Phase behavior and Li+ Ion conductivity of styrene‐ethylene oxide multiblock copolymer electrolytes

Solid polymer electrolytes are attractive materials for use as battery separators. Here, a molecular weight series of polystyrene–polyethylene oxide (PEO) multiblock copolymers was synthesized by the thiol–norbornene click reaction. The subsequent materials were characterized both neat and with a lithium bis‐(trifluoromethane)sulfonimide salt loading (Li)/(EO)] of 0.1. In general, neat samples demonstrated crystallinity scaling with PEO content. Lithium ion‐containing samples had broad scattering peaks, half of which displayed disordered scattering, even at the lowest block molecular weights (polystyrene = 1 kg/mol, PEO = 1 kg/mol). Fitting of disordered scattering data, using the random phase approximation, yielded χ_RPA and R_g values that were compared with recent predictive work by Balsara and coworkers. The predictions were accurate near the volume fraction f_PEO = 0.5 but deviated symmetrically with volume fraction asymmetry. Samples were also analyzed by electrochemical impedance spectroscopy for their potential to conduct lithium ions. Samples with f_PEO ≥ 0.5 demonstrated robust conductivity, whereas samples below this volume fraction conducted very poorly, with one exception (f_PEO = 0.24). This work expanded upon our recently reported approach to multiblock copolymer synthesis, demonstrating the improved access of materials to further our fundamental understanding of multiblock copolymers. Copyright © 2016 John Wiley & Sons, Ltd.