Infrared absorption of some high-purity chalcogenide glasses

New compouning techniques were devised to prepare high-purity Ge₂₈Sb₁₂Se₆₀ (TI 1173)and Ge₃₃As₁₂Se₅₅ TI 20). The methods were based on the combination of the reactant purification and compounding steps. The goal of the program was to establish the absorption limit for the glasses and to lower the absorption at 10.6 μm. At the present purity level, the GeSbSe glass is found to have an absorption level of about 0.01 cm^?1 at 10.6 μm while the absorption level for the GeAsSe glass is 0.05 cm^?1. Underlying causes for the limits are discussed along with the possibilities for improvement.