On the microwave absorption of superconducting Nb3Sn

Measurements ofdc-resistance, surface resistance at 9.6 GHz and x-ray diffraction were made on Nb₃Sn layers having thicknesses between 4 and 7 μ. Samples were prepared by condensing tin on niobium foil which was then annealed at high temperature. This process was repeated, in some cases as many as twenty times. The best samples showed steep transition curves close to 18.2 K. X-ray measurements indicated a high degree of stoechiometry. The surface resistance decreased from 5 · 10^?2Ω atT _c to a residual value of 3 · 10^?4 Ω. This relatively high value can be due to minor deviations from stoechiometry or possibly to similar mechanisms as proposed for pure elements.