High-temperature phases of montmorillonite synthetized from the oxides SiO2-Al2O3-MgO-CaO |
| |
| Authors: | V. Š. Fajnor H. Gerthofferová Ľ. Kuchta J. Masár |
| |
| Affiliation: | (1) Department of Inorganic Chemistry, Faculty of Natural Sciences, Comenius University, Mlynská dolina, 842 15 Bratislava;(2) Geological Institute, Faculty of Natural Sciences, Comenius University, Zadunajská 15, 851 01 Bratislava, Czechoslovakia |
| |
| Abstract: | The high-temperature (950–1500°) changes in synthetic montmorillonite of relatively simple chemical composition, studied by X-ray diffraction analysis, infrared spectroscopy and electron microscopy, are described. It was found that this montmorillonite belongs to the Wyoming type and the high-temperature phases involve cristobalite, mullite, anorthite and spinel. Only mullite crystallized from this sample on heating for two hours at 1500°.
Zusammenfassung Die durch Röntgendiffraktionsanalyse, Infrarotspektroskopie und Elektronenmikroskopie untersuchten Hochtemperatur (950–1500°) — Änderungen in synthetischem Montmorillonit verhältnismässig einfacher chemischer Zusammensetzung werden beschrieben. Es wurde gefunden, daß dieser Montmorillonit dem Typ Wyoming angehört und, daß die Hochtemperaturphasen Cristobalit, Mullit, Anorthit und Spinell enthalten. Aus dieser Probe kristalliesierte bei zweistündigem Erhitzen auf 1500°C nur Mullit.
                     ,           (950–1500°)  .  ,  ,  , ,  .  2 1500° .
|
| |
| Keywords: | |
| 本文献已被 SpringerLink 等数据库收录！ |
|