Combined theoretical and FTIR spectroscopic studies on hydrogen adsorption on the zeolites Na-FER and K-FER

The interaction between molecular hydrogen and the alkali-metal-exchanged zeolites Na-FER and K-FER at a low temperature was investigated by combining variable-temperature infrared spectroscopy and theoretical calculations by using a periodic DFT model. The experimentally determined values of standard adsorption enthalpy, DeltaH degrees , were -6.0 (+/-0.8) and -3.5 (+/-0.8) kJ mol(-1) for Na-FER and K-FER, respectively. These results were found to be in agreement with corresponding DeltaH degrees values obtained from calculations on the periodic model. Two types of alkali-metal cation sites in FER were found: channel intersection sites and channel wall sites. Calculations showed a similar interaction energy for both site types, and similar structures of adsorption complexes. Up to two dihydrogen molecules can be physisorbed on the alkali-metal cation located on the intersection of two channels, while only one H2 molecule is physisorbed on the cation at the channel wall site. The adsorption enthalpies of H2 on alkali-metal-exchanged FER are significantly smaller than those found previously for the MFI-type zeolites Na-ZSM-5 and K-ZSM-5, which is likely due to a difference in the alkali-metal cation coordination in the two zeolite frameworks.     

硅沸石完美骨架上的吸附Ⅱ.乙胺、正戊烷、乙醇在 FAU型沸石上的吸附热

用测定吸附等温线法研究乙胺、正戊烷和乙醇在疏水高硅FAU沸石上的吸附热效应。根据Clapeyron-Clausius方程,处理吸附等温线,得到不同覆盖度C(C=被吸附分子数/晶胞)的等量吸附热Qst(C)(一定覆盖度C时由Clapeyron-Clausius方程计算的吸附热)及平均等量吸附热Qst^*(一定温度区间里等量吸附热Qst的平均值),以及Qst^*与沸点蒸发热△Hv的差值△H1(定义为相互作用强度△H1=Qst^*-△Hv)。所研究的三种有机分子的△H1的次序为△H1(乙胺)>△H1(正戊烷)>>△H1(乙醇)。这与AT值(定义为脱附温度Td与吸附质的沸点温度Tb的差值,无需单位)有正相关关系。由AT值观察到的高硅FAU沸石Si-O骨架与被吸附乙胺之间可能存在的强相互作用、为本研究测定的热力学定量数据△H1值所证明。     

Vibrational and thermodynamic properties of Ar, N2, O2, H2 and CO adsorbed and condensed into (H,Na)-Y zeolite cages as studied by variable temperature IR spectroscopy

The adsorption of Ar, H2, O2, N2 and CO on (H,Na)-Y zeolite (Si/Al = 2.9, H+/Na+ approximately 5) has been studied at variable-temperature (90-20 K) and sub-atmospheric pressure (0-40 mbar) by FTIR spectroscopy. Unprecedented filling conditions of the zeolite cavities were attained, which allowed the investigation of very weakly adsorbed species and of condensed, liquid-like or solid-like, phases. Two pressure regimes were singled out, characterized by: (i) specific interaction at low pressure of the probe molecules (P) with the internal Br?nsted and Lewis sites, and (ii) multilayer adsorption at higher pressure. In the case of CO the perturbation of the protonic sites located inside the sodalite cages was also observed. As the molecule is too large to penetrate the sodalite cage, the perturbation is thought to involve a proton jump tunneling mechanism. The adsorption energy for the (HF)OH...P (P = Ar, H2, O2, N2 and CO) specific interaction involving the high frequency Br?nsted acid sites exposed in the supercages was derived following the VTIR (variable temperature infrared spectroscopy) method described by E. Garrone and C. Otero Areán (Chem. Soc. Rev., 2005, 34, 846).     

Adsorption of lanthanides on mordenite from nitrate medium

The adsorption of lanthanides (except for Pm) on mordenite was investigated under various solution conditions of nitrate ion concentrations ([NO*3]: 0.001-2 mol/dm3) and total lanthanide concentrations (0.0005 mol/dm3). Solutions of lanthanide nitrates were equilibrated with zeolite samples at 296 K. A concave tetrad effect was evident in the change of logK d values within the lanthanide series and an explanation by a comparison of covalence in Ln-O bonds existing in triple bond Al-O(1/3Ln)-Si species found in the zeolite phase and in Ln(H2O)3+x or Ln(NO3) n-3 n complexes formed in the aqueous phase is presented. The decreasing trend in C1 and C3 coefficients, which are the function of E1 and E3 Racah f-interelectron repulsion parameters, is evidence of the magnification of covalence in Ln-O bond in the series triple bond S-iO(1/3Ln)-Al triple bond 相似文献   

Equilibrium study of selected divalent d-electron metals adsorption on A-type zeolite

The objective of the presented study was to investigate the adsorption of Cu, Co, Mn, Zn, Cd and Mn on A-type zeolite. The isotherms for adsorption of metals from their nitrates were registered. The following adsorption constants K of metals were found: 162,890, 124,260, 69,025, 16,035, 10,254, and 151 [M(-1)] for Cu, Co, Mn, Zn, Cd, and Ni, respectively, for the concentration range 10(-4)-10(-3) M. On the other hand, the investigation of pH influence on the distribution constants of metals showed that the adsorption of metals proceeds essentially through an ion-exchange process, surface hydrolysis, and surface complexation. The supplementary results from DRIFT, scanning electron microscopy, and X-ray diffraction methods confirmed the presumption about the possible connection between the electronic structure of divalent ions and their adsorption behavior, showing that ions with d5 and d10 configurations such as Mn2+, Zn2+, Cd2+, with much weaker hydrolytic properties than Cu2+ and Ni2+, strongly interact with the zeolite framework and therefore their affinity to the zeolite phase is much stronger when compared with that of the Ni2+ ion, but at the same time not as strong as the affinity of the Cu2+ ion, the latter forming a new phase during the interaction with zeolite framework. For Zn2+, during inspection of the correlation between the proton concentration H/Al and zinc concentration Zn/Al on the zeolite surface, the formation of the surface complex [triple bond]S-OZn(OH) was proposed. A correlation between the heterogeneity of proton concentrations H/Al on Me-zeolite surfaces and the hydrolysis constants pKh of Me2+ ions was found.     

Hydrogen storage in low silica type X zeolites

Low silica type X zeolites (LSX, Si/Al = 1) fully exchanged by alkali-metal cations (Li(+), Na(+), and K(+)) were studied for their hydrogen storage capacities. Hydrogen adsorption isotherms were measured separately at 77 K and <1 atm, and at 298 K and <10 MPa. It was found that the hydrogen adsorption capacity of LSX zeolite depended strongly on the cationic radius and the density of the cations that are located on the exposed sites. The interaction energies between H(2) and the cations follow the order Li(+) > Na(+) > K(+), as predicted based on the ionic radii. Oxygen anions on zeolite framework were minor adsorption sites. Li-LSX had an H(2) capacity of 1.5 wt % at 77 K and 1 atm, and a capacity of 0.6 wt % at 298 K and 10 MPa, among the highest of known sorbents. The hydrogen capacity in LSX zeolite by bridged hydrogen spillover was also investigated. A simple and effective technique was employed to build carbon bridges between the H(2) dissociation catalyst and the zeolite to facilitate spillover of hydrogen atoms. Thus, the hydrogen storage capacity of Li-LSX zeolite was enhanced to 1.6 wt % (by a factor of 2.6) at 298 K and 10 MPa. This is by far the highest hydrogen storage capacity obtained on a zeolite material at room temperature. Furthermore, the adsorption rates were fast, and the storages were shown to be fully reversible and rechargeable. Further optimization of the bridge building technique would lead to an additional enhancement of hydrogen storage.     

Thermodynamics of hydrogen adsorption on the zeolite Li-ZSM-5

Thermodynamic characterisation of the adsorption process (at a low temperature) of dihydrogen on the zeolite Li-ZSM-5 was carried out by means of variable-temperature infrared spectroscopy, with the simultaneous measurement of temperature and equilibrium pressure. Adsorption renders the H–H stretching mode infrared active, at 4092 cm⁻¹. The standard adsorption enthalpy and entropy resulted to be ΔH⁰=−6.5(±0.5) kJmol⁻¹ and ΔS⁰=−90(±5) Jmol⁻¹ K⁻¹, respectively. The adsorption enthalpy is significantly larger than the liquefaction heat, and this fact renders Li-ZSM-5 a potential cryoadsorbent for hydrogen storage.     

CXN天然沸石的研究2: 吸附性质

采用N~2,NH~3,CO~2,乙烯,丙烯,水,甲醇,乙醇,丙醇等作为吸附剂,研究了由我国CXN天然沸石改性制得的H-STI和Na-STI沸石的吸附性质,H-STI和Na-STI沸石的BET表面积及微孔孔体积约为420m^2/g和0.20m^3/g。根据NH~3和CO~2在H-STI沸石上的吸附等温线计算得到它们的吸附热分别为44.8和26.5kJ/mol。乙烯,丙烯,甲醇,乙醇,丙醇等在Na-STI沸石上的吸附等温线表明该沸石对有机分子的吸附具有链长选择性。在低分压下水相对于甲醇的吸附量表明沸石具有一定的疏水性质。     

Surface photochemistry of Rh(CO)2 on zeolite Y-production of a stable coordinatively unsaturated rhodium monocarbonyl surface species at room temperature

The photochemical production and chemical reactivity of a new coordinatively unsaturated rhodium monocarbonyl species on the surface of dealuminated zeolite Y over a temperature range of 300-420 K and a pressure range from 10(-5) to 20 Torr has been studied. Using high vacuum techniques and transmission infrared spectroscopy, ultraviolet irradiation (350 +/- 50 nm) of supported Rh(CO)(2) surface species led to the production of stable, but reactive, =Rh(CO) surface species, characterized by an infrared band at 2023 cm(-1). The coordinatively unsaturated =Rh(CO) species convert to less reactive and coordinatively saturated Rh(CO) by thermal treatment above 370 K. The Rh(CO) species were characterized by an infrared band at 2013 cm(-1). An explanation of the mode of bonding of the rhodium monocarbonyl species to the zeolite surface is provided. Coordinatively unsaturated =Rh(CO) species captured N(2), H(2), and O(2) gas molecules near room temperature to produce a variety of mixed ligand rhodium surface complexes of the form Rh(CO)(N(2)), Rh(CO)(H(2)), Rh(CO)(H)(2), Rh(CO)(H), Rh(CO)(O), and Rh(O). Infrared band assignments for the new species are provided. The work provides new insight into the photochemical behavior of Rh(CO)(2) species supported on high-area zeolite materials and may improve our understanding of the role of active rhodium monocarbonyl species in the development of heterogeneous photocatalysts.     

FER型沸石的合成、结构与吸附性质

在TMEDA(四甲基乙基二胺)-Na2O-SiO2-Al2O3-H2O体系(I),Na2O-K2O-Al2O3-SiO2-H2O-HCO3^--CO3^2^-体系(II)及Py(吡啶)-PrNH2(正丙胺)-HF-SiO2-H2O体系(III)中, 分别合成了纯相FER沸石及FER硅沸石。用粉末XRD, FT-IR, 29Si MAS NMR及TG/DTA等表征其结构性质, 并用超微量电子真空吸附天平测定这些沸石样品对正己烷, 甲醇和水的吸附等温线。结果表明: 各体系合成的样品虽然结晶度高, 呈现出FER沸石的典型结构特征, 但由于它们的组成和晶格微结构不同, 热稳定性与吸附性质有明显的差异。在(I)体系中合成的FER沸石层错缺陷少, 晶格完美, 正己烷与甲醇的吸附量可达到理论值, 结构破坏温度为1190℃。红外精细谱及29Si MAS NMR高分辨谱证明FER硅沸石具有十分完美的骨架结构。由于晶胞收缩, 它对正己烷与甲醇吸附量略低于理论值, 并呈现出高度的疏水性。它的结构破坏温度高于1300℃。在(II)体系中合成的FER型沸石结构缺陷多, 沸石孔中的钾离子不易被质子完全交换。它的正己烷与甲醇吸附量均较低, 而水的吸附量相对较高。吸附现象表明, 正己烷和甲醇都被吸附于FER沸石的十元环主孔道中, 分压较高时, 甲醇可通过八元环进入小笼, 而水的吸附性质则主要与各样品的Si-OH缺陷及骨架中的阳离子含量有关。     

Adsorption of nitrogen, oxygen, and argon in cobalt(II)-exchanged zeolite X

Adsorption of nitrogen, oxygen, and argon on cobalt(II)-exchanged zeolite X at 288.2 and 303.0 K was studied. The nitrogen and oxygen adsorption capacities increase upon cobalt ion exchange up to 71%, beyond which it shows a decreasing trend because of the partial degradation of the zeolite structure during the cation exchange and high-temperature vacuum dehydration processes. The magnitude of the increase in the adsorption capacities for nitrogen is much higher than that of oxygen. The nitrogen/oxygen as well as nitrogen/argon selectivities in the low-pressure region increase with an increase in cobalt exchange. Marginal oxygen selectivity over argon is observed for zeolite samples with higher cobalt exchange. The heats of adsorption values for nitrogen and oxygen increase and that for argon remain unaffected by cobalt exchange in zeolite X. The very high nitrogen adsorption capacity, selectivity, and heat of adsorption in the low-pressure region for cobalt-exchanged zeolite X compared to the parent sodium form of the zeolite show stronger interaction between nitrogen molecules with the extraframework cobalt cations of the zeolite. This stronger interaction has been explained in terms of the pi-complexation between nitrogen molecules and cobalt cations of the zeolites, as confirmed by diffuse reflectance infrared Fourier transform spectroscopy, wherein the N[triple bond]N stretching frequency at 2099 cm(-1) is observed for N2 molecules adsorbed in NaCoX.     

Formation of M2+(O2)(C3H8) species in alkaline-earth-exchanged Y zeolite during propane selective oxidation

The adsorption of oxygen and d2-propane (CH3CD2CH3) on a series of alkaline-earth-exchanged Y zeolite at room temperature was studied with in situ infrared spectroscopy. Surprisingly at room temperature, oxygen adsorption led to the formation of supercage M2+(O2) species. Further, at low propane coverage, propane was found to adsorb linearly on Mg2+ cations, but a ring-adsorption structure was observed for propane adsorbing on Ca2+, Sr2+, and Ba2+ cations. It is demonstrated that O2 and propane can simultaneously attach to one active center (M2+) to form a M2+(O2)(C3H8) species, which is proposed to be the precursor in thermal propane selective oxidation. Selectivity to acetone in the propane oxidation reaction decreases with increasing temperature and cation size due to the formation of 2-propanol and carboxylate ions. An extended reaction scheme for the selective oxidation of propane over alkaline earth exchanged Y zeolites is proposed.     

Effects of adsorbate molecules on the quadrupolar interaction of framework aluminum atoms in dehydrated zeolite H,Na-Y

The effect of adsorbate molecules on the quadrupolar interaction of framework aluminum atoms with the electric field gradient in dehydrated zeolite H,Na-Y has been studied by (27)Al MAS NMR and (27)Al MQMAS NMR spectroscopy at magnetic fields of 9.4 and 17.6 T. Upon adsorption of molecules interacting with bridging OH groups by hydrogen bonds (acetonitrile and acetone), the quadrupole coupling constant of framework aluminum atoms was found to decrease from 16.0 MHz (unloaded zeolite) to 9.4 MHz. Adsorption of molecules, which cause a proton transfer from the zeolite framework to the adsorbates (ammonia and pyridine), reduces the quadrupole coupling constant to 3.8 MHz for coverages of 0.5-2 molecules per bridging OH group. The experiments indicate that the quadrupole coupling constant of framework aluminum atoms in dehydrated zeolite H,Na-Y reflects the chemical state of adsorbate complexes formed at bridging OH groups. In agreement with earlier investigations it was found that a proton affinity of the adsorbate molecules of PA = 812-854 kJ/mol is necessary to induce a proton transfer from the zeolite framework to the adsorbed compounds. This proton transfer is accompanied by a strong improvement of the tetrahedral symmetry of zeolitic framework AlO(4) tetrahedra and a decrease of the electric field gradient.     

Adsorption of CO and O2 on W2C(0001)

CO, O(2), and H(2) adsorption on a clean W(2)C(0001)√13×√13 R ± 13.9° reconstructed surface at room temperature (RT) were investigated using high-resolution electron energy loss spectroscopy (HREELS). The W(2)C(0001) adsorbs CO molecularly and adsorbs O(2) dissociatively, but does not adsorb H(2) at RT. In the CO adsorption system, two C-O stretching (antisymmetric CCO stretching) modes were found at 242.3 meV (1954 cm(-1)) and at 253.0 meV (2041 cm(-1)). The low-frequency site is occupied at first with subsequent conversion to the high-frequency site with increasing coverage. Additionally, a small peak was apparent at 104.5 meV (843 cm(-1)), and a middle peak at 50-51 meV (400-410 cm(-1)), which are assignable to a symmetric stretching mode and a hindered translational mode, respectively, of a CCO (ketenylidene) species. These observations are consistent with the CO adsorption model on top of the surface carbon. For oxygen adsorption, two adsorption states were found at 65.2-68.1 meV (526-549 cm(-1)) and 73.6 meV (594 cm(-1)): typical frequencies to oxygen adsorption on metal surfaces. Results suggest that atomic oxygen adsorption occurred on a threefold hollow site of the second W layer.     

Hydrogen chemisorption on gallium oxide polymorphs

The chemisorption of H(2) over a set of gallia polymorphs (alpha-, beta-, and gamma-Ga(2)O(3)) has been studied by temperature-programmed adsorption equilibrium and desorption (TPA and TPD, respectively) experiments, using in situ transmission infrared spectroscopy. Upon heating the gallium oxides above 500 K in 101.3 kPa of H(2), two overlapped infrared signals developed. The 2003- and 1980-cm(-1) bands were assigned to the stretching frequencies of H bonded to coordinatively unsaturated (cus) gallium cations in tetrahedral and octahedral positions [nu(Ga(t)-H) and nu(Ga(o)-H), respectively]. Irrespective to the gallium cation geometrical environment, (i) a linear relationship between the integrated intensity of the whole nu(Ga-H) infrared band versus the Brunauer-Emmett-Teller surface area of the gallia was found and (ii) TPA and TPD results revealed that molecular hydrogen is dissociatively chemisorbed on any bulk gallium oxide polymorph following two reaction pathways. An endothermal, homolytic dissociation occurs over surface cus-gallium sites at T > 450 K, giving rise to Ga-H(I) bonds. The heat and entropy of this type I hydrogen adsorption were determined by the Langmuir's adsorption model as Deltah(I) = 155 +/- 25 kJ mol(-1) and Deltas(I) = 0.27 +/- 0.11 kJ mol(-1) K(-1). In addition, another exothermic, heterolytic adsorption sets in already in the low-temperature region. This type of hydrogen chemisorption involves surface Ga-O-Ga species, originating GaO-H and Ga-H(II) bonds which can only be removed from the gallia surface after heating under evacuation at T > 650 K. The measured desorption energy of this last, second-order process was equal to 77 +/- 10 kJ mol(-1). The potential of the H(2) chemisorption as a tool to measure or estimate the specific surface area of gallia and to discern the nature and proportion of gallium cation coordination sites on the surface of bulk gallium oxides is also analyzed.     

Remarkable effect of the preparation technique on the state of cobalt ions in BEA zeolites evidenced by FTIR spectroscopy of adsorbed CO and NO, TPR and XRD

The state of cobalt in two BEA zeolites was studied by XRD, TPR, and FTIR spectroscopy using CO and NO as probe molecules. One of the samples, CoAlBEA (0.4 wt % of Co), was prepared by conventional ion exchange and the other, CoSiBEA (0.7 wt % Co), by a two-step postsynthesis method involving dealuminated SiBEA zeolite. The introduction of Co into SiBEA leads to an increase of unit cell parameters of the BEA structure and to the consumption of silanol groups in vacant T-sites of the dealuminated zeolite. In contrast, no structural changes are observed after incorporation of cobalt into AlBEA by ion-exchange. The reduction temperature of cobalt in CoSiBEA zeolite (1130 K), is much higher than for CoAlBEA and indicates a strong interaction of cobalt ions with SiBEA. Low-temperature CO adsorption on CoAlBEA results in (i) H-bonded CO, (ii) Co(3+)-CO adducts (2,208 cm(-1)) and (iii) a small amount of Co(2+)-CO complexes (2,188 cm(-1)). In agreement with these results, NO adsorption leads to the appearance of (i) NO(+) (2,133 cm(-1), formed with the participation of the zeolite acidic hydroxyls), (ii) Co(3+)-NO (1932 cm(-1)), and (iii) a small amount of Co(2+)(NO)(2) dinitrosyls (nu(s) = 1,898 and nu(as) = 1,814 cm(-1)). Low-temperature CO adsorption on CoSiBEA leads to formation of two kinds of Co(2+)-CO adducts (2,185 and 2,178 cm(-1)). No Co(3+) cations are detected. In line with these results, adsorption of NO reveals the existence of two kinds of Co(2+)(NO)(2) dinitrosyls (nu(s) = 1,888 and nu(as) = 1,808 cm(-1) and nu(s) = 1,878 and nu(as) = 1,799 cm(-1), respectively).     

Effects of toluene on thiophene adsorption over NaY and Ce(IV)Y zeolites

Zeolites NaY and Ce(IV)Y were employed as adsorbents to remove organic sulfur compounds from model gasoline(MG) solutions with and without toluene in static adsorption experiments at room temperature(RT) and atmospheric pressure.The adsorbents were characterized by XRD,XRF and pyridine infrared spectrum(IR).The adsorption experiments show that the desulfurization performance of Ce(IV)Y is much better than that of NaY.The sulfur removal over both NaY and Ce(IV)Y decreases with the increase of toluene concentration in MG,however,the decline tendency on Ce(IV)Y is smooth,and it is steep on NaY.FT-IR spectra of thiophene adsorption indicate that thiophene molecules are mainly adsorbed on NaY via π electron interaction,but on Ce(IV)Y,in addition to the π electron interaction,both Ce4+-S direct interaction and protonation of thiophene also play important roles.Toluene molecules are adsorbed on NaY also via π electron interaction.Although the amount of Brnsted acid sites is increased due to the introduction of Ce4+ ions into NaY zeolite,it is not found to influence the adsorption mode of toluene over Ce(IV)Y.Compared with NaY zeolite,the improved desulfurization performance over Ce(IV)Y for removing organic sulfur compounds from MG solution,especially those containing large amount of aromatics,may be ascribed to the direct Ce(IV)-S interaction,which is much resistant to the influence resulted from toluene adsorption.     

Spectroscopic and Kinetic Studies of the Reaction of CO+H(2)O and CO+O(2) and Decomposition of HCOOH on Au/H-Mordenite Catalysts

The surface species formed from the reaction of CO+H(2)O and CO+O(2) and decomposition of HCOOH on Au incorporated into H-mordenite zeolite have been studied by means of in situ FTIR spectroscopy. On H-mordenite, a bidentate formate species (2912, 1536, and 1390 cm(-1)) is produced upon exposure to the CO+H(2)O gas mixture at 323 K, as well as different carbonate-like species (1956, 1852, 1705, and 1360 cm(-1)). The latter species was extensively formed in a short time and was responsible for hindering the CO(2) adsorbed species. However, Au/H-mordenite presented different vibration modes of formate species with a high emphasis on the monodentate ones (2950, 2916, 2896, 1690, and 1340 cm(-1)). The HCOOH adsorption on Au/H-mordenite showed two bands at 1622 and 1590 cm(-1) of the nu(as)(OCO) species, suggesting the formation of two types of formate species. The decomposition rate of the formate species formed on Au moieties was faster than that formed on H-mordenite. This was consistent with the calculated activation energies of CO(2) formation that showed a lower value (40.1 kJ/mol) on the former sample than on the latter one (63.3 kJ/mol). A dehydrogenation mechanism is proposed (HCOOH-->H(2)+CO(2)) for the decomposition of HCOOH on the Au/H-mordenite catalyst. On the other hand, the Au/H-mordenite catalyst activated the CO oxidation reaction. This reaction proceeded mainly through the formation of carboxylate species at first, which tended to obviate with time, preferring the formate species. The latter species resulted from the interaction of CO with OH stretching of the zeolite assisted by the presence of gas phase O(2). The formate species is further decomposed with time to carbonate species. Copyright 2000 Academic Press.     

氢在沸石上的吸附行为

应用基于Ono-Kondo格子理论得到的通用吸附等温方程, 通过分析氢在不同温度下, 在沸石NaX、CaA、NaA和ZSM-5上的吸附数据, 确定了氢的最大单层吸附容量. 并引入维里吸附方程, 由第二维里吸附系数和圆柱孔的Lennard-Jones(12-6)势模型计算了氢与沸石微孔壁面的作用势. 结果表明, 通用吸附等温方程可较好地描述氢在沸石上的超临界吸附行为, 拟合所得的氢在沸石上的最大单层吸附容量与吸附剂相关, 而与吸附温度无关. 圆柱孔作用势模型计算所得的氢分子在沸石上的吸附作用势与吸附热相近. 氢分子间的作用力表现为吸引力.     

The leading role of association in framework modification of highly siliceous zeolites with adsorbed methylamine.

Affinity index (AT value), adsorption heat, X-ray diffraction (XRD), and 13C and 29Si magic-angle spinning (MAS) NMR, FTIR, and Raman spectroscopies were used to study the interaction of highly siliceous MFI-, FAU-, and FER-type zeolites with adsorbed methylamine (MA). Compared with the data for methanol, the much higher AT values and adsorption heats, and significant changes in XRD patterns, 29Si MAS NMR spectra, and FTIR spectra for the zeolites after adsorption of MA, revealed a strong hydrogen-bonding interaction between the perfect framework of the zeolites and the adsorbed MAs. This interaction results from the fact that the H atom of the amine group attacks the [Si-O] framework to form a Si-OHN bond, which leads to the appearance of Si-N bonds in the zeolites at 323 K. Therefore, the zeolite framework can be modified with MA under mild conditions. The highly siliceous MFI zeolite and the H-ZSM-5 zeolite with SiO2/Al2O3=31:1 were modified with MA and investigated by temperature-programmed desorption of CO2. The modified zeolites exhibited greatly enhanced basic properties in comparison with those of the raw materials. The influence of defects in the zeolite on the adsorption and the interaction with MA is discussed.