Preparation and characterization of lithium ion-conducting glass-ceramics in the Li1 + xCrxGe2 − x(PO4)3 system

Li₂O–Cr₂O₃–GeO₂–P₂O₅ based glasses were synthesized by a conventional melt-quenching method and successfully converted into glass-ceramics through heat treatment. Experimental results of DTA, XRD, ac impedance techniques and FESEM indicated that Li_1.4Cr_0.4Ge_1.6(PO₄)₃ glass-ceramics treated at 900 °C for 12 h in the Li_1 + xCr_xGe_2 − x(PO₄)₃ (x = 0–0.8) system exhibited the best glass stability against crystallization and the highest ambient conductivity value of 6.81 × 10⁻⁴ S/cm with an activation energy as low as 26.9 kJ/mol. In addition, the Li_1.4Cr_0.4Ge_1.6(PO₄)₃ glass-ceramics displayed good chemical stability against lithium metal at room temperature. The good thermal and chemical stability, excellent conducting property, easy preparation and low cost make it promising to be used as solid-state electrolytes for all-solid-state lithium batteries.     

Ternary [Al2O3–electrolyte–Cu] species: EPR spectroscopy and surface complexation modeling

Cu²⁺ binding on γ-Al₂O₃ is modulated by common electrolyte ions such as Mg²⁺, , and in a complex manner: (a) At high concentrations of electrolyte ions, Cu²⁺ uptake by γ-Al₂O₃ is inhibited. This is partially due to bulk ionic strength effects and, mostly, due to direct competition between Mg²⁺ and Cu²⁺ ions for the SO⁻ surface sites of γ-Al₂O₃. (b) At low concentrations of electrolyte ions, Cu²⁺ uptake by γ-Al₂O₃ can be enhanced. This is due to synergistic coadsorption of Cu²⁺ and electrolyte anions, and _. This results in the formation of ternary surface species (SOH₂SO₄Cu)⁺, (SOH₂PO₄Cu), and (SOH₂HPO₄Cu)⁺ which enhance Cu²⁺ uptake at pH < 6. The effect of phosphate ions may be particularly strong resulting in a 100% Cu uptake by the oxide surface. (c) EPR spectroscopy shows that at pH  pH_PZC, Cu²⁺ coordinates to one SO⁻ group. Phosphate anions form stronger, binary or ternary, surface species than sulfate anions. At pH  pH_PZC Cu²⁺ may coordinate to two SO⁻ groups. At pH  pH_PZC electrolyte ions and are bridging one O-atom from the γ-Al₂O₃ surface and one Cu²⁺ ion forming ternary [γ-Al₂O₃/elecrolyte/Cu²⁺] species.     

High performance protonic ceramic membrane fuel cells (PCMFCs) with Ba0.5Sr0.5Zn0.2Fe0.8O3−δ perovskite cathode

Protonic ceramic membrane fuel cells (PCMFCs) based on proton-conducting electrolytes have attracted much attention because of many advantages, such as low activation energy and high energy efficiency. BaZr_0.1Ce_0.7Y_0.2O_3−δ (BZCY7) electrolyte based PCMFCs with stable Ba_0.5Sr_0.5Zn_0.2Fe_0.8O_3−δ (BSZF) perovskite cathode were investigated. Using thin membrane BZCY7 electrolyte (about 15 μm in thickness) synthesized by a modified Pechini method on NiO-BZCY7 anode support, PCMFCs were assembled and tested by selecting stable BSZF perovskite cathode. An open-circuit potential of 1.015 V, a maximum power density of 486 mW cm⁻², and a low polarization resistance of the electrodes of 0.08 Ω cm² was achieved at 700 °C. The results have indicated that BZCY7 proton-conducting electrolyte with BSZF cathode is a promising material system for the next generation solid oxide fuel cells.     

Pulsed laser-induced oxygen deficiency at TiO2 surface: Anomalous structure and electrical transport properties

We have studied pulsed laser-induced oxygen deficiencies at rutile TiO₂ surfaces. The crystal surface was successfully reduced by excimer laser irradiation, and an oxygen-deficient TiO_2−δ layer with 160 nm thickness was formed by means of ArF laser irradiation at 140 mJ/cm² for 2000 pulses. The TiO_2−δ layer fundamentally maintained a rutile structure, though this structure was distorted by many stacking faults caused by the large oxygen deficiency. The electrical resistivity of the obtained TiO_2−δ layer exhibited unconventional metallic behavior with hysteresis. A metal–insulator transition occurred at 42 K, and the electrical resistivity exceeded 10⁴ Ω cm below 42 K. This metal–insulator transition could be caused by bipolaronic ordering derived from Ti–Ti pairings that formed along the stacking faults. The constant magnetization behavior observed below 42 K is consistent with the bipolaronic scenario that has been observed previously for Ti₄O₇. These peculiar electrical properties are strongly linked to the oxygen-deficient crystal structure, which contains many stacking faults formed by instantaneous heating during excimer laser irradiation.     

Electronic spectra of the linear magnesium-containing carbon chains MgC2nH (n = 1–5): A CASPT2 study

Complete active space self-consistent-field (CASSCF) approach has been used for the geometry optimization of the X²Σ⁺ and A²Π electronic states for the linear magnesium-containing carbon chains MgC_2nH (n = 1–5). Multireference second-order perturbation theory (CASPT2) has been used to calculate the vertical excitation energies from the ground to selected seven excited states, as well as the potential energy curves of two ²Σ⁺ and two ²Π electronic states. The studies indicate that the vertical excitation energies of the A²Π ← X²Σ⁺ transition for MgC_2nH (n = 1–5) are 2.837, 2.793, 2.767, 2.714, and 2.669 eV, respectively, showing remarkable linear size dependence. Compared with the previous TD-DFT and RCCSD(T) results, our estimates for MgC_2nH (n = 1–3) are in the best agreement with the available observed data of 2.83, 2.78, and 2.74 eV, respectively. In addition, the dissociation energies in MgC_2nH (n = 1–5) are also been evaluated.     

Synthesis, Structure, and Physical Studies of the New β-LiVOAsO4 Compound

Two new compounds of the A_xMOXO₄ family, β-LiVOAsO₄ and β-VOAsO₄, have been synthesized by solid state reaction and electrochemical lithium deintercalation from β-LiVOAsO₄, respectively. Both compounds are isostructural and are built like other β-VOXO₄ (X=S, P) by (VO₅)_∞ chains of distorted VO₆ octahedra connected via corner-shared AsO₄ tetrahedra. For β-LiVOAsO₄ the additional Li⁺ ions occupy chains of edge-shared octahedra running perpendicularly to the (VO₅)_∞ chains. The one-dimensional antiferromagnetic behavior suggested by the structure has been experimentaly confirmed. It is shown that lithium deintercalation occurs through a first-order transition at 4.02 V vs Li⁺/Li⁰. From chemical bond considerations it is shown why the redox potential of a given transition element M in a six-fold coordination involving (M=O)^m+ units lies between those observed in oxides and in M₂(XO₄)₃ compounds with (XO₄)ⁿ⁻ oxo anions (X=S, P, As).     

Solubility of (UO2)3(PO4)2?4H2O in H+-Na+-OH?-H2PO?4-HPO2?4-PO3?4-H2O and Its Comparison to the Analogous PuO2 +2 System

The objectives of this study were to address uncertainties in the solubility product of (UO₂)₃(PO₄)₂⋅4H₂O(c) and in the phosphate complexes of U(VI), and more importantly to develop needed thermodynamic data for the Pu(VI)-phosphate system in order to ascertain the extent to which U(VI) and Pu(VI) behave in an analogous fashion. Thus studies were conducted on (UO₂)₃(PO₄)₂⋅4H₂O(c) and (PuO₂)₃(PO₄)₂⋅4H₂O(am) solubilities for long-equilibration periods (up to 870 days) in a wide range of pH values (2.5 to 10.5) at fixed phosphate concentrations of 0.001 and 0.01 M, and in a range of phosphate concentrations (0.0001–1.0 M) at fixed pH values of about 3.5. A combination of techniques (XRD, DTA/TG, XAS, and thermodynamic analyses) was used to characterize the reaction products. The U(VI)-phosphate data for the most part agree closely with thermodynamic data presented in Guillaumont et al.,⁽¹⁾ although we cannot verify the existence of several U(VI) hydrolyses and phosphate species and we find the reported value for formation constant of UO₂PO⁻₄ is in error by more than two orders of magnitude. A comprehensive thermodynamic model for (PuO₂)₃(PO₄)₂⋅4H₂O(am) solubility in the H⁺-Na⁺-OH⁻-Cl⁻-H₂PO⁻₄-HPO²⁻₄-PO³⁻₄-H₂O system, previously unavailable, is presented and the data shows that the U(VI)-phosphate system is an excellent analog for the Pu(VI)-phosphate system.     

Preparation and hydrogen permeation of SrCe0.95Y0.05O3−δ asymmetrical membranes

Asymmetrical thin membranes of SrCe_0.95Y_0.05O_3−δ (SCY) were prepared by a conventional and cost-effective dry pressing method. The substrate consisted of SCY, NiO and soluble starch (SS), and the top layer was the SCY. NiO was used as a pore former and soluble starch was used to control the shrinkage of the substrate to match that of the top layer. Crack-free asymmetrical thin membranes with thicknesses of about 50 μm and grain sizes of 5–10 μm were successfully pressed on to the substrates. Hydrogen permeation fluxes (J_H2) of these thin membranes were measured under different operating conditions. At 950 °C, J_H2 of the 50 μm SCY asymmetrical membrane towards a mixture of 80% H₂/He was as high as 7.6 × 10⁻⁸ mol/cm² s, which was about 7 times higher than that of the symmetrical membranes with a thickness of about 620 μm. The hydrogen permeation properties of SCY asymmetrical membranes were investigated and activation energies for hydrogen permeation fluxes were calculated. The slope of the relationship between the hydrogen permeation fluxes and the thickness of the membranes was −0.72, indicating that permeation in SCY asymmetric membranes was controlled by both bulk diffusion and surface reaction in the range investigated.     

Preparation, characterization and the standard enthalpy of formation of La0.95MnO3+δ and Sm0.95MnO3+δ

Among the perovskites, the rare earth manganites find application in several electrochemical devices because of their enhanced thermodynamic stability. In this paper, we present the results obtained on the preparation and characterization of La_0.95MnO_3+δ and Sm_0.95MnO_3+δ which were prepared by the solid state and sol–gel methods. XRD characterization of the manganites indicated that the crystal structure depends on the method of preparation and heat treatments. The ratio of Mn³⁺ to Mn⁴⁺ in these samples also depended on the method of preparation and heat treatments, as indicated by thermogravimetric (TG) and temperature programmed reduction (TPR) studies in Ar + 5% H₂ atmosphere. The standard molar enthalpy of formation, which is a measure of the thermodynamic stability of these compounds were determined using an isoperibol calorimeter.     

Recombination of KrD and XeD ions with electrons

Recombination rate coefficients of protonated and deuterated ions KrH⁺, KrD⁺, XeH⁺ and XeD⁺ were measured using Flowing Afterglow with Langmuir Probe (FALP). Helium at 1600 Pa and at temperature 250 K was used as a buffer gas in the experiments. Kr, Xe, H₂ and D₂ were introduced to a flow tube to form the desired ions. Because of small differences in proton affinities of Kr, D₂ and H₂ mixtures of ions, KrD⁺/D₃⁺ and KrH⁺/H₃⁺ are formed in the afterglow plasma, influencing the plasma decay. To obtain a recombination rate coefficient for a particular ion, the dependencies on partial pressures of gases used in the ion formation were measured. The obtained rate coefficients, α_KrD+(250 K) = (0.9 ± 0.3) × 10⁻⁸ cm³ s⁻¹ and α_XeD+(250 K) = (8 ± 2) × 10⁻⁸ cm³ s⁻¹ are compared with α_KrH+(250 K) = (2.0 ± 0.6) × 10⁻⁸ cm³ s⁻¹ and α_XeH+(250 K) = (8 ± 2) × 10⁻⁸ cm³ s⁻¹.     

Sub- and post-micellar catalytic and inhibitory effects of cetlytrimethylammonium bromide in the permanganate oxidation of phenylalanine

The kinetics of phenylalanine (phe) oxidation by permanganate has been investigated in absence and presence of cetlytrimethylammonium bromide (CTAB) using conventional spectrophotometric technique. The rate shows first- and fractional-order dependence on [MnO₄⁻] and [phe] in presence of CTAB. At lower values of [CTAB] (≤10.0 × 10⁻⁴ mol dm⁻³), the catalytic ability of CTAB aggregates are strong. In contrast, at higher values of [CTAB] (≥10.0 × 10⁻⁴ mol dm⁻³), the inhibitory effect was observed in absence of H₂SO₄. We find that anions (Br⁻, Cl⁻ and NO₃⁻) in the form of sodium salts are strong inhibitors for the CTAB catalyzed oxidation. Kinetic and spectrophotometric evidences for the formation of an intermediate complex and an ion-pair complex between phe and MnO₄⁻, CTAB and MnO₄⁻, respectively, are presented. A mechanism consistent with kinetic results has been discussed. Complex formation constant (K_c) and micellar binding constant (K_s) were calculated at 30 °C and found to be K_c = 319 mol⁻¹ dm⁻³ and K_s = 1127 mol⁻¹ dm⁻³, respectively.     

Crystal structure refinement of basic tellurium nitrate: A reformulation as (Te2O4H)+(NO3)−

Basic tellurium nitrate crystallizes in the space group Pnma witha=14.607 (1),b=8.801 (1), andc=4.4633 (4) Å. Full-matrix least-squares refinement of automatic diffractometer data converged to a residualR=0.036 (R _w =0.046) for 899 independent reflections. A detailed analysis of the structural data leads us to reformulate this compound as (Te₂O₄H)⁺(NO₃)^– with a basic structural element consisting of a charged two-dimensional puckered Te₂O₄H⁺ network with discrete NO₃ ^– anions, an example of apositively-charged network structure.

---

Verfeinerung der Kristallstruktur von basischem Telluriumnitrat. Eine Umformulierung in (Te₂O₄H)⁺(NO₃)^–

Zusammenfassung Basisches Telluriumnitrat kristallisiert in der Raumgruppe Pnma mita=14,607 (1),b=8,801 (1) undc=4,4633 (4) Å. Die verfeinernde Auswertung der Diffraktometerdaten konvergierte zuR=0,036 (R _w =0.046) für 899 unabhängige Reflexe. Eine detaillierte Analyse der Strukturdaten führte zu einer Umformulierung dieser Verbindung als (Te₂O₄H)⁺(NO₃)^–, wobei die Basisstruktur aus einem geladenen, zweidimensionalen, gefalteten Te₂O₄H⁺ Netzwerk mit getrennten NO₃ ^– Anionen besteht. Es stellt dies ein Beispiel einerpositiv geladenen Netzstruktur dar.

     

Self-powdering and nonlinear optical domain structures in ferroelastic β′-Gd2(MoO4)3 crystals formed in glass

Ferroelastic β′-Gd₂(MoO₄)₃, (GMO), crystals are formed through the crystallization of 21.25Gd₂O₃–63.75MoO₃–15B₂O₃ glass (mol%), and two scientific curious phenomena are observed. (1) GMO crystals formed in the crystallization break into small pieces with a triangular prism or pyramid shape having a length of 50–500 μm spontaneously during the crystallizations in the inside of an electric furnace, not during the cooling in air after the crystallization. This phenomenon is called “self-powdering phenomenon during crystallization” in this paper. (2) Each self-powdered GMO crystal grain shows a periodic domain structure with different refractive indices, and a spatially periodic second harmonic generation (SHG) depending on the domain structure is observed. It is proposed from polarized micro-Raman scattering spectra and the azimuthal dependence of second harmonic intensities that GMO crystals are oriented in each crystal grain and the orientation of (MoO₄)²⁻ tetrahedra in GMO crystals changes periodically due to spontaneous strains in ferroelastic GMO crystals.     

Synthesis and ac susceptibility of YCa2Cu3O7−δ

The bulk superconducting YCa₂Cu₃O_7−δ compounds are prepared at an ordinary pressure of oxygen by conventional solid-state reaction method. The formation of sample is tested by means of XRD and is studied for their ac susceptibility below room temperature up to 77.5 K. The samples are found single-phase orthorhombic structure and found superconducting at 83.5 K. It is shown that the analysis is consistent with published data on YBa₂Cu₃O_7−δ oxide superconductor.     

A new generation of cyanide ion-selective membranes for flow injection application: part II. Comparative study of cyanide flow-injection detectors based on thin electroplated silver chalcogenide membranes

Using induced cathodic electrodeposition a number of silver chalcogenide thin layer membranes of non-trivial composition have been synthesized and their performance as ion-selective flow-injection potentiometric detectors (FIPDs) for free cyanide has been critically estimated in the context of the stringent requirements for toxic cyanide environmental monitoring. AgSCN/Ag₂S, Ag₂S, Ag_2+δSe, Ag_2+δSe_1−xTe_x (0 < δ < 0.25 and x ≈ 0.13), Ag₂Se and Ag₂Se_1−xTe_x electroplated membranes were selected for the present performance-based comparative study in order to obtain a feedback information about the effect of membrane composition. Both silver selenide and Te-doped silver selenide membranes, irrespective of their stoichiometry with respect to silver, exhibit the lowest detection limit for CN⁻ (52 ppb) with linear double-Nernstian response down to 130 ppb. The type of chalcogene anion in the membrane composition proves to exert dominant effect on the general performance characteristics of the newly developed FIPDs. The silver stoichiometry (intrinsic defects factor) and the inclusion of Te-dopant (extrinsic defects factor) have more pronounced effect on the profile of the output signal and exert moderate control on the detectors selectivity and baseline stability. This new generation of CN⁻—ion-selective membranes for FIPDs exhibits high selectivity against the common interferents present in cyanide effluents such as SCN⁻, S₂O₃²⁻, Cl⁻ and do not get poisoned in the presence of S²⁻. Moreover, their long-term stability and signal reproducibility, which make redundant the regular day-to-day calibration, coupled with the cost-effective technology for membranes preparation and easy re-generation make them attractive candidates for incorporation into automated in-field devices for in situ cyanide toxic species monitoring.     

Recombination of HCO and DCO ions with electrons

Recombination of HCO⁺ and DCO⁺ ions with electrons was studied in afterglow plasma. The flowing afterglow with Langmuir probe (FALP) apparatus was used to measure the recombination rate coefficients and their temperature dependencies in the range 150–270 K. To obtain a recombination rate coefficient for a particular ion, the dependencies on partial pressures of gases used in the ion formation were measured. The variations of α_HCO⁺(T) and α_DCO⁺(T) seem to obey the power law: α_HCO⁺(T) = (2.0 ± 0.6) × 10⁻⁷ (T/300)^−1.3 cm³ s⁻¹ and α_DCO⁺(T) = (1.7 ± 0.5) × 10⁻⁷ (T/300)^−1.1 cm³ s⁻¹ over the studied temperature range.     

Theoretical investigation on possible mechanisms on regioselective formation of (η-siloxyallyl)tungsten complexes

Selective formation of (η³-siloxyallyl)tungsten complexes by reaction of hydrido(hydrosilylene)tungsten complexes with α,β-unsaturated carbonyl compounds was reported experimentally. The mechanisms have been investigated by employing the model reaction of [Cp(CO)₂(H)WSi(H)–{C(SiH₃)₃}] (R), derived from the original experimental complex Cp′(CO)₂(H)WSi(H)–[C(SiMe₃)₃] (1a, Cp′ = Cp*; 1b, Cp′ = η⁵-C₅Me₄Et), with methyl vinyl ketone, under the aid of the density functional calculations at the b3lyp level of theory. It is theoretically predicted that the route involving migration of the hydride to silicon to afford a 16e intermediate [Cp(CO)₂W–SiH₂–{C(SiH₃)₃}] is inaccessible (route 2), supporting the proposition by experiments. Another route, via [2 + 4] cycloaddition followed by directly Si–H reductive elimination, is theoretically predicted to be accessible (route 1). In route 1, two possible paths with different attacking directions of the oxygen of methyl vinyl ketone at Si (WSi) are put forward. The attack at the Si atom from the hydride (H1) side of the plane W–Si–H1 in R is found to be preferred kinetically. The regioselectivity for formation of (η³-siloxyallyl)tungsten complexes, where only the exo-anti isomer was obtained, is discussed based on the consideration of thermodynamics and kinetics.     

Properties of the perovskites, SrMn1−xFexO3−δ (x=1/3, 1/2, 2/3)

The SrMn_1−xFe_xO_3−δ (x=1/3, 1/2, 2/3) phases have been prepared and are shown by powder X-ray and neutron (for x=1/2) diffraction to adopt an ideal cubic perovskite structure with a disordered distribution of transition-metal cations over the six-coordinate B-site. Due to synthesis in air, the phases are oxygen deficient and formally contain both Fe³⁺ and Fe⁴⁺. Magnetic susceptibility data show an antiferromagnetic transition at 180 and 140 K for x=1/3 and 1/2, respectively and a spin-glass transition at 5, 25, 45 K for x=1/3, 1/2 and 2/3, respectively. The magnetic properties are explained in terms of super-exchange interactions between Mn⁴⁺, Fe^(4+δ)+ and Fe⁽³⁺⁾⁺. The XAS results for the Mn-sites in these compounds indicate small Mn-valence changes, however, the Mn-pre-edge spectra indicate increased localization of the Mn-e_g orbitals with Fe substitution. The Mössbauer results show the distinct two-site Fe⁽³⁺⁾+/Fe^(4+δ)+ disproportionation in the Mn- substituted materials with strong covalency effects at both sites. This disproportionation is a very concrete reflection of a localization of the Fe-d states due to the Mn-substitution.     

Kinetics of adsorption of Saccharomyces cerevisiae mandelated dehydrogenase on magnetic Fe3O4–chitosan nanoparticles

The adsorption of Saccharomyces cerevisiae mandelated dehydrogenase (SCMD) protein on the surface-modified magnetic nanoparticles coated with chitosan was studied in a batch adsorption system. Functionalization of surface-modified magnetic particles was performed by the covalent binding of chitosan onto the surface of magnetic Fe₃O₄ nanoparticles. Characterization of these particles was carried out using FTIR spectra, transmission electron micrography (TEM), X-ray diffraction (XRD) and vibrating sample magnetometry (VSM). Magnetic measurement revealed that the magnetic Fe₃O₄–chitosan nanoparticles were superparamagnetic and the saturation magnetization was about 37.3 emu g⁻¹. The adsorption capacities and rates of SCMD protein onto the magnetic Fe₃O₄–chitosan nanoparticles were evaluated. The adsorption capacity was influenced by pH, and it reached a maximum value around pH 8.0. The adsorption capacity increased with the increase in temperature. The adsorption isothermal data could be well interpreted by the Freundlich isotherm model. The kinetic experimental data properly correlated with the first-order kinetic model, which indicated that the reaction is the adsorption control step. The apparent adsorption activation energy was 27.62 kJ mol⁻¹ and the first-order constant for SCMD protein was 0.01254 min⁻¹ at 293 K.     

Supramolecular aggregation in new crystals with nonlinear optical properties: 2-aminophenol-HClO4, 3-aminophenol-HClO4 and 4-aminophenol-HClO4

Three new hybrid crystals of 2-aminophenol-HClO₄ (2-AP-HClO₄, 1), 3-aminophenol-HClO₄ (3-AP-HClO₄, 2) and 4-aminophenol-HClO₄ (4-AP-HClO₄, 3) were obtained and their crystal structures determined. The 1 crystallises in centrosymmetric space group C2/c of monoclinic system while the other two (2 and 3) crystallise in the non-centro symmetric space group P2₁ and P2₁2₁2₁, respectively. The oppositely charged units of the crystals, i.e. positively charged 2-APH⁺, 3-APH⁺ and 4-APH⁺ and ClO₄⁻, interact via weak N⁺–HO and O–HO hydrogen bonds forming 3D-supramolecular network. Relative to KDP the SHG efficiencies are 0.62 for 2 and 0.33 for 3, measured at 1064 nm using the Kurtz–Perry method.