| Abstract: | A new monomer, 1,1′-bis(dimethylaminodimethylsilyl)ferrocene, was synthesized by two routes and polymerized with three aryl disilanols: dihydroxydiphenylsilane, 1,4-bis(hydroxydimethylsilyl)benzene, and 4,4′-bis(hydroxydimethylsilyl)biphenyl, yielding three different polysiloxanes. Melt polymerizations carried out at 1 torr pressure and 100°C resulted in the highest molecular weight polymers. Intramolecular cyclization competed with intermolecular chain extension in polymerization of the bis(aminosilane) with dihydroxydiphenylsilane, resulting in isolation of a bridged derivative, 1,3,5-trisila-2,4-dioxa-1,1,5,5-tetramethyl-3,3-diphenyl[5]ferrocenophane. Cyclization did not compete significantly during the formation of polymers from this bisaminosilane and the two remaining diols, as evidenced by higher yields and greater molecular weights. These polymers could be cast as tough flexible films, and fibers could be drawn from their melts. TGA and DSC data showed the polymer formed from 1,1′-bis(dimethylaminodimethylsilyl)ferrocene and 1,4-bis(hydroxydimethylsilyl)benzene to be at least as thermally stable as an arylene siloxane polymer which differed from the ferrocenylsiloxane structure only in the replacement of the ferrocene moiety with a p-substituted phenylene linkage. The ferrocene-containing polymers were generally hydrolytically stable under conditions of refluxing THF–H2O(10 : 1) for 1 hr. The polymer-forming reaction was found to follow second-order kinetics, and the specific rate constants for formation of two of the polymers were measured. |