Effects of low temperature irradiation with heavy ions on superconductor niobium

To study the effects of heavy ion irradiation at low temperature on type II superconductor Nb, the transition temperatureT _c , the normal state residual resistivityρ _B , the transition widthΔT _ph using oxygen ions of 25 MeV and subsequent thermal annealing were measured. The samples were held at temperatures <20 K during irradiation in a cryostat for in situ measurements. The maximum oxygen fluence was about 2·10¹⁵ cm^?2 corresponding a relatively high defect concentration. The heavy ion irradiation experiments are described. The critical temperatureT _c decreases with increasing residual resistivityρ _B . In agreement with the theory and experiments, the gap anisotropy parameter is 〈a ²〉=0.008, subsequent annealing shows a hysteresis ofT _c versusρ _B . The resistivity saturation value Δρ_BS = 2.55 μΩ cm was obtained and different recovery stages were found. Significant broadening of transition width during irradiation was observed.T _c andΔT _ph anneal to 60% in the temperature interval of (60–90) K. Oxygen induced effects as a simulation method of high neutron damage are compared with irradiation measurements using neutrons and deuterons.