The germanium-selenium phase diagram

The binary germanium—selenium system was investigated by differential thermal analysis; from the results a temperature-composition diagram was constructed. The existence of the two compounds GeSe and GeSe₂ was confirmed. Furthermore, it could be shown that between 920±4 and 939±2 K GeSe transforms to a high-temperature modification which is slightly richer in selenium and decomposes peritectically at 948±2 K. On the germanium-rich side of the system a monotectic equilibrium exists at 1 177±2 K. Two thermal effects, one between 908 and 918 K, the other one at 851±3 K, were shown to be non-equilibrium effects. GeSe and GeSe₂ form a eutectic at 856±2 K and 56.0±0.5 at% Se. The congruent melting point of GeSe₂ was determined as 1 015±2 K. Between GeSe₂ and Se another eutectic exists at 485±1 K and 94.5±0.5 at% Se.

---

Das Germanium-Selen-Phasendiagramm

Zusammenfassung Das Zweistoffsystem Germanium—Selen wurde mit Hilfe der Differenz-Thermo-Analyse untersucht; aus den Ergebnissen wurde einT-x-Zustandsdiagramm erstellt. Die Existenz der zwei Verbindungen GeSe und GeSe₂ wurde bestätigt. Weiters konnte gezeigt werden, daß zwischen 920±4 und 939±2 K GeSe sich in eine Hochtemperatur-Modifikation umwandelt, welche etwas selenreicher ist und bei 948±2 K peritektisch zerfällt. Auf der germaniumreichen Seite des Systems existiert bei 1 177±2 K ein monotektisches Gleichgewicht. Von zwei thermischen Effekten, einem zwischen 908 und 918 K und einem anderen bei 851±3 K, konnte gezeigt werden, daß sie auf fehlendes Gleichgewicht zurückzuführen sind. GeSe und GeSe₂ bilden ein Eutektikum bei 856±2 K und 56,0±0,5 At% Se. Der kongruente Schmelzpunkt von GeSe₂ wurde zu 1 015±2 K bestimmt. Zwischen GeSe₂ und Se existiert ein weiteres Eutektikum bei 485±1 K und 94,5±0,5 At% Se.