Nanostructured ultra-low-κ porous fluoropolymer composite films via plasma co-polymerization of hydrophobic and hydrophilic monomers and subsequent hydrolysis treatment |
| |
Authors: | Jiachun Feng Wei Huang |
| |
Institution: | a Key Laboratory of Molecular Engineering of Polymers of Ministry of Education, Department of Macromolecular Science, Fudan University, Shanghai 200433, PR China b Institute of Advanced Materials, Nanjing University of Posts and Telecommunications, Nanjing 210003, PR China |
| |
Abstract: | A new approach to fabricate porous nanostructured fluoropolymer composite films with a low dielectric constant (κ) was put forward at the first time. Initially, a film (pp-HDFD-PEGMA film) composed of dense, uniform, and well-defined nanospheres was controllably deposited on hydrogen-terminated silicon substrates by simultaneous plasma polymerization and deposition of a fluorine-containing hydrophobic monomer, 3,3,4,4,5,5,6,6,7,7,8,8,9,9,10,10,10-heptadecafluoro-1-decene (HDFD), and a hydrophilic monomer poly(ethylene glycol) methacrylate (PEGMA), using a pulsed plasma polymerization technique. Then, by hydrolysing the plasma co-deposited film in aqueous hydrochloric acid solution to effectively remove the soluble nanospheres or fragments which mainly derived from PEGMA, a nanoporous fluorocarbon film was achieved. Subsequently, a top poly(tetrafluoroethylene) layer was deposited via the magnetron sputtering process to cap and complete an encapsulated structure. The resulting bilayer composite film consisting of a layer of nanostructured fluorocarbon porous film and a layer of encapsulation fluorocarbon polymer has a κ value of 1.8. The morphology investigation of the plasma co-deposited film prior and after acid-treatment by field emission scanning electron microscopy (FESEM) and atomic force microscopy (AFM) confirmed the form of the nanospheres and nanoporous structure, while the chemical composition and structure analysis by X-ray photoelectron spectroscopy (XPS) revealed that after the acid-treatment, the porous nanostructured film are composed predominantly of mainly fluorocarbon polymer. |
| |
Keywords: | Plasma Co-polymerization Hydrolysis Porous Dielectric |
本文献已被 ScienceDirect 等数据库收录! |
|