The role of Mg2FeH6 formation on the hydrogenation properties of MgH2-FeFx composites

The hydrogenation properties of magnesium hydride mechanically milled with iron fluorides (FeF₂ and FeF₃), were investigated by Temperature Programmed Desorption (TPD) and volumetric methods using a Sieverts-type apparatus, as prepared upon dehydrogenation and finally upon subsequent hydrogenation. The activation energy of hydrogen desorption (E_a), calculated from the Kissinger formula using TPD measurements obtained with different heating rates, showed significant decreases of Ea in comparison to that of milled MgH₂ without any dopants. Moreover, the influence of these metal fluorides on the thermodynamics of the decomposition process was also examined. In the case of the FeF₂ dopant, rehydrogenation following desorption caused the complete decomposition of the iron fluoride to BCC iron and the formation of a predominant MgH₂ phase. In contrast to FeF₂, the addition of FeF₃ led to the formation of β-MgH₂ as a major phase coexisting with Mg₂FeH₆ and MgF₂ compounds. The presence of pure Fe in the MgH₂+FeF₂ composite, as opposed to MgH₂+FeF₃ containing Mg₂FeH₆ and MgF₂, did not cause any significant influence on the sorption properties of MgH₂. Moreover, the original material doped with FeF₃ predominantly showed iron in the Mg₂FeH₆ compound, while the FeF₂ dopant iron mostly showed the nearly pure BCC metallic phase