Defect Structure and Up-conversion Luminescence Properties of ZrO<Subscript>2</Subscript>:Yb<Superscript>3+</Superscript>,Er<Superscript>3+</Superscript> Nanomaterials

The up-converting ZrO₂:Yb³⁺,Er³⁺ nanomaterials were prepared with the combustion and sol–gel methods. FT-IR spectroscopy was used for analyzing the impurities. The crystal structures were characterized with X-ray powder diffraction and the mean crystallite sizes were estimated with the Scherrer formula. Up-conversion luminescence measurements were made at room temperature with IR-laser excitation at 977 nm. The IR spectra revealed the conventional and OH⁻ impurities for the combustion synthesis products. The structure of the ZrO₂:Yb³⁺, Er³⁺ nanomaterials was cubic except for the minor monoclinic and tetragonal impurities obtained with the sol–gel method. The materials showed red (650–700 nm) and green (520–560 nm) up-conversion luminescence due to the ⁴F_9/2→⁴I_15/2 and (²H_11/2, ⁴S_3/2)→⁴I_15/2 transitions of Er³⁺, respectively. The products obtained with the combustion synthesis exhibited the most intense luminescence intensity and showed considerable afterglow.     

共沉淀法制备Y2SiO5∶Er3+ ,Yb3+ ,Tm3+及其上转换发光性能研究

采用化学共沉淀法制备了系列Y_1.98-2xYb_2x Er_0.02SiO₅(0.00≤x≤0.15)以及Y_1.736Yb_0.24Er_0.02Tm_0.004SiO₅上转换发光材料,比较了室温下Y_1.98-2xYb_2x Er_0.02 SiO₅ (x=0.00,0.08)样品在400—1600 nm范围内的吸收光谱,测量了所有样品在976 nm OPO激光器激发下的上转换发射光谱,以及Er³⁺离子⁴S_3/2(⁴F_9/2)→⁴I_15/2,Tm³⁺离子¹G₄→³H₆荧光衰减曲线和不同激发功率下的上转换蓝光发射强度,从而分析讨论了Er³⁺,Tm³⁺在Y₂SiO₅中的上转换发光机理.研究结果表明:在1250 ℃相对较低的温度下合成了X2型单斜晶系Y₂SiO₅ ∶Ln³⁺(Ln³⁺=Er³⁺,Yb³⁺,Tm³⁺),Yb³⁺的敏化显著增强了样品在976 nm附近的吸收能力,并大幅度加宽了该处的吸收带.分析上转换发射光谱发现:上转换绿光和红光强度都随着Yb³⁺浓度的增加先增强后减弱,但红光的猝灭浓度较高,归因于Er³⁺→Yb³⁺反向能量传递ETU4和Yb³⁺→Er³⁺正向能量传递ETU3过程的发生;上转换蓝光发射是三光子吸收过程,是通过Yb³⁺,Tm³⁺之间三次声子辅助的能量转移方式实现的. 关键词： 上转换 共沉淀 2SiO₅∶Er³⁺')" href="#">Y₂SiO₅∶Er³⁺ 3+')" href="#">Yb³⁺ 3+')" href="#">Tm³⁺     

Sensitizer-dependent up-conversion of Ho<Superscript>3+</Superscript> in nanocrystalline Y<Subscript>2</Subscript>O<Subscript>3</Subscript>

Ho³⁺–Yb³⁺ co-doped Y₂O₃ nanocrystals were synthesized by firing hydroxy carbonate precursors. Yb³⁺-concentration-dependent up-conversion properties of Ho³⁺ in Y₂O₃ nanocrystals have been investigated. The relative intensity of up-converted red emission increases more quickly than that of the green and the near-infrared ones with the enhancement of the concentration of Yb³⁺. It is believed that the energy process ⁵ S ₂ (⁵F₄) (Ho) + ⁵ I ₇ (Ho) →⁵ I ₆ (Ho)+⁵ F ₅ (Ho) plays an important role in the population of the ⁵ F ₅ level of Ho³⁺. The result indicates that the intensity ratio of the green emission to the red one can be tuned by changing the sensitizer concentration. PACS 78.55.-m     

Er3+及Er3+/Yb3+掺杂ZrO2-Al2O3的制备及发光性质

采用共沉淀法制备了纳米晶ZrO₂-Al₂O₃∶Er³⁺发光粉体.所制备的粉体室温下具有Er3+离子特征荧光发射,主发射在绿光,其中位于547 nm、560 nm的绿光最强,并得出稀土离子与基质之间有能量传递.对不同煅烧温度下的样品研究表明:因不同温度下所制得的样品晶相不同.研究了纳米晶ZrO2-Al2O3∶Er3+及ZrO₂-Al₂O₃∶Er³⁺/Yb³⁺的上转换发光,并分析了上转换的跃迁机制.发现ZrO₂-Al₂O₃∶Er³⁺的绿光为双光子过程,而ZrO₂-Al₂O₃∶Er³⁺、Yb³⁺的上转换光谱中,红光和绿光也为双光子过程,而极弱的蓝光为三光子过程.讨论了Er³⁺的浓度猝灭现象.最适宜掺杂浓度的原子分数为2%（Er³⁺/Zr⁴⁺）.     

Yb3+敏化的Er3+/Ho3+共掺碲酸盐玻璃的上转换发光研究

用高温熔融法制备了系列Er³⁺/Yb³⁺共掺，Ho³⁺/Yb³⁺共掺，和Er³⁺/Yb³⁺/Ho³⁺三掺碲酸盐玻璃，在975nm激光抽运下三种掺杂玻璃中都出现了较强的绿光和红光上转换.研究了Yb³⁺离子对Er³⁺和Ho³⁺离子上转换发光强度的影响以及Yb³⁺→Er关键词： 3+/Yb³⁺/Ho³⁺共掺')" href="#">Er³⁺/Yb³⁺/Ho³⁺共掺 碲酸盐玻璃 光谱性质 上转换     

Ce3+对Er3+/Yb3+共掺TeO2-WO3-ZnO玻璃发光性能的影响

在Er³⁺/Yb³⁺共掺TeO₂-WO₃-ZnO玻璃中引入Ce³⁺，研究了Ce³⁺对Er³⁺1.5μm发射性能及其上转换发光性能的影响。结果表明，随Ce³⁺浓度的增加Er³⁺1.5μm波段的荧光强度先增强后降低，优化的Ce³⁺掺杂浓度在2.07×10²⁰/cm³左右；1.5μm波段的荧光寿命则随Ce³⁺浓度的增加有轻微降低，从3.4ms降到3.0ms，但Ce³⁺浓度的增加对1.5μm波段的荧光半高宽基本无影响；Er³⁺/Ce³⁺间的交叉弛豫Er³⁺(⁴I_11/2)+Ce³⁺(²F_5/2)→Er³⁺(⁴I_13/2)+Ce³⁺(²F_7/2)使玻璃的上转换发光强度大大降低，但在过高的Ce³⁺浓度下，Er³⁺/Ce³⁺间的另一交叉弛豫Er³⁺(⁴I_13/2)+Ce³⁺(²F_5/2)→Er³⁺(⁴I_15/2)+Ce³⁺(²F_7/2)则使Er³⁺⁴I_13/2能级粒子数减少，导致1.5μm波段荧光强度和荧光寿命降低. 关键词： 碲钨酸盐玻璃 发光性能 3+离子')" href="#">Er³⁺离子 3+离子')" href="#">Ce³⁺离子 交叉弛豫     

The up-conversion properties of Yb and Er doped Y4Al2O9 phosphors

Er³⁺ doped and Yb³⁺/Er³⁺ co-doped Y₄Al₂O₉ phosphors are prepared by the sol-gel method. The effect of dopant concentration on the structure and up-conversion properties is investigated by X-ray diffraction (XRD) and photoluminescence, respectively. XRD pattern indicates that the sample structure belongs to monoclinic. Under 980 nm excitation, the green and red up-conversion emissions are observed and the emission intensities depended on the Yb³⁺ ion concentration. The green up-conversion emissions decrease with the increase of Yb³⁺ concentration, while red emission increases as Yb³⁺ concentration increases from 0 to 8 at% and then decreases at high Yb³⁺ concentration. The mechanisms of the up-conversion emissions are discussed and results shows that in Er³⁺ and Yb³⁺/Er³⁺ co-doped system, cross-relaxation (CR) and energy transfer (ET) processes play an important role for the green and red up-conversion emissions.     

Luminescence of transparent glass ceramics containing Er<Superscript>3+</Superscript> and Yb<Superscript>3+</Superscript> zirconate-titanate nanocrystals

Luminescence regularities have been studied in new erbium/ytterbium materials based on glasses and glass ceramics of a magnesium-aluminosilicate system containing nanoscale erbium/ytterbium zirconate titanate crystals with the pyrochlore structure. Lifetimes of Yb³⁺ and Er³⁺ ions in the ² F_5/2 state and in the ⁴I_11/2 and ⁴I_13/2 states, respectively, and the efficiency of Yb³⁺ → Er³⁺ energy transfer have been evaluated. The identified spectral-luminescent characteristics of the studied glasses and glass ceramics co-doped with erbium and ytterbium ions show that these materials are promising media for producing laser generation in the spectral range around 1.5 μm.     

Intense Upconversion Luminescence of Yb<Superscript>3+</Superscript>-Er<Superscript>3+</Superscript> in Li<Subscript>2</Subscript>O Content Tungsten-tellurite Glasses

The Er³⁺ -Yb³⁺ codoped in Li₂O content tungsten -tellurite (TWL) transparent glasses are synthesized and measured the absorption, Raman and upconversion luminescence (UPL) spectra. At room temperature intense green emission peak at 560 nm ( ⁴S_3/2→⁴I_15/2) and red emission peak at 670 nm ( ⁴F_9/2→⁴I_15/2) of Er³⁺ observed even at minimum 86 mW pumping power of infrared 980 nm excitation. For structure of the TWL glass, Raman spectrum result revealed that an important role of WO₃ in the formation of glass network linkage with Li₂O. Under this influence estimated lifetime of the ⁴I_11/2 of Er³⁺ was 1.89 μs and due to lower phonon energy of the glass produce strong upconversion signal. The effect of Er₂O₃ concentration on emission intensity result indicated that green emission intensity initially increase in compare to red emission. Under the 980 nm pump power variation measured the relatively increases the red emission to the green emission intensity and analyze the possible upconversion mechanism and process.     

Polarized spectral properties of Er<Superscript>3+</Superscript> ions in NaGd(WO<Subscript>4</Subscript>)<Subscript>2</Subscript> crystal

Polarized spectral properties of Er³⁺:NaGd(WO₄)₂ single crystal are reported. The crystal was grown by the Czochralski method. The Judd–Ofelt theory was applied to analyze the polarized absorption spectra and then calculate the spontaneous emission probabilities, radiative lifetimes, and branching ratios. Fluorescence decay curves of the ⁴ I _13/2, ⁴ I _11/2, and ⁴ S _3/2 multiplets for the Er³⁺ ions were measured. Stimulated emission cross-sections of the ⁴ I _13/2→⁴ I _15/2 transition obtained by the Fuchtbauer–Ladenberg formula and the reciprocity method were compared. Multi-phonon relaxation rates of the crystal were estimated. Green up-conversion fluorescence around 531 and 552 nm was observed, and the possible up-conversion mechanisms were proposed. PACS 78.20.-e; 42.70.Hj     

Comparative Investigation on Nanocrystal Structure and Luminescence Properties of Gadolinium Molybdates Codoped with Er<Superscript>3+</Superscript>/Yb<Superscript>3+</Superscript>

This paper reports on the comparative investigation of nanocrystal structure and luminescence properties of Er³⁺/Yb³⁺-codoped gadolinium molybdate nanocrystals Gd₂(MoO₄)₃ and Gd₂MoO₆ synthesized by the Pechini method with citric acid and ethylene glycol. Their crystallization, structure transformation, and morphologies have been investigated by X-ray diffraction, thermogravimetric/differential scanning calorimetry, and transmission electron microscopy. It is noticed that Er³⁺/Yb³⁺-codoped monoclinic Gd₂(MoO₄)₃ nanocrystals have shown an intense upconversion through a sintering of the organic complex precursor at 600°C. Furthermore, it transforms to orthorhombic Gd₂(MoO₄)₃ when the precursor is sintered at 900°C. In counterpart of monoclinic Gd₂MoO₆, however, the monoclinic structure remains unchanged when the precursor is sintered at a temperature ranging from 600°C to 900°C. Intense visible emissions of Er³⁺ attributed to the transitions of ²H_11/2, ⁴S_3/2–⁴I_15/2 at 520 and 550 nm, and ⁴F_9/2–⁴I_15/2 at 650 nm have been observed upon an excitation with a UV source and a 980 nm laser diode, and the involved mechanisms have been explained. It is quite interesting to observe obvious differences both in the excitation and the upconversion emission spectra of Er³⁺/Yb³⁺-codoped Gd₂(MoO₄)₃ respectively with monoclinic and orthorhombic structure. The quadratic dependence of fluorescence on excitation laser power has confirmed that two-photons contribute to upconversion of the green–red emissions.     

Intense up-conversion emissions of Yb3+/Dy3+ co-doped Al2O3 nanopowders prepared by non-aqueous sol—gel method

Yb³⁺/Dy³⁺ co-doped Al₂O₃ nanopowders have been prepared by the non-aqueous sol-gel method and their up- conversion photoluminescence spectra are measured under excitation by 980-nm semiconductor laser. The results show that there are comparatively abundant spectra of up-conversion emissions centered at 378, 408, 527 and 543, and 663 nm, corresponding to ⁴G_9/2 → ⁶H_13/2, ⁴G_9/2 → ⁶H_11/2, ⁴I_15/2 → ⁶H_13/2, and ⁴F_9/2 → ⁶H_11/2 transitions of Dy³⁺, respectively. Two-photon and three-photon processes are involved in ultraviolet, violet, green, and red up-conversion emissions. The energy transition between Yb³⁺ and Dy³⁺ is discussed.     

VUV luminescence of Er<Superscript>3+</Superscript> ions in LiYF<Subscript>4</Subscript> and BaY<Subscript>2</Subscript>F<Subscript>8</Subscript> crystals

Vacuum ultraviolet luminescence of Er³⁺ ions in LiYF4 and BaY₂F₈ crystals has been investigated. It is revealed that under excitation by 193 nm radiation from an ArF excimer laser the interconfigurational 5d–4f radiative transitions in Er³⁺ ions are observed. It is shown that from the LiYF₄:Er crystal only the spin-forbidden luminescence (λ = 165 nm) is detected, whereas both the spin-forbidden (λ = 169 nm) and spin-allowed (λ = 160.5 nm) components are observed from the BaY₂F₈:Er crystal.     

980 nm激发下Er3+/Yb3+共掺杂ZrO2-Al2O3粉末的上转换发光特性

通过固相反应法制备了Er³⁺/Yb³⁺共掺杂ZrO₂-Al₂O₃粉末的样品，并对样品在980nm激光激发下的上转换发光特性进行了研究.从发射光谱可以发现，在可见光范围内有3个强的发光带，一个位于654nm附近的红光带和两个分别位于545nm、525nm附近的绿光带，分别对应于Er³⁺离子的以下辐射跃迁：⁴F_9/2→⁴I_15/2、⁴S_3/2→⁴I_15/2、 ²H_11/2→⁴I_15/2.其中又以Er³⁺离子的⁴F_9/2→⁴I_15/2跃迁产生的红色荧光辐射最强.对其上转换发光机制进行了分析，发现这三个发光过程都是双光子过程.对样品粉末进行了XRD检测，发现ZrO₂主要以立方相为主，并且计算得到了这种立方结构的晶格常数.Al₂O₃固溶于ZrO₂中，Al³⁺嵌入ZrO₂后产生氧空位，导致ZrO₂晶体的对称性降低，这种结构变化更有利于提高上转换效率，即上转换发光强度增强. 关键词： 3+/Yb³⁺')" href="#">Er³⁺/Yb³⁺ 上转换 2-Al₂O₃')" href="#">ZrO₂-Al₂O₃ 荧光 稀土     

Green,blue, red,near-infrared up-conversion luminescence of Yb<Superscript>3+</Superscript>/Er<Superscript>3+</Superscript>/Tm<Superscript>3+</Superscript> co-doped YVO<Subscript>4</Subscript> nanoparticles

YVO₄:Yb³⁺,Er³⁺; YVO₄:Yb³⁺,Tm³⁺; and YVO₄:Yb³⁺,Er³⁺,Tm³⁺ were all synthesized via sol-gel method with a subsequent thermal treatment. Specifically, YVO₄:Yb³⁺,Er³⁺,Tm³⁺ phosphors were prepared with different annealing temperatures to study the influence of temperature. The transmission electron microscope (TEM), scanning electron microscope (SEM), X-ray diffractometer (XRD), and photoluminescent (PL) spectrofluorometer were used to investigate the morphology, crystal structure, and up-conversion luminescent properties of all samples. In summary, all samples were granular-like nanoparticles and well crystallized with the same tetragonal phase as YVO₄. Under the irradiation at 980 nm, YVO₄:Yb³⁺,Er³⁺ phosphors can generate green emission at 525 and 553 nm and red emission at 657 nm, while YVO₄:Yb³⁺,Tm³⁺ phosphors can generate blue emission at 476 nm, red emission at 648 nm, and near-infrared emission at 800 nm. Notably, YVO₄:Yb³⁺,Er³⁺,Tm³⁺ samples can exhibit green emission, blue emission, red emission, and near-infrared emission at the same time, which might endow the as-prepared samples with potential applications in many fields, such as luminous paint, infrared detection, and biological label.     

Localized desvitrifiation in Er<Superscript>3+</Superscript>-doped strontium barium niobate glass by laser irradiation

Localized desvitrifiation in strontium barium niobate glass doped with Er³⁺ under laser irradiation has been carried out. The samples of this study have been fabricated by the melt quenching method and doped with 5% mol of Er³⁺. A 1.5-W cw Ar laser was focused on the sample to obtain desvitrifiation of the glass. Evidence of the changes induced by the Ar laser has been observed through the analysis of the photoluminescence of the Er³⁺ ions. The transitions corresponding to ²H_11/2→⁴I_15/2, ⁴S_3/2→⁴I_15/2 and ⁴F_9/2→⁴I_15/2 have been studied to analyze structure changes. Microluminescence measurements have been carried out to spatially select positions inside and outside the irradiated area. We have observed changes in the emission bands corresponding to these transitions. The emission bands from Er³⁺ ions in the irradiated zone show a resolved structure while they are broadened outside that area. These changes in the optical properties of the Er³⁺ ions indicate that the Ar-laser irradiation has produced a change in the local structure of the material. These results show that a localized desvitrifiation has been produced after the laser action and the transition from glass to glass ceramic has been completed.     

Optical character of Er/Yb co-doped P2O5-CaO-Na2O-Al2O3-AgO phosphate glass

The up-conversion (UC) and near infrared (NIR) luminescence of Er³⁺/Yb³⁺ co-doped phosphate glass are investigated. In the UC emission range, the 523 nm, 546 nm green emissions and the 659 nm red emission are observed. With the increasing pump power, the intensity ratios of I₅₂₃/I₆₅₉, I₅₄₆/I₆₅₉ and I₅₂₃/I₅₄₆ increase gradually. The phenomenon is reasonably interpreted by theoretical analysis based on steady state rate equations. The emission cross section of the infrared emission at 1546 nm is larger (about 6.7 × 10^− 21 cm²), which is suitable for making fiber amplifier.     

Ultraviolet and visible upconversion luminescence of Tm(0.1)Yb(5):FOV oxyfluoride nanophase vitroceramics

The ultraviolet upconversion luminescence of Tm³⁺ ions sensitized by Yb³⁺ ions in oxyfluoride nanophase vitroceramics when excited by a 975 nm diode laser was studied. An ultraviolet upconversion luminescence line positioned at 363.6 nm was found. It was attributed to the fluorescence transition of ¹D₂→³H₆ of Tm³⁺ ion. Several visible upconversion luminescence lines at 450.7 nm, (477.0 nm, 462.5 nm), 648.5 nm, (680.5 nm, 699.5 nm) and (777.2 nm, 800.7 nm) were also found, which result respectively from the fluorescence transitions of ¹D₂→³F₄, ¹G₄→³H₆, ¹G₄→³F₄, ³F₃→³H₆ and ³H₄→³H₆ of Tm³⁺ ion. The careful measurement and analysis of the variation of upconversion luminescence intensity F as a function of the 975 nm pumping laser power P prove that the upconversion luminescence of ¹D₂ state is partly a five-photon upconversion luminescence, and the upconversion luminescence of ¹G₄ state and ³H₄ state are respectively the three-photon and two-photon upconversion luminescence. The theoretical analysis suggested that the upconversion mechanism of the 363.6 nm ¹D₂→³H₆ upconversion luminescence is partly the cross energy transfer of {³H₄(Tm³⁺), ³F₄(Tm³⁺), ¹G₄(Tm³⁺)→¹D₂(Tm³⁺)} and {¹G₄(Tm³⁺)→³F₄(Tm³⁺), ³H₄(Tm³⁺)→¹D₂(Tm³⁺)} between Tm³⁺ ions. In addition, the upconversion luminescence of ¹G₄ and ³H₄ state results respectively from the sequential energy transfer {²F_5/2(Yb³⁺)→²F_7/2(Yb³⁺), ³H₄(Tm³⁺)→¹G₄(Tm³⁺)} and {²F_5/2(Yb³⁺) →²F_7/2(Yb³⁺), ³F₄(Tm³⁺)→³F₂(Tm³⁺)} from Yb³⁺ ions to Tm³⁺ ions. Supported by the National Natural Science Foundation of China (Grant No. 10674019)     

Er3+，Er3+/Yb3+掺杂氟化镧超微材料的光谱特性与上转换发光

采用共沉淀法制备了Er³⁺掺杂和Er³⁺/Yb³⁺共掺杂LaF₃超微材料,所制备的样品的颗粒呈球形,尺寸为250nm左右.计算得到Er³⁺单掺杂样品中对应着⁴S_3/2和⁴F_9/2能级的发光量子效率分别为67.0%和71.9%.研究发现,随着Yb³⁺离子浓度的增加 关键词： 3+')" href="#">Er³⁺ 3+')" href="#">Yb³⁺ 发光 能量传递     

Optical parameters of Nd3＋：Er3＋：yb3＋ co-doped borosilicate glasses and their energy transfers at high temperature

This paper reports that a series of Nd³⁺:Er³⁺:Yb³⁺ co-doped borosilicate glasses have been prepared and their absorption spectra measured. The J--O intensity parameters Ω_k (k=2, 4, 6), spontaneous radiative lifetime τ_rad, spontaneous transition probability A, fluorescence branching ratio β and oscillator strength f_ed of the Nd³⁺ ions at room temperature are calculated based on Judd--Ofelt (J--O) theory. The temperature dependence of the up-conversion photoluminescence characteristics in a Nd³⁺:Er³⁺:Yb³⁺ co-doped sample is studied under a 978 nm semiconductor laser excitation, and the energy transfer mechanisms among Yb³⁺, Er³⁺ and Nd³⁺ ions are analysed. The results show that the J--O intensity parameters Ω₂ increase when the Nd³⁺ concentration of the Nd³⁺:Er³⁺:Yb³⁺ co-doped borosilicate glasses increases. The possibility of spontaneous transition is small and lifetimes are long at levels of ⁴F_5/2 and ⁴F_3/2. The intensity of Nd³⁺ emissions at 595, 691, 753, 813 and 887 nm are markedly enhanced when the sample temperature exceeds 400 K. The reasons being the cooperation of the secondary sensitization from Er³⁺ to Nd³⁺ and the contribution of a multi-phonon.