Comparisons of glow-discharge polymerizations among tetramethylsilane,dimethyldimethoxysilane, and tetramethoxysilane

Glow-discharge polymerizations among tetramethylsilane, dimethyldimethoxysilane, and tetramethoxysilane were compared by elemental analyses and infrared spectroscopy. The elemental composition of the polymers prepared from the three monomers depended strongly on the operational conditions necessary to sustain a glow discharge, i.e., the W/FM parameter, where W is the rf power, F is the flow rate of the monomer, and M is the molecular weight of the monomer. Methoxy groups were more susceptible to glow discharge than methyl groups. Differences in chemical structure among these monomers appeared in the polymer structures formed when the glow-discharge polymerization was carried out at a low value of the W/FM parameter, while the differences disappeared at high values of the W/FM parameter, for analogous polymers. Substitution with methoxy groups was favorable for the formation of polymers of low carbon content only when the glow-discharge polymerization was performed at low values of W/FM.