| 水热法制备高纯超细CeO2-ZrO2复合氧化物 |
| |
| 引用本文： | 郑育英,黄慧民,邓淑华,李大光,余双平. 水热法制备高纯超细CeO2-ZrO2复合氧化物[J]. 无机化学学报, 2005, 21(8): 1227-1230 |
| |
| 作者姓名： | 郑育英 黄慧民 邓淑华 李大光 余双平 |
| |
| 作者单位： | 广东工业大学轻工化工学院,广州,510090 |
| |
| 基金项目： | 广东省重大专项(No.A10701)，广东省自然科学基金团队项目(No.04205301)资助。 |
| |
| 摘 要： | Superfine composite powders of CeO2-ZrO2 (CZ) and CeO2-ZrO2-La2O3 (CZL) were prepared by hydrothermal method. The effects of pH、temperature and time for hydrothermal process on the performance of the resulting powders were studied. The optimized reaction parameters were on follows: the precursor′s pH≈9.0, hydrothermal temperature of 200 ℃ holding for 2 h. Thermal stable powders with average particle size smaller than 10 nm and specific surface area of 171 m2·g-1 were obtained. A BET specific surface area was still at 44 m2·g-1 after calcination at 1 000 ℃ for 6 hours.
|
| 关 键 词： | 水热法； 氧化铈； 氧化锆 |
| 文章编号： | 1001-4861(2005)08-1227-04 |
| 收稿时间： | 2004-12-20 |
| 修稿时间： | 2004-12-20 |
Preparation of High Purity and Superfine CeO2-ZrO2 by Hydrothermal Method |
| |
| ZHENG Yu-Ying,HUANG Hui-Min,DENG Shu-Hu,LI Da-Guang and YU Shuang-Ping. Preparation of High Purity and Superfine CeO2-ZrO2 by Hydrothermal Method[J]. Chinese Journal of Inorganic Chemistry, 2005, 21(8): 1227-1230 |
| |
| Authors: | ZHENG Yu-Ying HUANG Hui-Min DENG Shu-Hu LI Da-Guang YU Shuang-Ping |
| |
| Affiliation: | Faculty of Light and Chemical Engineering, Guangdong University of Technology, Guangzhou 510090,Faculty of Light and Chemical Engineering, Guangdong University of Technology, Guangzhou 510090,Faculty of Light and Chemical Engineering, Guangdong University of Technology, Guangzhou 510090,Faculty of Light and Chemical Engineering, Guangdong University of Technology, Guangzhou 510090 and Faculty of Light and Chemical Engineering, Guangdong University of Technology, Guangzhou 510090 |
| |
| Abstract: | |
| |
| Keywords: | hydrothermal method ceria zirconia supercritical dryness |
| 本文献已被 万方数据 等数据库收录！ |
| 点击此处可从《无机化学学报》浏览原始摘要信息 |
|
点击此处可从《无机化学学报》下载全文 |
|