Magnetic properties of Co-ferrite-doped hydroxyapatite nanoparticles having a core/shell structure

The magnetic properties of Co-ferrite-doped hydroxyapatite (HAP) nanoparticles of composition Ca_10−3xFe_2xCo_x(PO₄)₆(OH)₂ (where x=0, 0.1, 0.2, 0.3, 0.4 and 0.5% mole) are studied. Transmission electron microscope micrograms show that the 90 nm size nanoparticles annealed at 1250 °C have a core/shell structure. Their electron diffraction patterns show that the shell is composed of the hydroxyapatite and the core is composed of the Co-ferrite, CoFe₂O₄. Electron spin resonance measurements indicate that the Co²⁺ ions are being substituted into the Ca(1) sites in HAP lattice. X-ray diffraction studies show the formation of impurity phases as higher amounts of the Fe³⁺/Co²⁺ ions which are substituted into the HAP host matrix. The presence of two sextets (one for the A-site Fe³⁺ and the other for the B-site Fe³⁺) in the Mössbauer spectrum for all the doped samples clearly indicates that the CoFe₂O₄.cores are in the ferromagnetic state. Evidence of the impurity phases is seen in the appearance of doublet patterns in the Mössbauer spectrums for the heavier-doped (x=0.4 and 0.5) specimens. The decrease in the saturation magnetizations and other magnetic properties of the nanoparticles at the higher doping levels is consistent with some of the Fe³⁺ and Co²⁺ which being used to form the CoO and Fe₂O₃ impurity phase seen in the XRD patterns.