Impedance spectroscopy and piezoresponse force microscopy analysis of lead-free (1 − x) K0.5Na0.5NbO3 − xLiNbO3 ceramics

(1 ? x) K_0.5Na_0.5NbO₃ ? xLiNbO₃ (where x = 0.0, 5.0, 5.5, 6.0, and 6.5 wt.%) (KNLN) perovskite structured ferroelectric ceramics were prepared by the solid-state reaction method. X-ray diffraction patterns indicate that single phase was formed for pure KNN while a small amount of second phase (K₆Li₄Nb₁₀O₃₀, ～3%) was present in LN doped KNN ceramics. Phase analysis indicated the change in the crystal structure from orthorhombic to tetragonal with increase in LN content. The electrical behavior of the ceramics was studied by impedance spectroscopy technique in the high temperature range. Impedance analysis was performed using an equivalent circuit model. The impedance response in pure KNN and KNLN ceramics could be deconvoluted into two contributions, associated with the bulk (grains) and the grain boundaries. Activation energies for conductivity were found to be strongly frequency dependent. The activation energy obtained from dielectric relaxation data was attributed to oxygen vacancies. From PFM we found that the composition with 6.5 wt.% LN displays stronger piezocontrast as compared to pure KNN implying an evidence of a pronounced piezoelectric coefficient.     

Synthesis and characterization of (Pr0.75Sr0.25)1 − xCr0.5Mn0.5O3 − δ as anode for SOFCs

The complex perovskite (Pr_0.75Sr_0.25)_1 − xCr_0.5Mn_0.5O_3 − δ (PSCM) has been prepared and studied as possible anode material for high-temperature solid oxide fuel cells (SOFCs). PSCM exhibits GdFeO₃-type structure and is both physically and chemically compatible with the conventional YSZ electrolyte. The reduction of PSCM resulted in structural change from orthorhombic Pbnm to cubic Pm-3m. Selected area electron diffraction (SAED) analysis on the reduced phases indicated the presence of a √2 × √2 × 2 superlattice. The total conductivity values of ∼ 75% dense Pr_0.75Sr_0.25Cr_0.5Mn_0.5O_3 − δ at 900 °C in air and 5% H₂/Ar are 9.6 and 0.14 S cm^− 1 respectively. The conductivity of PSCM drops with decreasing Po₂ and is a p-type conductor at all studied Po₂. The average TEC of Pr_0.75Sr_0.25Cr_0.5Mn_0.5O_3 − δ is 9.3 × 10^− 6 K^− 1, in the temperature range of 100–900 °C and is close to that of YSZ electrolyte. The anode polarization resistance of PSCM in wet 5%H₂ is 1.31 Ω cm² at 910 °C and in wet CH₄ at 930 °C; the polarization resistance is 1.29 Ω cm². PSCM was unstable at 900 °C in unhumidified hydrogen. Cell performance measurements carried out using graded PSCM and La_0.8Sr_0.2MnO₃ as anode and cathode respectively yielded a maximum power density of 0.18 W cm^− 2 in wet 5%H₂/Ar at 910 °C and the corresponding current density was 0.44 A cm^− 2 at 0.4 V. The activation energy for the electrochemical cell operating in wet (3% H₂O) 5%H₂/Ar fuel is 85 kJ mol^− 1.     

Improving La0.6Sr0.4Co0.2Fe0.8O3 − δ cathode performance by infiltration of a Sm0.5Sr0.5CoO3 − δ coating

La_xSr_1 ? xCo_yFe_1 ? yO_3 ? δ (LSCF) represents one of the state-of-the-art cathode materials for solid oxide fuel cells (SOFCs) due primarily to its high ionic and electronic conductivity. In this study, a one-step infiltration process has been developed to deposit, on the surface of a porous LSCF cathode, a thin film (50–100 nm) of Sm_0.5Sr_0.5CoO_3 ? δ (SSC), which is catalytically more active for oxygen reduction. Electrochemical impedance spectroscopy reveals that the SSC coating has dramatically reduced the polarization resistance of the cathode, achieving area-specific resistances of 0.036 Ω cm² and 0.688 Ω cm² at 750 °C and 550 °C, respectively. It has also maintained the stability of LSCF cathodes. In particular, the peak power densities are increased by ~ 22% upon the infiltration of SSC onto the porous LSCF cathodes of our best performing cells. These results demonstrate that a conductive backbone (e.g., LSCF) coated with a catalytic film (e.g., SSC) is an attractive approach to achieving an active and stable SOFC cathode for low-temperature solid oxide fuel cells.     

Electronic structure of CuClxBr1 − x,CuClxI1 − xand CuBrxI1 − xalloys

In this work, the electronic structure and disorder effects in copper halides alloys are studied by means of the full potential linearized augmented plane wave (FLAPW) method. The calculated bowing parameter shows that the main contribution is due to the relaxation effects, though the charge transfer remains relatively significant, while the volume deformation contribution is negligible. The total bowing is found to be small in the three studied alloys. Results agree well with experimental and available theoretical works.     

Ferroelectric relaxor properties of (1 − x)K0.5Na0.5NbO3–xBa0.5Ca0.5TiO3 ceramics

The Ba_0.5Ca_0.5TiO₃ (BCT) composition dependent dielectric and structural properties of (1?x)K_0.5Na_0.5NbO₃–xBa_0.5Ca_0.5TiO₃ powders were investigated. Room temperature x-ray diffraction revealed the powder structure to transform from orthorhombic to cubic with increasing BCT composition. The frequency dependent dielectric constant measurements revealed a shift in the temperature of the maximum dielectric constant for at frequencies, suggesting that the system exhibits ferroelectric relaxor behavior. The system containing 15% BCT showed the closest calculated Curie–Weiss exponent to 2, which the exponent for a relaxor ferroelectric.     

Effect of Eu dopant concentration in SrCe1 − xEuxO3 − δ on ambipolar conductivity

The europium dopant concentration in strontium cerate was studied to achieve maximum hydrogen permeation. In order to determine high ambipolar conductivity, total conductivity and open circuit potential measurements were performed. Among the three different compositions of Eu-doped SrCe_1 ? xEu_xO_3 ? δ (x = 0.1, 0.15 and 0.2) studied, SrCe_0.9Eu_0.1O_3 ? δ showed highest total conductivity between 600 °C and 900 °C. However, transference number measurements showed increasing electronic conductivity with increasing dopant concentration and a stronger temperature dependence for electronic conduction. Therefore, the highest ambipolar conductivity was obtained over the compositional range from SrCe_0.85Eu_0.15O_3 ? δ to SrCe_0.8Eu_0.2O_3 ? δ depending on temperature. Finally, the hydrogen permeation flux was calculated based on the ambipolar conductivity and compared with experimental results.     

Modification of B-site doping of perovskite LaxSr1 − xFe1 − y−zCoyCrzO3 − δ oxide by Mg2+ ion

Co-doping B-site of perovskite oxide La_xSr_1 ? xCo_yFe_1 ? yO_3 ? δ (LSCFO) with Cr⁶⁺ and Mg²⁺ ions has been attempted in this research for revamping chemical stability and oxygen ionic conductivity of this mixed conducting oxide. It is known that partial substitution for B-site cations of LSCFO by Cr gives rise to a significant improvement on chemical and thermal stability of the perovskite oxide. On the basis of this doped structure, introduction of an immaterial dose of Mg²⁺ ion into its B-site results in a microstructure consisting of smaller grains with higher density than its precursor. Furthermore, the resulting perovskite oxide La_0.19Sr_0.8Fe_0.69Co_0.1Cr_0.2 Mg_0.01O_3 ? δ (LSFCCMO) displays higher O^2? conductivity than the solely Cr-doped LSCFO besides the improved chemical stability against reduction in 5% CH₄/He stream at 850 °C. A detailed examination of the oxidation states of B-site transition metal ions by XPS has also been conducted as a part of structural characterizations of LSFCCMO. The assessment of relative O^2? conductivity shows that the grain boundary area plays a more important role than the bulk phase in facilitating ion transport, but with comparable boundary areas the higher densification level is favorable.     

High-temperature compressive creep behaviour of the perovskite-type oxide Ba0.5Sr0.5Co0.8Fe0.2O3 − δ

Compressive creep tests have been performed on perovskite-type Ba_0.5Sr_0.5Co_0.8Fe_0.2O_3 ? δ ceramics. The activation energy, stress exponent and inverse grain size exponent of the steady-state creep rates are evaluated at p(O₂) = 0.21 ? 10⁵ Pa and 0.01 ? 10⁵ Pa in the stress, temperature and grain size ranges 5–20 MPa, 1078–1208 K and 2.5–17.4 µm, respectively. The results indicate that the creep rate of Ba_0.5Sr_0.5Co_0.8Fe_0.2O_3 ? δ is controlled by diffusion of cations via both the oxide lattice (bulk diffusion) and along grain boundaries. The creep rate of Ba_0.5Sr_0.5Co_0.8Fe_0.2O_3 ? δ increases profoundly by more than one order of magnitude at 1153–1178 K, which is tentatively linked with the onset of the hexagonal-to-cubic phase transition in this compound.     

SrTiO3(100) − √5 × √5 − R26.6 surface observed by high-resolution scanning tunneling microscopy

SrTiO₃(100) – (√5 × √5) – R26.6 surfaces were studied by means of high-resolution scanning tunneling microscopy (STM) under ultrahigh vacuum conditions. By varying the bias voltage in the occupied state, it was possible to observe the arrangement of titanium and oxygen atoms in the unit cells of a (√5 × √5) surface superstructure, which revealed that the TiO₂ layer is the terminating plane of the (√5 × √5) surface. In the STM images, peculiar protrusions were seen at the oxygen fourfold hollow site responsible for √5 × √5 periodicity. The protrusions are asymmetrical in contrast, which would be an important consideration in proposing accurate structural models for (√5 × √5) surface superstructures.     

Excitonic magnetic polaron dynamics of MBE grown CdTe/Cd1 − xMnxTe,Cd1 − xMnxTe/Cd1 − vMgyTe single quantum wells in magneti fields

Excitonic lifetimes in Cd_1 − xMn_Ue2Te, Cd_1 − xMg_xTe epilayers and CdTe/Cd_1 − xMn_xTe, Cd_1 − xMn_xTe/Cd_1 − vMg_yTe single quantum wells with different well widths and Mn, Mg compositions are investigated. The excitonic lifetimes are found to reduce drastically by applying external magnetic fields to samples with giant Zeeman splittings. The observed phenomenon is interpreted in terms of the PL decay time contribution from the long-life dark excitons which can convert to excitons for recombinations by a spin-flip process. We attribute the lifetime reduction to the depletion of dark excitons due to their crossing over the exciton energies for dipole allowed transitions in magnetic fields.     

Water vapour solubility and conductivity study of the proton conductor BaCe(0.9 − x)ZrxY0.1O(3 − δ)

The perovskite BaCe_(0.9 ? x)Zr_xY_0.1O_(3 ? δ) has been prepared by solid state reaction at 1400 °C and conventional sintering at 1700 °C. Water uptake experiments performed between 400 and 600 °C, at a water vapour pressure of 0.02 atm, provide data on the concentration of protons incorporated in the sample. The direct current conductivity has been measured as a function of oxygen partial pressure, at a water vapour partial pressure of 0.015 atm. The total conductivity has been resolved into a p-type and an ionic component using a fitting procedure appropriate to the assumed defect model. An estimation of the protonic component was made by assuming a conductivity isotope effect between 1.4 and 1.8. The total conductivity, obtained using impedance spectroscopy has been measured as a function of temperature in the water and heavy water exchanged states. The activation energy has been found to be 0.56 eV to 0.59 eV in the water exchanged state with values 0.03 to 0.04 eV higher in the heavy water exchanged state. Impedance spectra measured at 200 °C showed a reduction in grain boundary resistivity with increasing cerium content. The stability of the compounds to carbon dioxide has been studied by thermogravimetry.     

Structural and electrochemical properties of layered lithium nitridocuprates Li3 − xCuxN

We report a systematic study of the layered lithium nitridocuprates Li_3 ? xCu_xN with 0.1 ≤ x ≤ 0.39. The structural data obtained from experimental XRD patterns, Rietveld refinements and unit cell parameters calculation vs x, indicate that copper (I) substitute interlayer lithium ions in the parent nitride Li₃N to form the Li_3 ? xCu_xN compound without any Li vacancy in the Li₂N^? layer. Electrochemical results report Li insertion into the corresponding layered structures cannot take place in the 1.2/0.02 V voltage range as in the case of lithium into nitridonickelates and nitridocobaltates. However, in the initial charge process of Li_3 ? xCu_xN at 1.4 V leading to a specific capacity higher than 1000 mA h/g, the oxidation of copper and nitride ions is probably involved inducing a strong structural disordering process. As a consequence a new rechargeable electrochemical system characterized by discharge–charge potential of ≈ 0.3 V/1.2 V appears from the second cycle. Cycling experiments 0.02 V voltage/0.02 V range induce a complete destruction of the layered host lattice and the presence of Cu₃N in the charge state suggests a conversion reaction. The capacity recovered in the 1.4/0.02 V range practically stabilizes around 500 mA h/g after 20 cycles.     

An oxygen permeable membrane La0.8Sr0.2(Ga0.8Mg0.2)1 − xCrxO3 − δ for a reduced atmosphere

Mixed electron hole and oxide ion conducting perovskite-type oxides, La_0.8Sr_0.2(Ga_0.8Mg_0.2)_1 ? xCr_xO_3 ? δ (0 ≤ x ≤ 1.0)_, were prepared by solid state reaction. The phase stability and the oxygen permeation properties of the oxides were examined as a function of the content of Cr. La_0.8Sr_0.2(Ga_0.8Mg_0.2)_1 ? xCr_xO_3 ? δ has a perovskite related tetragonal phase with x = 0.1 to 0.8. The total electrical conductivity of La_0.8Sr_0.2(Ga_0.8Mg_0.2)_1 ? xCr_xO_3 ? δ increases with increasing x. The oxygen permeation flux across the La_0.8Sr_0.2(Ga_0.8Mg_0.2)_1 ? xCr_xO_3 ? δ membranes at higher temperatures increases with x up to x = 04. The maximum oxygen permeation flux of 1.6 × 10^? 7 mol^? 1 cm^? 2 at 1100 °C in a oxygen activity gradient of air/10^? 2 Pa is observed in La_0.8Sr_0.2(Ga_0.8Mg_0.2)_0.6Cr_0.4O_3 ? δ. This perovskite-type oxide is stable under an oxygen partial pressure of 7 × 10^? 10 Pa at 1000 °C.     

Characterization of doped La0.7A0.3Cr0.5Mn0.5O3 − δ (A = Ca,Sr, Ba) electrodes for solid oxide fuel cells

Doped lanthanum manganese chromite based perovskite, La_0.7A_0.3Cr_0.5Mn_0.5O_3 ? δ (LACM, A = Ca, Sr, Ba), on yttria-stabilized zirconia (YSZ) electrolyte is investigated as potential electrode materials for solid oxide fuel cells (SOFCs). The electrical conductivity and electrochemical activity of LACM depend on the A-site dopant. The best electrochemical activity is obtained on the La_0.7Ca_0.3Cr_0.5Mn_0.5O_3 ? δ/YSZ (LCCM/YSZ) composite electrodes. The conductivity of LCCM is 29.9 S cm^? 1 at 800 °C in air, and the electrode polarization resistance (R_E) of the LCCM/YSZ composite cathode for the O₂ reduction reaction is 0.5 Ω cm² at 900 °C. The effect of Gd-doped ceria (GDC) impregnation on the LCCM cathode polarization resistances is also studied. GDC impregnation significantly enhances the electrochemical activity of the LCCM cathode. In the case of the 6.02 mg cm^? 2 GDC-impregnated LCCM cathode, R_E is 0.4 Ω cm² at 800 °C, ~ 60 times smaller than 24.4 Ω cm² measured on a LCCM cathode without the GDC impregnation. Finally the electrochemical activities of the doped lanthanum manganese chromites for the H₂ oxidation reaction are also investigated.     

Tuneability of Sm(1 − x)CexFeO3 ± λ perovskites: Thermal stability and electrical conductivity

Trimetallic perovskite oxides, Sm_(1 ? x)Ce_xFeO_3 ± λ (x = 0–0.05), were prepared by thermal decomposition of amorphous citrate precursors followed by calcinations. The material properties of the substituted perovskites were characterized by X-ray diffraction (XRD), X-ray florescence spectroscopy (XRF), scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). The doped materials exhibited a single perovskite phase in air up to 1350 °C and have specific surface areas in the range of 2.696–8.665 m²/g. In reducing atmosphere (5%v/vH₂/N₂), the unsubstituted perovskite (x = 0) decomposed into two phases while the ceria stabilized materials (x = 0.01, x = 0.03, x = 0.05) remained in a single phase as revealed by XRD analysis. Their conductivities were measured by the four point probe method in air and in dilute hydrogen (5%v/vH₂/N₂) separately. The ceria substituted materials show increased stability versus reduction and phase separation for a wide temperature range (up to 1000 °C). Although undoped SmFeO₃ has higher conductivity under oxidizing conditions than ceria doped SmFeO₃ due its p-type nature, the situation is reversed under reducing conditions. The ceria substituted perovskites (Sm_(1 ? x)Ce_xFeO_3 ± λ, x = 0–0.05) showed higher conductivity in reducing than in oxidizing conditions, suggesting that ceria doping at the A-site has changed the SmFeO₃ from p-type to n-type semi-conducting behavior.     

Oxygen nonstoichiometry and defect equilibrium in La2 − xSrxNiO4 + δ

Nonstoichiometric variation of oxygen content in La_2 ? xSr_xNiO_4 + δ (x = 0, 0.1, 0.2, 0.3, 0.4) and decomposition P(O₂) were determined by means of high temperature gravimetry and coulometric titration. The measurements were carried out in the temperature range between 873 and 1173 K and the P(O₂) range between 10^? 20 and 1 bar. La_2 ? xSr_xNiO_4 + δ showed the oxygen excess and the oxygen deficient compositions depending on P(O₂), temperature, and the Sr content. The value of partial molar enthalpy of oxygen approaches zero as δ increases in the oxygen excess region, which indicate that the interstitial oxygen formation reaction is suppressed as δ increase. The relationship between δ and logP(O₂) were analyzed by two types of defect equilibrium models. One is a localized electron model, and the other is a delocalized electron model. Both models can well explain the oxygen nonstoichiometry of La_2 ? xSr_xNiO_4 + δ with a regular solution approximation.     

Negative thermal expansion property of Er0.7Sr0.3NiO3 − δ

A new kind of negative thermal expansion (NTE) material of Er_0.7Sr_0.3NiO_3 − δ is synthesized by solid-state method and investigated. It is found that Er_0.7Sr_0.3NiO_3 − δ crystallizes in orthorhombic structure with rod-shaped grains. Ceramic Er_0.7Sr_0.3NiO_3 − δ exhibits NTE coefficient of $-39.0\times {10}^{-6}{\text{K}}^{-1}$ from 655 to 780 K. The results of X-ray diffraction, temperature dependence of Raman spectroscopy and differential scanning calorimetry (DSC) suggest that the NTE phenomenon relates to its phase transition from orthorhombic to rhombohedral.     

Predictions of the bonding properties inCd1 − xZnxTe

The electronic, optical and elastic properties of the ternary II–VI semiconductor alloys Cd_1 − x Zn _xTe are calculated by thesp³s ^*  semi-empirical tight-binding theory and the bond-orbital model. We found a nonlinear decrease of the transverse effective charge and refractive index and a nonlinear increase of the bandgap and elastic constants with increasing Zn composition x. For all these behaviours, the corresponding bowing factors are predicted. The results are compared with previous theoretical estimates and experiments.     

The effect of compositional disorder on electronic band structure in GaxIn1 − xAsySb1 − yalloys lattice matched to GaSb

A pseudopotential formalism coupled with the virtual crystal approximation are applied to study the effect of compositional disorder upon electronic band structure of cubic Ga_xIn_1 − xAs_ySb_1 − yquarternary alloys lattice matched to GaSb. The effects of compositional variations are properly included in the calculations. Our theoretical results show that the compositional disorder plays an important role in the determination of the energy band structure of Ga_xIn_1 − xAs_ySb_1 − y/GaSb and that the bowing parameter is dominated by the group V-anion-based sublattice. Moreover, the absorption at the fundamental optical gaps is found to be direct within a whole range of the x composition.     

Synthesis and electrical properties of nanocrystalline Ca1 − xEuxMnO3 ± δ (0.1 ≤ x ≤ 0.4) powders prepared at low temperature using citrate gel method

Nanopowders of Ca_1 − xEu_xMnO₃ (0.1 ≤ x ≤ 0.4) manganites were synthesized as a single phase using the auto gel-combustion method. The citrate method shows to be simple and appropriate to obtain single phases avoiding segregation or contamination. The Ca_1 − xEu_xMnO₃ system has been synthesized at 800 °C during 18 h, against the conventional method of mixing oxides used to obtain these materials at higher temperatures of synthesis. The formation reaction was monitored by X-ray diffraction (XRD) analysis and an infrared absorption technique (FTIR). The polycrystalline powders are characterised by nanometric particle size, ∼ 48 nm as determined from X-ray line broadening analysis using the Scherrer equation. Morphological analysis of the powders, using the scanning electron microscope (SEM), revealed that all phases are homogeneous and the europium-substituted samples exhibit a significant decrease in the grain size when compared with the undoped samples. The structure refinement by using the Rietveld method indicates that the partial calcium substitution by europium (for x ≥ 0.3) modifies the orthorhombic structure of the CaMnO₃ perovskite towards a monoclinic phase. All manganites show two active IR vibrational modes around 400 and 600 cm^− 1. The high temperature dependence of electrical resistivity (between 25 and 600 °C) allows us to conclude that all the samples exhibit a semiconductor behaviour and the europium causes a decrease in the electrical resistivity by more than one order of magnitude. The results can be well attributed to the Mn⁴⁺/Mn³⁺ ratio.