Preparation,characterization, and luminescence of (SBA-15) immobilized pepsin

SBA-15 mesoporous silica was synthesized by hydrothermal method and its surface was methylated by treatment with methyltrimethoxysilane. Pepsin was immobilized on the obtained materials giving host-guest composite materials (SBA-15)-pepsin and (methylated SBA-15)-pepsin. The optimum conditions for preparation of these materials were established. Methylated SBA-15 (M-SBA-15) has improved immobilization efficiency of enzyme compared to initial SBA-15 silica. It was shown that with the gradual increase of NaCl solution ionic strength the immobilized amount of enzyme was reduced. Powder X-ray diffraction and Fourier transform infrared spectroscopy showed that the host frameworks in the prepared host-guest composite materials are intact and the ordered structure was retained. Scanning electron microscopic studies revealed fibrous morphologic characteristics of the SBA-15 and the immobilized pepsin composite materials. The average particle diameter of (SBA-15)-pepsin composite was 338 ± 10 and 343 ± 10 nm for (M-SBA-15)-pepsin. The low temperature N₂ adsorption-desorption study at 77 K showed that the pore sizes and specific surface areas of the host-guest composite materials were smaller than those before the introduction of the enzyme, suggesting that the immobilized enzyme occupied a definite position in the host material pore channels. The UV-vis solid diffuse reflectance and luminescence studies showed that the enzyme was successfully immobilized on to the host material and that after the immobilization of enzyme on SBA-15 the conformation of pepsin macromolecule has not been changed.