Optical Spectra of Polygermane/Mesoporous Silica Nanocomposites |
| |
Authors: | Nina Ostapenko Nata Kozlova Shozo Suto Masato Nanjo Kunio Mochida |
| |
Affiliation: | 1. Institute of Physics, pr. Nauki 46, Kiev 03028, Ukraine;2. Tohoku University, 980-8578 Sendai, Japan;3. Tottori University, 680-855 Japan;4. Gakushuin University, 171-8588 Tokyo, Japan |
| |
Abstract: | Summary: The monitoring of poly(di-n-hexylgermane) (PDHG) optical spectra in a variety of structures ranging from a bulk film to a nanosize polymer confined into a nanopore of SBA-15 was performed using the fluorescence and fluorescence excitation spectra in the temperature range from 5 to 240 K as well as the absorption and FTIR spectra at room temperature. The observed data were compared with those obtained for poly(di-n-hexylsilane). It was shown that PDHG film absorption and fluorescence spectra strongly depend on the polymer thickness and consist of a number of bands which were assigned to centers with different amount of trans- and gauche- conformers of the polymer chains. Conformations of the polymer chains found in a thin film and in a 10 nm pore are similar while differing from the conformations of a thick film. Optical spectra of the confined PDHG are blue-shifted relative to those of a thin film. The PDHG polymer chain conformation becomes disordered with the decrease of the polymer film thickness and the nanopore size from 10 to 6 nm. |
| |
Keywords: | nanocomposites optical spectra poly(di-n-hexylgermane) SBA-15 films |
|
|