Simple but efficient synthesis of novel substituted benzimidazoles over ZrO2-Al2O3

Solid-acid catalytic materials such as ZrO₂-Al₂O₃ containing 80?mol% of ZrO₂ were prepared by the solution combustion method (SCM) using different fuels such as urea, hexamethylene tetramine, glycine, and sucrose. All the prepared solid acid catalytic materials were characterized for their physico-chemical properties like crystalinity, acidity, functionality and morphology. These materials were evaluated for their catalytic activity in the synthesis of a series of novel substituted benzimidazoles. The reaction conditions were optimized by varying the solvents, reaction temperature, weight of solid acid catalyst, molar ratio of the reactants, and reaction time. The ZrO₂-Al₂O₃ solid acid catalytic material prepared by urea as a fuel was found to be highly active, recyclable, and reusable in the synthesis of benzimidazoles. A possible reaction mechanism for the synthesis of benzimidazoles is also proposed.     

TMSCl/Fe(NO3)3-Catalyzed Synthesis of 2-Arylbenzothiazoles and 2-Arylbenzimidazoles Under Ultrasonic Irradiation

A convenient one-pot cyclocondensation method for benzothiazole and benzimidazole syntheses is described. A set of benzothiazoles and benzimidazoles were readily prepared from aromatic ortho-diamines or ortho-aminothiophenol and aldehydes using chlorotrimethylsilane in dimethylformamide as promoter and water scavenger under ultrasonic irradiation in good yields (84–97%).     

One‐Pot Synthesis of Benzimidazoles from o‐Nitroanilines under Microwaves via a Reductive Cyclization

An efficient microwave irradiation synthesis of 2‐substituted benzimidazoles in one step via the Na₂S₂O₄ reduction of o‐nitroanilines in the presence of aldehydes is described. The method is simple and a good option to obtain the title compounds in a very short time.     

Thermal decomposition studies of the polyhedral oligomeric silsesquioxane, POSSh, and when it is impregnated with the metallocene bis(eta5-cyclopentadienyl)zirconium (IV) dichloride or immobilized on silica

Thermal decomposition studies of the free polyhedral oligomeric silsesquioxane, POSS(h), and when this compound has been impregnated with Cp(2)ZrCl(2) (Cp=eta(5)-C(5)H(5)) or immobilized on SiO(2) were conducted using infrared emission spectroscopy (IES) over a 100-1000 degrees C temperature range and by thermogravimetric analysis (TGA). The organic groups in POSS(h) apparently decompose thermally into Si-CH(3), Si-H and other fragments. Upon impregnation with Cp(2)ZrCl(2), however, a different thermal decomposition pathway was followed and new infrared emission bands appeared in the 1000-900cm(-1) region suggesting the formation of Si-O-Zr moieties. When immobilized on SiO(2) and subjected to thermal decomposition, the POSS(h) compound lost its organic groups and the inorganic structure remaining was incorporated into the SiO(2) framework.     

具有分级多孔结构和光催化性质的核-壳纳米球(HP-Fe2O3@TiO2)

通过溶剂热和溶胶-凝胶涂层法, 设计并制备了具有分级多孔结构和光催化性质的核-壳纳米球(HP-Fe₂O₃@TiO₂). 透射电子显微镜(TEM)照片证明所得HP-Fe₂O₃@TiO₂样品具备分级多孔结构, 这是因为HP-Fe₂O₃@TiO₂的内核-Fe₂O₃具有大孔空隙, 同时外壳-TiO₂具有介孔空隙. 此外, 通过X射线衍射(XRD)、扫描电子显微镜(SEM)、高分辨透射电子显微镜(HRTEM)、X射线光电子能谱(XPS)以及氮气吸附-脱附曲线深入研究了HP-Fe₂O₃@TiO₂的结构及其性质. 分别在可见及紫外光照下, 研究了样品在H₂O₂体系下的光催化降解亚甲基蓝(MB)的性质. 所观察到的HP-Fe₂O₃@TiO₂纳米球的光催化性能, 可归因于核-壳结构的协同作用, 这进一步表明, TiO₂外壳对α-Fe₂O₃的光催化活性有重要影响作用. 在可见光照射下, HP-Fe₂O₃@TiO₂ (1 mL Ti(OC₄H₉)₄ (TBT))具有较优异的光催化活性. 同时, HP-Fe₂O₃@TiO₂ (4mL TBT)具备优异的单分散形貌, 并在紫外光照射下, 表现出最优的光催化活性.     

复合碳纳米管增强纳米Ag2CO3的可见光催化活性和稳定性

在二甲基甲酰胺溶液中, 通过简单的沉淀法制备了纳米Ag₂CO₃和碳纳米管(CNT)的复合物. 用X射线衍射(XRD)、傅里叶变换红外(FTIR)光谱、扫描电镜(SEM)和紫外-可见(UV-Vis)漫反射光谱(DRS)表征了所制备的Ag₂CO₃/CNT复合物, 通过在可见光下降解甲基橙(MO)检测了样品的光催化活性. 结果表明, 纳米Ag₂CO₃颗粒与CNT结合良好. CNT的含量为1.5% (w)的Ag₂CO₃/1.5% CNT复合物活性最高, 经过60 min 的降解, 甲基橙的降解率达到93%. 与纯相纳米Ag₂CO₃比较, CNT的加入还提高了Ag₂CO₃的稳定性, 经过三次循环降解, Ag₂CO₃/1.5% CNT复合物还能降解81%的甲基橙, 而纳米Ag₂CO₃只能降解59.5%的甲基橙. 其活性和稳定性提高的原因是由于CNT的高导电性, 它不仅促进了电子-空穴对的分离, 还能快速转移产生的光生电子.     

An easy one-step photocatalytic synthesis of 1-aryl-2-alkylbenzimidazoles by platinum loaded TiO2 nanoparticles under UV and solar light

One-pot synthesis of disubstituted benzimidazoles from N-substituted 2-nitroanilines or 1,2-diamines with 3-12 nm-sized platinum particles loaded on the TiO₂ using solar and UV-A light is described. 1-Aryl-2-alkylbenzimidazoles from 2-nitrodiphenylamines are formed by combined redox photocatalytic reaction, condensation and catalytic dehydrogenation on Pt-TiO₂. In case of diamines, this reaction is proceeded by Pt-TiO₂ assisted photocatalytic oxidation of an alcohol and a catalytic dehydrogenation of the intermediate on the surface of platinum nanoparticles. In both cases product formation was achieved by tandem photocatalytic and catalytic reactions on Pt-TiO₂.     

(Cl2AlNH2)n和(H2AlNH2)n(n=1～5)簇结构及其热力学性质

用HF自洽场理论和密度泛函理论(DFT)的B3LYP方法,在6 31G水平上研究了低聚物(Cl2AlNH2)n和(H2AlNH2)n(n=1～5)簇的几何构型、电子结构和聚合反应热力学性质,比较了两个系列化合物中化学键的强度.结果表明,Cl2AlNH2和H2AlNH2分子为C2 (EC)平面型结构,其中Al－N为由一个σ键和一个键组成的双键.(Cl2AlNH2)n和(H2AlNH2)n(n=1～5)分子为Dnh对称,Al－N是典型的σ单键 .低聚物(Cl2AlNH2)n和(H2AlNH2)n的稳定性顺序分别为: 3 > 2 > 4> 5 > 1和8 > 7 > 9 > 11 > 6.     

CO2在Na2Cr2O7溶液中的平衡溶解度模型

为研究重铬酸钠(Na₂Cr₂O₇)对CO₂溶解的影响, 本文在带有搅拌的气液相高压平衡釜内, 采用静态法测定了温度在313.2-333.2 K, 压力在0.1-1.9 MPa 范围内, 重铬酸钠浓度分别为0、0.361、0.650、0.901 mol·kg^-1 时, CO₂ 在Na₂Cr₂O₇溶液中的溶解度. 结果表明: (1) Na₂Cr₂O₇对CO₂ 的溶解有盐析效应; (2) CO₂ 在Na₂Cr₂O₇溶液中的溶解符合亨利定律, 并且CO₂溶解度是温度和Na₂Cr₂O₇浓度的函数, 且用改进的Setschenow方程和Peng-Robinson-Pitzer (PR-Pitzer)方程拟合了在此温度、压力及重铬酸钠浓度范围内的实验数据, 拟合效果较好, 并且其平均相对误差分别为4.24%和3.32%.     

Thermal decomposition of Me3SnO2PCl2, Me2Sn(O2PCl2)2 and Ph3SnO2PCl2

TG and DTA studies on Me₃SnO₂PCl₂, Me₂Sn(O₂PCl₂)₂ and Ph₃SnO₂PCl₂ were carried out under dynamic argon atmosphere. The results show that the decomposition proceeds in different stages leading to the formation of Sn₃(PO₄)₂ as a stable product. This compound was characterized by IR spectroscopy. Decomposition schemes involving reductive elimination reactions were proposed.     

Characterization of Cu-ZnO-Cr2O3/SiO2 catalysts and application to dehydrogenation of 2-butanol to 2-butanone

The Cu-ZnO-Cr₂O₃/SiO₂ catalysts were prepared by impregnation method, which exhibited high activity for the dehydrogenation of 2-butanol to 2-butanone. These catalysts were characterized by means of XRD, EPR and BET. The experimental results indicated that (i) the valence states of copper play a key role, (ii) groups of copper atoms were the main active sites in this reaction, and (iii) copper oxide would lead to the condensation product of 5-methyl-3-heptanone.     

PbCu3(OH)(NO3)(SeO3)3·1/2H2O und Pb2Cu3O2(NO3)2(SeO3)2: Synthese und Kristallstrukturuntersuchung

Crystals of PbCu₃(OH)(NO₃)(SeO₃)₃·1/2H₂O [a=7.761(3)Å,b=9.478(4)Å,c=9.514(4)Å, =66.94(2)°, =69.83(2)°, =81.83(2)°, space group P ,Z=2] and Pb₂Cu₃O₂(NO₃)₂(SeO₃)₂ [a=5.884(2)Å,b=12.186(3)Å,c=19.371(4)Å, space group Cmc2₁,Z=4] were synthesized under hydrothermal conditions. Their crystal structures were refined with three-dimensional X-ray data toR _w=0.033 resp. 0.055. In PbCu₃(OH)(NO₃)(SeO₃)₃·1/2H₂O the Cu atoms are [4+1] and [4+2] coordinated and via SeO₃ groups a three-dimensional atomic arrangement is built up. In Pb₂Cu₃O₂(NO₃)₂(SeO₃)₂ there are sheets, which are connected only via Pb-O bonds ranging from 2.98 Å to 3.16 Å.

     

ZnO/In2O3复合空心球的制备及其光电催化葡萄糖降解性能

通过葡萄糖协助的水热以及随后的退火处理两步法成功制备了系列ZnO/In₂O₃复合空心球. X射线衍射谱(XRD)表明, 经500 ℃退火制得的ZnO/In₂O₃复合空心球中ZnO以非晶态存在, 但是随着退火温度的提高, 其逐渐转变为纤锌矿结构. 场发射扫描电子显微镜(FE-SEM)和透射显微镜(TEM)结果表明, ZnO/In₂O₃复合材料具有空心球结构, 复合纳米颗粒之间结合紧密. 将ZnO/In₂O₃复合空心球组装成薄膜光电极, 研究了其光电催化降解葡萄糖的性能. 结果表明, 700 ℃退火处理的ZnO/In₂O₃复合空心球薄膜电极可产生最高的光致电流密度. 通过光致发光光谱(PL)发现, 与ZnO或In₂O₃空心球相比, ZnO/In₂O₃复合空心球的发光强度猝灭效果明显. 这是由于复合材料中晶界处产生的p-n结电场, 降低了光生电子-空穴对的复合几率, 从而使更多的光生电子可迁移到电极表面.     

MgH2+20%(w)MgTiO3复合材料的吸/放氢性能

为了降低MgH₂的吸放氢温度, 提高其吸放氢动力学性能, 本文通过球磨方法制备了MgH₂+20%(w)MgTiO₃复合储氢材料, 并研究了其储氢性能. X射线衍射(XRD)结果表明, MgTiO₃在与MgH₂球磨过程中生成Mg₂TiO₄和TiO₂, 并且Mg₂TiO₄和TiO₂在体系的吸放氢过程中保持稳定, 能够对MgH₂的吸放氢过程产生催化作用. 程序升温脱附和吸/放氢动力学测试结果表明, 添加MgTiO₃后MgH₂的初始放氢温度从389 ℃降至249 ℃.150 ℃下的吸氢量从0.977%(w)提高到2.902%(w), 350 ℃下的放氢量从2.319%(w)提高到3.653%(w). 同时, MgH₂放氢反应的活化能从116 kJ·mol^-1降至95.7 kJ·mol^-1. 与MgH₂相比, MgH₂+20%(w) MgTiO₃复合材料的热力学与动力学性能均有显著提高, 这主要是由于球磨和放氢过程中原位生成的TiO₂和Mg₂TiO₄具有良好的催化活性.     

TiO2柱撑海泡石负载Ni2P的噻吩加氢脱硫性能

以氢氧化镍为镍源, 亚磷酸为磷源, TiO₂柱撑海泡石(Ti-Sep)为载体, 采用浸渍法制备了含磷化镍前驱体的样品, 然后采用程序升温还原法制备了Ni质量分数(w)为5%-25%的Ni₂P/Ti-Sep催化剂, 并考察了其噻吩加氢脱硫性能. 采用X射线衍射(XRD)、N₂吸附-脱附、热重分析(TGA)、透射电子显微镜(TEM)和傅里叶变换红外(FTIR)光谱对催化剂样品进行了表征. 结果表明, 海泡石经TiO₂柱撑之后层间距增大, 比表面积和孔容都明显变大, 热稳定性增强, 活性组分Ni₂P能很好地分散在海泡石层间及表面, 并且没有破坏海泡石的层状结构. 上述原因导致Ni₂P/Ti-Sep催化剂的噻吩加氢脱硫活性明显优于Ni₂P/Na-Sep(NaCl改性海泡石)和Ni₂P/HCl-Sep(HCl改性海泡石)催化剂. 当Ni负载量为15% (w)时, Ni₂P/Ti-Sep催化剂具有最好的噻吩加氢脱硫性能; 在反应温度为400℃时, 噻吩转化率达100%.     

Preparation of ZrO2-TiO2-CeO2 and Its Application in the Selective Catalytic Reduction of NO with NH3

TiO₂,ZrO₂-TiO₂,andZrO₂-TiO₂-CeO₂ were prepared by co-precipitation method and characterized by X-ray diffraction (XRD), specific surface area measurements (BET), temperature programmed desorption (NH₃-TPD), oxygen storage capacity (OSC), and temperature programmed reduction (H₂-TPR). The results showed that ZrO₂-TiO₂-CeO₂ exhibited large number of surface strong acid, possessed some oxygen storage capacity, and strong redox property. The three materials were used as supports and the monolith catalysts were prepared with 1% (w) V₂O₅ and 9% (w)WO₃ for selective catalytic reduction (SCR) of NO with ammonia in the presence of excessive O₂, and the results of catalytic activity showed that the catalyst used ZrO₂-TiO₂-CeO₂ as support yielded nearly 100% NO conversion at 275 °C at a gas hourly space velocity (GHSV) of 10000 h⁻¹, and it had the best catalytic activity and showed great potential for practical application.     

纳米Ag@SiO2核壳结构的表面等离子体共振效应对铕配合物的荧光增强作用

分别制备了二氧化硅壳层厚度为10、25和80 nm的三种Ag@SiO₂纳米粒子, 合成了铕与不同比例苯甲酸根(BA)的配合物、铕与1, 10-邻菲罗啉(phen)及2, 2''-联吡啶(bpy)的配合物, 并对其进行表征. 表征结果推测配合物的组成为Eu(BA)_nCl_3-n·2H₂O (n=1, 2, 3)、Eu(phen)Cl₃·2H₂O和Eu(bpy)Cl₃·2H₂O. 配合物的荧光光谱显示, 在加入Ag@SiO₂纳米粒子后, 复合物的荧光强度有不同程度的增加, 这可能是由于表面等离子体共振造成的. 不同硅壳厚度的Ag@SiO₂纳米粒子的荧光增强顺序是25 nm>80 nm>10 nm, 这表明二氧化硅核壳厚度约25 nm时有较强的表面等离子体共振效应. 此外, 在这些复合物中, Eu(phen)Cl₃·2H₂O复合物的增强效果是最强的, 而Eu(BA)_nCl_3-n·2H₂O的增强效果是最弱的. 在三个苯甲酸铕配合物中, Eu(BA)₃·2H₂O的增强效果最弱, 其他两个苯甲酸铕复合物增强效果相对较好. 原因可能是含氮配合物(Eu(phen)Cl₃·2H₂O和Eu(bpy)Cl₃·2H₂O)可以和Ag@SiO₂更好地成键, 而苯甲酸铕配合物和Ag@SiO₂纳米粒子的作用相对较弱. Ag@SiO₂纳米粒子有望应用于增强稀土材料的发光.     

Characterization and reactivity of γ-Al_2O_3 supported Pd–Ni bimetallic nanocatalysts for selective hydrogenation of cyclopentadiene

Several g-Al2O3 supported Pd–Ni bimetallic nanocatalysts(Pd–Ni(x:y)/Al2O3; where x and y represent the mass ratio of Pd and Ni, respectively) were prepared by the impregnation method and used for selective hydrogenation of cyclopentadiene to cyclopentene. The Pd–Ni/Al2O3 samples were confirmed to generate Pd–Ni bimetallic nanoparticles by X-ray diffraction(XRD), X-ray photoelectron spectroscopy(XPS) and transmission electron microscopy(TEM). The catalytic activity was assessed in view of the effects of different mass ratios of Pd and Ni, temperature, pressure, etc. Among all the samples, the Pd–Ni(1:1)/Al2O3(PN-1:1) catalyst showed extremely high catalytic ability. The conversion of cyclopentadiene and selectivity for cyclopentene can be simultaneously more than 90%.     

Crystal structure of Li2Cu3(SeO3)2(SeO4)2

Summary Single crystal X-ray data of the hydrothermally grown new phase Li₂Cu₃(SeO₃)₂(SeO₄)₂ were measured with a four-circle diffractometer up to sin /=0.81 Å^–1 [I2/a,Z=4,V=1175.5 ų,a=16.293(6),b=5.007(2),c=14.448(6) Å, = 94.21(1)°]. The structure was determined by direct and Fourier methods and refined toR=0.034,R _w =0.027 for 2 086 independent reflections.Cu(1)^[4+1]O₅ forms a tetragonal pyramid, Cu(2)^{[4 + 2]}O₆ is a strongly elongated octahedron. The Li atom is surrounded by four O atoms forming a distorted tetrahedron. Se(IV)O₃ and Se(VI)O₄ groups are in accordance to literature, mean Se-O bond lengths are 1.714 and 1.644 Å.

---

Die Kristallstruktur von Li₂Cu₃(SeO₃)₂(SeO₄)₂

Zusammenfassung Einkristall-Röntgendaten der hydrothermal gezüchteten neuen Phase Li₂Cu₃(SeO₃)₂(SeO₄)₂ wurden mit einem Vierkreisdiffraktometer im Bereich bis zu sin /=0.81 Å^–1 gemessen [I2/a,Z=4,V=1175.5 ų,a=16.293(6),b=5.007(2),c=14.448(6) Å, =94.21(1)°]. Die Kristallstruktur wurde mittels direkter und Fourier-Methoden bestimmt und für 2 086 unabhängige Reflexe zuR=0.034,R _w =0.027 verfeinert.Cu(1)^[4+1]O₅ bildet eine tetragonale Pyramide, Cu(2)^[4+2]O₆ ist ein stark verlängertes Oktaeder. Das Li-Atom ist von vier O-Atomen in Gestalt eines verzerrten Tetraeders umgeben. Die Se(IV)O₃-und Se(VI)O₄-Gruppen entsprechen der Literatur, die mittleren Se-O-Abstände betragen 1.714 und 1.644 Å.

     

FeCl3-Doped Polyaniline Nanoparticles as Reusable Heterogeneous Catalyst for the Synthesis of 2-Substituted Benzimidazoles

FeCl₃-doped polyaniline nanoparticles efficiently catalyze the synthesis of 2-substituted benzimidazoles by the reaction of aldehydes with o-phenylenediamine. Synthesis and characterization of the catalyst are described, and the obtained results confirms good dispersion of the FeCl₃ on the polyaniline. Simple workup, mild reaction conditions, low cost, easy separation, and reusability of the catalyst are some advantages of this method.