| SYNTHESES AND PROPERTIES OF POLYPHENYL-1,2,4-TRIAZINES |
| |
| 引用本文： | 邢兰敏,白路娜,卢凤才. SYNTHESES AND PROPERTIES OF POLYPHENYL-1,2,4-TRIAZINES[J]. 高分子科学, 1985, 0(2): 150-156 |
| |
| 作者姓名： | 邢兰敏 白路娜 卢凤才 |
| |
| 作者单位： | Institute of Chemistry，Academia Sinica，Beijing，Institute of Chemistry，Academia Sinica，Beijing，Institute of Chemistry，Academia Sinica，Beijing |
| |
| 摘 要： | A series of aromatic poly--1, 2, 4-triazines have been prepared. Experimental results showedthat these polymers exhibited good thermally oxidative stability as determined by isothermal agingat 30℃for 200 hours in air. After submerging the coated wire in boiling water for 240 hours nochange in electrical insulation was detected. Polymer films also showed good tensile strength (1050-1400 kg/cm~2) at room temperature. Therefore aromatic poly-1, 2, 4-triazines demonstrate highperformance showing good potential for use as functional and structural resins in the environmentsdemanding high thermal stability and hydrolytic stability.
|
| 收稿时间： | 1984-10-08 |
SYNTHESES AND PROPERTIES OF POLYPHENYL-1,2,4-TRIAZINES* |
| |
| XING Lanmin,BAI Luna,LU Fengcai. SYNTHESES AND PROPERTIES OF POLYPHENYL-1,2,4-TRIAZINES*[J]. Chinese Journal of Polymer Science, 1985, 0(2): 150-156 |
| |
| Authors: | XING Lanmin BAI Luna LU Fengcai |
| |
| Affiliation: | Institute of Chemistry; Academia Sinica; Beijing |
| |
| Abstract: | A series of aromatic poly--1, 2, 4-triazines have been prepared. Experimental results showedthat these polymers exhibited good thermally oxidative stability as determined by isothermal agingat 30℃ for 200 hours in air. After submerging the coated wire in boiling water for 240 hours nochange in electrical insulation was detected. Polymer films also showed good tensile strength (1050-1400 kg/cm2) at room temperature. Therefore aromatic poly-1, 2, 4-triazines demonstrate highperformance showing good potential for use as functional and structural resins in the environments demanding high thermal stability and hydrolytic stability. |
| |
| Keywords: | |