Ni-B非晶态合金催化苯丙酮酸加氢合成苯丙氨酸

通过化学还原法制备了纳米非晶态Ni-B合金催化剂,考察了其对苯丙酮酸胺化加氢合成苯丙氨酸的催化性能.结果表明,相对于传统雷尼镍和漆原镍催化剂,非晶态合金催化剂表现出更为优异的活性和选择性,并且当非晶态Ni-B合金负载在SiO2载体上时,其活性和选择性均得到较大提高(高达97.67%).非晶态合金催化剂对苯丙氨酸合成反应表现出较好活性和选择性的原因主要是硼提供部分电子给镍的效应以及非晶态合金颗粒的纳米尺寸效应.     

非负载镍催化剂的2-乙基蒽醌加氢活性及其氢吸脱附性质

 分别制备了金属镍粉、兰尼镍、Ni-B非晶态合金及镧掺杂的Ni-B非晶态合金(Ni-B-La)催化剂,研究了催化剂的氢吸附和脱附性质以及对2-乙基蒽醌加氢反应的催化性能. 结果表明,金属镍粉、兰尼镍和Ni-B催化剂表面均具有两种氢吸附位: 弱吸附位和强吸附位. Ni-B-La催化剂表面只有氢的强吸附位,其强吸附氢量与兰尼镍相当. 推测只有氢的强吸附位是2-乙基蒽醌加氢反应的活性中心,并且Ni-B-La催化剂上的强吸附氢较兰尼镍上的更活泼,因而Ni-B-La非晶态合金催化剂对加氢反应的催化活性高于兰尼镍.     

非晶态合金催化剂NiB、NiB/TiO2的制备、表征及其环丁烯砜加氢催化活性的研究

分别采用化学还原法和浸渍还原法制备了系列NiB及NiB／TiO2非晶态合金催化剂，用XRD、ICP、SEM、SAED和DSC等技术对催化剂的物性进行了表征，并将其用于环丁烯砜加氢反应，研究了制备条件(镍硼摩尔比、滴加方式和金属离子浓度)对非晶态合金催化剂加氢活性的影响。结果表明，选择镍硼摩尔比为1：2，Ni^2 浓度为0．1mol／L，采用正滴加方式(将KBH4溶液滴加到Ni(NO3)2溶液中)所制得的NiB非晶态合金催化剂环丁烯砜加氢活性优于RaneyNi催化剂，对于NiB／TiO2负载型非晶态合金催化剂，镍的实际负载量达14．5％时，NiB／TiO2与NiB的环丁烯砜加氢催化活性相当。     

非晶态合金催化剂研究

本文对非晶态合金催化剂的制备及在催化领域中的应用进行了评述.通过骤冷法、化学还原法、浸渍还原法可以得到满足不同催化反应需要的非晶态合金催化剂,并可以通过制备条件的变化调变催化剂的性能.制备过程中焙烧温度、负载量以及不同催化剂载体的选用都会影响所得催化剂的性能.非晶态合金催化剂的非晶态结构、表面形态、活性中心分布等可以通过XRD、EXAFS、DSC、SEM、TEM、XPS等方法进行表征、定性.对于非晶态合金催化剂在含有不饱和基团化合物加氢反应中的研究、应用进行了阐述.     

高比表面NiP非晶态合金的制备及其催化性能

 以次磷酸和硝酸镍为原料,三正丙胺调节溶液的pH值,制备了具有高比表面积的NiP非晶态合金(ABET=200～300 m2/g). 采用ICP,XRD,TEM和N2物理吸附等方法对不同条件下制备的NiP非晶态合金进行了表征,并在250 ml高压反应釜中评价了NiP对环丁烯砜加氢反应的催化活性. 结果表明,在NiP非晶态合金的制备过程中,反应时间、磷/镍投料摩尔比和体系初始pH值等都会对NiP非晶态合金的物化性质产生影响. 制备温度对NiP非晶态合金的物化性质影响很大,温度高会使催化剂的氧化程度加深,催化活性随之迅速下降. 较适宜的NiP非晶态合金的制备温度为283～303 K,此温度范围内制得的NiP催化剂活性可达到90%以上,高于相同条件下使用次磷酸钠、镍盐和氢氧化钠制得的NiP非晶态合金催化剂(活性为50%～60%).     

乙二胺功能化处理CNTs对NiB/CNTs催化剂性能的影响

用乙二胺功能化处理碳纳米管,增强其亲水性,有利于非晶态合金在碳纳米管负载.用化学还原法制备NiB/CNTs非晶态合金,以苯加氢探针为反应考察催化剂的活性,利用XRD、ICP、BET、TEM、TPR、TPD等方法对催化剂进行表征,结果表明乙二胺功能化处理,CNTs比表面积增大,镍的负载量增多,镍硼颗粒细化,从而提高了非晶态NiB/CNTs的催化活性,增强了其抗硫性.     

以次磷酸镍为原料制备NiP和NiPB非晶态合金的新方法

以次磷酸镍为原料用化学还原法制备出了NiP和NiPB非晶态合金.用ICP、XRD和TEM等方法对催化剂物性进行了表征.研究了制备条件，如原料浓度、温度、pH值及引发剂的加入对制备NiP非晶态合金的影响.在300 K下所制备的NiP非晶态合金平均粒径约为30 nm.研究了原料浓度与原料配比对NiPB非晶态合金物性的影响，可通过改变原料浓度和配比得到所需组成的NiPB非晶态合金. NiPB非晶合金平均粒径约为15 nm.     

稀土对非晶态NiB合金催化剂性能的影响

研究了Ｅｕ,Ｇｄ,Ｔｂ对化学还原法制备非晶态ＮｉＢ合金催化剂的加氢及抗硫性能的影响。Ｅｕ,Ｇｄ,Ｔｂ的加入可提高ＮｉＢ合金的催化活性和抗硫性。其原因是稀土元素与ＮｉＢ合金间存在的相互作用。ＮｉＢ合金催化剂的活性中心与还原态的镍及镍＝硼－氧物种有关。     

非晶态超微粒子镍合金催化剂的研究 Ⅰ．Ni－B合金的制备及表征

非晶态超微粒子，镍基合金，硼合金，合金催化剂，表征     

镍－硼非晶态合金催化剂的ESR与DSC研究

镍－硼非晶态合金催化剂的ＥＳＲ与ＤＳＣ研究张菊，郑小明（杭州大学催化研究所，杭州３１００２８）王立（浙江大学高分子科学与工程学系，杭州３１００２７）关键词非晶态，镍－硼合金，电子自族共振，示差扫描量热法非晶态合金是一种新型的催化材料．用化学法制得的非...     

Skeletal Amorphous Nickel Based Alloy Catalysts and Magnetically Stabilized Bed Hydrogenation Technology

Looking toward 21 century, smaller, cleaner and more energy-efficient technology will be an important trend in the development of chemical industry. In light of the new process requirements, a number of technology breakthroughs have occurred. One of these discoveries, the magnetically stabilized bed (MSB), has been proven a powerful process for intensification. Since its initial research in the late 1980’s at Research Institute of Petroleum Processing (RIPP), the MSB technology and rela…     

载体TiO2对Co-P非晶态合金性质的影响

用还原沉积法分别合成了纯态Co-P非晶态合金和一种新型负载非晶态合金催化剂CoP/TiO₂, 用XRD, ICP, TEM, BET和DSC等手段对催化剂的物理性质进行了表征, 比较了它们的结构、组成、形貌、表面积及热稳定性等物理性质及其对PH₃分解的催化活性. 与纯态Co-P非晶态合金比较, CoP/TiO₂具有更大的表面积和较高的热稳定性及催化活性, 这缘于TiO₂载体与催化剂的相互作用以及载体对Co-P良好的分散性能.     

Ni-B非晶态合金催化剂用于卤代硝基苯液相加氢制卤代苯胺

 用化学还原法制备了Ni-B非晶态合金催化剂,并将其用于4种卤代硝基苯的液相加氢反应. 采用X射线衍射和透射电子显微镜研究了催化剂的非晶性质. 在373 K下处理2 h后催化剂保持非晶态结构,在773 K下处理2 h后催化剂完全晶化. 讨论了Ni-B非晶态合金催化剂的催化性能与其结构之间的关系,并与其它Ni基催化剂进行了比较. Ni-B非晶态合金催化剂不仅具有较高的催化活性,而且对卤代芳胺的选择性较高,脱卤率小于4%,优于其它Ni基催化剂.     

Structured Catalysts Prepared by Electroless Plating Technique onto a Metal Substrate, for a Wall-Type Hydrogen Production System

This article reviews our works on the structured catalysts for a wall-type hydrogen production system including methanol steam reforming (MSR), CO shift reaction (CO SR) and methanol decomposition (MD). The structured catalysts were copper-based, palladium-based and nickel-based catalysts. Such a series of structured catalysts were prepared by the electroless plating technique that is a novel method for preparing a structured type catalyst onto a metal-substrate. The copper-based catalyst exhibited high performance for MSR and CO SR, the palladium-based catalyst high for MSR, and the nickel-based catalyst high for MD. The catalytic properties of these catalysts were affected by the difference of the plating condition and the pretreatment condition prior to the reaction. In the copper-based catalyst, the reforming and shift activities were enhanced by the oxidation treatment. One of the factors of such activity enhancement by the oxidation was thought to be in close proximity existence of copper and zinc atoms. A lot of monodentate-type formate species having high reactivity was formed on the oxidized catalyst, which would be correlated to the activity enhancement. In the palladium-based catalyst, the reforming activity was improved by the continuous reduction treatment followed by the oxidation. Such continuous pretreatment formed the PdZn alloy species thought to be a reforming site in the surface layer. The decomposition performance of the nickel-based catalyst depended on the ratio of the crystallite size of nickel particles to that of aluminum particles. The electronic influence of zinc and phosphorous components incorporated in the plated layer contributed to the improvement of the selectivity of product.     

超细Pd—B／SiO2非晶态合金加氢反应的催化活性

采用浸渍法并通过ＫＢＨ４还原制备超细Ｐｄ－Ｂ／ＳｉＯ２非晶态合金催化剂,以硝基苯加氢生成苯胺为目标反应,考察了上述催化剂的活性和选择性及热稳定性,并与晶态Ｐｄ－Ｂ／ＳｉＯ２和Ｐｄ／ＳｉＯ２催化剂及非负载型Ｐｄ－Ｂ非晶态合金催化剂进行了比较。     

Characterization and Catalytic Properties of a Rapidly Quenched Ni-RE-P-AL Catalyst

IntroductionAmorphous.alloy has been found to have superior catalytic properties["']. However, asan applied catalyst, its small surface area and low thermal stability during the catalytic processare the encountered problems usually.In the previous study, we found that addition of a small amount of rare earth element effectively stabilized the amorphous phase in a Ni--P alloyL'~'j, and the surface area of the amorphous Ni--RE--P alloy could be greatly enlarged by introducing Al into the Ni-…     

Ni-Co-B非晶态合金的结构和催化活性的理论研究

利用一系列原子簇模型Ni~xCo~3~-~xB~2(x=1～3)对Ni-Co-B非晶态合金的电子结构进行了SCC-DV-Xα计算。结果表明,Ni-B非晶态合金的催化加氢活性可通过Co的引入而得到改进。结合EXAFS和活性试验的结果,得出Ni和Co对非晶态Ni-Co-B合金的结构的稳定性有一种协同作用的结论。     

Ni-B/SiO2非晶态催化剂应用于硝基苯液相加氢制苯胺

 考察了Ni－B／SiO2非晶态催化剂在高压液相硝基苯加氢制苯胺反应中的催化活性和选择性．研究表明,该催化剂不仅具有很高的催化活性,而且对苯胺的选择性较高,优于RaneyNi以及其它Ni基催化剂．晶化导致催化剂失活．载体的存在不仅能提高催化剂的分散度,而且能对非晶态结构起稳定化作用;将催化剂保存在乙醇中可保持其活性不变．结合催化剂的表征,讨论了Ni－B／SiO2非晶态催化剂的催化性能与其结构的关系．     

超细Co-B非晶态合金的制备及其催化乙腈加氢性能

报道了 一种用 于乙腈加 氢的 新 型 复合 型 催化 剂 超细 Ｃｏ Ｂ 非 晶 态合 金（ 粒 径 ６０ ｎ ｍ左右） , 其催 化性能显 著优于 其它 Ｃｏ 基催 化剂． 以此代替 工业用 Ｒａｎｅｙ Ｎｉ , 不 仅可 提高 对乙 胺的选择性 ,而且可 显著减轻 环境污 染． 通 过一系列 表征,讨 论了乙腈 在催化 剂活性位 的吸附 模式及催化加氢 反应机 理,由此对 其催化 性能与催 化剂结 构的关系 进行了说 明．     

非晶态超微粒子镍合金催化剂的研究──Ⅱ．Ni－B催化剂对苯加氢反应动力学的研究

非晶态超微粒子镍合金催化剂的研究──Ⅱ．Ｎｉ－Ｂ催化剂对苯加氢反应动力学的研究李同信，张秀峰，李合秋（中国科学院大连化学物理研究所，大连１１６０２３）靳常德，蒋育林，崔建彤，王大庆（大连理工大学化工学院，大连１１６０１１）关键词非晶态超微粒子，镍基合...