Comparative study of graphene aerogels synthesized using sol−gel method by reducing graphene oxide suspension

A graphene oxide aerogel synthesized from graphene oxide hydrogel and graphene aerogels have been synthesized using the sol?gel method by reducing a suspension of graphene oxide with various reducing agents: a mixture of hypophosphorous acid and iodine, L-ascorbic acid, sodium metabisulfite, and by hydrothermal treatment. The obtained aerogels have been studied by scanning electron microscopy, IR spectroscopy, Raman spectroscopy, X-ray powder diffraction, and X-ray photoelectron spectroscopy. Comparative studies of graphene aerogels have shown that their properties, namely density, specific surface area, reduction degree, surface morphology, defectiveness of graphene sheets, interlayer spacing, average sizes of coherent scattering regions, number of layers, and crystallite size in the basal plane in graphene crystallites depend on the method of synthesis.     

The Impact of SF<Subscript>6</Subscript> Plasma on the Properties of Graphene Oxide

The paper considers the effect of SF₆ plasma-chemical treatment on the processes of defect formation and the electrical properties of graphene oxide partially reduced by heat treatment. The fluorine content on the graphene oxide surface is shown to increase as a result of SF₆ plasma treatment, depending on the plasma power and the duration of the treatment. The measured electrical parameters testify increased resistance of graphene oxide films as a result of plasma treatment. The rate of resistance change depends on the thickness of the films and is minimal for thin structures (～10 nm). Further heating of graphene oxide decreases its resistance, but the content of surface fluorine changes insignificantly. Thin films (10-15 nm) exhibit the smallest change of their resistance as a result of annealing. The highest rate of resistance change is observed for non-fluorinated samples. The obtained data indicate that only several nanometers of nearsurface layers are subject to SF₆ plasma fluorination. The results testify the possibility of using SF₆ plasma treatment as an effective tool for selective fluorination of graphene oxide surface layers and controlled modification of its properties without changing the bulk properties of the material.     

Highly Concentrated Aqueous Dispersions of Graphene Exfoliated by Sodium Taurodeoxycholate: Dispersion Behavior and Potential Application as a Catalyst Support for the Oxygen‐Reduction Reaction

A high‐yielding exfoliation of graphene at high concentrations in aqueous solutions is critical for both fundamental study and future applications. Herein, we demonstrate the formation of stable aqueous dispersions of pristine graphene by using the surfactant sodium taurodeoxycholate under tip sonication at concentrations of up to 7.1 mg mL^?1. TEM showed that about 8 % of the graphene flakes consisted of monolayers and 82 % of the flakes consisted of less than five layers. The dispersions were stable regardless of freezing (?20 °C) or heat treatment (80 °C) for 24 h. The concentration could be significantly improved to about 12 mg mL^?1 by vacuum‐evaporation of the dispersions at ambient temperature. The as‐prepared graphene dispersions were readily cast into conductive films and were also processed to prepare Pt/graphene nanocomposites that were used as highly active electrocatalysts for the oxygen‐reduction reaction.     

Freestanding sulfonated graphene oxide paper: a new polymer electrolyte for polymer electrolyte fuel cells

Sulfonated graphene oxide paper was fabricated by vacuum filtration of a colloidal solution of sulfonated graphite oxide. Layer by layer assembly of graphene oxide nano sheets interconnects the conduction paths and therefore sulfonated graphene oxide exhibits good proton conductivity and fuel cell performance.     

Ultrafast room-temperature reduction of graphene oxide by sodium borohydride,sodium molybdate and hydrochloric acid

Since graphene-based materials have shown great potential in many fields,it is important to explore ultrafast and high-efficient methods to synthesize reduced graphene oxide(rGO) using inexpensive reducing agents under mild conditions.Here,we reported a novel method for the ultrafast chemical reduction of graphene oxide(GO) at room temperature using sodium borohydride(NaBH₄),sodium molybdate(Na₂MoO₄) and hydrochloric acid(HCl).The reduction was carried out within 2 min.A series of characterization results revealed that the obtained reduced graphene oxide has higher reduction degree than that synthesized by NaBH₄ alone at high temperature.Moreover,rGO electrode based on the present reducing method exhibited a superior specific capacitance of 139.8 F/g at a current density of1 A/g,indicating that it can be used as electrode materials for supercapacitors.     

Experimental study on thermo-physical and rheological properties of stable and green reduced graphene oxide nanofluids: Hydrothermal assisted technique

In this study a dehydration hydrothermal technique has been used to introduce a simple, environmentally friendly and facile method for manufacturing highly dispersed reduced graphene oxide for improving the thermo-physical and rheological properties of heat transfer liquids. The hydrothermal reduction of graphene oxide was verified by various characterizations methods such as UV–visible absorption spectroscopy, Zeta potential, Raman spectroscopy, X-ray photoemission spectroscopy, X-ray diffraction, Fourier transform infrared spectroscopy, and transmission electron microscopy. A thorough investigation was conducted on the thermo-physical properties of reduced graphene oxide at concentrations of 0.02, 0.04, 0.06, and 0.08?wt% under different temperatures. Significant improvements in electrical and thermal conductivity were obtained by adding a small amount of hydrothermal-assisted reduced graphene oxide (h-rGO) in the suspension. The viscosity and density remained relatively unchanged with the increase of concentrations where the pH was maintained within the desirable value, despite the fact that no additive was used during the reduction process. It is noteworthy to highlight that the h-rGO aqueous suspensions have shown Newtonian behavior. Results indicated that the h-rGO could be employed as a promising additive for conventional heat transfer liquids for different thermal applications.     

Fe2O3/rGO纳米复合物的制备及其储锂和储钠性能

金属氧化物可通过电化学转换反应与锂离子及钠离子发生多电子可逆结构转换,是一类极具应用前景的高容量锂离子和钠离子电池负极材料。实验以氧化石墨烯和铁盐为前驱体,采用简单的溶剂法,成功将Fe₂O₃纳米单晶粒子均匀负载于石墨烯的导电片层上,获得Fe₂O₃/rGO(还原氧化石墨烯)纳米复合材料。复合电极在锂离子和钠离子电池中都表现出优异的充放电性能和循环稳定性。实验结果表明石墨烯的包覆不仅能降低Fe₂O₃发生转换反应的电荷传递阻抗,而且能够稳定电极在循环过程中带来的结构转变,极大改善电极大电流充放能力和循环稳定性。本研究为发展高容量的锂离子和钠离子电池负极材料提供了可行的途径。     

Changes in the composition and properties of graphene oxide films under monochromatic vacuum UV radiation

The photolysis of a graphene oxide film by monochromatic vacuum UV radiation with a wavelength of 123.6 nm has been studied. It has been shown that photoreduction as a result of the detachment of the C?O polar groups is also accompanied by an increase in the conductivity, wettability, and surface energy of the graphene oxide film.     

改进液相氧化还原法制备高性能氢气吸附用石墨烯

以液相氧化还原法为基础,并在分散剂十二烷基苯磺酸钠(SDBS)作用下制备得到高质量石墨烯,有效避免了在此过程中石墨烯大量团聚的现象.采用X射线衍射(XRD)、拉曼光谱(RS)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)和原子力显微镜(AFM)等分析手段对石墨烯样品进行了表征.XRD结果体现了石墨、氧化石墨和石墨烯晶型结构的区别;SEM和TEM结果显示石墨烯呈网格状,表面平整,缺陷少;AFM分析表明样品中单层石墨烯厚度约为1.3 nm,同时也存在少许双层结构.BET测试法得到石墨烯的比表面积高达1206 m2·g-1,考察了石墨烯在高压条件下对H2的吸附性能.通过对方法改进前后所制备的石墨烯样品进行比较,结果表明,十二烷基苯磺酸钠的加入有效地减小了石墨烯的大量团聚,且得到了高质量的石墨烯.在25和55℃条件下,高质量石墨烯对氢气的吸附量分别达到1.7％(w)和1.1％(w),比之前研究结果有了很大提高.     

Electrically conductive nanocomposites with segregated structure based on poly(vinylidene fluoride-<Emphasis Type="Italic">co</Emphasis>-tetrafluoroethylene) and reduced graphene oxide

An approach was described to obtaining polymer composites with segregated structure that have high electrical conductivity at low concentrations of an electrically conductive filler. According to this approach, thin layers of electrically nonconductive nanodispersed graphene oxide are applied to the surface of polymer particles and conduction is produced by heat and chemical treatments. Hot pressing of the modified powder leads to combination of layers of the graphene-like filler to form a single electrically conductive network. For the first time, reduction of graphene oxide on the surface of polymer particles with hydrazine vapor at room temperature was performed. Comparison of the electrical conductivities of composites obtained by the thermal and chemical methods of graphene oxide reduction showed that the chemical reduction method gives composites with higher conductivities than the thermal method does. The maximum conductivity (0.5 S/m) was reached in a composite containing 0.6% chemically reduced graphene oxide.     

Bio‐inspired method to fabricate poly‐dopamine/reduced graphene oxide composite membranes for dyes and heavy metal ion removal

Due to the narrow layer spacing, graphene oxide (GO) composite membrane usually exhibits a relatively low water flux in the process of wastewater treatment. In this study, GO was reduced to reduced graphene oxide through a bio‐inspired method, which was functionalized modified by poly‐dopamine (PDA). Then a series of PDA/reduced graphene oxide sheet films were prepared by vacuum filtration on the surface of cellulose acetate membrane (under the pressure of −0.1 MPa). The result indicated that the novel membranes had an excellent stability owing to the cross‐link of PDA. In addition, the hydrophilicity of membrane was increased significantly after PDA modification, which presented a superior water flux than pure GO composite membrane. More importantly, as‐prepared membranes were successfully applied for the removal of dyes (including Congo red, methylene blue, and rhodamine B) and heavy mental ion (Cu(II)) from simulated wastewater. This work might provide a new method for preparation and application of GO composite membranes.     

Brodie's or Hummers’ Method: Oxidation Conditions Determine the Structure of Graphene Oxide

Synthesis and studies of graphite oxide started more than 150 years ago and turned into a boom by the measurements of the outstanding physical properties of graphene. A series of preparation protocols emanated trying to optimize the synthesis of graphene oxide in order to obtain a less defective material, as source for graphene. However, over-oxidation of the carbon framework hampered establishing structure-property relationships. Here, the fact that two different synthetic methods for graphene oxide preparation lead to very similar types of graphene oxide with a preserved graphene lattice is demonstrated. Either sodium chlorate in nitric acid (similar to Brodie's method) or potassium permanganate in sulfuric acid (similar to Hummers’ method) treatment are possible; however, reaction conditions must be controlled. With a preserved carbon lattice analytical differences between the samples relate to the altered on-plane functionality. Consequently, terming preparation protocols “according to Brodie's/Hummers’ method” is not sufficient.     

膨胀石墨层间生长高活性氧化锌及其光催化性能

以醋酸锌和膨胀石墨为原料, 采用真空辅助压力诱导手段使反应溶液注入膨胀石墨层间, 在180℃下溶剂热反应12 h, 一步得到氧化锌纳米棒/石墨烯复合光催化剂, 采用X射线衍射仪(XRD)和透射电子显微镜(TEM)等对复合光催化剂的结构和形貌进行了表征. 结果表明, 合成的氧化锌纳米棒具有六方晶系纤锌矿结构; 氧化锌纳米棒在石墨烯表面分散性较好, 其平均直径约50 nm, 长度约150~200 nm. 所得氧化锌纳米棒/石墨烯复合材料对亚甲基蓝的降解效率优于目前应用最广泛的光催化剂Degussa P25.     

Adsorption of carbon dioxide on graphene oxide supported layered double oxides

Adsorption of CO₂ on layered double oxides supported on graphene oxide has been studied under dry and wet conditions. In the first exposure to the adsorptive gas, the isotherms obtained for supported and unsupported materials are shown to fit to the Freundlich model indicating the existence of heterogeneous adsorption sites. After multiple temperature-swing cycles, the adsorption capacity decreased and the data is better described by the Langmuir model. The presence of graphene oxide is shown to reduce the loss of adsorption capacity, and helps to maintain the heterogeneity of the basic sites on the adsorbents. The use of wet gas mixtures was found to have a positive effect on the CO₂ adsorption capacity of the graphene oxide hybrids. The presence of residual sodium on the materials resulted in a Freundlich isotherm with increased adsorption capacity.     

Effect of exfoliation temperature on carbon dioxide capture of graphene nanoplates

Thermally exfoliated graphene nanoplates were found to be a novel high efficiency sorbent for the capture of CO(2). The exfoliated graphene nanoplates were expanded successfully from graphite oxide by a low-heat treatment at temperatures ranging from 150 to 400°C under vacuum conditions. The texture was analyzed by N(2) full isotherms and XRD. The CO(2) capture characteristics of the graphene nanoplates at 25°C and 30bar were examined using a pressure-composition-temperature apparatus. The inter-layer spacing of the graphene layers and pore structure on the CO(2) capture capacities were studied as a function of the processing conditions. The prepared graphene nanoplates exhibited high capture capacities, up to 248wt.%, at 25°C and 30bar. The improved CO(2) capture capacity of the graphene nanoplates was attributed to the larger inter-layer spacing and higher interior void volume.     

氧化石墨烯-海藻酸钠-壳聚糖复合支架的制备及表征

通过冷冻干燥技术, 将不同量的氧化石墨烯与海藻酸钠和壳聚糖复合, 构建复合支架材料. 研究了不同的氧化石墨烯含量(质量分数0, 0.3%, 0.5%, 0.7%, 1%)对支架材料微观结构、 孔隙率、 溶胀比、 体外降解性能、 机械性能及生物相容性的影响, 以确定复合支架中最佳氧化石墨烯含量. 研究结果表明, 复合材料呈固态海绵状结构, 具有一定的形态可塑性; 扫描电子显微镜观察发现, 各组支架均为三维网状结构, 随着氧化石墨烯含量的增加, 孔隙尺寸逐渐降低, 孔壁厚度增加, 孔隙尺寸在140~240 μm之间; 随氧化石墨烯含量的增加, 复合支架溶胀比和体外降解速率逐渐降低, 而机械强度明显增强; 体外细胞毒性显示, 当氧化石墨烯质量分数为0.3%时, 细胞存活率最高, 而当氧化石墨烯含量增高时, 细胞活性会被明显抑制, 造成细胞死亡. 因此, 氧化石墨烯在复合支架中最佳含量为0.3%.     

Dispersion of graphene oxide and its flame retardancy effect on epoxy nanocomposites

Graphene oxide was prepared by ultrasonication of completely oxidized graphite and used to improve the flame retardancy of epoxy.The epoxy/graphene oxide nanocomposite was studied in terms of exfoliation/dispersion,thermal stability and flame retardancy.X-ray diffraction and transmission electron microscopy confirmed the exfoliation of the graphene oxide nanosheets in epoxy matrix.Cone calorimeter measurements showed that the time to ignition of the epoxy/graphene oxide nanocomposite was longer than that of neat epoxy.The heat release rate curve of the nanocomposite was broadened compared to that of neat epoxy and the peak heat release rate decreased as well.     

Study of tin dioxide–sodium stannate composite obtained by decomposition of peroxostannate as a potential anode material for lithium-ion batteries

A tin dioxide–sodium stannate composite has been obtained by the thermal treatment of sodium peroxostannate nanoparticles at 500°C in air. X-ray powder diffraction study has revealed that the composite includes crystalline phases of cassiterite SnO₂, sodium stannate Na₂Sn₂O₅, and sodium hexahydroxostannate Na₂Sn(OH)₆. Scanning electron microscopy has shown that material morphology does not change considerably as compared with the initial tin peroxo compound. Electrochemical characteristics have been compared for the anodes of lithium-ion batteries based on tin dioxide–sodium stannate composite and anodes based on a material manufactured by the thermal treatment of graphene oxide–tin dioxide–sodium stannate composite at 500°C in air.     

Studies of the vibronic interaction between Eu3+ ions and glass-forming units in oxide glasses

Vibronic spectra involving intramolecular vibrations of glass-forming units have been measured for the f–f transitions of Eu³⁺ ions doped into sodium germanate and sodium silicate glasses. It is shown, from the analysis of relative intensities of these spectra, that the interaction of the Eu³⁺ ion with the vibrations of the surrounding forming units of oxide glasses is well described by the electric multipole–multipole interaction.     

Free‐standing and Flexible MoS2/rGO Paper Electrode for Amperometric Detection of Folic Acid

The development of flexible electrodes is of considerable current interest because of the increasing demand for modern electronics, portable medical products, and compact devices. We report a new type of flexible electrochemical sensor fabricated by integrating graphene and MoS₂ nanosheets. A highly flexible and free‐standing conductive MoS₂ nanosheets/reduced graphene oxide (MoS₂/rGO) paper was prepared by a two‐step process: vacuum filtration and chemical reduction treatment. The MoS₂/graphene oxide (MoS₂/GO) paper obtained by a simple filtration method was transformed into MoS₂/rGO paper after a chemical reduction process. The obtained MoS₂/rGO paper was characterized by scanning electron microscopy, X‐ray diffraction spectroscopy, X‐ray photoelectron spectroscopy, Raman spectroscopy, electrochemical impedance spectroscopy. The electrochemical behavior of folic acid (FA) on MoS₂/rGO paper electrode was investigated by cyclic voltammetry and amperometry. Electrochemical experiments indicated that flexible MoS₂/rGO composite paper electrode exhibited excellent electrocatalytic activity toward the FA, which can be attributed to excellent electrical conductivity and high specific surface area of the MoS₂/rGO paper. The resulting biosensor showed highly sensitive amperometric response to FA with a wide linear range.