Electronic structure of CuClxBr1 − x,CuClxI1 − xand CuBrxI1 − xalloys

In this work, the electronic structure and disorder effects in copper halides alloys are studied by means of the full potential linearized augmented plane wave (FLAPW) method. The calculated bowing parameter shows that the main contribution is due to the relaxation effects, though the charge transfer remains relatively significant, while the volume deformation contribution is negligible. The total bowing is found to be small in the three studied alloys. Results agree well with experimental and available theoretical works.     

Impedance spectroscopy and piezoresponse force microscopy analysis of lead-free (1 − x) K0.5Na0.5NbO3 − xLiNbO3 ceramics

(1 ? x) K_0.5Na_0.5NbO₃ ? xLiNbO₃ (where x = 0.0, 5.0, 5.5, 6.0, and 6.5 wt.%) (KNLN) perovskite structured ferroelectric ceramics were prepared by the solid-state reaction method. X-ray diffraction patterns indicate that single phase was formed for pure KNN while a small amount of second phase (K₆Li₄Nb₁₀O₃₀, ～3%) was present in LN doped KNN ceramics. Phase analysis indicated the change in the crystal structure from orthorhombic to tetragonal with increase in LN content. The electrical behavior of the ceramics was studied by impedance spectroscopy technique in the high temperature range. Impedance analysis was performed using an equivalent circuit model. The impedance response in pure KNN and KNLN ceramics could be deconvoluted into two contributions, associated with the bulk (grains) and the grain boundaries. Activation energies for conductivity were found to be strongly frequency dependent. The activation energy obtained from dielectric relaxation data was attributed to oxygen vacancies. From PFM we found that the composition with 6.5 wt.% LN displays stronger piezocontrast as compared to pure KNN implying an evidence of a pronounced piezoelectric coefficient.     

Phase transitions and dielectric properties of (1 − x)KNbO3 − xK0.5Bi0.5TiO3 ceramics synthesized by a stirred hydrothermal process

Dielectric ceramic materials (1 − x) KNbO₃ − xK_0.5Bi_0.5TiO₃ (0 ≤ x ≤ 0.3) have been successfully synthesized via a stirred (dynamic) hydrothermal method. The microstructure, relative density and dielectric properties were studied as a function of KBT doping. The structure of the solid solutions changed from orthorhombic (x = 0; 0.05) to tetragonal (x = 0.1; x = 0.3) at room temperature. The morphotropic phase limit was obtained at x = 0.075 where we have noted the coexistence of the orthorhombic and tetragonal structures. The mean value of the measured dielectric permittivity ε_r was 700 and dielectric loss tanδ was about 0.06 at room temperature. The dielectric properties of the studied ceramics, from 80 to 450 K, depend not only on their microstructure but also on their relative density. A relaxation behavior was observed for the tanδ curves at temperature below 150 K. The activation energy (E_a) of this phenomenon increases from 0.15 to 0.34 eV with the increase of KBT amount. The conductivity σ_ac remains constant at about 10⁻⁶ S m⁻¹.     

Improving La0.6Sr0.4Co0.2Fe0.8O3 − δ cathode performance by infiltration of a Sm0.5Sr0.5CoO3 − δ coating

La_xSr_1 ? xCo_yFe_1 ? yO_3 ? δ (LSCF) represents one of the state-of-the-art cathode materials for solid oxide fuel cells (SOFCs) due primarily to its high ionic and electronic conductivity. In this study, a one-step infiltration process has been developed to deposit, on the surface of a porous LSCF cathode, a thin film (50–100 nm) of Sm_0.5Sr_0.5CoO_3 ? δ (SSC), which is catalytically more active for oxygen reduction. Electrochemical impedance spectroscopy reveals that the SSC coating has dramatically reduced the polarization resistance of the cathode, achieving area-specific resistances of 0.036 Ω cm² and 0.688 Ω cm² at 750 °C and 550 °C, respectively. It has also maintained the stability of LSCF cathodes. In particular, the peak power densities are increased by ~ 22% upon the infiltration of SSC onto the porous LSCF cathodes of our best performing cells. These results demonstrate that a conductive backbone (e.g., LSCF) coated with a catalytic film (e.g., SSC) is an attractive approach to achieving an active and stable SOFC cathode for low-temperature solid oxide fuel cells.     

Modification of B-site doping of perovskite LaxSr1 − xFe1 − y−zCoyCrzO3 − δ oxide by Mg2+ ion

Co-doping B-site of perovskite oxide La_xSr_1 ? xCo_yFe_1 ? yO_3 ? δ (LSCFO) with Cr⁶⁺ and Mg²⁺ ions has been attempted in this research for revamping chemical stability and oxygen ionic conductivity of this mixed conducting oxide. It is known that partial substitution for B-site cations of LSCFO by Cr gives rise to a significant improvement on chemical and thermal stability of the perovskite oxide. On the basis of this doped structure, introduction of an immaterial dose of Mg²⁺ ion into its B-site results in a microstructure consisting of smaller grains with higher density than its precursor. Furthermore, the resulting perovskite oxide La_0.19Sr_0.8Fe_0.69Co_0.1Cr_0.2 Mg_0.01O_3 ? δ (LSFCCMO) displays higher O^2? conductivity than the solely Cr-doped LSCFO besides the improved chemical stability against reduction in 5% CH₄/He stream at 850 °C. A detailed examination of the oxidation states of B-site transition metal ions by XPS has also been conducted as a part of structural characterizations of LSFCCMO. The assessment of relative O^2? conductivity shows that the grain boundary area plays a more important role than the bulk phase in facilitating ion transport, but with comparable boundary areas the higher densification level is favorable.     

Effect of Eu dopant concentration in SrCe1 − xEuxO3 − δ on ambipolar conductivity

The europium dopant concentration in strontium cerate was studied to achieve maximum hydrogen permeation. In order to determine high ambipolar conductivity, total conductivity and open circuit potential measurements were performed. Among the three different compositions of Eu-doped SrCe_1 ? xEu_xO_3 ? δ (x = 0.1, 0.15 and 0.2) studied, SrCe_0.9Eu_0.1O_3 ? δ showed highest total conductivity between 600 °C and 900 °C. However, transference number measurements showed increasing electronic conductivity with increasing dopant concentration and a stronger temperature dependence for electronic conduction. Therefore, the highest ambipolar conductivity was obtained over the compositional range from SrCe_0.85Eu_0.15O_3 ? δ to SrCe_0.8Eu_0.2O_3 ? δ depending on temperature. Finally, the hydrogen permeation flux was calculated based on the ambipolar conductivity and compared with experimental results.     

On the superconductivity and structural properties of YBa2Cu3 − xCdxO7 − y

A series of superconducting cuprates with the nominal composition YBa₂Cu_3 − xCd_xO_7 − yand the effect of Cd substitution on Cu sites in this compound is presented. X-ray powder diffraction patterns for these cadmium cuprates with reduced diamagnetism indicate an orthorhombic unit cell like-perovskite structure for (0 ≤ x ≤ 0.15), while for higher Cd concentration, i.e.x = 1.0 the material is polyphasic. The observed superconducting transition temperature of the samples is nearly the same ([formula] K), except for (x = 1.0) whereT_cdrops to 72 K and a transition from metallic to semiconducting behavior of the normal state of the resistivity is observed. Such a decrease inT_cfor higher Cd concentration could be attributed to the presence of the green phase in this composition.     

Ferroelectric relaxor properties of (1 − x)K0.5Na0.5NbO3–xBa0.5Ca0.5TiO3 ceramics

The Ba_0.5Ca_0.5TiO₃ (BCT) composition dependent dielectric and structural properties of (1?x)K_0.5Na_0.5NbO₃–xBa_0.5Ca_0.5TiO₃ powders were investigated. Room temperature x-ray diffraction revealed the powder structure to transform from orthorhombic to cubic with increasing BCT composition. The frequency dependent dielectric constant measurements revealed a shift in the temperature of the maximum dielectric constant for at frequencies, suggesting that the system exhibits ferroelectric relaxor behavior. The system containing 15% BCT showed the closest calculated Curie–Weiss exponent to 2, which the exponent for a relaxor ferroelectric.     

Excitonic magnetic polaron dynamics of MBE grown CdTe/Cd1 − xMnxTe,Cd1 − xMnxTe/Cd1 − vMgyTe single quantum wells in magneti fields

Excitonic lifetimes in Cd_1 − xMn_Ue2Te, Cd_1 − xMg_xTe epilayers and CdTe/Cd_1 − xMn_xTe, Cd_1 − xMn_xTe/Cd_1 − vMg_yTe single quantum wells with different well widths and Mn, Mg compositions are investigated. The excitonic lifetimes are found to reduce drastically by applying external magnetic fields to samples with giant Zeeman splittings. The observed phenomenon is interpreted in terms of the PL decay time contribution from the long-life dark excitons which can convert to excitons for recombinations by a spin-flip process. We attribute the lifetime reduction to the depletion of dark excitons due to their crossing over the exciton energies for dipole allowed transitions in magnetic fields.     

SrTiO3(100) − √5 × √5 − R26.6 surface observed by high-resolution scanning tunneling microscopy

SrTiO₃(100) – (√5 × √5) – R26.6 surfaces were studied by means of high-resolution scanning tunneling microscopy (STM) under ultrahigh vacuum conditions. By varying the bias voltage in the occupied state, it was possible to observe the arrangement of titanium and oxygen atoms in the unit cells of a (√5 × √5) surface superstructure, which revealed that the TiO₂ layer is the terminating plane of the (√5 × √5) surface. In the STM images, peculiar protrusions were seen at the oxygen fourfold hollow site responsible for √5 × √5 periodicity. The protrusions are asymmetrical in contrast, which would be an important consideration in proposing accurate structural models for (√5 × √5) surface superstructures.     

High-temperature compressive creep behaviour of the perovskite-type oxide Ba0.5Sr0.5Co0.8Fe0.2O3 − δ

Compressive creep tests have been performed on perovskite-type Ba_0.5Sr_0.5Co_0.8Fe_0.2O_3 ? δ ceramics. The activation energy, stress exponent and inverse grain size exponent of the steady-state creep rates are evaluated at p(O₂) = 0.21 ? 10⁵ Pa and 0.01 ? 10⁵ Pa in the stress, temperature and grain size ranges 5–20 MPa, 1078–1208 K and 2.5–17.4 µm, respectively. The results indicate that the creep rate of Ba_0.5Sr_0.5Co_0.8Fe_0.2O_3 ? δ is controlled by diffusion of cations via both the oxide lattice (bulk diffusion) and along grain boundaries. The creep rate of Ba_0.5Sr_0.5Co_0.8Fe_0.2O_3 ? δ increases profoundly by more than one order of magnitude at 1153–1178 K, which is tentatively linked with the onset of the hexagonal-to-cubic phase transition in this compound.     

Hole superconductivity in Nd2 − zCezCuO4

The reclassification of Nd_2 − zCe_zCuO₄from an electron superconductor to a hole superconductor is suggested by simple valence and electrostatics arguments: In Nd_2 − zCe_zCuO₄, isolated Ce substituting for Nd is not an electron donor; the proposed actual dopant is a defect-complex of Ce and interstitial oxygen which provides holes, making Nd_2 − zCe_zCuO₄a hole superconductor.     

Oxygen nonstoichiometry and defect equilibrium in La2 − xSrxNiO4 + δ

Nonstoichiometric variation of oxygen content in La_2 ? xSr_xNiO_4 + δ (x = 0, 0.1, 0.2, 0.3, 0.4) and decomposition P(O₂) were determined by means of high temperature gravimetry and coulometric titration. The measurements were carried out in the temperature range between 873 and 1173 K and the P(O₂) range between 10^? 20 and 1 bar. La_2 ? xSr_xNiO_4 + δ showed the oxygen excess and the oxygen deficient compositions depending on P(O₂), temperature, and the Sr content. The value of partial molar enthalpy of oxygen approaches zero as δ increases in the oxygen excess region, which indicate that the interstitial oxygen formation reaction is suppressed as δ increase. The relationship between δ and logP(O₂) were analyzed by two types of defect equilibrium models. One is a localized electron model, and the other is a delocalized electron model. Both models can well explain the oxygen nonstoichiometry of La_2 ? xSr_xNiO_4 + δ with a regular solution approximation.     

Predictions of the bonding properties inCd1 − xZnxTe

The electronic, optical and elastic properties of the ternary II–VI semiconductor alloys Cd_1 − x Zn _xTe are calculated by thesp³s ^*  semi-empirical tight-binding theory and the bond-orbital model. We found a nonlinear decrease of the transverse effective charge and refractive index and a nonlinear increase of the bandgap and elastic constants with increasing Zn composition x. For all these behaviours, the corresponding bowing factors are predicted. The results are compared with previous theoretical estimates and experiments.     

The effect of compositional disorder on electronic band structure in GaxIn1 − xAsySb1 − yalloys lattice matched to GaSb

A pseudopotential formalism coupled with the virtual crystal approximation are applied to study the effect of compositional disorder upon electronic band structure of cubic Ga_xIn_1 − xAs_ySb_1 − yquarternary alloys lattice matched to GaSb. The effects of compositional variations are properly included in the calculations. Our theoretical results show that the compositional disorder plays an important role in the determination of the energy band structure of Ga_xIn_1 − xAs_ySb_1 − y/GaSb and that the bowing parameter is dominated by the group V-anion-based sublattice. Moreover, the absorption at the fundamental optical gaps is found to be direct within a whole range of the x composition.     

Coverage dependence of glycine adsorption on the Ge(100) − 2 × 1 surface

A combination of infrared spectroscopy, X-ray photoelectron spectroscopy and density functional theory has been used to investigate the adsorption behavior of glycine at the Ge(100) ? 2 × 1 surface under ultrahigh vacuum conditions. Comparison of experimental and simulated IR spectra indicates that at 310 K, glycine adsorbs on Ge(100) ? 2 × 1 via O–H dissociation, with some fraction of the products also forming an N dative bond to a neighboring germanium atom. O–Ge dative bonding is not observed. As coverage increases, the surface concentration of the monodentate O–H dissociated adduct increases, while that of the N dative-bonded species appears constant. XPS data support and clarify the IR findings and reveal new insights, including the presence at higher coverage of a minor product that has undergone dual O–H and N–H dissociation. These findings are supported by the calculated energy diagrams, which indicate that the reaction of a glycine molecule on the Ge(100) ? 2 × 1 surface via O–H dissociation and interdimer N dative bonding is both kinetically and thermodynamically favorable and that N–H dissociation of this adduct is feasible at room temperature given incomplete thermal accommodation along the reaction pathway.     

Pressure and compositional dependence of electric conductivity in the (Mg1 − xFex)1 − δO (x = 0.01–0.40) solid-solution

(Mg_1 ? xFe_x)_1 ? δO (x = 0.01–0.43) single crystals (~ 8 mm in diameter) were made by a melt-growth method. Electrical conductivity measurements were carried out as functions of temperature and frequency by a complex impedance method under pressure (~ 43 GPa and ~ 673 K and at 0.1 MPa and ~ 1400 K). Our experimental results show a change in charge transport mechanism in the (Mg_1 ? xFe_x)_1 ? δO solid solution at high temperature. The temperature of inflection point of the slope in Arrhenius plots depend greatly on both composition and extrinsic factors of crystals. The low-temperature conduction mechanism in (Mg_1 ? xFe_x)_1 ? δO solid solution is small polaron. Pressure effect of the electric conductivity was observed and the conductivity increased to 0.5 at log scale of S/m with increasing pressure up to 43.4 GPa. The activation energy was decreased linearly with increasing pressure. Chemical composition and homogeneity of specimen rather than pressure greatly influence the electric conductivity. The activation energy of 2.37(4) eV for the (Mg_0.99Fe_0.01)_1 ? δO solid solution might correspond to a migration enthalpy of O ions through thermally formed defects. It is proposed that a possible dominant electrical conduction mechanism in ferropericlase under the lower mantle conditions, at least in the higher temperature region, is super ionic conduction.     

Water vapour solubility and conductivity study of the proton conductor BaCe(0.9 − x)ZrxY0.1O(3 − δ)

The perovskite BaCe_(0.9 ? x)Zr_xY_0.1O_(3 ? δ) has been prepared by solid state reaction at 1400 °C and conventional sintering at 1700 °C. Water uptake experiments performed between 400 and 600 °C, at a water vapour pressure of 0.02 atm, provide data on the concentration of protons incorporated in the sample. The direct current conductivity has been measured as a function of oxygen partial pressure, at a water vapour partial pressure of 0.015 atm. The total conductivity has been resolved into a p-type and an ionic component using a fitting procedure appropriate to the assumed defect model. An estimation of the protonic component was made by assuming a conductivity isotope effect between 1.4 and 1.8. The total conductivity, obtained using impedance spectroscopy has been measured as a function of temperature in the water and heavy water exchanged states. The activation energy has been found to be 0.56 eV to 0.59 eV in the water exchanged state with values 0.03 to 0.04 eV higher in the heavy water exchanged state. Impedance spectra measured at 200 °C showed a reduction in grain boundary resistivity with increasing cerium content. The stability of the compounds to carbon dioxide has been studied by thermogravimetry.     

An oxygen permeable membrane La0.8Sr0.2(Ga0.8Mg0.2)1 − xCrxO3 − δ for a reduced atmosphere

Mixed electron hole and oxide ion conducting perovskite-type oxides, La_0.8Sr_0.2(Ga_0.8Mg_0.2)_1 ? xCr_xO_3 ? δ (0 ≤ x ≤ 1.0)_, were prepared by solid state reaction. The phase stability and the oxygen permeation properties of the oxides were examined as a function of the content of Cr. La_0.8Sr_0.2(Ga_0.8Mg_0.2)_1 ? xCr_xO_3 ? δ has a perovskite related tetragonal phase with x = 0.1 to 0.8. The total electrical conductivity of La_0.8Sr_0.2(Ga_0.8Mg_0.2)_1 ? xCr_xO_3 ? δ increases with increasing x. The oxygen permeation flux across the La_0.8Sr_0.2(Ga_0.8Mg_0.2)_1 ? xCr_xO_3 ? δ membranes at higher temperatures increases with x up to x = 04. The maximum oxygen permeation flux of 1.6 × 10^? 7 mol^? 1 cm^? 2 at 1100 °C in a oxygen activity gradient of air/10^? 2 Pa is observed in La_0.8Sr_0.2(Ga_0.8Mg_0.2)_0.6Cr_0.4O_3 ? δ. This perovskite-type oxide is stable under an oxygen partial pressure of 7 × 10^? 10 Pa at 1000 °C.     

Ga-induced restructuring of Si(5 5 12) − 2 × 1 reconstructed surface at room temperature

Motivated by the need to form 1D-nanostructured dopants on silicon surfaces, we have attempted to grow Ga on the high index Si(5 5 12) surface which has a highly trenched (1D) morphology. The evolution of the interface with Ga adsorption in the monolayer regime has been probed by in situ AES, LEED and EELS. Controlling the kinetics by changing the Ga flux rates shows an interesting difference in the 1.0 to 1.5 ML region. The low flux rate (0.03 ML/minute) results in a Frank van der Merwe (layer by layer) growth mode up to 2 ML, while the higher flux rate (0.1 ML/minute) shows a transient island formation after the completion of 1 ML. The low rate shows the formation of 2 × (3 3 7) and (2 2 5) superstructures, while only the 2 × (3 3 7) is observed in a wide coverage range for the higher rate. The results demonstrate the ability to kinetically control the surface phases with different electronic properties of this technologically important interface.