New high temperature polymers. I. Wholly aromatic ordered copolyamides
Authors:J Preston
Abstract:Wholly aromatic ordered copolyamides of unusually high thermal stability were prepared by the condensation of aromatic diacid chlorides with symmetrical diamines containing preformed aromatic amide units in an ordered arrangement. The preservation of order in the condensation step was assured by using interfacial or solution polymerization techniques at temperatures below 50°C. Each polymer contains units derived from aminobenzoic acids, arylene diamines, and arylene diacids. By use of para- and meta- phenylene units, eight different polymers are possible; all were prepared. Differential thermal analyses and thermogravimetric analyses showed these polymers to have melting points or decomposition temperatures in a range from 410°C. for the all-meta polymer to 555°C. for the all-para one. Substitution of the internal N-hydrogens of the diamines with methyl groups or phenyl groups leads to additional ordered copolymers. Several were prepared, but their melting points were much lower than those of the parent polymers limiting their usefulness in high temperature applications. Tough pliable films were prepared from all eight unsubstituted polymers, and crystalline fibers with tenacities of ca. 6 g./den. were prepared from three of the polymers. The properties of the fibers were retained to a high degree even when determined at temperatures up to 400°C. Fibers aged at 300°C. for extended periods of time showed remarkable retention of fiber properties.
Keywords:
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号