Mg doping behavior of MOVPE InxGa1−xN (x∼0.4)

The Mg doping behavior of MOVPE indium gallium nitride (InGaN), such as secondary ion mass spectrometry (SIMS) Mg profile, crystalline quality and n–p conversion of the films are described and discussed in this paper. The SIMS analysis reveals that the memory effect of Cp₂Mg as a doping source deteriorates the controllability of Mg doping level and profile, especially for thin (−0.4 μm) InGaN. The high residual donors (10¹⁹–10²⁰ cm⁻³) in InGaN with In content from 0.05 to 0.37 can be compensated by Mg doping and p-type conduction is obtained for those with In content up to 0.2. It is found that a higher Cp₂Mg flow rate is needed to get p-type conduction in InGaN with a higher In content x; for example, Cp₂Mg/(TEG+TMI)≈0.5% for x=0 (GaN), ≈2% for x=0.05 and ≈4% for x=0.2. Such a high Cp₂Mg flow rate is needed due to the high residual donor concentration (10¹⁹–10²⁰ cm⁻³) of InGaN films and the low activation efficiency of Mg. The crystalline quality of InGaN is deteriorated with increasing In content as well as Mg doping level. To achieve a p-type InGaN with a lower Mg doping, it is essential to improve the crystalline quality of non-doped InGaN. For this purpose, the use of a thicker GaN interlayer is effective.