| Abstract: | The ion etching technique has been applied to a morphological study of mechanically blended polypropylene (PP) with high-density polyethylene (HDPE). Samples blended to PP/HDPE compositions of 65/35 and 85/15 by weight were highly drawn and then heat treated for 30 min at selected temperatures up to 163°C. When these samples are carefully ion-etched several features are observed in electron micrographs, namely (i) crosshatched, and (ii) twisted or layered textured inclusions of HDPE crystals within arrays of lamellalike PP crystals situated perpendicular to the direction of drawing. X-ray diffraction measurements of the drawn samples heat treated in the range 145–163°C for 30 min shows that oriented HDPE crystallizes with b-axis orientation along the drawing direction. Supporting evidence is obtained from electron diffraction measurements. The molecular weight of the HDPE component is a major factor in the b-axis-oriented growth of HDPE crystals in PP/HDPE blends. |