Investigation of processing,thermal, and mechanical properties of a new composite matrix‐benzoxazine containing aldehyde group

A new benzoxazine aldehyde group containing monomer 3‐phenyl‐6‐formyl‐3, 4‐dihydro‐2H‐1, 3‐benzoxazine (Ald‐B) was synthesized via the Mannich reaction of formaldehyde, p‐hydroxybenzaldehyde, and aniline. The viscosities and curing behavior of the resins were studied. The results indicated that Ald‐B has an initial viscosity lower than 0.110 Pa s at 90°C and the maximum temperature of the exotherm was at 196°C. Dynamic mechanical analysis (DMA) of the copolymer of Ald‐B and methylenedianiline‐type bis‐benzoxazine (B‐BOZ) showed only one T_g of 251°C and high crosslink density in the matrix. The thermal stability of the copolymer was improved noticeably and the char yield at 800°C is 68.4%. The tensile strength and flexural strength of this resin cast are 72 and 137 MPa, respectively. Copyright © 2009 John Wiley & Sons, Ltd.