Enhancement of the photoluminescence and long afterglow properties of Ca<Subscript>2</Subscript>MgSi<Subscript>2</Subscript>O<Subscript>7</Subscript>:Eu<Superscript>2+</Superscript> phosphor by Dy<Superscript>3+</Superscript> co-doping

The Ca₂MgSi₂O₇:Eu²⁺ and Ca₂MgSi₂O₇:Eu²⁺, Dy³⁺ long afterglow phosphors were synthesized under a weak reducing atmosphere by the traditional high temperature solid state reaction method. The synthesized phosphors were characterized by powder X-ray diffraction (XRD) and energy dispersive X-ray spectroscopy (EDX) techniques. The luminescence properties were investigated using thermoluminescence (TL), photoluminescence (PL), long afterglow, mechanoluminescence (ML), and ML spectra techniques. The crystal structure of sintered phosphors was an akermanite type structure, which belongs to the tetragonal crystallography. TL properties of these phosphors were investigated, and the results were also compared. Under the ultraviolet excitation, the emission spectra of both prepared phosphors were composed of a broad band peaking at 535 nm, belonging to the broad emission band. When the Ca₂MgSi₂O₇:Eu²⁺ phosphor is co-doped with Dy³⁺, the PL, afterglow and ML intensity is strongly enhanced. The decay graph indicates that both the sintered phosphors contain fast decay and slow decay process. The ML intensities of Ca₂MgSi₂O₇:Eu²⁺ and Ca₂MgSi₂O₇:Eu²⁺, Dy³⁺ phosphors were proportionally increased with the increase of impact velocity, which suggests that this phosphor can be used as sensors to detect the stress of an object.     

Photocatalysis enhancement of CaAl<Subscript>2</Subscript>O<Subscript>4</Subscript>:Eu<Superscript>2+</Superscript>, Nd<Superscript>3+</Superscript>@TiO<Subscript>2</Subscript> composite powders

CaAl₂O₄:Eu²⁺, Nd³⁺@TiO₂ composite powders were synthesized by a sol–gel method under mild conditions (i.e. low temperature and ambient pressure). The as-prepared powders were characterized by transmission electron microscopy (TEM) and analyzed by X-ray diffraction (XRD). The photocatalytic behavior of the TiO₂-base surfaces was evaluated by the degradation of nitrogen monoxide gas. It suggested that CaAl₂O₄:Eu²⁺, Nd³⁺@TiO₂ composite powders were composed of anatase titania and that CaAl₂O₄:Eu²⁺, Nd³⁺. TiO₂ particles were deposited on the surface of CaAl₂O₄:Eu²⁺, Nd³⁺ to form uniform film. CaAl₂O₄:Eu²⁺, Nd³⁺@TiO₂ composite powders exhibited higher photocatalytic activity compared with pure TiO₂ under visible light. And the result also clearly indicated that the long afterglow phosphor absorbed and stored lights for the TiO₂ to remain photocatalytic activity in the dark.     

Optical energy storage properties of Sr<Subscript>2</Subscript>MgSi<Subscript>2</Subscript>O<Subscript>7</Subscript>:Eu<Superscript>2+</Superscript>,R<Superscript>3+</Superscript> persistent luminescence materials

The details of the mechanism of persistent luminescence were probed by investigating the trap level structure of Sr₂MgSi₂O₇:Eu²⁺,R³⁺ materials (R: Y, La-Lu, excluding Pm and Eu) with thermoluminescence (TL) measurements and Density Functional Theory (DFT) calculations. The TL results indicated that the shallowest traps for each Sr₂MgSi₂O₇:Eu²⁺,R³⁺ material above room temperature were always ca. 0.7 eV corresponding to a strong TL maximum at ca. 90 °C. This main trap energy was only slightly modified by the different co-dopants, which, in contrast, had a significant effect on the depths of the deeper traps. The combined results of the trap level energies obtained from the experimental data and DFT calculations suggest that the main trap responsible for the persistent luminescence of the Sr₂MgSi₂O₇:Eu²⁺,R³⁺ materials is created by charge compensation lattice defects, identified tentatively as oxygen vacancies, induced by the R³⁺ co-dopants.     

Effects of boric acid on structural and luminescent properties of BaAl<Subscript>2</Subscript>O<Subscript>4</Subscript>:(Eu<Superscript>2+</Superscript>, Dy<Superscript>3+</Superscript>) phosphors

Eu²⁺/Dy³⁺-codoped BaAl₂O₄ phosphors were prepared by conventional solid-state reaction with boric acid flux. The effects of boric acid on structural and luminescent properties of BaAl₂O₄:(Eu²⁺, Dy³⁺) were investigated. The crystallinity of BaAl₂O₄ improved with increasing amount of H₃BO₃. Incorporation of Eu²⁺ and Dy³⁺ ions into effective lattice sites was promoted by H₃BO₃ addition. As a result, Eu²⁺ emission in BaAl₂O₄ was greatly enhanced by H₃BO₃, and the duration of persistent luminescence increased with the amount of H₃BO₃. However, the decay lifetime of persistent luminescence was not strongly influenced by the amount of H₃BO₃.     

Eu<Superscript>3+</Superscript>-doped LaPO<Subscript>4</Subscript> and LaAlO<Subscript>3</Subscript> nanosystems and their luminescence properties

Eu³⁺ ion-doped LaPO₄ nanowires or nanorods have been successfully synthesized by a simple hydrothermal method. The influence of varying the hydrothermal and subsequent sintering conditions on the morphology and structure of the LaPO₄ host has been investigated by scanning electron microscopy (SEM) and X-ray diffraction (XRD). For comparison, the Eu³⁺ ions were also doped into monoclinic monazite LaPO₄ nanoparticles and perovskite LaAlO₃ nanoparticles. The relative intensities of the emission lines of the LaPO₄:Eu³⁺ nanosystems were essentially independent of their shape. The optimal doping concentrations in the monoclinic LaPO₄ and perovskite LaAlO₃ nanosystems were determined to be about 5.0 and 3.5 mol%, respectively. Under appropriate UV-radiation, the red light emitted from LaAlO₃:Eu³⁺ (3.5 mol%) was brighter than that from LaPO₄:Eu³⁺ (5.0 mol%) nanomaterial, resulting from differences in their spin-orbit couplings and covalence, which indicates that the nanoscale LaAlO₃ is a promising host material for rare earth ions. Electronic Supplementary Material  Supplementary material is available for this article at and is accessible for authorized users. Supported by the National Natural Science Foundation of China (Grant Nos. 20873039 & 90606001), Hunan Provincial Natural Science Foundation (No. 07jj4002), and the Students Innovation Training Fund of Hunan University     

Eu<Superscript>3+</Superscript>-fluorescence properties in nano-crystallized SnO<Subscript>2</Subscript>-SiO<Subscript>2</Subscript> glass-ceramics

Fluorescence and spectral hole burning properties of Eu³⁺ ions were studied in nanocrystals-precipitated SnO₂-SiO₂ glasses. The glasses were prepared to contain various amount of Eu₂O₃ using the sol-gel method, in which SnO₂ nanocrystals were precipitated by heating in air. In the glasses containing Eu₂O₃ less than 1%, the Eu³⁺ ions were preferentially doped in the SnO₂ nanocrystals and their fluorescence intensities were enhanced by the energy transfer due to the recombination of electrons and holes excited in SnO₂ crystals. The SnO₂ nanocrystals-precipitated glasses exhibited the persistent spectral holes with the depth of ∼25% of the total fluorescence intensities of the Eu³⁺ ions. With the increasing Eu₂O₃ concentration, the amount of SnO₂ nanocrystals decreased and the Sn⁴⁺ ions formed the random glass structure together with the silica network. This structure change induced the fluorescence intensities and the hole depth to decrease.     

A new phosphor with flower-like structure and luminescent properties of Sr<Subscript>2</Subscript>MgSi<Subscript>2</Subscript>O<Subscript>7</Subscript>: Eu<Superscript>2+</Superscript>, Dy<Superscript>3+</Superscript> long afterglow materials by sol–gel method

The flower-like phosphors of Sr₂MgSi₂O₇: Eu²⁺, Dy³⁺ with high brightness and long afterglow were obtained by sol–gel method. X-ray diffraction pattern (XRD) shows that single-phased Sr₂MgSi₂O₇ phosphor is prepared by sol–gel method under 1250 °C. Scanning electron microscope (SEM) indicates that the phosphor consists of nano-sized whiskers which are detected for the first time in Eu²⁺ and Dy³⁺ co-doped long-lasting phosphorescence silicates. Furthermore, the investigation on the mechanism indicates that the internal structure and gas, liquid and solid phase effect play important roles in the formation of flower-like Sr₂MgSi₂O₇: Eu²⁺, Dy³⁺ nanostructure. Finally, the optical properties of flower-like Sr₂MgSi₂O₇ nanostructure have been characterized by photoluminescence (PL) spectra.     

Preparation and Characterization of GdTaO<Subscript>4</Subscript>:Eu<Superscript>3+</Superscript> Sol-Gel Luminescence Thin Films

High quality GdTaO₄:Eu³⁺ luminescence films have been successfully prepared through a modified sol-gel process. The films were prepared using inorganic materials as raw materials, and the thermal decomposition and UV assisted technique were introduced to improve the quality of the film and reduce the period for forming the thick film. Results of structural studies by atomic force microscopy (AFM) and X-ray diffraction (XRD) showed that the surface was smooth and the structure was monoclinic with the average grain size of about 55 nm. The emission and excitation spectra of the film were investigated. Related to the transition ⁵ D₀ →⁷ F₁ and ⁵ D₀→⁷ F₂ of Eu³⁺ ions, the main luminescence peaks were observed at 591 and 611 nm respectively, and the luminescence peak at 345 nm was detected simultaneously related to the TaO₄³⁻ emission. Transmission spectrum and decay curve of the luminescence are also presented in this paper.     

Near-infrared quantum cutting in Tb<Superscript>3+</Superscript> and Yb<Superscript>3+</Superscript>-doped Y<Subscript>2</Subscript>O<Subscript>3</Subscript> nanophosphors

Properties of the quantum-cutting phosphors are dependent on various factors such as dopant concentration, crystallinity, homogeneity, particle size and surface morphology. Effective control of the above parameters can enhance the quantum-cutting ability of the phosphor material. Nano-sized particles of Y₂O₃:Tb³⁺,Yb³⁺ were prepared with a solution-based co-precipitation method and subsequent calcination. Effective control of the reaction parameters and doping concentration helped to produce uniform nanostructures with high quantum-cutting efficiency up to 181.1 %. The energy transfer mechanism between Tb³⁺ and Yb³⁺ was studied by considering their spectroscopic properties and time-resolved spectroscopy. The high efficiency and small particle size of the quantum-cutting phosphor Y₂O₃:Tb³⁺,Yb³⁺ make it a suitable candidate for its application in solar cells.     

Local structure and photoluminescent characteristics of Eu<Superscript>3+</Superscript> in ZnO–SiO<Subscript>2</Subscript> glasses

The photoluminescence properties of xZnO–(100−x)SiO₂ (x = 0, 5, 10, 20) containing 1% Eu₂O₃ prepared by a sol–gel method were systematically investigated. The results indicated that the relative proportion of f–f transitions to charge transfer (CT) absorption decreased with the increase of ZnO concentration. The intensity of ⁵D₀–⁷F_J transitions of Eu³⁺ ions was enhanced with the increase of ZnO content due to local structure changes and decreased quantities of Eu³⁺ ions clusters. The results of fluorescence line narrow (FLN) spectra indicated that Eu³⁺ ions occupied one site in SiO₂ glass and two sites in ZnO–SiO₂ glasses. The second-order crystal field parameters were calculated. B₂₀ and B₂₂ for site 1 increased with excitation energy, while ones hardly changed for site 2.     

UV excited green luminescence of SrAl<Subscript>2</Subscript>O<Subscript>4</Subscript>:Eu<Superscript>2+</Superscript>, Dy<Superscript>3+</Superscript> nanophosphor

Eu, Dy co-doped strontium aluminate nanophosphors were prepared by the combustion synthesis method. Their structure and morphology were investigated by X-ray diffraction (XRD), scanning electron microscopy, transmission electron microscopy (TEM), and Fourier transform infrared spectroscopy. According to the XRD and the TEM analysis, the average crystallite size was found to be in the nanometer range. The phase structure of the prepared nanophosphor is consistent with a standard monoclinic phase with a space group P2₁. The prepared SrAl₂O₄:Eu²⁺, Dy³⁺ nanophosphor emitted green light with a peak at 510 nm showing blue shift, which is due to the reduction in the particle size. Two distinct peaks were observed in the ML intensity versus time curve. The two peaks in ML indicate the presence of charge transfer in an ML process.     

Two color up-conversion emissions of Er<Superscript>3+</Superscript>-doped Al<Subscript>2</Subscript>O<Subscript>3</Subscript> nanopowders prepared by non-aqueous sol-gel method

Er³⁺-doped Al₂O₃ nanopowders have been prepared by the non-aqueous sol-gel method using the aluminum isopropoxide as precursor, acetylacetone as a chelating agent, nitric acid as a catalyzer, and hydrated erbium nitrate as a dopant under isopropanol environment. The different phase structure, including three crystalline types of (Al, Er)₂O₃ phases, α, γ, θ, and an Er–Al–O stoichiometric compound phase, Al₁₀Er₆O₂₄, was observed for the 0.01–0.5 mol% Er³⁺-doped Al₂O₃ nanopowders at the sintering temperature of 1,000 °C. The green and red up-conversion emissions centered at about 523, 545 and 660 nm, corresponding respectively to the ²H_11/2, ⁴S_3/2→⁴I_15/2 and ⁴F_9/2→⁴I_15/2 transitions of Er³⁺, were detected by a 978 nm semiconductor laser diodes excitation. With increasing Er³⁺ doping concentration from 0.01 to 0.1 mol%, the intensity of the green and red emissions increased with a decrease of the intensity ratio of the green to red emission. When the Er³⁺ doping concentration rose to 5 mol%, the intensity of the green and red emissions decreased with an increase of their intensity ratio. The maximum intensity of both the green and red emissions with the minimum of intensity ratio was obtained, respectively, for the 0.1 mol% Er³⁺-doped Al₂O₃ nanopowders composed of a single α-(Al,Er)₂O₃ phase. The intensity ratio of the green emission at 523 and 545 nm increased monotonously for all Er³⁺ doping concentrations. The two-photon absorption up-conversion process was involved in the green and red up-conversion emissions of the Er³⁺-doped Al₂O₃ nanopowders.     

Ionic liquid-based hydrothermal synthesis of Lu2O3 and Lu2O3:Eu3+ microcrysals

Uniform and well-defined Lu₂O₃ and Lu₂O₃:Eu³⁺ microarchitectures have been successfully synthesized via a green and facile ionic liquid-based hydrothermal method followed by a subsequent calcination process. Novel 3D micro-rodbundles and 1D microrods of Lu₂O₃ and Lu₂O₃:Eu³⁺ were controllably obtained through this method. X-ray powder diffraction, scanning electron microscopy, transmission electron microscopy and photoluminescence spectra were used to characterize the micromaterials. The proposed formation mechanisms have been investigated on the basis of a series of SEM studies of the products obtained at different hydrothermal durations. The results indicated that hydrothermal temperature and the ionic liquid-tetrabutylammonium hydroxide were two key factors for the formation as well as the morphology control of the Lu₂O₃ and Lu₂O₃:Eu³⁺ microarchitectures.     

Hexametavanadates M<Stack><Subscript>4</Subscript><Superscript>+</Superscript></Stack>M<Superscript>2+</Superscript>(VO<Subscript>3</Subscript>)<Subscript>6</Subscript>: Thermal stability and luminescent characteristics

Rhombohedral hexametavanadates K₄Sr(VO₃)₆, K₄Ba(VO₃)₆, Rb₄ Ba(VO₃)₆, and Cs₄Ba(VO₃)₆ melt incongruently in the temperature range of 491 to 600°C. Cooling of peritectic melts yields mixtures of compounds typical of M₂⁺O-M²⁺O-V₂O₅ systems, far from equilibrium and depending on the cooling kinetics. The vanadate Cs₄Ba(VO₃)₆ undergoes reversible polymorphic transformation at 360°C. All compounds show broad-band luminescence with a maximum of the luminescence spectrum at 490–590 nm with three types of excitation. The vanadates K₄Sr(VO₃)₆ and Rb₄Ba(VO₃)₆ show the highest luminescence intensity at room temperature. The latter is also most efficient at liquid nitrogen temperatures. The luminescence spectra depend on the excitation of vanadates. Three hypotheses were put forward to interpret this finding. The nature of luminescence is attributed to the relaxation of electronic excitation in [VO₄]³⁻ structural tetrahedra present in the vanadates. The performance characteristics of luminophores were determined. These luminophores may be promising as X-ray luminescent screens, radioluminescence indicators, and light-emitting diode devices.     

Adsorption behavior of <Superscript>99</Superscript>Tc on Fe,Fe<Subscript>2</Subscript>O<Subscript>3</Subscript> and Fe<Subscript>2</Subscript>O<Subscript>4</Subscript>

Summary The adsorption of ⁹⁹Tc on the adsorbers Fe, Fe₂O₃ and Fe₃O₄ was studied by batch experiments under aerobic and anoxic conditions. The effects of pH and CO₃^2- concentration of the simulated ground water on the adsorption ratios were also investigated, and the valences of Tc in solution after the adsorption equilibrium were studied by solvent extraction. The adsorption isotherms of TcO₄- on the adsorbers Fe, Fe₂O₃ and Fe₃O₄ were determined. Experimental results have shown that the adsorption ratio of Tc on Fe decreases with the increase of pH in the range of 5-12 and increases with the decrease of the CO₃^2- concentration in the range of 10^-8M-10^-2M. Under aerobic conditions, the adsorption ratios of ⁹⁹Tc on Fe₂O₃ and Fe₃O₄ were not influenced by pH and CO₃^2-concentration. When Fe was used as adsorbent, Tc existed mainly in the form of Tc(IV) after equilibrium and in the form of Tc(VII) when the adsorbent was Fe₂O₃ or Fe₃O₄ under aerobic conditions. The adsorption ratios of Tc on Fe, Fe₂O₃ and Fe₃O₄ decreased with the increase of pH in the range of 5-12 and increased with the decrease of the CO₃^2- concentration in the range of 10^-8M-10^-2M under anoxic conditions. Tc existed mainly in the form of Tc(IV) after equilibrium when Fe, Fe₂O₃ and Fe₃O₄ was the adsorbent under anoxic conditions. The adsorption isotherms of TcO_4- on the adsorbers Fe, Fe₂O₃ and Fe₃O₄ are fairly in agreement with the Freundlich’s equation under both aerobic and anoxic conditions.     

Solubility and hydrolysis of lutetium at different [Lu<Superscript>3+</Superscript>]<Subscript>initial</Subscript>

Solubility product (Lu(OH)_3(s)⇆Lu³⁺+3OH⁻) and first hydrolysis (Lu³⁺+H₂O⇆Lu(OH)²⁺+H⁺) constants were determined for an initial lutetium concentration range from 3.72·10⁻⁵ mol·dm⁻³ to 2.09·10⁻³ mol·dm⁻³. Measurements were made in 2 mol·dm⁻³ NaClO₄ ionic strength, under CO₂-free conditions and temperature was controlled at 303 K. Solubility diagrams (pLu_aq vs. pC _H) were determined by means of a radiochemical method using ¹⁷⁷Lu. The pC _H for the beginning of precipitation and solubility product constant were determined from these diagrams and both the first hydrolysis and solubility product constants were calculated by fitting the diagrams to the solubility equation. The pC _H values of precipitation increases inversely to [Lu³⁺]_initial and the values for the first hydrolysis and solubility product constants were log₁₀ β* _Lu,H = −7.92±0.07 and log₁₀ K*_sp,Lu(OH)3 = −23.37±0.14. Individual solubility values for pC _H range between the beginning of precipitation and 8.5 were S _Lu3+ = 3.5·10⁻⁷ mol·dm⁻³, S _Lu(OH)2+ = 6.2·10⁻⁷ mol·dm⁻³, and then total solubility was 9.7·10⁻⁷ mol·dm⁻³.     

Photoluminescence and structural characteristics of Lu2O3:Eu nanocrystallites in silica matrix

Two silica ceramics were obtained by mixing nanocrystalline Lu₂O₃:Eu³⁺ with silica sol using the sol-gel technique. The synthesis procedure for both samples differed in the pH of the sol and time of the sol condensation before substrates were mixed together, which implied their different optical properties. The first one has the same spectroscopic properties as Lu₂O₃:Eu³⁺ nanocrystallites with an exception of small lowering of the charge transfer (CT) band intensity. This feature is preserved up to about 950 °C. Above this temperature, nanocrystallites of Lu₂O₃:Eu³⁺ react with the silica matrix synthesis pyrosilicate (Lu₂Si₂O₇). The Eu³⁺ ions occupy only one crystallographic site in the crystal lattice for low concentration of the activator (1%) and two sites for higher concentration (10%). The second sample exhibits different Eu³⁺ emission than Lu₂O₃:Eu³⁺ nanocrystallites and, additionally, a broad band of the matrix originating at the green region of the spectrum. Sintering the sample at higher temperatures leads to disappearance of this broad emission and continuous changes of the Eu³⁺ emission because of the progressive conversion of the Lu₂O₃:Eu³⁺ to pyrosilicate. At 1300 °C for both samples, the reaction of synthesis lutetium pyrosilicate is completed. Structural characteristic of the samples is presented and correlate with the decay profile of the Eu³⁺ emission.     

Ionic conduction of a high-temperature modification of Lu<Subscript>2</Subscript>Ti<Subscript>2</Subscript>O<Subscript>7</Subscript>

A nanoceramic product of the composition Lu₂Ti₂O₇ is synthesized by a coprecipitation method with a subsequent sublimation drying and an annealing at 650–1650°C. The conduction of Lu₂Ti₂O₇ synthesized at 1650°C is ionic (10^–3 S cm^–1 at 800°C). Thus, a new material with a high ionic conduction has been discovered. The ordering in Lu₂Ti₂O₇ is studied by methods of RFA, RSA, IK spectroscopy, electron microscopy, and impedance spectroscopy. The existence of a low-temperature phase transition fluorite-pyrochlore at 800°C and a high-temperature conversion order-disorder at 1650°C are established.Translated from Elektrokhimiya, Vol. 41, No. 3, 2005, pp. 298–303.Original Russian Text Copyright © 2005 by Shlyakhtina, Ukshe, Shcherbakova.     

The monooxidation of ethylene with hydrogen peroxide on the per-FTPhPFe<Superscript>3+</Superscript>OH/Al<Subscript>2</Subscript>O<Subscript>3</Subscript> biomimetic

The gas-phase monooxidation of ethylene by hydrogen peroxide on a biomimetic heterogeneous catalyst (per-FTPhPFe³⁺OH/Al₂O₃) was studied under comparatively mild conditions. The biomimetic oxidation of ethylene with hydrogen peroxide was shown to be coherently synchronized with the decomposition of H₂O₂. Depending on reaction medium conditions, one of two desired products was formed, either ethanol or acetaldehyde. The kinetics and probable mechanism of ethylene transformation were studied.     

Silicate complexation of NpO<Subscript>2</Subscript><Superscript>+</Superscript> ion in perchlorate media

Complexation behavior of NpO₂ ⁺ with ortho-silicic acid (o-SA) has been studied using solvent extraction at ionic strengths varying from 0.10 to 1.00M (NaClO₄) at pcH 3.68±0.08 and 25 °C with bis-(2-ethylhexyl) phosphoric acid (HDEHP) as the extractant. The stability constant value (log β₁) for the 1:1 complex, NpO₂(OSi(OH)₃), was found to decrease with increase in ionic strength of the aqueous phase [6.83±0.01 at I=0.10M to 6.51±0.02 at I = 1.00M]. These values have been fitted in the SIT model expression and compared with similar values of complexation of the metal ions Am³⁺, Eu³⁺, UO₂ ²⁺, PuO₂ ²⁺, Np⁴⁺, Ni²⁺ and Co²⁺. The speciation of NpO₂ ⁺-o-silicate/carbonate system has been calculated as a function of pcH under ground water conditions. On leave from Radiochemistry Division, Bhabha Atomic Research Centre, Trombay, Mumbai-400 085, India.