Immobilization of yttrium over crystalline titania

A co-precipitation method was adopted for the immobilization of yttrium radioactive waste over crystalline titania. A high uptake of⁹¹Y was observed over the preformed hydrous titania. Weighable quantity of Y was coprecipitated with Ti(IV) hydroxide and a maximum of 38 wt% was found to be adsorbed. Mixed masses were calcined separately at 800 and 1000°C for 20 hours, and soxhlet leach tests at 97°C, repeated 7 times at an interval of 24 hours, showed the release of yttrium in the order of 10^–1 and 10^–2 g·m^–2·d^–1, respectively. X-ray powder diffraction analysis revealed that the yttrium was immobilized in the titania crystal lattice which suffered some structural changes with the formation of new mineral phase Y₂Ti₂O₇ which is accompanied by rutile and little quantity of anatase form of titania at 800°C, and only rutile form of titania at 1000°C.