Microwave absorption properties of rod-shaped Co-Ni-P shells prepared by metallizing Bacillus

The rod-shaped Co-Ni-P shells were prepared by metalling Bacillus. The microstructures and composition of the shells were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM) and energy dispersive analysis (EDS). The electromagnetic parameters were measured by the coaxial line method in the frequency of 2-18 GHz. It was found that the Bacillus were successfully coated with Co-Ni-P, and the inner structure of the shells are hollow in structure. The shells exhibit excellent microwave absorption properties in 5-17 GHz frequency. The microwave reflection loss is above −10 dB in 5.38-16.6 GHz frequency. The maximum microwave reflection loss reaches −35.83 dB at 9.12 GHz for samples thickness 2.4 mm, and the widest bandwidth for microwave reflection loss above −10 dB is about ∼5.32 GHz for samples thickness 2.0 mm. These results confirm the feasibility of applying Bacillus as biotemplates for fabrication of the metallic shells as lightweight microwave absorption materials are very promising for applications.     

Electromagnetic and microwave absorption properties of Fe3O4 magnetic films plated on hollow glass spheres

Magnetic hollow spheres of low density were prepared by plating Fe₃O₄ magnetic films on hollow glass spheres using ferrite plating. The complex permeability and permittivity of spheres–wax composites were measured in the range of 2–18 GHz. The complex permeability and permittivity increased, and the dielectric and magnetic losses were improved as the volume fraction of the magnetic spheres in the composites increased from 60% to 80%, which also resulted in a great improvement of microwave absorption properties. For composites with volume fraction 80%, its magnetic resonance frequency was at about 13 GHz and it appeared three loss peaks in the calculated reflection loss curves; the bandwidth less than −10 dB was almost 4 GHz which was just in the Ku-band frequencies (12–18 GHz) and a minimum reflection loss of −20 dB was obtained when the thickness was 2.6 mm; the microwave absorbing properties were mainly due to the magnetic loss. The results showed that the magnetic spheres composites were good and light microwave absorbers in the Ku-band frequencies.     

Microwave absorption properties of composite powders with low density

The composites of barium ferrite coated on hollow ceramic microspheres were prepared using sol-gel technique. The crystal structure, morphology and microwave absorption properties of composite powders with different weight ratio of microspheres were studied with XRD, EDS, FESEM and vector network analyzer. The results show that the microwave absorption properties of composite powders are greatly improved. The maximum microwave loss of composite powders reaches 31 dB with an amount of 50 wt.% microspheres, and its density is only about 1.80 g/cm³. The effect of hollow ceramic microspheres on the microwave absorption property is also discussed.     

Microwave absorption properties of one thin sheet employing carbonyl-iron powder and chlorinated polyethylene

To solve more and more serious electromagnetic interference problem, one thin microwave absorbing sheet employing carbonyl-iron powder (CIP) and chlorinated polyethylene (CPE) was prepared. The pattern, static magnetic properties and phase of CIP were characterized by scanning electron microscope (SEM), vibrating sample magnetometer (VSM) and X-ray diffraction (XRD), respectively. The electromagnetic parameters of CIP were measured in the frequency range of 2-18 GHz, and the electromagnetic loss mechanisms of the powder were discussed. The microwave absorption properties of composite sheets with different thicknesses and CIP ratios in matrix were investigated by measuring reflection loss (RL) in 2-18 GHz frequency range using the arch method. The results showed that appropriate CIP content and thickness could greatly improve microwave absorption properties in lower frequency range. For the sample with the weight ratio (CIP:CPE) of 16:1 and 1.5 mm thickness, the bandwidth (RL below −10 dB) achieved 1.1 GHz (2-3.1 GHz), and the minimum reflection loss value was obtained −13.2 dB at 2.2 GHz. This suggested that CIP/CPE composites could be applied as thin microwave absorbers in S-band (2-4 GHz).     

Electromagnetic wave absorption properties of carbonyl iron-ferrite/PMMA composites fabricated by hybridization method

The surface of carbonyl iron powder or a mixture of carbonyl iron and ferrite was coated with polymethylmethacrylate (PMMA) microspheres by a hybridization method to make hybrid powders, and then electromagnetic wave absorption properties of the hybrid composites prepared with these hybrid powders have been investigated. As for the carbonyl iron/PMMA hybrid composite, the reflection loss less than −20 dB could be achieved in a frequency range of 1.7–5.0 GHz when the composite thickness was below 5.00 mm. In the case of the carbonyl iron-ferrite/PMMA hybrid composite, a similar reflection loss was observed in a frequency range of 4.3–13.0 GHz. Thus, the addition of ferrite was found to be useful for achieving a large absorption in a wide frequency range, especially for higher frequency values. Simulated values for the minimum reflection loss are well agreed with actually measured ones, because of homogeneous distribution of carbonyl iron and/or ferrite in these hybrid composites.     

Enhanced microwave absorption in ZnO/carbonyl iron nano-composites by coating dielectric material

The microwave absorption properties of zinc oxide/carbonyl iron composite nanoparticles fabricated by high energy ball milling were studied at 0-20 GHz. Experiments showed that ZnO as a kind of dielectric material coating carbonyl iron particles made the bandwidth of reflection loss (RL)<−5 dB expanding to the low frequency, and enhanced absorption effect obviously. For a 3 mm thickness absorber of ZnO/carbonyl iron after 30 h milling, the values of RL<−5 dB and RL<−8 dB were obtained in the frequency range from 7.0 GHz to 17.8 GHz and from 9.8 dB to 14.9 dB, respectively, and its strongest RL peak was −29.34 dB at 13.59 GHz. The magnetic loss of carbonyl iron particles and the dielectric loss of ZnO particles were the main mechanisms of microwave absorption for the composites.     

Adjustable microwave absorption properties of flake shaped (Ni0.5Zn0.5)Fe2O4/Co nanocomposites with stress induced orientation

Flake shaped (Ni_0.5Zn_0.5)Fe₂O₄/Co nanocomposites were successfully fabricated by co-precipitating of Ni-Zn ferrite on the surface of cobalt nanoflakes. The electromagnetic characteristics of the samples were studied at the frequency of 0.1–14 GHz. The results showed that the cobalt nanoflakes in compacted nanocomposites were well orientated, and the nanocomposites were characterized with low optimal reflection loss (RL) of −33.8 dB at 11.5 GHz and broad RL bandwidth for <−20 dB in the frequency range of 7.6–12.1 GHz. At the same time, the position of the absorptive band can be adjusted by changing the mass ratio of ferrite to cobalt in the nanocomposites. It is proposed that the excellent microwave absorption properties are related to the combination of strong shape anisotropy of cobalt nanoflakes and adjustable dielectric loss.     

Preparation, characterization and microwave absorption properties of electroless Ni-Co-P-coated SiC powder

Silicon carbide particles reinforced nickel-cobalt-phosphorus matrix composite coatings were prepared by two-step electroless plating process (pre-treatment of sensitizing and subsequent plating) for the application to lightweight microwave absorbers, which were characterized by scanning electron microscopy (SEM), X-ray diffraction analysis (XRD), vibrating sample magnetometer (VSM) and vector network analyzer, respectively. The results show that Ni-Co-P deposits are uniform and mixture crystalline of α-Co and Ni₃P and exhibit low-specific saturation magnetization and low coercivity. Due to the conductive and ferromagnetic behavior of the Ni-Co thin films, high dielectric constant and magnetic loss can be obtained in the microwave frequencies. The maximum microwave loss of the composite powder less than −32 dB was found at the frequency of 6.30 GHz with a thickness of 2.5 mm when the initial atomic ratio of Ni-Co in the plating bath is 1.5.     

Preparation and microwave absorption properties of electroless Co-P-coated nickel hollow spheres

Co-P-coated nickel hollow spheres (NHSs) were prepared by electroless plating technology. The morphology and component content of Co-P coating varies with the change of sodium citrate concentration in elctroless plating solution. And as phosphorus content increases in coatings, resulting in smaller grain, coercivity of microspheres decreases. The microwave absorption properties of spheres-wax composite were investigated in the range of 2-18 GHz. Both permittivity and permeability increase with an increase of cobalt content in coatings. For composite layer, a minimal reflection loss (RL, −36.9 dB) of was predicted at 8.1 GHz with a thickness of 3 mm.     

γ-MnO2/polyaniline composites: Preparation, characterization, and applications in microwave absorption

MnO₂/doped polyaniline (PANI) is prepared by an in situ polymerization method using γ-MnO₂ as the addition agent and hydrochloric acid as the doping agent. Products are characterized by FT-IR, UV-vis, XRD, and TEM. Conductivity, electromagnetic properties, and microwave absorption properties are first discussed on the basis of structural characterization. The as-prepared products of MnO₂/PANI are partially crystalline in nature and spherical in pattern with grain sizes of 50-70 nm. MnO₂ particles are successfully decorated with doped PANI. MnO₂/PANI displays moderate electric conduction, excellent dielectric losses, and microwave absorption capabilities. Compared to pure MnO₂, the dielectric and reflection loss properties of MnO₂/PANI composites exhibit significant improvements, with an effective absorption band at 5 GHz under −10 dB and maximum reflection loss of −21 dB at 13.56 GHz. Pure MnO₂ shows an effective absorption band of 3 GHz under −10 dB and a maximum reflection loss of −14.20 dB at 11.5 GHz. Thus, MnO₂/PANI composites are found to be a promising microwave absorption material.     

Electromagnetic properties and microwave absorption of W-type hexagonal ferrites doped with La

W-type barium hexaferrites with compositions of Ba₁Co_0.9Zn_1.1Fe₁₆O₂₇ and Ba_0.8La_0.2Co_0.9Zn_1.1Fe₁₆O₂₇ were synthesized by the sol-gel method. The electromagnetic properties and microwave absorption behavior of these two ferrites were studied in the 2-18 GHz frequency range. The microstructure and morphology of the ferrites were characterized by X-ray diffraction (XRD), and scanning electron microscopy (SEM) techniques. The complex permittivity spectra, the complex permeability spectra and microwave reflection loss were measured by a microwave vector network analyzer. The XRD patterns show that the main phase of the Co₂W ferrite forms without other intermediate phases when calcined at 1200 °C. The SEM images indicate that flake-like hexagonal crystals distribute uniformly in the materials. Both the magnetic and dielectric losses are significantly enhanced by partial substitution of La³⁺ for Ba²⁺ in the W-type barium hexaferrites. The microwave absorption property of the La³⁺ doping W-type hexaferrite sample is enhanced with the bandwidth below −10 dB around 8 GHz and the peak value of reflection loss about −39.6 dB at the layer thickness of 2 mm.     

Microwave absorption properties of Ce-substituted M-type barium ferrite

Ce-substituted barium ferrite with chemical composition BaCe_0.05Fe_11.95O₁₉ has been prepared by the citrate sol-gel method. The phase composition of BaCe_0.05Fe_11.95O₁₉ was characterized by X-ray powder diffraction analysis (XRD). The complex permittivity and complex permeability, microwave absorption properties of the resulting powder were measured by the transmission/reflection coaxial line method in the range of 8-13 GHz. The results show that the resulting powder has a minimum reflection loss value of - 37.4 dB at 12.8 GHz with a matching thickness of 3.5 mm.     

Preparation, and magnetic and electromagnetic properties of La-doped strontium ferrite films

SrLa_xFe_12−xO₁₉ films (x=0-1.0) with large magneto-crystalline anisotropy were synthesized on SiO₂ substrate by sol-gel and self-propagating high-temperature synthesis technique. The films were characterized by various experimental techniques including X-ray diffraction analysis, Field Emission Scanning Electron Microscope, Atomic Force Microscopy, Vibrating Sample Magnetometry and vector network analyzer. The results show that La ions completely enter into strontium ferrite lattice without changing the ferrite appearance; its grain size is approximately 40-80 nm, its length is 100 nm; the magnetoplumbite structure is proved through testing a concertina form of the crystal grain; the maximum coercivity is 5986 Oe at x=0.2; La-doped films possess a wider microwave absorption frequency range with better gross loss angle tangent (tan δ>0.1), from 9 to 10.5 GHz at x=0.2, where the maximum value of tan δ reaches 0.2709. The La-doped films reach smaller nanometer size, better magnetic properties and microwave absorption properties with the doping of lanthanum.     

Determining factors for high performance silicone rubber microwave absorbing materials

Silicone rubber microwave absorbing materials (RMAMs) based on ferrite as the major absorbent were prepared by the mechanical blending method. The determining factors for the complex permittivity, complex permeability, and reflectivity of RMAM were thoroughly investigated with various samples including different crystal structures of Ba-ferrite (M-type, W-type, and Y-type), the ferrite with doped elements (Ba, Sr), the materials' thickness, the combination ratio of ferrite and carbonyl iron. The effects of surface modification and loading amount of ferrite on the mechanical properties, processing performance, and absorbing property of RMAM were also assessed. The results show that W-type Ba-ferrite based RMAM exhibits better absorbing property at high frequencies (8-18 GHz) than the other two barium ferrites (M-type and Y-type) based ones, and the absorbing property of RMAM based on Sr-ferrite is best. As the thickness of RMAM and the amount of absorbents increase, the absorption peak moves toward low frequency, the absorption frequency bandwidth is narrowed, and the reflectivity first decreases and later increases. The optimum thickness is 1.5-1.7 mm, and the amount of ferrite is 450 parts per hundreds of rubber (phr). Surface modification of the absorbent with silane coupling agent could improve the mechanical properties and processing performance of RMAM. It is concluded that there will be a synergistic effect when carbonyl iron (CI) is used in combination with Sr-ferrite (Sr-W) in an appropriate proportion. When the total volume fraction of absorbents is 51%, the optimum ratio of Cl to Sr-W is 17:34, the absorption frequency bandwidth (<−10 dB) is about 8 GHz, and the absorption area is −99 dB.     

Microwave absorption properties of Sr2FeMoO6 nanoparticles

The microwave absorption properties of nanosized double perovskite Sr₂FeMoO₆ and epoxy resin composites were investigated in the frequency range of 2-18 GHz using the coaxial method. The Sr₂FeMoO₆ composites with an optimal 20 wt% epoxy resin showed a strong electromagnetic attenuation of −49.3 dB at 8.58 GHz with a matching thickness of 2.15 mm. Moreover the optimum absorption frequency at which the reflection loss is less than −20 dB, which corresponds to 99% reflection loss of the incident microwave, is from 5.7 to 13.2 GHz with the matching thickness ranging from 3.0 to 1.5 mm. The excellent microwave-absorption properties are a consequence of a proper electromagnetic match due to the existence of the insulating matrix of anti-site defects and anti-phase domains, which not only contribute to the dielectric loss but also to the reduced eddy current loss.     

Electromagnetic and microwave absorption properties of carbonyl iron/La0.6Sr0.4MnO3 composites

In this work carbonyl iron/La_0.6Sr_0.4MnO₃ composites were prepared to develop super-thin microwave absorbing materials. The complex permittivity, permeability and microwave absorption properties are investigated in the frequency range of 8-12 GHz. An optimal reflection loss of −12.4 dB is reached at 10.5 GHz with a matching thickness of 0.8 mm. The thickness of carbonyl iron/La_0.6Sr_0.4MnO₃ absorber is thinner, compared with conventional carbonyl iron powders with the same absorption properties. The bandwidth with a reflection loss exceeding −7.4 dB is obtained in the whole measured frequency range with the thickness of 0.8 mm. The excellent microwave absorption properties are attributed to a better electromagnetic matching established by the combination of the enhanced dielectric loss and nearly invariable magnetic loss with the addition of La_0.6Sr_0.4MnO₃ nanoparticles in the composites. Our work indicates that carbonyl iron/La_0.6Sr_0.4MnO₃ composites may have an important application in wide-band and super-thin electromagnetic absorbers in the frequency range of 8−12 GHz.     

The influence of temperature on magnetic and microwave absorption properties of Fe/graphite oxide nanocomposites

Fe/graphite oxide nanocomposites were prepared by inserting Fe³⁺ into layers of graphite oxide and then reducing Fe³⁺/graphite oxide compound at different reduced reaction temperatures in H₂. The composition, crystal structure, magnetic and microwave absorption properties of Fe/graphite oxide nanocomposites were investigated using elemental analysis, transmission electron microscope (TEM), X-ray diffraction (XRD), magnetic hysteresis curve and electromagnetic parameter analysis. The results show that the densities of samples are 2.43–2.47 g/cm³ and the nanocomposites are soft magnetic materials. The optimum reduced reaction temperature for preparing Fe/graphite oxide nanocomposites is 600 °C. With the increase of the thickness of the sample, the matching frequency tends to shift to the lower frequency region, and theoretical reflection loss becomes less at the matching frequency. Microwave absorption property of Fe/graphite oxide nanocomposites prepared at 600  °C (FeGO600) is the best. When the thickness is 1 mm, the maximum theoretical reflection loss of FeGO600 is −9 dB and the frequency region in which the maximum reflection loss is more than −6.0 dB is 11–18 GHz. In conclusion, FeGO600 is a good candidate for microwave absorbent due to its low density, wide frequency region for microwave absorption and large reflection loss.     

Microwave absorbing properties of rare-earth elements substituted W-type barium ferrite

W-type barium ferrites Ba(MnZn)_0.3Co_1.4R_0.01Fe_15.99O₂₇ with R=Dy, Nd and Pr were prepared by chemical coprecipitation method. Effects of rare-earth elements (RE) substitution on microstructural and electromagnetic properties were analyzed. The results show that a small amount of RE³⁺ ions can replace Fe³⁺ ions and adjust hyperfine parameters. An obvious increase in natural resonance frequency and high frequency relaxation, and a sharp decrease for complex permittivity have been observed. Furthermore, the matching thickness and the reflection loss (RL) of one-layer ferrite absorber were calculated. It reveals that thin and broad-band can be obtained by RE-substitution. But only when the magnetic moment of RE³⁺ is higher than that of Fe³⁺, can substitution be effective for higher RL. Dy-substituted ferrite composite has excellent microwave absorption properties. The frequency (with respect to −10 dB RL) begins from 9.9 GHz, and the bandwidth reaches far more than 8.16 GHz. The peak value is −51.92 dB at a matching thickness of 2.1 mm.     

Optimization of electromagnetic matching of carbonyl iron/BaTiO3 composites for microwave absorption

Microwave absorbing materials filled with BaTiO₃ and carbonyl iron (CI) particles with various weight fractions (BaTiO₃/CI particles=100/0 to 0/100) are investigated. The dielectric and magnetic properties of the absorbers can be tuned by changing the weight ratio of BaTiO₃/CI particles in the frequency range of 2-18 GHz. Numerical simulations are also performed to design a single-layer and double-layer absorber. The minimum reflection loss of the composite filled with 20 wt% BaTiO₃ and 60 wt% CI particles at 2.0 mm thickness can be reached to −42 dB at 4.1 GHz. With the weight ratio of CI particles in the composite increased, the microwave absorption peak shifted to the lower frequency region. By using a double-layer absorber structure, the microwave absorption performance of the absorber is enhanced. The result shows that the total thickness of the absorber can be reduced below 1.4 mm by using a matching layer filled with 50 wt% BaTiO₃, and an absorption layer filled with 60 wt% BaTiO₃ and 20 wt% CI particles, whereas the reflection loss below −10 dB can be obtained in the frequency range of 10.8-14.8 GHz and the minimum reflection loss of −59 dB can be obtained at 12.5 GHz.     

Magnetic properties of La-Co substituted M-type strontium hexaferrites prepared by polymerizable complex method

Magnetic properties of La-Co substituted M-type strontium hexaferrites were studied. The samples were prepared by polymerizable complex method. Crystal structure of samples has been investigated by powder X-ray diffraction (XRD). Single-phase M-type strontium hexaferrites with chemical composition of Sr_1.05−xLa_xFe_12−xCo_xO₁₉ (x=0-0.4) were formed by heating at 1173 K for 24 h in air. Magnetic properties were discussed by measurements of M-H curves with vibrating sample magnetometer (VSM). La-Co substituted M-type strontium hexaferrites prepared by polymerizable complex method showed typical magnetic hysteresis of hard ferrite. The coercive force increased significantly by La-Co substitution with polymerizable complex method. Maximum coercive force achieved in this study is 8.0 kOe (640 kA/m). Scanning electron microscopy revealed that the prepared ferrite particles have plate-like shape of diameter range between 20 and 500 nm.