Cyclopolymerization XXXIII. Radical polymerizations and copolymerizations of 1,6-dienes with 2-phenylallyl group and thermal properties of polymers derived therefrom

Radical polymerizations of α-allyloxymethylstyrene (1) and copolymerizations of α-(2-phenylallyloxy)methylstyrene (2) were undertaken to acquire comprehensive understanding on polymerization behavior of these dienes and to get polymers with high thermal stability and high glass transition temperature (T_g). One of the monofunctional counterparts of 1 is a derivative of α-methylstyrene, the ceiling temperature of which is low, and the other is an allyl compound that is well-known for the low homopolymerization tendency. This means that the intermolecular propagation reactions leading to pendant uncyclized units are suppressed during the polymerization of 1 to yield highly cyclized polymers. In fact, the degree of cyclization of poly(1) obtained at 140 °C attained the value 92%. Structural studies revealed that repeat cyclic units of poly(1) consist exclusively of five-membered rings. Poly(1) was found to be stable up to 300 °C, but its T_g values were detected at around 100 °C. They are considerably lower than the targeted values which should lie between 180 and 220 °C. An additional drawback of poly(1) is its low molecular weight probably due to a degradative chain transfer. For this reason, copolymerizations of 2 with 1 and with styrene were also carried out to seek for the possibility to control the thermal properties precisely. Monomer 2 was chosen, since it has been reported in our previous work that it yields polymers with thermal stability up to 300 °C and T_g higher than 250 °C. Copolymerization of 2 with styrene afforded polymers with desired thermal properties and high molecular weight.