后发现,Tb元素的掺杂使得最大磁熵变值减小,但同时增大了相对制冷温区.电性测量结果表明,x=0.025的样品在高温区的导电机制可以用小极化子模型解释,与母体三维变程跳跃模型不同;当温度降低至三维长程铁磁有序温度(T_c~(3D))附近时,掺杂样品发生金属绝缘相变;掺杂后样品在T_c~(3D)附近,磁电阻取得极大值(约为56%),表明是本征磁电阻效应.     

Multi-magnetic phases in Fe1−xNixTa2O6

X-ray, neutron diffraction and magnetic susceptibility are reported for Fe_xNi_1−xTa₂O₆ mixed oxides. X-ray refinement indicates homogeneous samples for all the reported concentrations. The neutron-diffraction measurements reveal magnetic structures with double propagation vectors. This system exhibits at least two bicritical points at about x=0.15 and 0.60. For these concentrations, at low temperatures, the system shows the coexistence of two magnetic structures. This bicritical behaviour is interpreted as induced by competition between the different magnetic structures.     

Dynamical effects in magnetic and transport properties of phase separated La0.5Ca0.5Mn0.95Fe0.05O3

We have measured transport and magnetic properties of polycrystalline La_0.5Ca_0.5Mn_0.95Fe_0.05O₃, a phase separated manganite with ferromagnetic ground state. Cooling rate dependences and time relaxation were found; the coexistence of ferromagnetic and charge ordered regions determines a dynamics which influences physical properties. We show that a dynamical contribution to the resistivity can account for the observed cooling rate dependence and ageing effects on this phase separated manganite.     

Composition and thermal-induced effects on the optical constants of Ge20Se80−xBix thin films

 The effects of composition and thermal annealing near crystallization temperature, T_c on the optical and structural properties of Ge₂₀Se_80−xBi_x (x=0, 2.5, 5 and 7.5 at%) was investigated. The influence of incorporation Bi content in Ge₂₀Se_80−xBi_x system results in a gradual decrease in the indirect optical gap from 1.89 to 1.44 eV, this behavior can be explained as increased tailing. On annealing, the optical band gap E_g decreases gradually for the crystallized films while the refractive index increases, this behavior can be attributed to transformation from amorphous to crystalline and was explained in the light of dangling bond model. The refractive index n of as-prepared and annealed films has been analyzed according to the Wwmple–DiDominico single oscillator model and the values of E_o and E_d were determined. The effect of annealing on the nature and degree of crystallization has been investigated by studying the structure using transmission electron microscope, X-ray diffraction and scanning electron microscope.     

Evidence of glassy ferromagnetic phase and kinetic arrest of electronic phase in Sm0.35Pr0.15Sr0.5MnO3 manganites

The effect of doping of rare earth Pr³⁺ ion as a replacement of Sm³⁺ in Sm_0.5Sr_0.5MnO₃ is investigated. Temperature dependent dc and ac magnetic susceptibility, resistivity, magnetoresistance measurements on chemically synthesized (Sm_0.5−xPr_x)Sr_0.5MnO₃ show various unusual features with doping level x=0.15. The frequency independent ferromagnetic to paramagnetic transition at higher temperature (∼191 K) followed by a frequency dependent reentrant magnetic transition at lower temperature (∼31 K) has been observed. The nature of this frequency dependent reentrant magnetic transition is described by a critical slowing down model of spin glasses. From non-linear ac susceptibility measurements it has been confirmed that the finite size ferromagnetic clusters are formed as a consequence of intrinsic phase separation, and undergo spin glass-like freezing below a certain temperature. There is an unusual observation of a 2nd harmonic peak in the non-linear ac susceptibility around this reentrant magnetic transition at low temperature (∼31 K). Arrott plots at 10 and 30 K confirm the existence of glassy ferromagnetism below this low temperature reentrant transition. Electronic- and magneto-transport measurements show a strong magnetic field—temperature history dependence and strong irreversibility with respect to the sweeping of magnetic field. These results are attributed to the effect of phase separation and kinetic arrest of the electronic phase in this phase separated manganite at low temperatures.     

Magnetic properties of Lu2Co17−xSix single crystals

The Co-sublattice anisotropy in Lu₂Co₁₇ consists of four competitive contributions from Co atoms at crystallographically different sites in the Th₂Ni₁₇-type of crystal structure, which result in the appearance of a spontaneous spin-reorientation transition (SRT) from the easy plane to the easy axis at elevated temperatures. In order to investigate this SRT in detail and to study the influence of Si substitution for Co on the magnetic anisotropy, magnetization measurements were performed on single crystals of Lu₂Co_17−xSi_x (x=0−3.4) grown by the Czochralski method. The SRT in Lu₂Co₁₇ was found to consist of two second-order spin reorientations, “easy-plane”–“easy-cone” at T_SR1≈680 K and “easy-cone”–“easy-axis” at T_SR2≈730 K. Upon Si substitution for Co, both SRTs shift toward the lower temperatures in Lu₂Co₁₆Si (T_SR1≈75 K and T_SR2≈130 K) with the further onset of the uniaxial type of magnetic anisotropy in the whole range of magnetic ordering for Lu₂Co_17−xSi_x compounds with x>1 due to a weakening of the easy-plane contribution from the Co atoms at the 6g and 12k sites to the total anisotropy.