Tm3+/Yb3+共掺铋碲酸盐玻璃中的高效蓝色上转换荧光

制备了高折射率Tm³⁺/Yb³⁺共掺杂铋碲酸盐玻璃，利用棱镜耦合法测量出玻璃在632.8和1550nm波长处的折射率分别为2.0365和1.9795. 对玻璃的吸收、荧光和红外透过光谱展开了测试与分析，根据Judd-Ofelt理论对吸收光谱进行拟合，求得Tm³⁺的振子强度参数Ω_t(t=2，4，6)分别为3.90×10^-20, 2.03×10^-20和9.03×10^{-2 关键词： 3+}/Yb³⁺共掺')" href="#">Tm³⁺/Yb³⁺共掺 铋碲酸盐玻璃 光谱参数 上转换荧光     

Upconversion luminescence of Tm/Yb-codoped oxyhalide tellurite glasses

Thermal stability, Raman spectra and blue upconversion luminescence properties of Tm³⁺/Yb³⁺-codoped halide modified tellurite glasses have been studied. The results showed that the mixed halide modified tellurite glass (TFCB) has the best thermal stability, the lowest phonon energies and the strongest upconversion emissions. The effect of halide on upconversion intensity is observed and discussed and possible upconversion mechanisms are evaluated. The intense blue upconversion luminescence of Tm³⁺ in TFCB glass may be a potentially useful material for developing upconversion optical devices.     

Yb3+敏化的Er3+/Ho3+共掺碲酸盐玻璃的上转换发光研究

用高温熔融法制备了系列Er³⁺/Yb³⁺共掺，Ho³⁺/Yb³⁺共掺，和Er³⁺/Yb³⁺/Ho³⁺三掺碲酸盐玻璃，在975nm激光抽运下三种掺杂玻璃中都出现了较强的绿光和红光上转换.研究了Yb³⁺离子对Er³⁺和Ho³⁺离子上转换发光强度的影响以及Yb³⁺→Er关键词： 3+/Yb³⁺/Ho³⁺共掺')" href="#">Er³⁺/Yb³⁺/Ho³⁺共掺 碲酸盐玻璃 光谱性质 上转换     

Upconversion luminescence of Er/Yb-codoped natrium-germanium-bismuth glasses

The absorption and upconversion fluorescence spectra of a series of Er³⁺/Yb³⁺-codoped natrium-germanium-bismuth glasses have been studied. The transition probabilities, excited state lifetimes, and the branching ratios have been predicted for Er³⁺ based on the Judd-Ofelt theory. At room temperature, an upconversion efficiency of 6.1×10⁻² has been obtained for the green emission from the glass with 0.5 wt% Er₂O₃ and 3.0 wt% Yb₂O₃ pumped by 980 nm radiation with an intensity of 270 W/cm². And the “standardized” efficiency for green upconversion light is higher than that reported in lead-germanate, lead-tellurite-germanate, and silicate glasses. The results indicate that the Er³⁺/Yb³⁺-codoped natrium-germanium-bismuth oxide glass may be a potential material for developing upconversion optic devices.     

卤化铅调整Tm3+/Yb3+共掺碲酸盐玻璃上转换发光研究

研究了卤化铅调整Tm³⁺/Yb³⁺共掺碲酸盐玻璃的热稳定性能、Raman 光谱和上转 换发光光谱，分析了Tm³⁺/Yb³⁺共掺氧卤碲酸盐玻璃的上转换发光 机理.结果发 现：混合卤化铅调整Tm³⁺/Yb³⁺共掺碲酸盐玻璃具有好的热稳定性 能、低的声 子能量、强的上转换蓝光.这表明混合卤化铅调整Tm³⁺/Yb³⁺共掺碲 酸盐玻璃是一种上转换蓝光激光器的潜在基质材料. 关键词： 氧卤碲酸盐玻璃 上转换光谱 发光机理 上转换蓝光激光器     

Tm3+/Yb3+共掺氧卤碲酸盐玻璃上转换发光研究

研究了Tm³⁺/Yb³⁺共掺氧卤碲酸盐玻璃的上转换发光光谱，分析了Tm₂O₃含量对Tm³⁺/Yb³⁺共掺氧卤碲酸盐玻璃上转换发光的影响机理.结果表明：在Tm³⁺/Yb³⁺共掺氧卤碲酸盐玻璃的上转换发光中，Tm³⁺存在较强的浓度猝灭效应.随Tm₂O₃含量增加，Tm³⁺的上转换蓝光和红光强度先增加，后降低，在0.1mol% Tm₂O₃达到最大.该结果有助于进一步提高Tm³⁺的上转换发光效率.     

Effect of ZnO as modifier on up and downconversion properties of Ho/Yb doped tellurite glasses

Optical absorption and photoluminescent properties of Ho³⁺/Yb³⁺ co-doped tellurite and zinc tellurite glasses are investigated. The effect of zinc oxide as a modifier on the luminescence properties of above mentioned samples has been explored. Two intense upconversion emission bands centered at 546 (⁵F₄ + ⁵S₂ → ⁵I₈) and 660 nm (⁵F₅ → ⁵I₈) are observed on excitation with 976 nm diode laser. Zinc oxide acts as a quencher for 976 nm excited upconversion emission. The up and downconversion emission spectra are recorded with 532 nm excitation source also. In this case zinc oxide improves the up and downconversion emissions. A large enhancement in upconversion intensity has been observed when Ho³⁺ ion is co-doped with Yb³⁺ ion. The dependence of upconversion intensities on excitation power and on temperature has also been studied. The power dependence study shows a quadratic dependence of the fluorescence intensity on the excitation power while a decrement in emission intensity of all the transitions at different rates with increase in temperature is observed in temperature dependence study. The possible mechanisms are also discussed in order to understand the upconversion and energy transfer processes.     

Upconversion luminescence and mechanisms in Yb-sensitized Tm-doped oxyhalide tellurite glasses

Effect of Yb₂O₃ content on upconversion luminescence and mechanisms in Yb³⁺-sensitized Tm³⁺-doped oxyhalide tellurite glasses were investigated under 980 nm excitation. Intense blue and relatively weak red upconversion emission centered at 476 and 649 nm corresponding to the transitions ¹G₄→³H₆ and ¹G₄→³H₄ of Tm³⁺, respectively, are simultaneously observed at room temperature. The results show that upconversion blue and red emission intensities of Tm³⁺ first increase, reach its maximum at Yb₂O₃%=3 mol%, and then decrease with increasing Yb₂O₃ content. The effect of Yb₂O₃ content on upconversion intensity is discussed, and possible effect mechanisms are evaluated. The investigated results were conducing to increase upconversion luminescence efficiency of Tm³⁺.     

Influence of Yb doping concentration on upconversion luminescence of Er in Lu2O3 phosphor

Cubic phase Lu₂O₃:Er³⁺/Yb³⁺ nanocrystal phosphors were prepared by sol–gel method. Fourier transform infrared (FT-IR) spectra were measured to evaluate the vibrational feature of the samples. Green and red radiations were observed upon 980 nm diode laser excitation. Laser power and Er³⁺ or Yb³⁺ doping concentration dependence of upconversion luminescence were studied to understand upconversion mechanisms. Excited state absorption, cross relaxation and energy transfer processes are the possible mechanisms for the visible emissions.     

Upconversion and color tunability in Tm/Ho/Yb doped low phonon energy bismuth tellurite glasses

Low phonon energy Tm³⁺/Ho³⁺/Yb³⁺ triply doped bismuth tellurite glasses exhibiting multicolor upconversion fluorescences have been fabricated and characterized. The multicolor fluorescence composed of three primary colors green, red and blue upconversion emissions from Ho³⁺ and Tm³⁺ has been investigated. By adjusting the excitation power, the fluorescence colors can be tuned from multicolor to white color, and the dependence of color tunability on pump power has been presented in the CIE 1931 chromaticity diagram. With the increase in pumping power, the color coordinates move along the down-left direction and hit the equal energy point. The upconversion and color tunability via changing the pump power of infrared excitation in Tm³⁺/Ho³⁺/Yb³⁺ triply doped bismuth tellurite glasses will lead to new breakthrough in the field of three-dimensional solid-state displays and white-light emitting devices.     

Structural and upconversion fluorescence properties of Er/Yb-codoped oxychloride lead-germanium-bismuth glass

Structural and infrared-to-visible upconversion fluorescence properties of Er³⁺/Yb³⁺-codoped oxychloride lead-germanium-bismuth glass have been studied. The Raman spectrum investigation indicates that PbCl₂ plays an important role in the formation of glass network, and has an important influence on the upconversion luminescence owing to lower phonon energy. Intense green and red emissions centered at 525, 546, and 657 nm, corresponding to the transitions ²H_11/2→⁴I_15/2, ⁴S_3/2→⁴I_15/2, and ⁴F_9/2→⁴I_15/2, respectively, were observed at room temperature. The quadratic dependence of the 525, 546, and 657 nm emissions on excitation power indicates that a two-photon absorption process occurs under 975 nm excitation.     

Upconversion luminescence in Er-doped germanate-oxyfluoride and tellurium-germanate-oxyfluoride transparent glass-ceramics

Upconversion luminescence has been studied for Er³⁺ in a germanate-oxyfluoride and a tellurium-germanate-oxyfluoride transparent glass-ceramic using 800 nm excitation. Significantly increased upconversion luminescence was observed from transparent glass-ceramics compared with that from their corresponding as-prepared glasses. In addition to a strong green emission centered at 545 nm from ⁴S_3/2 state and a weaker red emission centered at 662 nm from ⁴F_9/2 state generally seen from Er³⁺-doped glasses, a violet emission centered at 410 nm from ²H_9/2 state and a near-ultra-violet emission centered at 379 nm from ⁴G_11/2 state were also observed from transparent glass-ceramics. The upconversion luminescence of Er³⁺ ions in transparent glass-ceramics revealed sharp Stark-splitting peaks generally seen in a crystal host. The increased upconversion efficiency is attributed to the decreased effective phonon energy and the increased energy transfer between excited ions when Er³⁺ ions were incorporated into the precipitated β-PbF₂ nanocrystals.     

Preparation and upconversion properties of Ba2ErF7 and Ba2ErF7:Yb powders

Novel Ba₂ErF₇ and Yb³⁺-doped Ba₂ErF₇ powders were synthesized by a coprecipitation method. In Ba₂ErF₇ sample, abundant upconverted emission bands from violet to infrared region are observed under 980 nm excitation, whereas only green and red emissions are observed under 812 nm excitation. Under the two excitations, the luminescence decay curves of the green and red emissions are measured and the quenching behaviors of Yb³⁺ doping are also explored. It is found that a suitable Yb³⁺ concentration can efficiently enhance the intensity ratio of the blue and violet emissions to the green and red ones, which may be due to the competition between the energy transfer process from Er³⁺ to Yb³⁺ and the sensitizing process from Yb³⁺ to Er³⁺ in Ba₂ErF₇:Yb³⁺. This indicates that the Yb³⁺-doped Ba₂ErF₇ might be a good candidate for blue and violet upconversion phosphor.     

Energy transfer and frequency upconversion in Yb3+–Er3+-doped PbO-GeO2 glass containing silver nanoparticles

We report the infrared-to-visible frequency upconversion in Er³⁺–Yb³⁺-codoped PbO-GeO₂ glass containing silver nanoparticles (NPs). The optical excitation is made with a laser at 980 nm in resonance with the ²F_5/2→²F_7/2 transition of Yb³⁺ ions. Intense emission bands centered at 525, 550, and 662 nm were observed corresponding to Er³⁺ transitions. The simultaneous influence of the Yb³⁺→Er³⁺ energy transfer and the contribution of the intensified local field effect due to the silver NPs give origin to the enhancement of the whole frequency upconversion spectra.     

Upconversion luminescence of colloidal solution of Y2O3 nano-particles doped with trivalent rare-earth ions

We have studied upconversion luminescence of colloidal solution of Y₂O₃ nano-particles codoped with 1 mol% Er³⁺ and 5 mol% Yb³⁺. Y₂O₃ nano-particles codoped with 1 mol% Er³⁺ and 5 mol% Yb³⁺ show sintering and agglomeration, because they are synthesized by firing a hydroxy carbonate precursor. Colloidal solution of Y₂O₃ nano-particles codoped with 1 mol% Er³⁺ and 5 mol% Yb³⁺ is prepared through two-step dispersion process and the average diameter of the primary nano-particles is about 50 nm. Under excitation with 980-nm laser diode, upconversion luminescence of colloidal solution of the primary Y₂O₃ nano-particles codoped with 1 mol% Er³⁺ and 5 mol% Yb³⁺ in methyl isobuthyl ketone strongly appeared near 660 nm and weakly near 550 nm.     

Upconversion fluorescence property of Er/Yb-codoped novel bismuth-germanium glass

Infrared-to-visible upconversion fluorescence property of Er³⁺/Yb³⁺-codoped novel bismuth-germanium glass under 975 nm LD excitation has been studied. Intense green and red emissions centered at 525, 546 and 657 nm, corresponding to the transitions ²H_11/2→⁴I_15/2, ⁴S_3/2→⁴I_15/2, and ⁴F_9/2→⁴I_15/2, respectively, were observed at room temperature. The quadratic dependence of the 525, 546 and 657 nm emissions on excitation power indicates that a two-photon absorption process occurs. The structure of the bismuth-germanium glass has been investigated by peak-deconvolution of FT-Raman spectrum, and the structural information was obtained from the peak wavenumbers. This novel bismuth-germanium glass with low maximum phonon energy (∼750 cm⁻¹) can be used as potential host material for upconversion lasers.     

Yb3+/Er3+共掺锗碲酸盐玻璃上转换发光增强机理的研究

玻璃的最大声子能量决定稀土离子的上转换发光强度，但本研究发现：Yb³⁺/Er ³⁺共掺锗碲酸盐玻璃在980nm LD抽运下，上转换荧光强度随着Bi₂O ₃对PbO的取代和碱 金属离子半径的增大而明显增强.而Raman光谱显示基质玻璃的最大声子能量并不随Bi ₂O₃对PbO的取代和碱金属离子半径的增大而变化，但玻璃的最大声子密 度随着Bi₂O₃对PbO 取代和碱金属离子半径的增大而降低.从玻璃无辐射跃迁概率的角度，通过分析表明，最大 声子密度的降低是玻璃上转换发光强度增强的主要原因.     

Upconversion emission enhancement in Er/Yb-codoped BaTiO3 nanocrystals by tridoping with Li ions

Er³⁺/Yb³⁺/Li⁺-tridoped BaTiO₃ nanocrystals were prepared by a sol-gel method to improve the upconversion (UC) luminescence of rare-earth doped BaTiO₃ nanoparticles. Effects of Li⁺ ion on the UC emission properties of the Er³⁺/Yb³⁺/Li⁺-tridoped BaTiO₃ nanocrystals were investigated. The results indicated that tridoping with Li⁺ ion enhanced the visible green and red UC emissions of Er³⁺/Yb³⁺-codoped BaTiO₃ nanocrystals under the excitation of a 976 nm laser diode. X-ray diffraction and decay time of the UC luminescence were studied to explain the reasons of the enhancement of UC emission intensity. X-ray diffraction results gave evidence that tridoping with Li⁺ ion decreased the local symmetry of crystal field around Er³⁺, which increased the intra-4f transitions of Er³⁺ ion. Moreover, lifetimes in the intermediate ⁴ S_3/2 and ⁴I_11/2 (Er) states were enhanced by Li⁺ ion incorporation in the lattice. Therefore, it can be concluded that Li⁺ ion in rare-earth doped nanocrystals is effective in enhancing the UC emission intensity.     

Infrared-to-visible upconversion in Er and Er/Yb activated Sb2O4 nanopowders prepared by sol-gel route

We prepared Er³⁺ doped and Er³⁺/Yb³⁺ codoped Sb₂O₄ nanocrystals by the sol-gel method. The Raman, X-ray diffraction (XRD), transmission electron microscope (TEM), and photoluminescence spectra of the samples were studied. The phonon energy of the Sb₂O₄ nanocrystals is very low (the maximum value being 461 cm⁻¹). The upconversion (UC) red emission of the Er³⁺/Yb³⁺ codoped sample is very strong at 975 nm laser diode excitation. The Sb₂O₄ nanocrystals will be a promising luminous material.     

The up-conversion properties of Yb and Er doped Y4Al2O9 phosphors

Er³⁺ doped and Yb³⁺/Er³⁺ co-doped Y₄Al₂O₉ phosphors are prepared by the sol-gel method. The effect of dopant concentration on the structure and up-conversion properties is investigated by X-ray diffraction (XRD) and photoluminescence, respectively. XRD pattern indicates that the sample structure belongs to monoclinic. Under 980 nm excitation, the green and red up-conversion emissions are observed and the emission intensities depended on the Yb³⁺ ion concentration. The green up-conversion emissions decrease with the increase of Yb³⁺ concentration, while red emission increases as Yb³⁺ concentration increases from 0 to 8 at% and then decreases at high Yb³⁺ concentration. The mechanisms of the up-conversion emissions are discussed and results shows that in Er³⁺ and Yb³⁺/Er³⁺ co-doped system, cross-relaxation (CR) and energy transfer (ET) processes play an important role for the green and red up-conversion emissions.