Performance and stability of niobium-substituted Ba0.5Sr0.5Co0.8Fe0.2O3 − δ membranes

The phase stability, thermal expansion, electrical conductivity, and oxygen permeation of perovskite-type oxides Ba_0.5Sr_0.5(Co_0.8Fe_0.2)_1 − xNb_xO_3 − δ (x = 0 − 0.2) have been investigated. Room-temperature X-ray diffraction of as-prepared powders indicates that in the investigated compositional range solid solutions are formed. Long-term annealing experiments both in flowing air and nitrogen, at 750 °C, demonstrate that the phase instability observed in parent Ba_0.5Sr_0.5Co_0.8Fe_0.2O_3 − δ (BSCF) is suppressed already at the minimum substitution of 5 mol% of niobium for (Co, Fe). Both electrical conductivity and thermal expansion are found to decrease with increasing niobium concentration, which behaviors can be explained by defect chemical considerations, taking into account charge compensation mechanisms by doping BSCF with Nb⁵⁺ donor cations. The oxygen permeation flux of 10 mol% Nb-substituted BSCF, in the range 800-900 °C, is reduced by 10% relative to that found for parent BSCF. Switching from helium to a CO₂-containing purge gas results in a severe reduction or cessation of the oxygen flux. Options are discussed to avoid undesired formation of surface carbonates.     

Electrical Properties of Fe-doped Perovskite-like BaNb0.75-xFexNa0.25O3-δ (0.05 < x < 0.5)

In this paper, we report the electrical properties of Fe-doped perovskite-like compounds with a nominal chemical formula of BaNb_0.75-xNa_0.25Fe_xO_3-δ (0.05 < x < 0.5) (BNF). Various solid-state structural and electrical characterization techniques, including powder X-ray diffraction (PXRD), scanning electron microscopy (SEM), alternating current (AC) impedance spectroscopy and direct current (DC) methods were used for characterization. PXRD patterns for BNF members show the formation of perovskite-like structure. The total electrical conductivity values were determined under ambient air and wet air in the temperature up to 700 °C. The Fe concentration was strongly correlated to the conductivity response, with the x = 0.5 member exhibiting the highest conductivity in air. A relationship between the humidity content and conductivity in air was also observed in low Fe concentration BNF members (x = 0.5, 0.15), suggesting the presence of potential proton conduction; while the conductivity of high Fe content samples (x ≥ 0.3) showed little dependence on the humidity. The chemical stability of BNF samples was investigated in boiling H₂O and in flowing 100% CO₂ at elevated temperatures and the results demonstrated that all members were structurally stable under both conditions, except the x = 0.5 member which decomposed into BaCO₃ in the presence of CO₂ at 800 °C.     

Characterization of Ln0.5M0.5FeO3-δ (Ln = La, Nd, Sm; M = Ba, Sr) perovskites as SOFC cathodes

Ln_0.5M_0.5FeO_3-δ (Ln = La, Nd, Sm; M = Ba, Sr) perovskites have been synthesised by the glycine-nitrate route in order to obtain compounds with good morphological and electrical characteristics to be used as SOFC cathodes. A systematic study of the influence of the average ionic radius of the A cation (<r_A>), on the structural, morphological and electrical properties of these perovskites has been performed. The obtained materials have been characterised by ICP-AES analysis, X-ray powder and neutron powder diffraction, scanning electron microscopy and four-probe conductivity measurements. In this study <r_A> has been changed in the range 1.34 ≥ <r_A > ≥ 1.25 Å, while keeping constant the doping level, x = 0.5 (in A position) and A cation size disorder, σ² (r_A) = 0.0161 Å². Overall, the sample with the higher average ionic radius showed the highest values of conductivity. Chemical compatibility of the proposed cathodes with yttria-stabilised zirconia electrolyte (YSZ) has also been analysed. The data indicate that additional phase formations exist in all systems at temperatures above ~ 1000 °C.     

Investigations on the thermo-chemical stability and electrical conductivity of K-doped Ba3 − xKxCaNb2O9 − δ (x = 0.5, 0.75, 1, 1.25)

In this paper, we report the synthesis, crystal structure and electrical transport properties of new K-doped Ba₃CaNb₂O₉ (BCN) and investigate their chemical stability in H₂O and pure CO₂ at elevated temperature. The powder X-ray diffraction (PXRD) of Ba_2.5K_0.5CaNb₂O_9 − δ, Ba_2.25K_0.75CaNb₂O_9 − δ, Ba₂KCaNb₂O_9 − δ, and Ba_1.75K_1.25CaNb₂O_9 − δ showed the formation of a single-phase double perovskite (A₃BB^/₂O₉)-like cell with a lattice constant of a ∼ 2a_p (where a_p is a simple perovskite cell of ∼ 4 Å). Perovskite-like structure was found to be retained after treating with CO₂ at 700 °C and also after boiling H₂O for 120 h. The lattice constant of CO₂ and H₂O treated samples was found to be comparable to that of the corresponding as-prepared compound. The total electrical conductivity of all the investigated K-doped BCN increases with increasing K content in BCN in various atmospheres, including air, dry H₂, wet N₂ and wet H₂. The electrical conductivity in dry and wet H₂ atmospheres was found to be higher than that of air in the temperature range of 300-700 °C, while in wet N₂ a slightly lower value was observed. Among the compounds investigated in the present study Ba_1.75K_1.25CaNb₂O_9 − δ showed the highest total electrical conductivity of 1 × 10^− 3 S/cm in dry H₂ at 700 °C with an activation energy of 1.28 eV in the temperature range of 300-700 °C.     

Interaction of H2S with α-Fe2O3(0 0 0 1) surface

The atomic-scale structural changes in an α-Fe₂O₃ (hematite) (0 0 0 1) surface induced by sulfidation and subsequent oxidation processes were studied by X-ray photoemission spectroscopy, LEED, and X-ray standing wave (XSW) measurements. Annealing the α-Fe₂O₃(0 0 0 1) with a H₂S partial pressure of 1 × 10⁻⁷ Torr produced iron sulfides on the surface as the sulfur atoms reacted with the substrate Fe ions. The oxidation state of the substrate Fe changed from 3+ to 2+ as a result of the sulfidation. The XSW measured distance of the sulfur atomic-layer from the unrelaxed substrate oxygen layer was 3.16 Å. The sulfide phase consisted of three surface domains identified by LEED. Formation of the two-dimensional FeS₂ phase with structural parameters consistent with an outermost layer of (1 1 1) pyrite has been proposed. Atomic oxygen exposure oxidized the surface sulfide to a sulfate () and regenerated the α-Fe₂O₃(0 0 0 1) substrate, which was indicated by a (1 × 1) LEED pattern and the re-oxidization of Fe to 3+.     

Surface and redox chemistry of Sm0.95Ce0.05Fe1 − xNixO3 − δ perovskites

A new series of perovskite materials with formula Sm_0.95Ce_0.05Fe_1 − xNi_xO_3 − δ (0 ≤ x ≤ 0.10) has been prepared by sol-gel combustion via a citrate precursor route. X-ray diffraction data showed that materials prepared by this method had a single orthorhombic phase belonging to the Pnma (62) space group. The study of powders sintered in air and in reducing atmospheres reveals that these materials do not show phase separation in air (up to 1350 °C) nor under 5% v/v H₂/N₂ (up to 700 °C), but a phase separation of Sm₂O₃ does occur at and above 800 °C under 5% v/v H₂/N₂ without deterioration of the perovskite phase. The surfaces of all the powders (fresh, in-situ reduced and ex-situ reduced) were Sm rich, and multiple oxidation states for Fe were observed. XP analysis of in-situ reduced samples (800 °C and above) shows that metallic Fe forms in all nickel doped materials except x = 0.07. The surface oxygen vacancies and percentages of lattice and adsorbed oxygen for this series of Ni doped materials were determined and the oxygen recapturing ability is explained in terms of the multiple oxidation states of Fe.     

Rovibrational spectroscopy of the Fermi-interacting ν4 = 1 and ν3 = ν6 = 1 levels of DCF3

The high-resolution infrared spectrum of deuterated fluoroform (DCF₃) was studied in the 700 and 1200 cm⁻¹ regions, with the aim of assigning and analyzing the ν₄ CF₃ asymmetric stretching vibration. The Fermi-type anharmonic coupling between the ν₄ = 1 and ν₃ = ν₆ = 1 rovibrational levels, already mentioned in an early work of Ruoff et al. [Spectrochimica Acta Part A 31A (1975) 1099-1100], was studied here for the first time under high resolution. Assignments in the ν₃ + ν₆/ν₄ band system were confirmed and extended by the identification of the ν₃ + ν₆ − ν₆ and ν₄-ν₆ bands in the 700 cm⁻¹ region, the latter being enhanced near the Fermi crossings of the studied levels. Data from both the hot and difference bands were included in the analysis. The close separation of the studied vibrational levels of about 14.8 cm⁻¹ produces a large variety of resonance crossings which involve levels with . Besides the Fermi () and Coriolis () resonances, they were accounted for by inclusion of additional higher-order ( and ) interaction terms between the vibrational states. The least-squares fit of more that 16,000 vibration-rotation transitions provides a quantitative reproduction of data in all bands.     

The rotational spectra of the υ8 = υ9 = 1 and υ6 = υ7 = 1 interacting vibrational states of nitric acid (HNO3)

The analysis of the rotational spectrum of HNO₃ has been extended to include the υ₈ = υ₉ = 1 state at 1205.7 cm⁻¹ and the υ₆ = υ₇ = 1 state at 1223.4 cm⁻¹. Based on 78-519 GHz data, the assignments in the 8¹9¹ vibrational state have been significantly expanded from the previously reported microwave measurements [T.M. Goyette, F.C. De Lucia, J. Mol. Spectrosc. 139 (1990) 241-243]. A new microwave analysis is also reported for the 6¹7¹ vibrational state. A simultaneous analysis takes into account the localized ΔK_a = ±2 Fermi resonances between the vibrational states, describes the torsional splitting of 3.3 and 1.4 MHz for the 8¹9¹ and 6¹7¹ states respectively, and fits to experimental accuracy over 1500 rotational transition frequencies that extend up to J = 59. Infrared energy levels [A. Perrin, J.-M. Flaud, F. Keller, A. Goldman, R. D. Blatherwick, F. J. Murcray, C. P. Rinsland, J. Mol. Spectrosc. 194 (1999) 113-123] were also included in the analysis and fit to experimental accuracy. Measurement of strongly perturbed transitions in each vibrational state provide a determination of the band origin difference of 17.733184(17) cm⁻¹. The rotational constants agree well with those predicted by vibrational-rotational constants of the fundamental modes. Furthermore, the analysis will provide a very accurate simulation of the infrared spectrum of HNO₃ in the 8.3 μm region.     

Surface studies of 2,4-pentanedione on γ-Al2O3/NiAl (1 0 0) and NiAl (1 0 0)

The chemical compound 2,4-pentanedione (Hacac) has been shown to etch the oxidized metal surfaces metals such as copper and nickel, but not their unoxidized surfaces. Here it is shown that on the γ-Al₂O₃/NiAl (1 0 0) surface (oxidized NiAl (1 0 0)) etching of aluminum occurs at 170 K and 750 K. Reflection-absorption infrared spectroscopy (RAIRS) is used to show that Hacac binds to both the clean, metallic and oxidized surfaces, but decomposition and combustion products dominate on the metallic surface and no etching occurs. The binding process that involves a deprotonation reaction of the enol species was identified by redshift in the carbonyl peaks and the appearance of an Al-H peak observed in the IR spectrum. The implication of these results is that there is both an unusual low temperature and high temperature etching of the alumina by bound acac.     

Structure, electrical properties and temperature characteristics of?Bi0.5Na0.5TiO3–Bi0.5K0.5TiO3–Bi0.5Li0.5TiO3 lead-free piezoelectric ceramics

(1−x−y)Bi_0.5Na_0.5TiO₃–xBi_0.5K_0.5TiO₃– yBi_0.5Li_0.5TiO₃ lead-free piezoelectric ceramics have been prepared by an ordinary sintering technique, and their structure, electrical properties, and temperature characteristics have been studied systematically. The ceramics can be well-sintered at 1050–1150 °C. The increase in K⁺ concentration decreases the grain-growth rate and promotes the formation of grains with a cubic shape, while the addition of Li⁺ decreases greatly the sintering temperature and assists in the densification of BNT-based ceramics. The results of XRD diffraction show that K⁺ and Li⁺ diffuse into the Bi_0.5Na_0.5TiO₃ lattices to form a solid solution with a pure perovskite structure. As x increases from 0.05 to 0.50, the ceramics transform gradually from rhombohedral phase to tetragonal phase and consequently a morphotropic phase boundary (MPB) is formed at 0.15≤x≤0.25. The concentration y of Li⁺ has no obvious influence on the crystal structure of the ceramics. Compared with pure Bi_0.5Na_0.5TiO₃, the partial substitution of K⁺ and Li⁺ for Na⁺ lowers greatly the coercive field E _c and increases the remanent polarization P _r of the ceramics. Because of the MPB, lower E _c and large P _r, the piezoelectricity of the ceramics is improved significantly. For the ceramics with the compositions near the MPB (x=0.15–0.25 and y=0.05–0.10), the piezoelectric properties become optimum: piezoelectric coefficient d ₃₃=147–231 pC/N and planar electromechanical coupling factor k _P=20.2–41.0%. In addition, the ceramics exhibit relaxor characteristic, which probably results from the cation disordering in the 12-fold coordination sites. The depolarization temperature T _d shows a strong dependence on the concentration x of K⁺ and reaches the lowest values at the MPB. The temperature dependences of the ferroelectric and dielectric properties at high temperatures may imply that the ceramics may contain both the polar and non-polar regions at temperatures above T _d.     

Si doped Cu0.5Tl0.5Ba2Ca2Cu3O10−δ superconductors

The Si doped (Cu_0.5Tl_0.5)Ba₂Ca₂Cu_3−ySi_yO_10−δ (y=0, 0.25, 0.5, 0.75, 1.0, 1.25) superconductor samples have been synthesized to investigate the effect of mobile carriers on the critical temperature and magnitude of diamagnetism of this family of cuprates. The Si doped samples have tetragonal structure as observed from the X-ray diffraction spectra. The c-axis length of the unit cell of (Cu_0.5Tl_0.5)Ba₂Ca₂Cu_3−ySi_yO_10−δ was increased after the increase of Si concentration, whereas the critical temperature and the magnitude of diamagnetism have been decreased. The decrease in T_c(0) and magnitude of diamagnetism is possibly due to the deficiency of carriers in CuO₂/SiO₂ planes caused by the +4 state of Si atoms. However, the post-annealing of these samples in oxygen atmosphere has increased the critical temperature and the magnitude of diamagnetism. The FTIR absorption measurements of (Cu_0.5Tl_0.5)Ba₂Ca₂Cu_3−ySi_yO_10−δ samples have shown a softening of the apical oxygen mode of the type Cu(1)O_ACu(2) and TlO_ACu(2) with increased concentration of Si in the unit cell; the softening of this mode is directly linked with the increase in the c-axis lattice parameter of the (Cu_0.5Tl_0.5)Ba₂Ca₂Cu_3−ySi_yO_10−δ superconductor.     

K0.5Bi0.5TiO3—Na0.5Bi0.5TiO3系统铁电陶瓷相界的X射线研究

用X射线衍射方法测定了K_0.5Bi_0.5TiO₃—Na_0.5Bi_0.5TiO₃系统不同组分试样的点阵常数和相变温度,确定了四方-三方相界组成。给出了K_0.5Bi_0.5TiO₃和Na_0.5Bi_0.5TiO₃的多晶X射线衍射数据。 关键词：     

Structural and optical properties of Ga2(1−x)In2xO3 films prepared on α-Al2O3 (0 0 0 1) by MOCVD

Ga_2(1−x)In_2xO₃ thin films with different indium content x [In/(Ga + In) atomic ratio] were prepared on α-Al₂O₃ (0 0 0 1) substrates by the metal organic chemical vapor deposition (MOCVD). The structural and optical properties of the Ga_2(1−x)In_2xO₃ films were investigated in detail. Microstructure analysis revealed that the film deposited with composition x = 0.2 was polycrystalline structure and the sample prepared with x up to 0.8 exhibited single crystalline structure of In₂O₃. The optical band gap of the films varied with increasing Ga content from 3.72 to 4.58 eV. The average transmittance for the films in the visible range was over 90%.     

Oxidation mechanism and ferryl domain formation on the α-Fe2O3 (0 0 0 1) surface

Recent experimental evidence calls for a reinterpretation of the oxidized structure in chemically distinct domains of the hematite (0 0 0 1) surface as the ferryl (FeO) termination rather than the bulk terminated O₃-Fe-Fe-R structure. Although this interpretation is consistent with experimental data and ab initio thermodynamics calculations, it raises serious questions about how molecular oxygen can be dissociated on a surface where reactive iron centers are slightly more than 5 Å apart. Here, we propose a novel cooperative bimolecular mechanism that provides a reasonable pathway for the formation of the unusual ferryl surface termination and should be readily reversible, which is important for understanding the function of hematite surfaces as an oxidation catalyst.     

Highly thermal stable transparent conducting SnO2:Sb epitaxial films prepared on α-Al2O3 (0 0 0 1) by MOCVD

Antimony-doped tin oxide (SnO₂:Sb) single crystalline films have been prepared on α-Al₂O₃ (0 0 0 1) substrates by metal organic chemical vapor deposition (MOCVD). The antimony doping was varied from 2% to 7% (atomic ratio). Post-deposition annealing of the SnO₂:Sb films was carried out at 700-1100 °C for 30 min in atmosphere ambient. The effect of annealing on the structural, electrical and optical properties of the films was investigated in detail. All the SnO₂:Sb films had good thermal stability under 900 °C, and the 5% Sb-doped SnO₂ film exhibited the best opto-electrical properties. Annealed above 900 °C, the 7% Sb-doped SnO₂ film still kept high thermal stability and showed good electrical and optical properties even at 1100 °C.     

Structural and photoluminescence properties of SnO2:Ga films deposited on α-Al2O3 (0 0 0 1) by MOCVD

Gallium-doped tin oxide (SnO₂:Ga) films have been prepared on α-Al₂O₃ (0 0 0 1) substrates at 500 °C by the pulse mode metalorganic chemical vapor deposition (MOCVD) method. The relative amount of Ga (Ga/(Ga+Sn) atomic ratio) varied from 3% to 15%. Post-deposition annealing of the films was carried out at different temperatures for 1.5 h in ambient atmosphere . The structural, electrical, optical and photoluminescence (PL) properties of the films have been investigated as a function of annealing temperature. All the films have the rutile structure of pure SnO₂ with a strong (2 0 0) preferred orientation. A single ultraviolet (UV) PL peak near 337.83 nm was observed at room temperature for the 3% Ga-doped as-grown film and near 336 nm for the 15%-doped film, which can be ascribed to electron transition from the oxygen vacancy and interstitial Ga³⁺ donor levels to the acceptor level formed by the substitution of Ga³⁺ for the Sn site. After annealing, the luminescence spectra have changed a little bit, which is being discussed in detail.     

Dielectric properties of Cu0.5Tl0.5Ba2Ca3Cu4O12−δ bulk superconductor

The dielectric properties of Cu_0.5Tl_0.5Ba₂Ca₃Cu₄O_12−δ superconductor samples were studied at 79 and 290 K by means of capacitance (C) and conductance (G) measurements with the test frequency (f) in the range of 10 kHz to 10 MHz. A negative capacitance (NC) phenomenon has been observed, which is most likely arising due to higher Fermi level of ceramic superconductor samples than metal electrodes. Also the NC may be due to the space charge located at the multiple insulator–superconductor interfaces (grain boundaries) in the materials. The negative dielectric constant (ε′) and loss factor (tan δ) show strong dispersion at low frequencies. The lower thermal agitation at 79 K may enhance the polarizability and hence the dielectric constants (ε′ and ε″).     

Characterization of YSr2Fe3O8 − δ as electrode materials for SOFC

YSr₂Fe₃O_8 − δ was prepared by traditional solid state reaction method and characterized by X-ray diffraction, ac impedance, dc conductivity, dilatometry and thermogravimetric analysis for possible use in solid oxide fuel cells (SOFCs). YSr₂Fe₃O_8 − δ crystallizes with tetragonal symmetry in the space group P4/mmm and found to be stable at high temperatures under H₂ and air. Four probe dc electrical conductivity measurements show that the conductivity increases up to 745 K and then decreases with temperature; the highest conductivity σ_745K = 43.5 S cm^− 1. The n-type conductivity at low oxygen partial pressure (pO₂) changes to p-type at high pO₂. Polarization behavior was investigated measuring the ac impedance response in symmetrical cell arrangements in air with YSZ and GDC electrolytes. Cathodic area specific resistance (ASR) varies with firing temperature. The lowest area specific resistance was observed with a GDC electrolyte fired at 1000 °C. In case of YSZ, ASR increases and in case of GDC, ASR decreases in air when electrode firing temperature decreases. At 800 °C ASRs are 0.20 Ω cm² and 0.65 Ω cm² with GDC and YSZ electrolytes, respectively, in air. Fuel cell measurements with symmetrical electrodes were performed using a thin YSZ electrolyte under H₂ at anode and air at cathode, show that the power density is about 0.035 W/cm² at 900 °C.