Reversible addition–fragmentation chain transfer polymerization of glycidyl methacrylate with 2‐cyanoprop‐2‐yl 1‐dithionaphthalate as a chain‐transfer agent

A reversible addition–fragmentation chain transfer (RAFT) agent, 2‐cyanoprop‐2‐yl 1‐dithionaphthalate (CPDN), was synthesized and applied to the RAFT polymerization of glycidyl methacrylate (GMA). The polymerization was conducted both in bulk and in a solvent with 2,2′‐azobisisobutyronitrile (AIBN) as the initiator at various temperatures. The results for both types of polymerizations showed that GMA could be polymerized in a controlled way by RAFT polymerization with CPDN as a RAFT agent; the polymerization rate was first‐order with respect to the monomer concentration, and the molecular weight increased linearly with the monomer conversion up to 96.7% at 60 °C, up to 98.9% at 80 °C in bulk, and up to 64.3% at 60 °C in a benzene solution. The polymerization rate of GMA in bulk was obviously faster than that in a benzene solution. The molecular weights obtained from gel permeation chromatography were close to the theoretical values, and the polydispersities of the polymer were relatively low up to high conversions in all cases. It was confirmed by a chain‐extension reaction that the AIBN‐initiated polymerizations of GMA with CPDN as a RAFT agent were well controlled and were consistent with the RAFT mechanism. The epoxy group remained intact in the polymers after the RAFT polymerization of GMA, as indicated by the ¹H NMR spectrum. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2558–2565, 2004     

Synthesis of well‐defined glycidyl methacrylate based block copolymers with self‐activation and self‐initiation behaviors via ambient temperature atom transfer radical polymerization

Well‐defined glycidyl methacrylate (GMA) based di‐ and triblock copolymers, with self‐activation and self‐initiation behaviors by incorporation of 2‐(diethylamino) ethyl methacrylate (DEA) blocks, were synthesized via ambient temperature atom transfer radical polymerization (ATRP). The stability of the GMA pendant oxirane rings in tertiary amine environments at ambient temperature was investigated. More importantly, both self‐activation behavior in oxirane ring opening addition reaction and self‐initiation behavior in post‐cure oxirane ring opening crosslinking of these block copolymers were evidenced by ¹H NMR studies. The results demonstrated that the reactivity of pendent oxirane rings was strongly dependant on the nucleophilicity and steric hindrance of tertiary amine moieties and temperature. This facilitated the synthesis of well‐defined block copolymers of GMA and DEA via sequential monomer addition ATRP, particularly for polymerization of GMA monomer at ambient temperature. Moreover, these one‐component GMA based block polymers have novel self‐activation and self‐initiation properties, rendering some potential applications in both enzyme immobilization and GMA‐based thermosetting materials. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 2947–2958, 2007     

Reversible addition–fragmentation chain transfer polymerization of alkyl‐2‐cyanoacrylates: An assessment of livingness

Alkyl 2‐cyanoacrylates (CAs) are primarily used as instant adhesives, including those sold under the Loctite brand. The adhesive action can be inhibited with acid stabilizers allowing radical polymerization to be employed. The following article details the first attempted controlled/living radical polymerization of alkyl CAs: Reversible addition fragmentation chain transfer (RAFT) polymerization mediated by a poly(methyl methacrylate) dithiobenzoate macroRAFT agent for three different CA monomers (ethyl 2‐cyanoacrylate, n‐butyl 2‐cyanoacrylate, and 2‐phenylethyl cyanoacrylate) allowed the preparation of the first block copolymers of this challenging but commercially important monomer class. Nevertheless, GPC with UV detection indicated significant loss of the RAFT end‐group for all three CAs limiting control/living character. © 2016 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2017 , 55, 1397–1408     

Are o‐nitrobenzyl (meth)acrylate monomers polymerizable by controlled‐radical polymerization?

We report on the controlled‐radical polymerization of the photocleavable o‐nitrobenzyl methacrylate (NBMA) and o‐nitrobenzyl acrylate (NBA) monomers. Atom transfer radical polymerization (ATRP), reversible addition‐fragmentation chain transfer polymerization (RAFT), and nitroxide‐mediated polymerization (NMP) have been evaluated. For all methods used, the acrylate‐type monomer does not polymerize, or polymerizes very slowly in a noncontrolled manner. The methacrylate‐type monomer can be polymerized by RAFT with some degree of control (PDI ∼ 1.5) but leading to molar masses up to 11,000 g/mol only. ATRP proved to be the best method since a controlled‐polymerization was achieved when conversions are limited to 30%. In this case, polymers with molar masses up to 17,000 g/mol and polydispersity index as low as 1.13 have been obtained. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 6504–6513, 2009     

Synthesis of di‐ and tri‐tertiary amine containing methacrylic monomers and their (co)polymerization via RAFT

The synthesis, reversible addition‐fragmentation chain transfer (RAFT) (co)polymerization, and aqueous phase behavior of three methacrylic monomers containing two or three pendent tertiary amine functional groups are described. Homopolymerizations were conducted with 1‐methyl‐1‐cyanoethyl dithiobenzoate (CPDB) under bulk conditions following standard RAFT procedures. All three monomers, 1,3‐bis(dimethylamino)propan‐2‐yl methacrylate ( M1 ), 1‐(bis(3‐(dimethylamino)propyl) amino)propan‐2‐yl methacrylate ( M2 ), and 2‐((2‐(2‐(dimethylamino)ethoxy)ethyl) methylamino)ethyl acrylate ( M3 ), polymerized in a controlled manner as evidenced by the kinetic and molecular weight profiles. Homopolymerizations conducted at a lower ratio of CPDB:AIBN proceeded faster than those at a higher ratio. Subsequently, the facile copolymerization behavior of M1 and M3 was demonstrated via the synthesis of a range of statistical copolymers with hexyl and lauryl methacrylate comonomers containing 10–90 mol % hydrophobic comonomer. Finally, the aqueous‐solution characteristics of the M1 – M3 homopolymers were briefly examined. All three homopolymers were shown to undergo phase transitions in aqueous media in response to changes in both temperature and pH. Specifically, 1 wt % solutions of poly M1 were shown to possess an LCST of ～22 °C, that of poly M2 at ～33 °C, and for poly M3 the observed cloud point was ～63 °C. Additionally, all homopolymers became hydrophobic and phase separated at high solution pH. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 1877–1890, 2009     

Highly efficient and well‐controlled ambient temperature RAFT polymerization of glycidyl methacrylate under visible light radiation

A range of well‐defined poly(glycidyl methacrylate) (PGMA) polymers and their corresponding block copolymers were synthesized via 2‐cyanoprop‐2‐yl(4‐fluoro) dithiobenzoate or CPFDB‐mediated ambient temperature reversible addition fragmentation chain transfer radical polymerization or RAFT polymerization under environmentally friendly visible light radiation (λ = 405–577 nm), using a (2,4,6‐trimethylbenzoyl) diphenylphosphine oxide photoinitiator. As comparison, CPFDB‐mediated ambient temperature RAFT polymerizations of glycidyl methacrylate (GMA) under both full‐wave radiation (λ = 254–577 nm) and long‐wave radiation (λ = 365–577 nm) were also studied in this article. The results indicated that CPFDB moieties were significantly photolyzed under either full‐wave radiation or long‐wave radiation, thus undermining the controlled behavior of these RAFT processes. Whereas this photolysis was significantly suppressed under visible light radiation, thus CPFDB functionalities exerted well control over RAFT process, leading to a remarkably living behavior up to 90% GMA monomer conversions. This strategy facilitates the facile synthesis of well‐defined PGMA polymers. More importantly, under visible light radiation, a relatively high initial molar ratio of GMA to CPFDB and TPO led to shortening initialization period of RAFT process and accelerating overall polymerization rate. These effects are remarkably in favor of the facile synthesis of well‐defined PGMA polymers and PGMA‐based copolymers with high molecular weights. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 5091–5102, 2007     

Propagation kinetics of free‐radical polymerizations in ionic liquids

Propagation rate coefficients, k_p, of methyl methacrylate (MMA) and glycidyl methacrylate (GMA) homopolymerizations were measured at ambient pressure in four ionic liquids (ILs): 1‐ethyl‐3‐methylimidazolium ([emim]) ethyl sulfate and [emim] hexyl sulfate as well as butyl‐3‐methylimidazolium ([bmim]) hexafluorophosphate and [bmim] tetrafluoroborate via the pulsed‐laser polymerization size‐exclusion chromatography technique. In passing from bulk polymerization at 40 °C polymerization in IL solution containing 20 vol % monomer, k_p is enhanced by up to a factor of 4 with MMA and by a factor of 2 with GMA. This enhancement of k_p primarily results from a lowering of activation energy upon partial replacement of monomer by ionic liquid species. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 1460–1469, 2008     

Synthesis and copolymerization of new phosphorus‐containing acrylates

Two phosphorus‐containing acrylate monomers were synthesized from the reaction of ethyl α‐chloromethyl acrylate and t‐butyl α‐bromomethyl acrylate with triethyl phosphite. The selective hydrolysis of the ethyl ester monomer with trimethylsilyl bromide (TMSBr) gave a phosphonic acid monomer. The attempted bulk polymerizations of the monomers at 57–60 °C with 2,2′‐azobisisobutyronitrile (AIBN) were unsuccessful; however, the monomers were copolymerized with methyl methacrylate (MMA) in bulk at 60 °C with AIBN. The resulting copolymers produced chars on burning, showing potential as flame‐retardant materials. Additionally, α‐(chloromethyl)acryloyl chloride (CMAC) was reacted with diethyl (hydroxymethyl)phosphonate to obtain a new monomer with identical ester and ether moieties. This monomer was hydrolyzed with TMSBr, homopolymerized, and copolymerized with MMA. The thermal stabilities of the copolymers increased with increasing amounts of the phosphonate monomer in the copolymers. A new route to highly reactive phosphorus‐containing acrylate monomers was developed. A new derivative of CMAC with mixed ester and ether groups was synthesized by substitution, first with diethyl (hydroxymethyl)phosphonate and then with sodium acetate. This monomer showed the highest reactivity and gave a crosslinked polymer. The incorporation of an ester group increased the rate of polymerization. The relative reactivities of the synthesized monomers in photopolymerizations were determined and compared with those of the other phosphorous‐containing acrylate monomers. Changing the monomer structure allowed control of the polymerization reactivity so that new phosphorus‐containing polymers with desirable properties could be obtained. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 2207–2217, 2003     

Preparation of chiral amino acid materials and the study of their interactions with 1,1‐Bi‐2‐naphthol

The amino acid tryptophan has been converted into acrylamide monomers using L /D ‐tryptophan methyl ester forming the enantiopure chiral monomers. Attempts were made to polymerize these monomers via reversible addition fragmentation chain transfer (RAFT) polymerization to form poly(tryptophan). Unfortunately, this proved difficult, and instead, a postpolymerization modification route was used by first synthesizing poly(pentafluorophenyl acrylate) via RAFT, which was then substituted with L ‐tryptophan methyl ester to give poly(L ‐tryptophan). The interactions of the newly synthesized tryptophan monomers, as well as previously reported phenylalanine monomers, were studied in the presence of rac‐BINOL. It has been shown that the enantiomers of tryptophan have a stronger interaction with BINOL than phenylalanine and this has been attributed to the larger π system on the side chain. By monitoring the shifts and splitting of the phenolic protons of BINOL, it has been observed that S‐BINOL interacts more favorably with L ‐monomer enantiomers and R‐BINOL with D ‐monomer enantiomers. Similar interactions have also been seen with poly(phenylalanine) and the newly synthesized poly(tryptophan) materials. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012     

Emulsion and controlled miniemulsion polymerization of the renewable monomer γ‐methyl‐α‐methylene‐γ‐butyrolactone

The kinetics of free‐radical emulsion polymerization of γ‐methyl‐α‐methylene‐γ‐butyrolactone (MeMBL), a renewable monomer related to methyl methacrylate, are presented in detail for the first time, and stable polymer latices are prepared. The effects of different reaction parameters on free‐radical emulsion polymerization of MeMBL are presented. Homogeneous nucleation is asserted to be the dominant path for particle formation. Miniemulsion copolymerization of MeMBL and styrene is also reported. In this case, the homogeneous nucleation process appears limited when using an oil soluble initiator. Both the RAFT miniemulsion polymerizations and RAFT bulk polymerizations are well controlled and narrow polydispersity copolymers are produced. Rate retardation is observed in the RAFT miniemulsion polymerizations compared with the free‐radical polymerization and RAFT bulk polymerizations and the possible causes of the retardation are discussed. The reactivity ratios of MeMBL and styrene in RAFT bulk copolymerization are also determined. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 5929–5944, 2008     

Synthesis and self‐assembly of stimuli‐responsive amphiphilic block copolymers based on polyhedral oligomeric silsesquioxane

A novel POSS‐containing methacrylate monomer (HEMAPOSS) was fabricated by extending the side chain between polyhedral oligomeric silsesquioxane (POSS) unit and methacrylate group, which can efficiently decrease the steric hindrance in free‐radical polymerization of POSS‐methacrylate monomer. POSS‐containing homopolymers (PHEMAPOSS) with a higher degree of polymerization (DP) can be prepared using HEMAPOSS monomer via reversible addition–fragmentation chain transfer (RAFT) polymerization. PHEMAPOSS was further used as the macro‐RAFT agent to construct a series of amphiphilic POSS‐containing poly(N, N‐dimethylaminoethyl methacrylate) diblock copolymers, PHEMAPOSS‐b‐PDMAEMA. PHEMAPOSS‐b‐PDMAEMA block copolymers can self‐assemble into a plethora of morphologies ranging from irregular assembled aggregates to core‐shell spheres and further from complex spheres (pearl‐necklace‐liked structure) to large compound vesicles. The thermo‐ and pH‐responsive behaviors of the micelles were also investigated by dynamic laser scattering, UV spectroscopy, SEM, and TEM. The results reveal the reversible transition of the assembled morphologies from spherical micelles to complex micelles was realized through acid‐base control. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2014 , 52, 2669‐2683     

One‐pot synthesis of hyperbranched glycopolymers by RAFT polymerization

Soluble hyperbranched glycopolymers were prepared by copolymerization of glycan monomers with reversible addition‐fragmentation chain transfer polymerization (RAFT) inimers in a simple one‐pot reaction. Two novel RAFT inimers, 2‐(methacryloyloxy)ethyl 4‐cyano‐4‐(phenylcarbonothioylthio)pentanoate (MAE‐CPP) and 2‐(3‐(benzylthiocarbonothioylthio)propanoyloxy)ethyl acrylate (BCP‐EA) were synthesized and used to prepare hyperbranched glycopolymers. Two types of galactose‐based saccharide monomers, 6‐O‐methacryloyl‐1,2:3,4‐di‐O‐isopropylidene‐D ‐galactopyranose (proGal‐M) and 6‐O‐(2′‐acrylamido‐2′‐methylpropanoate)‐1,2:3,4‐di‐O‐isopropylidene‐D ‐galactopyranose (proGal‐A), containing a methacrylate and an acrylamide group, respectively, were also synthesized and polymerized under the mediation of the MAE‐CPP and BCP‐EA inimers, respectively. In addition, hyperbranched poly(proGal‐M), linear poly(proGal‐A), and hyperbranched poly(proGal‐A) were generated and their polymerization kinetics were studied and compared. An unexpected difference was observed in the kinetics between the two monomers during polymerization: the relationship between polymerization rate and concentration of inimer was totally opposite in the two monomer–inimer systems. Branching analysis was conducted by using degree of branching (DB) as the measurement parameter. As expected, a higher DB occurred with increased inimer content. Furthermore, these polymers were readily deprotected by hydrolysis in trifluoroacetic acid solution resulting in water‐soluble polymers. The resulting branched glycopolymers have potential as biomimetics of polysaccharides. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012     

Latices of poly(fluoroalkyl mathacrylate)‐b‐poly(butyl methacrylate) copolymers prepared via reversible addition–fragmentation chain transfer polymerization

Poly(fluoroalkyl mathacrylate)‐block‐poly(butyl methacrylate) diblock copolymer latices were synthesized by a two‐step process. In the first step, a homopolymer end‐capped with a dithiobenzoyl group [poly(fluoroalkyl mathacrylate) (PFAMA) or poly(butyl methacrylate) (PBMA)] was prepared in bulk via reversible addition–fragmentation chain transfer (RAFT) polymerization with 2‐cyanoprop‐2‐yl dithiobenzoate as a RAFT agent. In the second step, the homopolymer chain‐transfer agent (macro‐CTA) was dissolved in the second monomer, mixed with a water phase containing a surfactant, and then ultrasonicated to form a miniemulsion. Subsequently, the RAFT‐mediated miniemulsion polymerization of the second monomer (butyl methacrylate or fluoroalkyl mathacrylate) was carried out in the presence of the first block macro‐CTA. The influence of the polymerization sequence of the two kinds of monomers on the colloidal stability and molecular weight distribution was investigated. Gel permeation chromatography analyses and particle size results indicated that using the PFAMA macro‐CTA as the first block was better than using the PBMA RAFT agent with respect to the colloidal stability and the narrow molecular weight distribution of the F‐copolymer latices. The F‐copolymers were characterized with ¹H NMR, ¹⁹F NMR, and Fourier transform infrared spectroscopy. Comparing the contact angle of a water droplet on a thin film formed by the fluorinated copolymer with that of PBMA, we found that for the diblock copolymers containing a fluorinated block, the surface energy decreased greatly, and the hydrophobicity increased. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 471–484, 2007     

Reversible addition–fragmentation chain transfer polymerization of 2‐naphthyl acrylate with 2‐cyanoprop‐2‐yl 1‐dithionaphthalate as a chain‐transfer agent

The reversible addition–fragmentation chain transfer (RAFT) polymerizations of 2‐naphthyl acrylate (2NA) initiated by 2,2′‐azobisisobutyronitrile were investigated with 2‐cyanoprop‐2‐yl 1‐dithionaphthalate (CPDN) as a RAFT agent at various temperatures in a benzene solution. The results of the polymerizations showed that 2NA could be polymerized in a controlled way by RAFT polymerization with CPDN as a RAFT agent; the polymerization rate was first‐order with respect to the monomer concentration, and the molecular weight increased linearly with the monomer conversion. The polydispersities of the polymer were relatively low up to high conversions in all cases. The chain‐extension reactions of poly(2‐naphthyl acrylate) (P2NA) with methyl methacrylate and styrene successfully yielded poly(2‐naphthyl acrylate)‐b‐poly(methyl methacrylate) and poly(2‐naphthyl acrylate)‐b‐polystyrene block polymers, respectively, with narrow polydispersities. The P2NA obtained by RAFT polymerization had a strong ultraviolet absorption at 270 nm, and the molecular weights had no apparent effect on the ultraviolet absorption intensities; however, the fluorescence intensity of P2NA increased as the molecular weight increased and was higher than that of 2NA. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 2632–2642, 2005     

Novel perfluorocyclobutyl aryl ether‐based well‐defined amphiphilic block copolymer

A series of fluorine‐containing amphiphilic diblock copolymers comprising hydrophobic poly(p‐(2‐(p‐tolyloxy)perfluorocyclobutoxy)phenyl methacrylate) (PTPFCBPMA) and hydrophilic poly(2‐(diethylamino)ethyl methacrylate) (PDEAEMA) segments were synthesized via successive reversible addition fragmentation chain transfer (RAFT) polymerizations. RAFT homopolymerization of p‐(2‐(p‐tolyloxy)perfluorocyclobutoxy)phenyl methacrylate was first initiated by 2,2′‐azobisisobutyronitrile using cumyl dithiobenzoate as chain transfer agent, and the results show that the procedure was conducted in a controlled way as confirmed by the fact that the number‐average molecular weights increased linearly with the conversions of the monomer while the polydispersity indices kept below 1.30. Dithiobenzoate‐capped PTPFCHPMA homopolymer was then used as macro‐RAFT agent to mediate RAFT polymerization of 2‐(diethylamino)ethyl methacrylate, which afforded PTPFCBPMA‐b‐PDEAEMA amphiphilic diblock copolymers with different block lengths and narrow molecular weight distributions (M_w/M_n ≤ 1.28). The critical micelle concentrations of the obtained amphiphilic diblock copolymers were determined by fluorescence spectroscopy technique using N‐phenyl‐1‐naphthylamine as probe. The morphology and size of the formed micelles were investigated by transmission electron microscopy and dynamic light scattering, respectively. © 2011 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2011     

Synthesis and polymerization of phosphorus‐containing acrylates

Novel phosphorus‐containing acrylate monomers were synthesized by two different routes. The first involved the reaction of ethyl α‐chloromethyl acrylate and t‐butyl α‐bromomethyl acrylate with diethylphosphonoacetic acid. The monomers were bulk‐ and solution‐polymerized at 56–64 °C with 2,2′‐azobisisobutyronitrile. The ethyl ester monomer showed a high crosslinking tendency under these conditions. The selective hydrolysis of the ethyl ester phosphonic ester compound was carried out with trimethylsilyl bromide, producing a phosphonic acid monomer. In the second route, ethyl α‐hydroxymethyl acrylate and t‐butyl α‐hydroxymethyl acrylate were reacted with diethylchlorophosphate. The bulk homopolymerization and copolymerization of these monomers with methyl methacrylate and 2,2′‐azobisisobutyronitrile gave soluble polymers. The attempted hydrolysis of the monomers was unsuccessful because of the loss of the diethylphosphate group. The relative reactivities of the monomers in the photopolymerizations were also compared. The ethyl α‐hydroxymethyl acrylate/diethylphosphonic acid monomer showed higher reactivity than the other monomers, which may explain the crosslinking during the polymerization of this monomer. The reactivities of other derivatives were similar, but the rates of polymerization were slow in comparison with those of methyl methacrylate. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 3221–3231, 2002     

Synthesis of poly(tert‐butyl acrylate‐block‐vinyl acetate) copolymers by combining ATRP and RAFT polymerizations

The synthesis of poly(tert‐butyl acrylate‐block‐vinyl acetate) copolymers using a combination of two living radical polymerization techniques, atom transfer radical polymerization (ATRP) and reversible addition‐fragmentation chain transfer (RAFT) polymerization, is reported. The use of two methods is due to the disparity in reactivity of the two monomers, viz. vinyl acetate is difficult to polymerize via ATRP, and a suitable RAFT agent that can control the polymerization of vinyl acetate is typically unable to control the polymerization of tert‐butyl acrylate. Thus, ATRP was performed to make poly(tert‐butyl acrylate) containing a bromine end group. This end group was subsequently substituted with a xanthate moiety. Various spectroscopic methods were used to confirm the substitution. The poly(tert‐butyl acrylate) macro‐RAFT agent was then used to produce (tert‐butyl acrylate‐block‐vinyl acetate). © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 7200–7206, 2008     

RAFT made methacrylate copolymers for reversible pH‐responsive nanoparticles

In this study, we designed and investigated pH‐responsive nanoparticles based on different ratios of monomers with primary, secondary or tertiary amino groups. For this purpose, copolymers of methyl methacrylate (MMA) with different compositions of amino methacrylates (2‐(dimethylamino)ethyl methacrylate (DMAEMA), 2‐(tert‐butylamino)ethyl methacrylate (tBAEMA) and 2‐aminoethyl methacrylate hydrochloride (AEMA·HCI)) were synthesized using the reversible addition‐fragmentation chain transfer (RAFT) polymerization process. The controlled nature of the radical polymerization was demonstrated by kinetic studies. All copolymers show low dispersities (?_M < 1.2) with amino contents between 9 and 21 mol %. For the nanoparticle formation, nanoprecipitation with subsequent solvent evaporation was used. All suspensions were characterized by dynamic light scattering (DLS) and scanning electron microscopy (SEM). Different initial conditions of the formulations resulted in differently sized nanoparticles that have monomodal size distributions, relatively narrow polydispersity index (PDI) values and positive zeta potential values. The pH‐stability test results demonstrated that, depending on the structure and amount of the amino content, the obtained nanoparticles reveal a reversible pH‐response, such as dissolution at acidic pH values. The ability of the nanoparticles to encapsulate guest molecules was confirmed by pyrene fluorescence studies. The cytotoxicity assay results showed that the nanoparticles did not have any significant cytotoxic effect. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2015 , 53, 2711–2721     

Development of reactive methacrylates based on glycidyl methacrylate

Six methacrylate monomers have been synthesized for use as reactive diluents in dental composites and evaluated to investigate the relationship between molecular structure and monomer reactivity. Four were synthesized by reactions of glycidyl methacrylate (GMA) with various acids, 2‐(2‐methoxyethoxy)acetic acid ( 1 ), 2‐(2‐(2‐methoxyethoxy)ethoxy)acetic acid ( 2 ), cyanoacetic acid ( 3 ), and benzoic acid ( 4 ); others were synthesized by reactions of GMA with diethyl hydrogen phosphate ( 5 ) or methanol ( 6 ). Monomers 1 and 2 are novel, 3 seems to be novel, 4 and 6 were synthesized via a novel method, and the synthesis of 5 was described in the literature. The monomers showed high crosslinking tendencies during thermal bulk polymerizations. The photo‐, homo‐, and copolymerization behavior of the monomers with 2,2‐bis[4‐(2‐hydroxy‐3‐methacryloyloxy)phenyl]propane (Bis‐GMA) were investigated. The maximum rate of polymerizations of monomers 2 – 6 was found to be greater than triethyleneglycol dimethacrylate, Bis‐GMA, 2‐hydroxyethyl methacrylate, and glycerol dimethacrylate. For the more reactive monomers ( 2 , 3 , and 4 ), the oxygen sensitivity of polymerization was found to be low due to a hydrogen abstraction/chain transfer reaction. The computationally calculated dipole moment and lowest unoccupied molecular orbital energies indicated that there seems to be a correlation between these quantities and reactivity for ester linked monomers ( 1 – 5 ), which was also supported by ¹³C NMR data. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 3787–3796, 2010     

SET‐RAFT of MMA mediated by ascorbic acid‐activated copper oxide

In this work, cupric oxide (CuO) or cuprous oxide (Cu₂O) was used as the catalyst for the single electron transfer‐reversible addition‐fragmentation chain transfer (SET‐RAFT) polymerization of methyl methacrylate in the presence of ascorbic acid at 25 °C. 2‐Cyanoprop‐2‐yl‐1‐dithionaphthalate (CPDN) was used as the RAFT agent. The polymerization occurred smoothly after an induction period arising from the slow activation of CuO (or Cu₂O) and the “initialization” process in RAFT polymerization. The polymerizations conveyed features of “living”/controlled radical polymerizations: linear evolution of number‐average molecular weight with monomer conversion, narrow molecular weight distribution, and high retention of chain end fidelity. From the polymerization profile, it was deduced that the polymerization proceeded via a conjunct mechanism of single electron transfer‐living radical polymerization (SET‐LRP) and RAFT polymerization, wherein CPDN acting as the initiator for SET‐LRP and chain transfer agent for RAFT polymerization. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012