Long-range ordering in the Bi1−xAexFeO3−x/2 perovskites: Bi1/3Sr2/3FeO2.67 and Bi1/2Ca1/2FeO2.75

Two-ordered perovskites, Bi_1/3Sr_2/3FeO_2.67 and Bi_1/2Ca_1/2FeO_2.75, have been stabilized and characterized by transmission electron microscopy, Mössbauer spectroscopy and X-ray powder diffraction techniques. They both exhibit orthorhombic superstructures, one with a≈b≈2a_p and c≈3a_p (S.G.: Pb2n or Pbmn) for the Sr-based compound and one with a≈b≈2a_p and c≈8a_p (S.G.: B222, Bmm2, B2mm or Bmmm) for the Ca-based one. The high-resolution transmission electron microscopy (HRTEM) images evidence the existence of one deficient [FeO_x]_∞ layer, suggesting that Bi_1/3Sr_2/3FeO_2.67 and Bi_1/2Ca_1/2FeO_2.75 behave differently compared to their Ln-based homolog. The HAADF-STEM images allow to propose a model of cation ordering on the A sites of the perovskite. The Mössbauer analyses confirm the trivalent state of iron and its complex environment with three types of coordination. Both compounds exhibit a high value of resistivity and the inverse molar susceptibility versus temperature curves evidence a magnetic transition at about 730 K for the Bi_1/3Sr_2/3FeO_2.67 and a smooth reversible transition between 590 and 650 K for Bi_1/2Ca_1/2FeO_2.75.     

A structural study of the perovskite series Ca1−xNaxTi1−xTaxO3

Compounds in the solid solution series Ca_1−xNa_xTi_1−xTa_xO₃ were synthesized at 1300 °C, followed by annealing at 850 °C or 800 °C with quenching and/or slow cooling to room temperature. Rietveld refinement of their powder X-ray diffraction patterns show that all compounds are single-phase ternary perovskites which adopt the space group Pbnm (a≈b≈√2a_p; c≈2a_p; Z=4) at ambient conditions. The unit cell parameters and cell volumes of the compounds increase regularly with increasing values of x. The coordination of the A-site cations changes throughout the series from eight for CaTiO₃ to nine for NaTaO₃. Compounds with 0?x ?0.4 have A-site cations in eight fold coordination, whereas the coordination of those with 0.4<x<0.9 is ambiguous. Analysis of the crystal chemistry of the compounds shows that the change in coordination at x=0.4 is related to the departure of the B-site cations from the second coordination sphere of the A-site cations, as in compounds with x>0.4 the A-^IIO distances become less than the A-B intercation distances. Contemporaneous with these coordination changes, the tilt angles of the BO₆ polyhedra decrease with increasing values of x. This solid solution series is unusual in that these structural and coordination changes occur regardless that Goldschmidt tolerance factors remain essentially constant at approximately 0.89, and observed tolerance factors, assuming eight fold coordination of the A-site cations, range only from 0.91 to 0.93 (0?x?0.8).     

High Lithium Capacity MxV2O5Ay·nH2O for Rechargeable Batteries

The aqueous synthesis and electrochemical properties of nanocrystalline M_xV₂O₅A_y·nH₂O are described. It is easily and quickly prepared by precipitation from acidified vanadate solutions. M_xV₂O₅A_y·nH₂O has been characterized by X-ray powder diffraction, electron microscopy, TGA, chemical analyses, and electrochemical studies. The atomic structure is related to that of xerogel-derived V₂O₅·nH₂O. In M_xV₂O₅A_y·nH₂O, M is a cation from the starting vanadate salt and A is an anion from the mineral acid. This material exhibits high, reversible Li capacity and may be considered for use in a cathode in primary and secondary batteries. The lithium capacity of an electrode composed of M_xV₂O₅A_y·nH₂O/EPDM/carbon (88/4/8) is ∼380(mA h)/g (C/80 rate) and the energy density is ∼1000(W h)/kg (120-μm-thick cathode, 4-1.5 V, versus Li metal anode). Critical parameters identified in the synthesis of M_xV₂O₅A_y·nH₂O, with respect to achieving high Li-ion insertion capacity, are acid/vanadium ratio, starting vanadate salt, and temperature. Inclusion of carbon black in the synthesis yields a composite that maintains the high Li capacity, lowers the electrochemical-cell polarization, and preserves the lithium capacity at higher discharge rates. Li-ion coin cells, using pre-lithiated graphite anodes, exhibit electrochemical performance comparable to that of Li-metal coin cells.     

Structure refinement, dielectric, pyroelectric and Raman characterizations of Ba1−xLax(1−y)/2Euxy/2Nax/2TiO3 solid solution

The perovskite-type oxides Ba_1−xLa_x(1−y)/2Eu_xy/2Na_x/2TiO₃ (0?x?0.5 and xy=0.04) were synthesized and characterized by X-ray diffraction as well as dielectric measurements and Raman spectroscopy. The crystal structure of these ceramics has been determined by the Rietveld refinement powder X-ray diffraction data at room temperature. These compounds crystallize at room temperature in tetragonal space group P4mm for 0?x?0.1 and in the cubic group for 0.2?x?0.5. The phase transition temperature T_C (or T_m) decreases as x content increases. The degree of diffuseness of the phase transition is more pronounced for higher x content, implying the existence of a composition-induced diffuse phase transition of the ceramics with x?0.1. The evolution of the Raman spectra was studied as a function of various compositions at room temperature. The polarization state was checked by pyroelectric measurements.     

Electronic and magnetic properties of LaNi1−xCoxO3, LaCo1−xFexO3 and LaNi1−xFexO3

LaNi_1?xCo_xO₃ shows itinerant d-electron behavior similar to LaNiO₃ up to x = 0.5. In the range 0.5 < x < 1.0, the cobalt spin state equilibrium is markedly affected; the localized-itinerant electron transition of LaCoO₃ is not seen when x < 0.95. In LaCo_1?xFe_xO₃, itinerancy of d-electrons decreases with increase in x and the compositions with x > 0.5 are similar to LaFeO₃. If x > 0.1, the localized-itinerant electron transition is not seen and the cobalt spin state equilibrium is considerably altered. In LaNi_1?xFe_xO₃, itinerancy decreases with increase in x. These observations can be satisfactorily explained in terms of Goodenough's energy band schemes.     

Visible light-sensitive yellow TiO2−xNx and Fe-N co-doped Ti1−yFeyO2−xNx anatase photocatalysts

Nitrogen substituted yellow colored anatase TiO_2−xN_x and Fe-N co-doped Ti_1−yFe_yO_2−xN_x have been easily synthesized by novel hydrazine method. White anatase TiO_2−δ and N/Fe-N-doped samples are semiconducting and the presence of ESR signals at g ∼1.994-2.0025 supports the oxygen vacancy and g∼4.3 indicates Fe³⁺ in the lattice. TiO_2−xN_x has higher conductivity than TiO_2−x and Fe/Fe-N-doped anatase and the UV absorption edge of white TiO_2−x extends in the visible region in N, Fe and Fe-N co-doped TiO₂, which show, respectively, two band gaps at ∼3.25/2.63, ∼3.31/2.44 and 2.8/2.44 eV. An activation energy of ∼1.8 eV is observed in Arrhenius log resistivity vs. 1/T plots for all samples. All TiO₂ and Fe-doped TiO₂ show low 2-propanol photodegradation activity but have significant NO photodestruction capability, both in UV and visible regions, while standard Degussa P-25 is incapable in destroying NO in the visible region The mid-gap levels that these N and Fe-N-doped TiO₂ consist may cause this discrepancy in their photocatalytic activities.     

Tolerance factor rules for Sr1−x−yCaxBayMnO3 perovskites

Synthesis of new perovskite Sr_1−x−yCa_xBa_yMnO_3−δ compounds is described in detail and dependence of their phase stability and structural distortions on the tolerance factor is discussed. Oxygen contents have been measured over extended temperature and composition ranges. Neutron powder diffraction was used to precisely measure the A-O and Mn-O bond lengths and derive accurate interatomic distances [Ca-O], [Sr-O], [Ba-O], and [Mn-O]. By using these parameters instead of tabulated ionic radii we have derived the functional dependence of the tolerance factor t=t(x,y,T,δ) on composition, temperature, and oxygen content. At a fixed oxygen content, the tolerance factor is an increasing function of temperature as a result of greater thermal expansion of the average 〈A-O〉 bond relative to the 〈Mn-O〉 bond. We find that the stability of the perovskite phase at high temperature is governed, as expected, by the magnitude of tolerance factor (t?1) which can be adjusted by controlling the oxygen content 3−δ. This dependence of the tolerance factor on oxygen content and temperature can be utilized to design synthesis conditions for the controlled formation of the new, kinetically stable, perovskite phases.     

The Ba1−ySryMnO3−x system

Subsolidus phase relations at ambient atmospheric pressure and elevated temperatures in the Ba_1?ySr_yMnO_3?x system were investigated by quenching, gravimetric, and X-ray diffraction methods. The system is not binary above ～1035°C because of reactions with atmospheric oxygen. The air isolar, P_O2 = 0.2 atm, was characterized at 1225, 1375, 1490, and 1610°C. Seven oxygen-deficient phases including a perovskite phase characterize the system. Their stability depends on the values of y and x in Ba_1?ySr_yMnO_3?x. The cell dimensions of these phases expand as x increases at fixed y. These seven modifications can be retained in stoichiometric form by oxidation at lower temperatures.     

Synthesis of homologously pure bacteriochlorophyll-e and f analogues from BChls-c/d via transformation of the 7-methyl to formyl group and self-aggregation of synthetic zinc methyl bacteriopheophorbides-c/d/e/f in non-polar organic solvent

Homologously pure methyl bacteriopheophorbides-e and f (BPhes-e/f_M) were prepared from modification of naturally occurring bacteriochlorophylls-c and d (BChls-c/d), respectively, by transformation of the methyl to formyl group at the 7-position. The absolute configuration of the 1-hydroxyethyl group at the 3-position of (Zn-)BPhes-e/f_M was determined from comparison with structurally known BChl-c/d epimers. Visible spectra of synthetic (Zn-)BPhe-c/d/e/f_M showed that the 7¹-oxidation and the 8²/12¹/20-methylation affected Soret, Q_x and Q_y bands of both the monomeric (in a polar organic solvent) and oligomeric species (in a non-polar solvent).     

Nouveaux echangeurs cationiques avec une structure a tunnels entrecroises: Les oxydes A12M33O90 et A12M33O90, 12H2O

New oxides with A₁₂M₃₃O₉₀ formula (A = Rb, Cs, Tl) have been synthesized. They crystallize in the trigonal system and can be described by pyrochlore and A₂M₇O₁₈ phases intergrowth. Cationic ionexchange properties of these compounds are brought out in aqueous solutions and in solid state. So, new hydrated oxides are prepared and their thermal decomposition has been studied. Relations between ionexchange properties and structure are discussed.     

Etude par diffraction neutronique de la phase “Cs4−xYb12F40−x” (0 ≤ x ≤ 1): Hypothèse structurale

The structure of the phase Cs_4?xYb₁₂F_40?x(0 ≤ x ≤ 1) has been determined by a single-crystal neutron diffraction study. It has been solved in the space group P6₃mc and refined to the best R factor of 0.0535 for the formula Cs_3.4Yb₁₂F_39.4 (324 independent reflections). Three edge-sharing pentagonal bipyramids surrounding three ytterbium atoms form Yb₃F₁₆ groups and the structure is described as the superposition, according to the sequence A₁A₂B₁B₂A₁A₂…, of sheets of corner-sharing Yb₃F₁₆ groups with a possible transformation of bipyramids into octahedra in the A₂ and B₂ layers. These sheets are joined together by the axial fluorine atoms of the bipyramids or octahedra. Cesium atoms are located in the tunnels formed by their stacking. It is shown that the Cs_4?xYb₁₂F_40?x phase (0 ≤ x ≤ 1) is an intermediate step of the Cs_4?xYb₁₂F_40?x solid solution observed with 0 ≤ x ≤ 2 and corresponds to a superstructure of the high-temperature YbF₃ phase.     

Synthesis and properties of the Co7Se8−xSx and Ni7Se8−xSx solid solutions

We report the synthesis and elementary properties of the Co₇Se_8−xS_x (x=0-8) and Ni₇Se_8−xS_x (x=0-7) solid solutions. Both systems form a NiAs-type structure with metal vacancies. In general, the lattice parameters decrease with increasing x, but in the Ni₇Se_8−xS_x system c increases on going from x=5 to 7. Magnetic susceptibility measurements show that all samples exhibit temperature-independent paramagnetism from 25-250 K. Samples within the Co₇Se_8−xS_x system, as well as Ni₇Se₈ and Ni₇SeS₇, were found to be poor metals with resistivities of ∼0.20 and ∼0.06 mΩ cm at 300 K, respectively. The Sommerfeld constant (γ) was determined from specific heat measurements to be ∼13 mJ/mol_CoK² and ∼7 mJ/mol_NiK² for Co₇Se_8−xS_x and Ni₇Se_8−xS_x, respectively.     

Phase segregation in the Gd1−xSrxFeO3−δ series

Gd_1−xSr_xFeO_3−δ ferrites have been studied by means of X-ray powder diffraction in the whole composition range. Single-phase solid solution is found for x<0.09 and for x>0.63. At intermediate Sr content, phase segregation takes place. Compounds with x?0.05 crystallize in the orthorhombic structure, space group Pbnm. Oxygen-deficient Gd_1−xSr_xFeO_3−δ with x?2/3 are cubic or nearly cubic. The oxygen vacancies stabilize the cubic phase for x=2/3 whereas highly oxidized samples show an orthorhombic distortion, which has not been observed earlier. Magnetic and electrical properties have been measured for the single-phase solid solutions. Gd_1−xSr_xFeO_3−δ compounds with x?2/3 order antiferromagnetically below ∼100 K. In the paramagnetic region, their susceptibility follows the Curie-Weiss law in all but SrFeO_2.96 compound. These ferrites show semiconducting behavior in the electrical transport likely related to atomic disorder. We find that the conductivity activation energy becomes larger by increasing either the Gd content or the oxygen vacancies.     

Local environment in Ba2In2−xWxO5+3x/2 oxide ion conductors

The actual oxygen environment of the tungsten dopant in the Ba₂In_2−xW_xO_5+3x/2 solid solution was revealed by combining X-ray absorption spectroscopy at the tungsten L_I and L_III edges and at the indium L_I edge. Whatever the substitution ratio, the tungsten atoms exhibit a regular octahedral environment. When the substitution ratio increases, the oxygen vacancies are progressively filled until their total occupancy for x=2/3. For x?0.3, the perovskite structure is stabilised; the tungsten atoms are randomly distributed in the structure. Although X-ray diffraction revealed a cubic symmetry for these compositions, a local distortion of the indium environment is observed when a tungsten atom is in its surrounding.     

Luminescent and structural properties of the series Ba6−xEuxTi2+xTa8−xO30 and Ba4−yKyEu2Ti4−yTa6+yO30

The series Ba_6−xEu_xTi_2+xTa_8−xO₃₀ and Ba_4−yK_yEu₂Ti_4−yTa_6+yO₃₀ have been synthesized at 1400°C in air. They exhibit efficient excitation at about 400 nm and typical emission of Eu³⁺ at about 580-620 nm, form solid solutions within 0.0?x?2.0 and 0?y?4 respectively, and crystallized in P4/mbm at room temperature with Eu atoms occupied at centrosymmetric site (0, 0, 0). Their conductivity is very low (2.8×10⁻⁶ Ω⁻¹ cm⁻¹ at 740°C for Ba₆Ti₂Ta₈O₃₀).     

HRTEM study of cation-deficient perovskite-related AnBn−δO3n (n?4δ) microphases in the Ba5Nb4O15-BaTiO3 system

The occurrence of coherent intergrowths of cation-deficient perovskites in the Ba₅Nb₄O₁₅-BaTiO₃ system has been examined by high-resolution transmission electron microscopy and selected area electron diffraction. Because of their structural similarity, the simple members Ba₅Nb₄O₁₅ (n=5) and Ba₆TiNb₄O₁₈ (n=6) form coherent intergrowths—noted 5^P6¹—by the juxtaposition along the c-axis of P perovskite-like blocks n=5 and one perovskite-like block n=6, with P=1, 2 and 3. More generally, the ability to form intergrowths in the hexagonal perovskite systems is discussed considering the structural characteristics of the simple members. Examples taken from various systems show that the formation of such intergrowths is highly dependent on the size of the A cation present in simple members.     

Thermoelectric properties of polycrystalline La1−xSrxCoO3

Thermoelectric properties of polycrystalline La_1−xSr_xCoO₃, where Sr²⁺ is substituted in La³⁺ site in perovskite-type LaCoO₃, have been investigated. Sr-doping increases the electrical conductivity (σ) of La_1−xSr_xCoO₃, and also decreases the Seebeck coefficient (S) for 0.01?x?0.40. A Hall coefficient measurement reveals that the increase in electrical conductivity arises from increases in both carrier concentration and the Hall mobility. The decrease in the Seebeck coefficient is caused by a decrease in carrier effective mass as well as increase in carrier concentration. The highest power factor (σS²) is 3.7×10⁻⁴ W m⁻¹ K⁻² at 250 K for x=0.10. The thermal conductivity (κ) is about 2 W m⁻¹ K⁻¹ at 300 K for 0?x?0.04, and increases for x?0.05 because of an increase in heat transport by conductive carrier. The thermoelectric properties of La_1−xSr_xCoO₃ are improved by Sr-doping, and the figure of merit (Z=σS² κ⁻¹) reaches 1.6×10⁻⁴ K⁻¹ for x=0.06 at 300 K (ZT=0.048). For heavily Sr-doped samples, the thermoelectric properties diminish mainly because of the decrease in the Seebeck coefficient and the increase in thermal conductivity.     

Structural Characterization of the Complex Perovskites Ba1−xLaxTi1−xCrxO3

The series Ba_1−xLa_xTi_1−xCr_xO₃ (0≤x≤1) was synthesized at 1400°C for about 60 h. Their structure was carefully analyzed by the use of powder X-ray diffraction and Rietveld analysis software GSAS (General Structure Analysis System). Four solid solutions are found in this series: tetragonal solid solution Ba_1−xLa_xTi_1−xCr_xO₃ (0≤x≤0.029), cubic solid solution Ba_1−xLa_xTi_1−xCr_xO₃ (0.0365≤x≤0.600), rhombohedral solid solution Ba_1−xLa_xTi_1−xCr_xO₃ (0.700≤x≤0.873), and orthorhombic solid solution Ba_1−xLa_xTi_1−xCr_xO₃ (0.956≤x≤1). There are corresponding two-phase regions between the adjacent two solid solutions. The detailed lattice parameters are presented. The relationship between the lattice parameters and the composition of the solid solutions is developed.     

Tl1−xNaxNb2PO8 and Related Compounds, Isostructural with Ca0.5+xCs2Nb6P3O24

Compounds A_2/3A′_1/3M₂XO₈ (A=Tl, Rb, Cs; A′=Na, Ag; M=Nb, Ta; X=P, As) have been synthesized using the ceramic method. The sodium and potassium compounds (A= Na and K) have been prepared by an ion exchange reaction starting from their thallium analogues. These materials are isotypic with Tl_1−xNa_xNb₂PO₈ (x=0.21) the structure of which has been determined by using X-ray single-crystal data. The space group is R32, the cell constants are a_H=13.369(2), c_H=10.324(3) Å and z=9. This compound is isostructural with Ca_0.5+xCs₂ Nb₆P₃O₂₄. Its three-dimensional framework [Nb₂PO₈]_n, built up from NbO₆ octahedra and corner-sharing PO₄ tetrahedra, delimits tunnels running along c_H and cavities accommodating Tl⁺ and Na⁺ cations, respectively. The K_2/3Na_1/3Nb₂PO₈ structure, refined using X-ray powder data, showed that K⁺ cations are spread like the Tl+ ones over many sites, but more excentred from the tunnel axis. The isotypy of these compounds is also revealed by the similarity of the infrared and Raman spectra. The nonlinear optical study showed a behavior similar to that of the KDP for all the compounds. The ionic conductivity measurements gave high activation energies and low conductivity values for these materials.