Effect of SnO2 Nanocrystals on the Emission of Eu3+ Ions in Silica Matrix

Silica xerogels containing Eu³⁺ ions and SnO₂ nanocrystals were prepared in the sol‐gel process, and characterized by x‐ray diffraction (XRD) and photoluminescence spectra. Under the excitation at 393 nm, characteristic emission of Eu³⁺ ions at 614 nm was enhanced with increasing amount of SnO₂ nanocrystals. Moreover, when the Eu³⁺/SnO₂ co‐doped samples were excited at 345 nm, corresponding to the sideband of SnO₂ nanocrystals, the emission of Eu³⁺ ions at 614 nm was clearly observed, while no emission of Eu³⁺ ions for the Eu³⁺‐doped sample. It may be ascribed to the energy transfer from SnO₂ conduction band to Eu³⁺ conduction band. Further experimental results suggest that the energy transfer may be achieved through surface transition state.